CN106367893A - Bio-degradable non-woven fabric material and preparation method thereof - Google Patents
Bio-degradable non-woven fabric material and preparation method thereof Download PDFInfo
- Publication number
- CN106367893A CN106367893A CN201610761312.3A CN201610761312A CN106367893A CN 106367893 A CN106367893 A CN 106367893A CN 201610761312 A CN201610761312 A CN 201610761312A CN 106367893 A CN106367893 A CN 106367893A
- Authority
- CN
- China
- Prior art keywords
- filtering layer
- fine filtering
- nonwoven cloth
- cloth material
- coarse filtration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of control of saline and alkaline land, and particularly relates to a bio-degradable non-woven fabric material and a preparation method thereof. The non-woven fabric material is provided with a rough filtering layer and a fine filtering layer, wherein the fine filtering layer consists of polypropylene resin, polyolefin resin, zinc stearate, an antioxidant and a degrading agent, and the rough filtering layer consists of animal fibers, plant fibers, stone meal and an adhesive. The non-woven fabric material prepared by the method is not only excellent in water draining effect and free from blocking a water drain hole, but also bio-degradable.
Description
Technical field
The invention belongs to Saline-alkali Field Control technical field is and in particular to a kind of biodegradable nonwoven cloth material and its system
Preparation Method.
Background technology
Saline-alkali soil is solonchak and the general name of alkaline earth and various salinization, alkali-affected soil.Solonchak refers to soluble organic fraction in soil
Content reaches to a certain degree, and the g and D of plant can be produced with the great soil group of substantially harm.Alkaline earth refers to contain greatly in soil
Amount commutativity ion, quantity reaches the degree that can endanger plant growing and develop, and makes the soil that soil property changes.
The salinization of soil of soil refers to due to a large amount of accumulation of salt basic ion in soil, the process that soil types gradually changes to saline-alkali soil, its
Influence factor includes natural cause and anthropic factor.Easily hardened phenomenon in salt affected soil under normal circumstances, leads to soil
Porosity diminishes, and the gas permeability of soil and water penetration are deteriorated, and badly influence the metabolism of Soil Microorganism, reduce the work of various enzymes
Property and the mineralization degree of carbon, nitrogen, the conversion of soil with organic matter is slack-off, eventually results in soil increasingly barren.Soil contains
The a large amount of salt ions having also can badly influence the normal physiological function of salt-soda soil plant, suppresses its g and D.In addition, with
The development of social economy and the continuous aggravation of mankind's activity, saline alkali land resource increasingly receives publicity, irrational irrigation is made
Degree also results in Pedotransfer function aggravation.Second Committee International Sustainable Development conference is just pointed out, following meeting seriously threatens the world
Agricultural sustainable development be soil salinization of soil, desertification and the big problem of soil erosion 3.
The technical measures that closed drainage technology is farmland stain, damage or crop failure caused by waterlogging is prevented and treated and Saline-alkali Field Control is important are wide at home and abroad
General use.In order to prevent grogs blocking hidden pipe, improve the lasting effectiveness of closed drainage efficiency and draining it will usually outside hidden pipe
Parcel nonwoven cloth material, existing nonwoven cloth material is easily corrupt, and easily causes the blocking of osculum, thus affecting drainage effect,
Moreover, also easily cause environmental pollution because not degradable.
Content of the invention
Invention broadly provides a kind of biodegradable nonwoven cloth material and preparation method thereof, the non-woven fabrics material of preparation
Material not only has excellent drainage effect, does not block osculum, and biodegradable.Its technical scheme is as follows: described nonwoven
Cloth material is provided with coarse filtration layer and fine filtering layer, fine filtering layer material by acrylic resin, vistanex, zinc stearate, antioxidant,
Degradation agent forms, and coarse filtration layer material is made up of animal fiber, Plant fiber, rubble powder, binding agent.
