CN106336580A - Impact-resistant and flame-retardant cable material - Google Patents
Impact-resistant and flame-retardant cable material Download PDFInfo
- Publication number
- CN106336580A CN106336580A CN201610747709.7A CN201610747709A CN106336580A CN 106336580 A CN106336580 A CN 106336580A CN 201610747709 A CN201610747709 A CN 201610747709A CN 106336580 A CN106336580 A CN 106336580A
- Authority
- CN
- China
- Prior art keywords
- parts
- maleic anhydride
- copolymer
- agent
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cable material in the field of electric wire and cable materials, and particularly relates to an impact-resistant and flame-retardant cable material. The impact-resistant and flame-retardant cable material is prepared from, by weight, 20 parts of ethylene and a copolymer thereof, 60 parts of a thermoplastic elastomer, 7 parts of polyethylene-propylene, 5 parts of a compatilizer, 3 parts of modified polyphenylene ether resin powder, 100 parts of a flame retardant, 2 parts of an auxiliary, 150 parts of ethylene-propylene-diene monomer rubber, 150 parts of SEBS503 and/or maleic anhydride-grafted SEBS, 150 parts of a plasticizing softener, 2 parts of pigments, 12 parts of a cross-linking agent, 70 parts of liquid-reinforced softened rubber and 180 parts of a reinforcing agent. A cable made of the cable material has the advantages of the excellent combustion supporting property, flexibility, impact resistance, environmental stress resistance and the like and cannot be cracked due to the fact that cracks are generated. Due to the fact that a filling agent is added, a cable sheath achieves the good thermal stability.
Description
Technical field
The present invention relates to the cable material in a kind of wire cable material field, particularly to a kind of resistance to impact flame-retardant cable material.
Background technology
With global economy fast development, people constantly strengthen to the understanding of electric wire aging initiation fire accident, right
The environment friendly of electric wire requires also more and more higher.Halogen burning produce poison gas to the harm of human body and environment be
Well-known.So, how to reduce the occurrence index being caused by electric wire and death rate during fire occurs?Low cigarette,
Halogen, fire-retardant, environmental protection, the developing direction becoming wires and cables industry such as high temperature resistant.Halogen-free flame-retardant wire cable, can be good at
Solve the problems, such as the contaminative to environment and injury is produced to the person, but be to meet Flame Retardancy and physical and mechanical properties
Balance, adds antimony oxide sometimes in halogen-free flame-retardant system, and antimony oxide, during production and processing and use, connects
After tactile human body skin, human body can be produced with certain harm (pruitus, redness), more seriously causing death, at present
Some terminal clients clearly prohibit the use of to the electric wire containing antimony oxide.
At present, existing CABLE MATERIALS adopts low density polyethylene (LDPE) (ldpe) and ethylene-vinyl acetate copolymer (eva) is base
Quasi- raw material adds fire retardant and auxiliary agent is plasticated and made.Product hardness between 90-93 degree a, move, bend by inconvenience in use.Resistance
Combustion type Plastic-sheathed Cable material adopts neoprene (cr) and haloflex (cpe), and flame-retardant system adopts antimony oxide, ten bromines two
Phenylate, chlorinated paraffin, phosphate, i.e. antimony-chloro- bromo- phosphorus flame-retardant system.Because in a large amount of halogens and rubber itself contain a large amount of chlorine from
Son, is burning and will necessarily produce a large amount of hydrogen halides during fire-retardant, forming strong the suffocating and to ring to life entity
The severe contamination in border.And, in the production process of existing domestic production technique, need to add the sulfuration of certain toxic side effect
Auxiliary agent (steam pipeline) sulfuration under high temperature, condition of high voltage, equipment is complicated, and capital intensive, in raw and auxiliary material and reaction by-product
There are a large amount of poisonous and harmful substances, production process high temperature, high pressure have serious hidden danger;Produce simultaneously and consume greatly, give up
Product rate is high, causes production cost to improve;And there is a large amount of " three wastes " discharge, form rugged environment pollution.It can be said that existing work
Skill belongs to the handicraft product of " high energy consumption, maximum discharge, high pollution ", does not meet current national product, industrial policy and development completely
Long-term interest.Therefore, halogen-free stibium-free high fire-retardance thermoplastic cable material is the development trend of current wires and cables industry.
