CN106335113B - A kind of processing method of wicker for improving the yield of woven products - Google Patents
A kind of processing method of wicker for improving the yield of woven products Download PDFInfo
- Publication number
- CN106335113B CN106335113B CN201610733324.5A CN201610733324A CN106335113B CN 106335113 B CN106335113 B CN 106335113B CN 201610733324 A CN201610733324 A CN 201610733324A CN 106335113 B CN106335113 B CN 106335113B
- Authority
- CN
- China
- Prior art keywords
- parts
- wicker
- baking
- juice
- immersion treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of processing methods of wicker for promoting knitting yield rate, comprising the following steps: (1) removes blade, after wicker harvesting, wicker is used sodium acetate solution immersion treatment 0.5-1h, then uses potassium sulfate solution immersion treatment 1-1.5h；(2), wicker is wrapped up using mixed soil, then 1-2h is toasted at 50-52 DEG C, it keeps toasting everywhere in baking process uniformly, the wicker for being wrapped in mixed soil after baking is put into immersion treatment 12-30min in the treatment fluid that temperature is 28-35 DEG C rapidly after the completion of baking；(3), being dried to moisture content after cleaning the wicker that step (2) is handled well at 42-45 DEG C is 35-40%, is woven.Cracking rate by the braiding of the present invention treated wicker is low, and braiding yield rate reaches 97.2% or more, is able to ascend 10-20% relative to conventional method, economic benefit is obvious.
Description
Technical field
The invention belongs to woodwork process fields, and in particular to a kind of processing side for the wicker for promoting knitting yield rate
Method.
Background technique
In recent years, with people's increasingly attaching importance to environmental protection, wicker products become more and more popular, wicker products not only beautiful outline form
It sees, it can be used repeatedly, and environmental protection, will not generate pollution, can also be made with spontaneous corrosion as fertilizer or fuel after damage
With.
Wicker is a kind of common wicker plaiting article raw material, still, easily occurs cracking during wicker braiding or phenomenon of rupture,
It causes the service life of wicker products to shorten, also reduces the quality of wicker products, now in order to reduce cracking rate, promote braiding
The yield rate of product, often carrying out immersion treatment using softening agent will cause the corrosion of wicker although can be carried out softening, drop
Low service life.
Summary of the invention
The object of the present invention is to provide a kind of processing methods of wicker for promoting knitting yield rate, use special method
And inorganic agent is handled, and the woven performance of wicker is improved, and promotes the yield rate of braiding.
The invention is realized by the following technical scheme:
A kind of processing method for the wicker promoting knitting yield rate, comprising the following steps:
(1), blade is removed after wicker harvesting, the sodium acetate solution immersion treatment for the use of mass fraction being 1.2% by wicker
0.5-1h, the potassium sulfate solution immersion treatment 1-1.5h for the use of mass fraction being then 2 %；
(2), the wicker that step (1) is handled well is wrapped up using mixed soil, mixed soil is with a thickness of 1-1.5cm, then in 50-
1-2h is toasted at 52 DEG C, is kept toasting everywhere in baking process uniformly, will be wrapped in mixing after baking rapidly after the completion of baking
The wicker of mud is put into immersion treatment 12-30min in the treatment fluid that temperature is 28-35 DEG C；
The mixed soil is mixed by following raw material by weight: 35-40 parts of yellow glue mud, 0.2-0.5 parts of copper sulphate, wood
1.25-1.5 parts of matter cellulose, 8-12 parts of ginger juice, 2-5 parts of lemon juice, 4-6 parts of plant ash, 15-30 parts of water；
The treatment fluid is prepared from the following raw materials by weight: 2.5-3.2 parts of sodium citrate, 3-5 parts of glacial acetic acid, fatty alcohol
3.15-4.5 parts of polyoxyethylene ether, 35-50 parts of water；
(3), being dried to moisture content after cleaning the wicker that step (2) is handled well at 42-45 DEG C is 35-40%, is compiled
It knits.