Preferably, fine filtering layer material is by weight by acrylic resin 20-40 part, vistanex 20-30 part, Hard Fat
Sour zinc 1-10 part, antioxidant 1-5 part, degradation agent 1-5 part composition;Coarse filtration layer material is by animal fiber 20-50 part, Plant fiber
20-30 part, rubble powder 1-5 part, binding agent composition 0.1-1 part composition.
Preferably, described antioxidant is thiodipropionate antioxidant, and described degradation agent is ferric stearate.
Preferably, described vistanex is grafted for maleic anhydride acrylic resin or the polyethylene of maleic anhydride grafting
Resin.
Preferably, Plant fiber be one of tencel fiber, Caulis Sacchari sinensis, corn stalk, straw, rice straw, bamboo pole, reed rod or
Several, animal fiber is ox hair and/or Pilus Caprae seu Oviss.
Preferably, described adhesive is pva glue.
Preferably, the thickness of coarse filtration layer is 0.1-1mm, and in coarse filtration layer, chemical fibre rugosity is 300-700 μm, coarse filtration layer hole
Footpath is 5-100 μm;The thickness of fine filtering layer is 0.01-0.1mm, and in fine filtering layer, chemical fibre rugosity is 10-100 μm, fine filtering layer hole
Footpath is 0.01-1 μm.
A kind of preparation method of biodegradable nonwoven cloth material, comprises the following steps:
A () weighs the material preparing fine filtering layer, to high-speed kneading machine, heating melting, and knead 25-30min;
B batch mixing is added melting extrusion molding in double screw extruder by (), be fine filtering layer;
C () is 1-100 μ by being ground into particle diameter in the animal fiber of preparation coarse filtration layer, Plant fiber, rubble powder to pulverizer
The powder of m, is subsequently adding binding agent and is stirred mixing;
D mixture prepared by step (c) is compiled into net through lapper by ();
E coarse filtration layer, fine filtering layer are stacked and are laminated on netted conveyer belt by () successively, send into hot air processing, use 150-170
DEG C Hot-blast Heating 2-4 minute, formed nonwoven cloth material.
Using above-mentioned biodegradable nonwoven cloth material and preparation method thereof, the invention has the advantages that
Nonwoven cloth material is prepared using the different double layer fibre layer of thickness, on the premise of ensureing to filter debris, water penetration
Good, and will not easily be torn to shreds in work progress, biodegradable, will not be to environment.
Specific embodiment
Embodiment 1
1. the biodegradable nonwoven cloth material in a kind of salt-soda soil, described nonwoven cloth material is provided with coarse filtration layer and fine filtering
Layer.
Fine filtering layer material is by weight by 30 parts of acrylic resin, 25 parts of vistanex, 5 parts of zinc stearate, thio
2 parts of dipropionate kind antioxidant, 2 parts of compositions of ferric stearate degradation agent;
Coarse filtration layer material is formed 1 part and is formed by 40 parts of animal fiber, 25 parts of Plant fiber, 3 parts of rubble powder, pva glue.
The acrylic resin that described vistanex is grafted for maleic anhydride.
Plant fiber be tencel fiber, Caulis Sacchari sinensis, corn stalk, straw, rice straw, bamboo pole, reed rod with the mixing of arbitrary proportion,
Animal fiber is ox hair.
2. the preparation method of above-mentioned biodegradable nonwoven cloth material is:
A () weighs the material preparing fine filtering layer, to high-speed kneading machine, heating melting, and knead 25-30min;
B batch mixing is added melting extrusion molding in double screw extruder by (), be fine filtering layer;
C () is 50 μm by being ground into particle diameter in the animal fiber of preparation coarse filtration layer, Plant fiber, rubble powder to pulverizer
Powder, is subsequently adding binding agent and is stirred mixing;
D mixture prepared by step (c) is compiled into net through lapper by ();
E coarse filtration layer, fine filtering layer are stacked and are laminated on netted conveyer belt by () successively, send into hot air processing, with 160 DEG C
Hot-blast Heating 3 minutes, forms nonwoven cloth material.