Content of the invention
It is an object of the invention to the above-mentioned deficiency in the presence of overcoming prior art, provide a kind of resistance to impact flame retardant wire
Cable material.
In order to realize foregoing invention purpose, the invention provides technical scheme below: a kind of resistance to impact flame-retardant cable material,
It includes by weight:
(1), ethene and its 20 parts of copolymer, described ethene and its copolymer are ethylene-vinyl acetate copolymer, ethene-the third
Olefin(e) acid methacrylate copolymers or one or more mixture of ethylene-methyl acrylate copolymer;
(2), 60 parts of thermoplastic elastomer (TPE), described thermoplastic elastomer (TPE) be SIS,
SBS, hydrogenated styrene-butadiene-styrene block copolymers mix for one or more
Compound;
(3), 7 parts of polyethylene/propylene, described polyethylene/propylene is low density polyethylene (LDPE), LLDPE, high density
One or more of polyethylene, metallocene PE, polypropylene mixture;
(4), 5 parts of compatilizer, described compatilizer is maleic anhydride grafted ethene-acetate ethylene copolymer, maleic anhydride is grafted second
Alkene-octene copolymer, maleic anhydride grafted ethene-methyl acrylate copolymer, maleic anhydride grafted linear low density polyethylene,
One or more of maleic anhydride inoculated polypropylene mixture;
(5), 3 parts of modified polyphenylene ether resin powder, described modified polyphenylene ether resin powder is that inherent viscosity is surveyed at 30 DEG C in chloroform
It is set to the modified polyphenylene ether resin powder of 0.3-0.55dl/g;
(6), 100 parts of fire retardant, described fire retardant be hydroxide, organic hypophosphite fire retardant, in melamine compound
Compounding form for one or more;
(7), 2 parts of auxiliary agent, described auxiliary agent is zinc stearate, stearic acid, Tissuemat E, antioxidant, ultra-violet absorber, hydroxide
Magnesium, aluminium hydroxide, Firebrake ZB, lubricant, antioxidant, one or more mixture of crosslinking coagent taic;
(8), 150 parts of ethylene propylene diene rubber, in 4725p and 3722p that ethylene propylene diene rubber produces for du pont company
Plant or two kinds;
(9), sebs503 and/or maleic anhydride 150 parts of sebs of grafting;
(10), 150 parts of plasticising softening agent, described plasticising softening agent is selected from one of naphthenic oil, 26# white oil, 32# white oil or several
Kind;
(11), 2 parts of pigment, described pigment is selected from titanium dioxide, fluorescent whitening agent, pthalocyanine blue, phthalocyanine green, lithol rubine, lithol
That bright red, one or more of permanent yellow, benzidine yellow, carbon black;
(12), 12 parts of crosslinking agent, described crosslinking agent is selected from double (t-butylperoxyisopropyl) benzene and 2,5- dimethyl -2, and 5 is (double
Tert-butyl hydroperoxide) one of hexane or two kinds;
(13), liquid strengthens 70 parts of softened rubber, and it is liquid polyisobutene and liquid polybutadiene that described liquid strengthens softened rubber
One of alkene or two kinds;
(14), 180 parts of reinforcing agent, described reinforcing agent is selected from the maleic anhydride grafting poly- third of polypropylene, percent grafting 2wt%-9wt%
In alkene, acrylonitrile-butadiene-styrene copolymer, the maleic anhydride grafted polystyrene of percent grafting 9wt%-15wt% one
Plant or several;
(15), antioxidant 300 part, described antioxidant is thiobisphenol kind antioxidant.
Described wherein hydroxide is one of magnesium hydroxide, aluminium hydroxide or two kinds of mixtures;
Organic hypophosphite fire retardant is methyl hypo-aluminum orthophosphate, Methylethyl hypo-aluminum orthophosphate, phenyl hypo-aluminum orthophosphate, divinyl
One or more of aluminum phosphate, divinyl zinc hypophosphite fire retardant mixture;
Melamine compound is one of melamine cyanurate, melamine pyrophosphate, polyphosphoric acid melamine or many
Plant mixture.
