CN106476364A - 汽车地毯防尘抗菌垫 - Google Patents
汽车地毯防尘抗菌垫 Download PDFInfo
- Publication number
- CN106476364A CN106476364A CN201610948921.XA CN201610948921A CN106476364A CN 106476364 A CN106476364 A CN 106476364A CN 201610948921 A CN201610948921 A CN 201610948921A CN 106476364 A CN106476364 A CN 106476364A
- Authority
- CN
- China
- Prior art keywords
- layer
- antibacterial
- dust
- foaming layer
- foaming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种汽车地毯防尘抗菌垫,包括:表面抗菌层、第一发泡层、中间抗菌层、第二发泡层和底部垫板层,第一发泡层和第二发泡层与中间抗菌层的上下两个表面直接贴合在一起,表面抗菌层通过粘结剂连接在第一发泡层的上表面,底部垫板层通过粘结剂连接在第二发泡层的下表面,第一发泡层和第二发泡层内部形成有充气管路,表面抗菌层上还分布有多个防滑突起。通过上述方式,本发明汽车地毯防尘抗菌垫减少灰尘的吸附,具有抗菌面广和高效杀菌等的优点,可以预防病菌传播,为乘客提供舒适整洁的汽车室内环境,还具有减震缓冲的效果,保障驾驶的安全性。
Description
技术领域
本发明涉及汽车内饰件技术领域,特别是涉及一种汽车地毯防尘抗菌垫。
背景技术
随着我国汽车工业的发展,人们对汽车的外观、舒适性、安全性和节能性等要求也不断提高,因此汽车内饰件的用量和质量也在不断提高。
汽车内饰件主要是指汽车内部改装所用到的汽车产品,涉及到汽车内部的方方面面,比如汽车防晒膜、汽车握手套、汽车地垫、汽车防滑垫和坐垫等等,均是汽车内饰用产品。
目前汽车室内垫容易吸附灰尘,导致病菌的吸附和传播,进而影响了汽车室内环境,同时现有的汽车室内垫缓冲能力不佳,会影响驾驶过程的安全性。
发明内容
本发明主要解决的技术问题是提供一种汽车地毯防尘抗菌垫,减少灰尘的吸附,具有抗菌面广和高效杀菌等的优点,可以预防病菌传播,为乘客提供舒适整洁的汽车室内环境,还具有减震缓冲的效果,保障驾驶的安全性。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种汽车地毯防尘抗菌垫,包括:表面抗菌层、第一发泡层、中间抗菌层、第二发泡层和底部垫板层,第一发泡层和第二发泡层与中间抗菌层的上下两个表面直接贴合在一起,表面抗菌层通过粘结剂连接在第一发泡层的上表面,底部垫板层通过粘结剂连接在第二发泡层的下表面,第一发泡层和第二发泡层内部形成有充气管路,表面抗菌层上还分布有多个防滑突起。
在本发明一个较佳实施例中,所述第一发泡层和第二发泡层为聚丙烯粒子微孔发泡层。
在本发明一个较佳实施例中,所述表面抗菌层为纳米银纤维与纺织纤维混纺制成。
在本发明一个较佳实施例中,所述中间抗菌层为纳米二氧化钛抗菌层。
在本发明一个较佳实施例中,所述粘结剂均匀分布在表面抗菌层的上表面和底部垫板层的上表面,粘结剂为复合纳米银抗菌粘结剂。
本发明的有益效果是:本发明汽车地毯防尘抗菌垫减少灰尘的吸附,具有抗菌面广和高效杀菌等的优点,可以预防病菌传播,为乘客提供舒适整洁的汽车室内环境,还具有减震缓冲的效果,保障驾驶的安全性。
附图说明
为了更清楚地说明本发明实施例中的技术方案,下面将对实施例描述中所需要使用的附图作简单地介绍,显而易见地,下面描述中的附图仅仅是本发明的一些实施例,对于本领域普通技术人员来讲,在不付出创造性劳动的前提下,还可以根据这些附图获得其它的附图,其中:
图1是本发明的汽车地毯防尘抗菌垫一较佳实施例的结构示意图;
附图中各部件的标记如下:100、表面抗菌层,200、第一发泡层,300、中间抗菌层,400、第二发泡层,500、底部垫板层,600、防滑突起,700、充气管路。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本发明的一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
请参阅图1,本发明实施例包括:
一种汽车地毯防尘抗菌垫,包括:表面抗菌层100、第一发泡层200、中间抗菌层300、第二发泡层400和底部垫板层500。
表面抗菌层100为纳米银纤维与纺织纤维混纺制成,可以吸附汽车室内的灰尘杂质,起到抗菌防尘的效果。
表面抗菌层100上还分布有多个防滑突起600,一方面起到了防滑效果,保障乘车安全性,另一方面还减少灰尘的吸附,为乘客提供舒适整洁的汽车室内环境。
中间抗菌层300为纳米二氧化钛抗菌层,无毒无味和无刺激性,具有抗菌面广和高效杀菌等的优点,可以预防病菌传播。
第一发泡层200和第二发泡层400为聚丙烯粒子微孔发泡层,具有高效的缓冲吸震效果,采用两层发泡层起到了双重缓冲吸震效果。
第一发泡层200和第二发泡层400与中间抗菌层的上下两个表面直接贴合在一起。
表面抗菌层100通过粘结剂连接在第一发泡层200的上表面,底部垫板层500通过粘结剂连接在第二发泡层400的下表面。
第一发泡层200和第二发泡层400内部形成有充气管路700,可以进一步起到缓冲吸震效果,当驾驶员在刹车时可以进一步进行减震缓冲,保证了驾驶员开车过程的安全性。
粘结剂均匀分布在表面抗菌层100的上表面和底部垫板层500的上表面,粘结剂为复合纳米银抗菌粘结剂,在进行粘合的同时还起到了抗菌杀菌效果。
本发明汽车地毯防尘抗菌垫的有益效果是:
减少灰尘的吸附,具有抗菌面广和高效杀菌等的优点,可以预防病菌传播,为乘客提供舒适整洁的汽车室内环境,还具有减震缓冲的效果,保障驾驶的安全性。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其它相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (5)
1.一种汽车地毯防尘抗菌垫,其特征在于,包括:表面抗菌层、第一发泡层、中间抗菌层、第二发泡层和底部垫板层,第一发泡层和第二发泡层与中间抗菌层的上下两个表面直接贴合在一起,表面抗菌层通过粘结剂连接在第一发泡层的上表面,底部垫板层通过粘结剂连接在第二发泡层的下表面,第一发泡层和第二发泡层内部形成有充气管路,表面抗菌层上还分布有多个防滑突起。
2.根据权利要求1所述的汽车地毯防尘抗菌垫,其特征在于,所述第一发泡层和第二发泡层为聚丙烯粒子微孔发泡层。
3.根据权利要求1所述的汽车地毯防尘抗菌垫,其特征在于,所述表面抗菌层为纳米银纤维与纺织纤维混纺制成。
4.根据权利要求1所述的汽车地毯防尘抗菌垫,其特征在于,所述中间抗菌层为纳米二氧化钛抗菌层。
5.根据权利要求1所述的汽车地毯防尘抗菌垫,其特征在于,所述粘结剂均匀分布在表面抗菌层的上表面和底部垫板层的上表面,粘结剂为复合纳米银抗菌粘结剂。