The thickness preparing its coarse filtration layer of nonwoven cloth material completing is 0.5mm, and in coarse filtration layer, chemical fibre rugosity is 500 μ
M, coarse filtration layer aperture is 50 μm.The thickness of fine filtering layer is 0.1mm, and in fine filtering layer, chemical fibre rugosity is 50 μm, fine filtering layer aperture
For 0.05 μm.
Embodiment 2
1. the biodegradable nonwoven cloth material in a kind of salt-soda soil, described nonwoven cloth material is provided with coarse filtration layer and fine filtering
Layer.
Fine filtering layer material is by weight by 20 parts of acrylic resin, 20 parts of vistanex, 10 parts of zinc stearate, thio
5 parts of dipropionate kind antioxidant, 1 part of composition of ferric stearate degradation agent;
Coarse filtration layer material is formed 0.5 part and is formed by 50 parts of animal fiber, 30 parts of Plant fiber, 1 part of rubble powder, pva glue.
The polyvinyl resin that described vistanex is grafted for maleic anhydride.
Plant fiber is tencel fiber, and animal fiber is Pilus Caprae seu Oviss.
2. the preparation method of above-mentioned biodegradable nonwoven cloth material is:
A () weighs the material preparing fine filtering layer, to high-speed kneading machine, heating melting, and knead 30min;
B batch mixing is added melting extrusion molding in double screw extruder by (), be fine filtering layer;
C () is 1 μm by being ground into particle diameter in the animal fiber of preparation coarse filtration layer, Plant fiber, rubble powder to pulverizer
Powder, is subsequently adding binding agent and is stirred mixing;
D mixture prepared by step (c) is compiled into net through lapper by ();
E coarse filtration layer, fine filtering layer are stacked and are laminated on netted conveyer belt by () successively, send into hot air processing, with 170 DEG C
Hot-blast Heating 2 minutes, forms nonwoven cloth material.
The thickness preparing its coarse filtration layer of nonwoven cloth material completing is 0.1mm, and in coarse filtration layer, chemical fibre rugosity is 700 μ
M, coarse filtration layer aperture is 100 μm.The thickness of fine filtering layer is 0.1mm, and in fine filtering layer, chemical fibre rugosity is 10 μm, fine filtering layer aperture
For 0.01 μm.
Embodiment 3
1. the biodegradable nonwoven cloth material in a kind of salt-soda soil, described nonwoven cloth material is provided with coarse filtration layer and fine filtering
Layer.
Fine filtering layer material is by weight by 40 parts of acrylic resin, 30 parts of vistanex, 1 part of zinc stearate, antioxygen
1 part of agent, 5 parts of compositions of degradation agent;
Coarse filtration layer material is formed 0.1 part and is formed by 20 parts of animal fiber, 20 parts of Plant fiber, 5 parts of rubble powder, pva glue.
Described antioxidant is thiodipropionate antioxidant, and described degradation agent is ferric stearate.
Acrylic resin that described vistanex is grafted for maleic anhydride and the polyvinyl resin of maleic anhydride grafting with
The mixing of arbitrary proportion.
Plant fiber is Caulis Sacchari sinensis, corn stalk, straw, rice straw, bamboo pole, the mixing of reed rod, and animal fiber is ox hair and sheep
The mixing of hair.
2. the preparation method of above-mentioned biodegradable nonwoven cloth material is:
A () weighs the material preparing fine filtering layer, to high-speed kneading machine, heating melting, and knead 30min;
B batch mixing is added melting extrusion molding in double screw extruder by (), be fine filtering layer;
C () is 100 μm by being ground into particle diameter in the animal fiber of preparation coarse filtration layer, Plant fiber, rubble powder to pulverizer
Powder, be subsequently adding binding agent be stirred mix;
D mixture prepared by step (c) is compiled into net through lapper by ();
E coarse filtration layer, fine filtering layer are stacked and are laminated on netted conveyer belt by () successively, send into hot air processing, with 170 DEG C
Hot-blast Heating 2 minutes, forms nonwoven cloth material.