Compared with prior art, beneficial effects of the present invention: the cable that the cable material of the present invention is produced has excellent
The features such as combustion-supporting property, pliability, resistance to impact, environmental stress resistance, be not in crackle so that ftractureing, simultaneously in order to overcome it easy
The shortcoming of combustion, with the addition of a series of auxiliary agent such as aluminium hydroxide, magnesium hydroxide.Improve the flame-retarding characteristic of cable sheath, be both not
Add the material of halide, make cable sheath Halogen.With the addition of filler, make cable sheath thermal stability good.
Specific embodiment
With reference to test example and specific embodiment, the present invention is described in further detail.But this should not be understood
Scope for the above-mentioned theme of the present invention is only limitted to below example, all belongs to this based on the technology that present invention is realized
The scope of invention.
Embodiment 1
A kind of resistance to impact flame-retardant cable material, it includes by weight:
(1), ethene and its 20 parts of copolymer, described ethene and its copolymer are ethylene-vinyl acetate copolymer, ethene-the third
Two kinds of mixtures of olefin(e) acid methacrylate copolymers, ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate copolymer are respectively 8 parts
With 12 parts;
(2), 60 parts of thermoplastic elastomer (TPE), described thermoplastic elastomer (TPE) be SIS,
SBS, three kinds of mixtures of hydrogenated styrene-butadiene-styrene block copolymers,
Described thermoplastic elastomer (TPE) is SIS, s-B-S block is common
Polymers, three kinds of mixtures of hydrogenated styrene-butadiene-styrene block copolymers are respectively 21 parts, 23 parts and 17 parts;
(3), 7 parts of polyethylene/propylene, described polyethylene/propylene is low density polyethylene (LDPE), LLDPE, high density
Polyethylene, four kinds of mixtures of metallocene PE, described polyethylene/propylene be low density polyethylene (LDPE), LLDPE,
High density polyethylene (HDPE), metallocene PE are respectively 1 part, 2 parts, 1 part, 3 parts;
(4), 5 parts of compatilizer, described compatilizer is maleic anhydride grafted ethene-acetate ethylene copolymer, maleic anhydride is grafted second
Two kinds of mixtures of alkene-octene copolymer, described maleic anhydride grafted ethene-acetate ethylene copolymer, maleic anhydride grafted ethene-
Two kinds of mixtures of octene copolymer are respectively 2 parts and 3 parts;
(5), 3 parts of modified polyphenylene ether resin powder, described modified polyphenylene ether resin powder is that inherent viscosity is surveyed at 30 DEG C in chloroform
It is set to the modified polyphenylene ether resin powder of 0.3-0.55dl/g;
(6), 100 parts of fire retardant, described fire retardant is hydroxide, two kinds of organic hypophosphite fire retardant is compounding forms, described
Hydroxide, organic hypophosphite fire retardant are respectively 42 parts and 58 parts;
(7), 2 parts of auxiliary agent, described auxiliary agent is magnesium hydroxide, two kinds of mixtures of aluminium hydroxide, respectively for 1 part;
(8), 150 parts of ethylene propylene diene rubber, the 4725p that ethylene propylene diene rubber produces for du pont company;
(9), sebs503 and/or maleic anhydride grafting sebs150 part;
(10), 150 parts of plasticising softening agent, described plasticising softening agent is selected from naphthenic oil;
(11), 2 parts of pigment, described pigment be selected from titanium dioxide, two kinds of fluorescent whitening agent, respectively 1 part;
(12), 12 parts of crosslinking agent, described crosslinking agent is selected from double (t-butylperoxyisopropyl) benzene;
(13), liquid strengthens 70 parts of softened rubber, and it is liquid polyisobutene that described liquid strengthens softened rubber;
(14), 180 parts of reinforcing agent, described reinforcing agent be selected from polypropylene, acrylonitrile-butadiene-styrene copolymer, two kinds, point
Wei 113 parts and 67 parts;
(15), antioxidant 300 part, described antioxidant is thiobisphenol kind antioxidant.
Described wherein hydroxide is magnesium hydroxide, two kinds of mixtures of aluminium hydroxide;
Organic hypophosphite fire retardant is methyl hypo-aluminum orthophosphate, Methylethyl hypo-aluminum orthophosphate, phenyl hypo-aluminum orthophosphate, divinyl
Three kinds of mixtures of aluminum phosphate;
Melamine compound is melamine cyanurate, two kinds of mixtures of melamine pyrophosphate.
