CN106493351A - A kind of bathroom spray head stainless steel flexible hose and preparation method thereof - Google Patents
A kind of bathroom spray head stainless steel flexible hose and preparation method thereof Download PDFInfo
- Publication number
- CN106493351A CN106493351A CN201610983123.0A CN201610983123A CN106493351A CN 106493351 A CN106493351 A CN 106493351A CN 201610983123 A CN201610983123 A CN 201610983123A CN 106493351 A CN106493351 A CN 106493351A
- Authority
- CN
- China
- Prior art keywords
- parts
- stainless steel
- flexible hose
- steel flexible
- spray head
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of bathroom spray head stainless steel flexible hose and preparation method thereof.The stainless steel flexible hose includes the following raw material that counts by weight：32 42 parts of stainless steel SUS304,12 20 parts of ceramic powder, 58 parts of polyethylene, 14 parts of zinc chloride, 0.3 0.8 parts of preservative, 10 20 parts of carbon fiber, 29 parts of powder of straw, 12 28 parts of glycerine, 12 parts of levelling agent, 2 10 parts of iron chloride, 19 parts of ammonium chloride.First by zinc chloride, iron chloride and ammonium chloride Hybrid Heating, then grind after be immersed stainless steel SUS304, again with ceramic powder, polyethylene, preservative, carbon fiber, powder of straw and glycerine Hybrid Heating, finally viscosity is adjusted with levelling agent to 2,000 2500 Pa s proceed to die for molding, stainless steel flexible hose of lowering the temperature to obtain.Preparation method of the present invention is simple, and gained stainless steel flexible hose folding ability is strong, good heat preservation performance, and corrosion resistance is strong, and market prospects are good.
Description
Technical field
The invention belongs to stainless steel flexible hose field, and in particular to a kind of bathroom spray head stainless steel flexible hose and its preparation side
Method.
Background technology
With growth in the living standard, every household has all loaded onto shower facilities, and that bath is lived is rushed in shower into people
Part.During Long-Time Service, the stainless steel flexible hose connected between shower nozzle and valve switch is often distorted, and the time one is grown, no
Steel mesh rupture outside the rust soft net of steel, can leak during water flowing, it is impossible to normal use.In addition, existing stainless steel flexible hose thermal insulation
Very poor, if hand-held shower rushes bath, water temperature is overheated also to be ironed.Accordingly, it would be desirable to a kind of thermal insulation is good, stainless steel resistant to bending
Flexible pipe.
Content of the invention
For the deficiencies in the prior art, it is an object of the invention to provide a kind of bathroom spray head stainless steel flexible hose and its system
Preparation Method, the stainless steel flexible hose thermal insulation are good, folding, and preparation method is simple, low cost, with good market before
Scape.
For solving prior art problem, the technical scheme that the present invention takes is：
A kind of bathroom spray head stainless steel flexible hose, including the following raw material that counts by weight：Stainless steel SUS304 32-42 parts,
Ceramic powder 12-20 parts, polyethylene 5-8 parts, zinc chloride 1-4 parts, preservative 0.3-0.8 parts, carbon fiber 10-20 parts, powder of straw 2-9
Part, glycerine 12-28 parts, levelling agent 1-2 parts, iron chloride 2-10 parts, ammonium chloride 1-9 parts.
Used as preferably, above-mentioned bathroom spray head stainless steel flexible hose, including the following raw material that counts by weight：Stainless
40 parts of steel SUS304,15 parts of ceramic powder, 6 parts of polyethylene, 2 parts of zinc chloride, 0.3 part of preservative, 18 parts of carbon fiber, powder of straw 7
Part, 20 parts of glycerine, 1 part of levelling agent, 6 parts of iron chloride, 2 parts of ammonium chloride.
Used as preferably, the length of the carbon fiber is 6-8mm.
The preparation method of above-mentioned bathroom spray head stainless steel flexible hose, comprises the following steps：
Step 1, weighs raw material, by zinc chloride, iron chloride and ammonium chloride mix, be heated to while stirring 50-70 DEG C first mix
Compound；
Step 2, stainless steel SUS304 is immersed and is continued to be heated to 80-90 DEG C in the first mixture, and taken after being incubated 20-30 minutes
Go out, then the second mixture is ground to obtain with ball mill；
Step 3, the second mixture, ceramic powder, polyethylene, preservative, carbon fiber, powder of straw and glycerine is put in reactor and is added
Heat adjusts solution viscosity with levelling agent and proceeds to die for molding to 2000-2500 Pa s to 100-120 DEG C, and constant speed is down to
Room temperature obtains stainless steel flexible hose.