The thickness preparing its coarse filtration layer of nonwoven cloth material completing is 1mm, and in coarse filtration layer, chemical fibre rugosity is 700 μm,
Coarse filtration layer aperture is 5 μm.The thickness of fine filtering layer is 0.01mm, and in fine filtering layer, chemical fibre rugosity is 50 μm, and fine filtering layer aperture is
0.01μm.
Performance test
The nonwoven cloth material that Example 1-3 preparation completes, measures its filter efficiency etc., test result is as shown in table 1 below:
Table 1 results of property
Classification | Embodiment 1 | Embodiment 2 | Embodiment 3 |
Filter efficiency (%) | 99.2 | 99.1 | 99.0 |
Highest heatproof (DEG C) | 200 | 187 | 150 |
Displacement (l/m2) | 0.77 | 0.74 | 0.70 |
Service life (year) | 3.5 | 4 | 3 |
It will be apparent to those skilled in the art that can technical scheme as described above and design, make other various
Corresponding change and deformation, and all these change and deformation all should belong to the protection domain of the claims in the present invention
Within.
Claims (8)
1. a kind of biodegradable nonwoven cloth material it is characterised in that: described nonwoven cloth material is provided with coarse filtration layer and fine filtering layer,
Fine filtering layer material is made up of acrylic resin, vistanex, zinc stearate, antioxidant, degradation agent, and coarse filtration layer material is by moving
Fibres, Plant fiber, rubble powder, binding agent composition.
2. biodegradable nonwoven cloth material according to claim 1 it is characterised in that: fine filtering layer material is by weight
Meter is by acrylic resin 20-40 part, vistanex 20-30 part, zinc stearate 1-10 part, antioxidant 1-5 part, degradation agent 1-
5 parts of compositions;Coarse filtration layer material is made up of animal fiber 20-50 part, Plant fiber's 20-30 part, rubble powder 1-5 part, binding agent
0.1-1 part forms.
3. biodegradable nonwoven cloth material according to claim 1 it is characterised in that: described antioxidant be thio
Dipropionate kind antioxidant, described degradation agent is ferric stearate.
4. biodegradable nonwoven cloth material according to claim 1 it is characterised in that: described vistanex be horse
Maleic anhydride grafted acrylic resin or the polyvinyl resin of maleic anhydride grafting.
5. biodegradable nonwoven cloth material according to claim 1 it is characterised in that: Plant fiber is that tencel is fine
One or more of dimension, Caulis Sacchari sinensis, corn stalk, straw, rice straw, bamboo pole, reed rod, animal fiber is ox hair and/or Pilus Caprae seu Oviss.
6. biodegradable nonwoven cloth material according to claim 1 it is characterised in that: described adhesive be pva glue.
7. biodegradable nonwoven cloth material according to claim 1 it is characterised in that: the thickness of coarse filtration layer be 0.1-
1mm, in coarse filtration layer, chemical fibre rugosity is 300-700 μm, and coarse filtration layer aperture is 5-100 μm;The thickness of fine filtering layer is 0.01-
0.1mm, in fine filtering layer, chemical fibre rugosity is 10-100 μm, and fine filtering layer aperture is 0.01-1 μm.
8. a kind of preparation method of biodegradable as claimed in claim 1 nonwoven cloth material it is characterised in that: include with
Lower step:
A () weighs the material preparing fine filtering layer, to high-speed kneading machine, heating melting, and knead 25-30min;
B batch mixing is added melting extrusion molding in double screw extruder by (), be fine filtering layer;
C () is 1-100 μm by being ground into particle diameter in the animal fiber of preparation coarse filtration layer, Plant fiber, rubble powder to pulverizer
Powder, is subsequently adding binding agent and is stirred mixing;
D mixture prepared by step (c) is compiled into net through lapper by ();
E coarse filtration layer, fine filtering layer are stacked and are laminated on netted conveyer belt by () successively, send into hot air processing, with 150-170 DEG C
Hot-blast Heating 2-4 minute, forms nonwoven cloth material.