CN106497152A - 一种可提高分散性和黑度的色素炭黑的生产工艺 - Google Patents

一种可提高分散性和黑度的色素炭黑的生产工艺 Download PDF

Info

Publication number
CN106497152A
CN106497152A CN201610911169.1A CN201610911169A CN106497152A CN 106497152 A CN106497152 A CN 106497152A CN 201610911169 A CN201610911169 A CN 201610911169A CN 106497152 A CN106497152 A CN 106497152A
Authority
CN
China
Prior art keywords
carbon black
colour carbon
acetic acid
colour
blackness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610911169.1A
Other languages
English (en)
Inventor
孙鹏
王俊杰
侯利恒
张浩勇
蒋凯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Baicheng Zhongtan Technology Co Ltd
Original Assignee
Baicheng Zhongtan Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baicheng Zhongtan Technology Co Ltd filed Critical Baicheng Zhongtan Technology Co Ltd
Priority to CN201610911169.1A priority Critical patent/CN106497152A/zh
Publication of CN106497152A publication Critical patent/CN106497152A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种可提高分散性和黑度的色素炭黑的生产工艺，属于化工材料生产加工技术领域。本发明以普通色素炭黑为原料，经过添加剂预设、湿法造粒、干燥处理、产品收集检验的深度加工处理得到的色素炭黑产品，该工艺具有提高色素炭黑分散性和黑度的优点。

Description

一种可提高分散性和黑度的色素炭黑的生产工艺
技术领域
本发明涉及一种炭黑的生产工艺，特别是一种可提高分散性和黑度的色素炭黑的生产工艺，属于化工材料生产加工技术领域。
背景技术
炭黑(英文名：carbon black)，又名灯墨、碳黑，是一种无定形碳。轻、松而极细的黑色粉末，表面积非常大，范围从10～3000m2/g，是含碳物质(煤、天然气、重油、燃料油等)在空气不足的条件下经不完全燃烧或受热分解而得的产物。比重1.8-2.1。由天然气制成的称"气黑"，由油类制成的称"灯黑"，由乙炔制成的称"乙炔黑"。此外还有"槽黑"、"炉黑"。按炭黑性能区分有"补强炭黑"、"导电炭黑"、"耐磨炭黑"等。可作黑色染料，用于制造中国墨、油墨、油漆等，也用于做橡胶的补强剂。
色素炭黑是以黑度、色相、流动等性能特征，以及制造和改性的方法来命名的。目前国内主要采用油炉法生产色素炭黑，由于目前国内多采用橡胶用炭黑经过改变粒径和结构制备色素炭黑，产品多采用小粒径低结构的形式，产品因结构低，黑度差与同种进口产品相比存在很大差异，虽然在结构粒径上模仿进口产品但在实际应用中却得不到推广和认可。
为了解决发生在色素炭黑生产过程中的不足，提高色素炭黑的使用性能，有必要提供一种在提高分散性亲水性的同时提升色素炭黑的黑度的色素炭黑的加工生产工艺。
发明内容
本发明的目的在于提供一种可提高分散性和黑度的色素炭黑的生产工艺。
本发明阐述了一种可提高分散性和黑度的色素炭黑的生产工艺，其包括以下步骤：
步骤一：添加剂预设：将p-19阴离子聚丙烯酸钠盐分散剂加入分散剂储罐，经过流量计轴向喷入湿法造粒机前段与普通粉状炭黑混合；取乙酸和水，将乙酸和水按3.5-4:1000的比例进行配比，使PH值保持在在4.5-5.5的范围内，将其输入乙酸储罐内；
步骤二：湿法造粒：乙酸和水的混合液在静态混合器末端与造粒液体混合，径向喷入湿法造粒机中与粉状炭黑混合搅拌，在湿法造粒机中形成微小的含炭黑颗粒；
步骤三：干燥处理：将含色素炭黑的颗粒输入干燥机中进行干燥处理，干燥温度控制在110-125℃；；
步骤四：产品收集检验：干燥后的色素炭黑经过提升机进入产品储罐，并对色素炭黑的进行检测，合格后出厂。
本发明的积极效果在于：
1、本发明主要利用p-19阴离子聚丙烯酸钠盐和乙酸两种药品的特性，将其添加到色素炭黑中，使药品在炭黑表面发生化学反应(利用乙酸的羧基团)，从而改善色素炭黑的品质，提高了色素炭黑的分散性和黑度。
附图说明
图1为本发明的流程示意图。
具体实施方式
为能详细说明本发明，下面结合具体实施例对本发明做进一步详细的描述。
实施例1
一种可提高分散性和黑度的色素炭黑的生产工艺，其包括以下步骤：
步骤一：添加剂预设：将p-19阴离子聚丙烯酸钠盐分散剂加入分散剂储罐，经过流量计轴向喷入湿法造粒机前段与普通粉状炭黑混合；取乙酸和水，将乙酸和水按3.5-4:1000的比例进行配比，使PH值保持在在4.5-5.5的范围内，将其输入乙酸储罐内；
步骤二：湿法造粒：乙酸和水的混合液在静态混合器末端与造粒液体混合，径向喷入湿法造粒机中与粉状炭黑混合搅拌，在湿法造粒机中形成微小的含炭黑颗粒；
步骤三：干燥处理：将含色素炭黑的颗粒输入干燥机中进行干燥处理，干燥温度控制在110-125℃；；
步骤四：产品收集检验：干燥后的色素炭黑经过提升机进入产品储罐，并对色素炭黑的进行检测，合格后出厂。
试验一：
对本实施例1中的色素炭黑和普通色素炭黑进行对比试验，结果如下：
通过试验对比可以得出，在造粒工序添加化学药品(p-19阴离子聚丙烯酸钠盐、乙酸)，可显著提高炭黑的分散性和黑度。
以上对本发明的实施例进行了详细说明，但所述的内容仅为本发明的较佳实施例，不能仅以实施例限定本发明的保护范围。

Claims (1)

1.一种可提高分散性和黑度的色素炭黑的生产工艺，其特征在于：包括以下步骤：
步骤一：添加剂预设：将p-19阴离子聚丙烯酸钠盐分散剂加入分散剂储罐，经过流量计轴向喷入湿法造粒机前段与普通粉状炭黑混合；取乙酸和水，将乙酸和水按3.5-4:1000的比例进行配比，使PH值保持在在4.5-5.5的范围内，将其输入乙酸储罐内；
步骤二：湿法造粒：乙酸和水的混合液在静态混合器末端与造粒液体混合，径向喷入湿法造粒机中与粉状炭黑混合搅拌，在湿法造粒机中形成微小的含炭黑颗粒；
步骤三：干燥处理：将含色素炭黑的颗粒输入干燥机中进行干燥处理，干燥温度控制在110-125℃；；
步骤四：产品收集检验：干燥后的色素炭黑经过提升机进入产品储罐，并对色素炭黑的进行检测，合格后出厂。
CN201610911169.1A 2016-10-19 2016-10-19 一种可提高分散性和黑度的色素炭黑的生产工艺 Pending CN106497152A (zh)