It is preferably as preparation method, in step 1, mixing speed is 340-400rpm.
It is preferably as preparation method, in step 2, the particle diameter of the second mixture is 300 mesh.
It is preferably as preparation method, in step 3, the speed of temperature-reduction at constant speed is 10 DEG C/min.
Beneficial effect
A kind of effective stainless steel of bathroom spray head stainless steel soft, zinc chloride, ammonium chloride and the iron chloride that the present invention is provided is main
Raw material, reduces the zinc-plated step of stainless steel flexible hose, improves the corrosion resistance of stainless steel flexible hose, in addition, it is high to add fiber content
Powder of straw and carbon fiber be raw material, substantially increase that folding ability is strong and effect of heat insulation.Preparation method of the present invention is simple,
And with low cost, therefore there are good market prospects.
Specific embodiment
Embodiment 1
A kind of bathroom spray head stainless steel flexible hose, including the following raw material that counts by weight：32 parts of stainless steel SUS304, pottery
12 parts of porcelain powder, 5 parts of polyethylene, 1 part of zinc chloride, 0.3 part of preservative, carbon fiber 10 part of the length for 6mm, 2 parts of powder of straw, glycerine
12 parts, 1 part of levelling agent, 2 parts of iron chloride, 1 part of ammonium chloride.
The preparation method of above-mentioned bathroom spray head stainless steel flexible hose, comprises the following steps：
Step 1, weighs raw material, and zinc chloride, iron chloride and ammonium chloride are mixed, 50 is heated to while stirring with the speed of 340rpm
DEG C the first mixture；
Step 2, stainless steel SUS304 is immersed and is continued to be heated to 80 DEG C in the first mixture, and taking-up is placed in after being incubated 20 minutes
Dry at 120 DEG C in baking oven, then 300 the second mixtures of purpose are ground to obtain with ball mill；
Step 3, the second mixture, ceramic powder, polyethylene, preservative, carbon fiber, powder of straw and glycerine is put in reactor and is added
Heat adjusts solution viscosity with levelling agent and proceeds to die for molding to 2000 Pa s to 100 DEG C, permanent with the speed of 10 DEG C/min
Prompt drop obtains stainless steel flexible hose to room temperature.
Embodiment 2
A kind of bathroom spray head stainless steel flexible hose, including the following raw material that counts by weight：Counted including following by weight
Raw material：40 parts of stainless steel SUS304,15 parts of ceramic powder, 6 parts of polyethylene, 2 parts of zinc chloride, 0.3 part of preservative, length is 6mm
18 parts of carbon fiber, 7 parts of powder of straw, 20 parts of glycerine, 1 part of levelling agent, 6 parts of iron chloride, 2 parts of ammonium chloride.
The preparation method of above-mentioned bathroom spray head stainless steel flexible hose, comprises the following steps：
Step 1, weighs raw material, and zinc chloride, iron chloride and ammonium chloride are mixed, it is heated to the speed of 380rpm while stirring
60 DEG C obtain the first mixture；
Step 2, stainless steel SUS304 is immersed and is continued to be heated to 85 DEG C in the first mixture, and taking-up is placed in after being incubated 25 minutes
Dry at 130 DEG C in baking oven, then 300 the second mixtures of mesh are ground to obtain with ball mill；
Step 3, the second mixture, ceramic powder, polyethylene, preservative, carbon fiber, powder of straw and glycerine is put in reactor and is added
Heat adjusts solution viscosity with levelling agent and proceeds to die for molding to 2200 Pa s to 110 DEG C, permanent with the speed of 10 DEG C/min
Prompt drop obtains stainless steel flexible hose to room temperature.
Embodiment 3
A kind of bathroom spray head stainless steel flexible hose, including the following raw material that counts by weight：Stainless steel SUS304 32-42 parts,
Ceramic powder 12-20 parts, polyethylene 5-8 parts, zinc chloride 1-4 parts, preservative 0.3-0.8 parts, length are 8mm carbon fiber 10-20 parts,
Powder of straw 2-9 part, glycerine 12-28 parts, levelling agent 1-2 parts, iron chloride 2-10 parts, ammonium chloride 1-9 parts.