Claims (2)
1. a kind of resistance to impact flame-retardant cable material it is characterised in that: it includes by weight:
(1), ethene and its 20 parts of copolymer, described ethene and its copolymer are ethylene-vinyl acetate copolymer, ethene-the third
Olefin(e) acid methacrylate copolymers or one or more mixture of ethylene-methyl acrylate copolymer;
(2), 60 parts of thermoplastic elastomer (TPE), described thermoplastic elastomer (TPE) be SIS,
SBS, hydrogenated styrene-butadiene-styrene block copolymers mix for one or more
Compound;
(3), 7 parts of polyethylene/propylene, described polyethylene/propylene is low density polyethylene (LDPE), LLDPE, high density
One or more of polyethylene, metallocene PE, polypropylene mixture;
(4), 5 parts of compatilizer, described compatilizer is maleic anhydride grafted ethene-acetate ethylene copolymer, maleic anhydride is grafted second
Alkene-octene copolymer, maleic anhydride grafted ethene-methyl acrylate copolymer, maleic anhydride grafted linear low density polyethylene,
One or more of maleic anhydride inoculated polypropylene mixture;
(5), 3 parts of modified polyphenylene ether resin powder, described modified polyphenylene ether resin powder is that inherent viscosity is surveyed at 30 DEG C in chloroform
It is set to the modified polyphenylene ether resin powder of 0.3-0.55dl/g;
(6), 100 parts of fire retardant, described fire retardant be hydroxide, organic hypophosphite fire retardant, in melamine compound
Compounding form for one or more;
(7), 2 parts of auxiliary agent, described auxiliary agent is magnesium hydroxide, aluminium hydroxide, Firebrake ZB, lubricant, antioxidant, crosslinking coagent taic
One or more mixture;
(8), 150 parts of ethylene propylene diene rubber, in 4725p and 3722p that ethylene propylene diene rubber produces for du pont company
Plant or two kinds;
(9), sebs503 and/or maleic anhydride 150 parts of sebs of grafting;
(10), 150 parts of plasticising softening agent, described plasticising softening agent is selected from one of naphthenic oil, 26# white oil, 32# white oil or several
Kind;
(11), 2 parts of pigment, described pigment is selected from titanium dioxide, fluorescent whitening agent, pthalocyanine blue, phthalocyanine green, lithol rubine, lithol
That bright red, one or more of permanent yellow, benzidine yellow, carbon black;
(12), 12 parts of crosslinking agent, described crosslinking agent is selected from double (t-butylperoxyisopropyl) benzene and 2,5- dimethyl -2, and 5 is (double
Tert-butyl hydroperoxide) one of hexane or two kinds;
(13), liquid strengthens 70 parts of softened rubber, and it is liquid polyisobutene and liquid polybutadiene that described liquid strengthens softened rubber
One of alkene or two kinds;
(14), 180 parts of reinforcing agent, described reinforcing agent is selected from the maleic anhydride grafting poly- third of polypropylene, percent grafting 2wt%-9wt%
In alkene, acrylonitrile-butadiene-styrene copolymer, the maleic anhydride grafted polystyrene of percent grafting 9wt%-15wt% one
Plant or several;Described auxiliary agent is selected from one of zinc stearate, stearic acid, Tissuemat E, antioxidant, ultra-violet absorber or several
Kind;
(15), antioxidant 300 part, described antioxidant is thiobisphenol kind antioxidant.
2. a kind of resistance to impact flame-retardant cable material according to claim 1 it is characterised in that:
Described wherein hydroxide is one of magnesium hydroxide, aluminium hydroxide or two kinds of mixtures;
Organic hypophosphite fire retardant is methyl hypo-aluminum orthophosphate, Methylethyl hypo-aluminum orthophosphate, phenyl hypo-aluminum orthophosphate, divinyl
One or more of aluminum phosphate, divinyl zinc hypophosphite fire retardant mixture;
Melamine compound is one of melamine cyanurate, melamine pyrophosphate, polyphosphoric acid melamine or many
Plant mixture.