The preparation method of above-mentioned bathroom spray head stainless steel flexible hose, comprises the following steps：
Step 1, weighs raw material, and zinc chloride, iron chloride and ammonium chloride are mixed, 70 is heated to while stirring with the speed of 400rpm
DEG C the first mixture；
Step 2, stainless steel SUS304 is immersed and is continued to be heated to 90 DEG C in the first mixture, and taking-up is placed in after being incubated 30 minutes
Dry at 120-140 DEG C in baking oven, then 300 the second mixtures of mesh are ground to obtain with ball mill；
Step 3, the second mixture, ceramic powder, polyethylene, preservative, carbon fiber, powder of straw and glycerine is put in reactor and is added
Heat adjusts solution viscosity with levelling agent and proceeds to die for molding to 2500 Pa s to 120 DEG C, permanent with the speed of 10 DEG C/min
Prompt drop obtains stainless steel flexible hose to room temperature.
Performance test
The bathroom spray head of the present invention is detected that with stainless steel flexible hose data are as shown in the table.Stainless steel flexible hose external skin temperatures
Measurement be that stainless steel flexible hose of the present invention and existing stainless steel flexible hose are passed through 100 DEG C of hot water, then survey outside stainless steel flexible hose
The temperature on surface.
As can be seen that the stainless steel flexible hose good combination property of the present invention, durable in use from upper table data, and preparation method is simple
Easy, with good market prospects.
The above, only presently preferred embodiments of the present invention not makees any pro forma restriction to the present invention；All
Those skilled in the art, it should be appreciated that the principle of the simply explanation invention described in above-described embodiment and specification, is not taking off
On the premise of the technology of the present invention spirit and scope, the present invention also have a little change, modification with develop equivalent variations, all according to
To the change of any equivalent variations made for any of the above embodiments, modification and develop etc. according to the substantial technological of the present invention, all should include
Within the scope of the present invention.
Claims (7)
1. a kind of bathroom spray head stainless steel flexible hose, it is characterised in that including the following raw material that counts by weight：Stainless steel
SUS304 32-42 parts, ceramic powder 12-20 parts, polyethylene 5-8 parts, zinc chloride 1-4 parts, preservative 0.3-0.8 parts, carbon fiber
10-20 parts, powder of straw 2-9 part, glycerine 12-28 parts, levelling agent 1-2 parts, iron chloride 2-10 parts, ammonium chloride 1-9 parts.
2. a kind of bathroom spray head stainless steel flexible hose according to claim 1, it is characterised in that including following by weight
The raw material of number meter：40 parts of stainless steel SUS304,15 parts of ceramic powder, 6 parts of polyethylene, 2 parts of zinc chloride, 0.3 part of preservative, carbon are fine
18 parts of dimension, 7 parts of powder of straw, 20 parts of glycerine, 1 part of levelling agent, 6 parts of iron chloride, 2 parts of ammonium chloride.
3. a kind of bathroom spray head stainless steel flexible hose according to claim 1, it is characterised in that the length of the carbon fiber
For 6-8mm.
4. the preparation method based on a kind of bathroom spray head stainless steel flexible hose described in claim 1, it is characterised in that include with
Lower step：
Step 1, weighs raw material, by zinc chloride, iron chloride and ammonium chloride mix, be heated to while stirring 50-70 DEG C first mix
Compound；
Step 2, stainless steel SUS304 is immersed and is continued to be heated to 80-90 DEG C in the first mixture, and taken after being incubated 20-30 minutes
Go out, then the second mixture is ground to obtain with ball mill；
Step 3, the second mixture, ceramic powder, polyethylene, preservative, carbon fiber, powder of straw and glycerine is put in reactor and is added
Heat adjusts solution viscosity with levelling agent and proceeds to die for molding to 2000-2500 Pa s to 100-120 DEG C, and constant speed is down to
Room temperature obtains stainless steel flexible hose.
5. a kind of preparation method of bathroom spray head stainless steel flexible hose according to claim 4, it is characterised in that step 1
Middle mixing speed is 340-400rpm.
6. a kind of preparation method of bathroom spray head stainless steel flexible hose according to claim 4, it is characterised in that step 2
In the second mixture particle diameter be 300 mesh.
7. a kind of preparation method of bathroom spray head stainless steel flexible hose according to claim 4, it is characterised in that step 3
The speed of middle temperature-reduction at constant speed is 10 DEG C/min.