Preferably, the wicker continues to use soak immersion treatment 0.5h, then dries after the processing of step (3)
It does to moisture content in 32-35%, the soak is made using following component by weight: 6-7 parts of urea, sodium acetate 2.1-2.5
Part, 0.5-1.2 parts of benzene sulfonic acid sodium salt, 22-25 parts of water.
Preferably, the mixed soil is mixed by following raw material by weight: 38 parts of yellow glue mud, 0.32 part of copper sulphate,
1.4 parts of lignocellulosic, 9 parts of ginger juice, 3.5 parts of lemon juice, 5 parts of plant ash, 22 parts of water.
Preferably, the treatment fluid is prepared from the following raw materials by weight: 2.8 parts of sodium citrate, 4.5 parts of glacial acetic acid, rouge
4.2 parts of fat alcohol polyoxyethylene ether, 40 parts of water.
Preferably, the ginger juice is the juice that fresh ginger squeezes, and the lemon juice is the juice that Fresh Lemon squeezes.
After the completion of braiding without sunlight irradiation under natural air drying.
Beneficial effects of the present invention: the processing method of wicker provided by the invention is just located using the wicker after freshly harvested
Reason, there is wicker good flexibility further enhance its flexibility after treatment at this time, using mixed soil and its
He is handled treatment fluid, and improves flexibility, and the crust and woody part that not will cause wicker are from improving crack resistence
Performance, the cracking rate by the braiding of the present invention treated wicker is low, and braiding yield rate reaches 97.2% or more, relative to normal
Rule method is able to ascend 10-20%, and economic benefit is obvious.
Specific embodiment
Embodiment 1
A kind of processing method for the wicker promoting knitting yield rate, comprising the following steps:
(1), blade is removed after wicker harvesting, the sodium acetate solution immersion treatment for the use of mass fraction being 1.2% by wicker
0.75h, the potassium sulfate solution immersion treatment 1.2h for the use of mass fraction being then 2%；
(2), the wicker that step (1) is handled well is wrapped up using mixed soil, mixed soil is with a thickness of 1.3cm, then at 51 DEG C
Lower baking 1.5h keeps in baking process toasting everywhere uniformly, rapidly by the mixed soil that is wrapped in after baking after the completion of baking
Wicker is put into immersion treatment 22min in the treatment fluid that temperature is 30 DEG C；
(3), being dried to moisture content after cleaning the wicker that step (2) is handled well at 44 DEG C is 38%, is woven；Institute
Wicker is stated after the processing of step (3), continues to use soak immersion treatment 0.5h, is then dried to moisture content 34%, institute
It states soak to be made using following component by weight: 6.5 parts of urea, 2.4 parts of sodium acetate, 1 part of benzene sulfonic acid sodium salt, 22 parts of water.
The mixed soil is mixed by following raw material by weight: 38 parts of yellow glue mud, 0.32 part of copper sulphate, wood fibre
Plain 1.4 parts, 9 parts of ginger juice, 3.5 parts of lemon juice, 5 parts of plant ash, 22 parts of water.
The treatment fluid is prepared from the following raw materials by weight: 2.8 parts of sodium citrate, 4.5 parts of glacial acetic acid, fatty alcohol polyoxy
4.2 parts of vinethene, 40 parts of water.
Embodiment 2
A kind of processing method for the wicker promoting knitting yield rate, comprising the following steps:
(1), blade is removed after wicker harvesting, the sodium acetate solution immersion treatment for the use of mass fraction being 1.2% by wicker
0.75h, the potassium sulfate solution immersion treatment 1.2h for the use of mass fraction being then 2%；
(2), the wicker that step (1) is handled well is wrapped up using mixed soil, mixed soil is with a thickness of 1.3cm, then at 51 DEG C
Lower baking 1.5h keeps in baking process toasting everywhere uniformly, rapidly by the mixed soil that is wrapped in after baking after the completion of baking
Wicker is put into immersion treatment 22min in the treatment fluid that temperature is 30 DEG C；
(3), being dried to moisture content after cleaning the wicker that step (2) is handled well at 44 DEG C is 38%, is woven.
The mixed soil is mixed by following raw material by weight: 38 parts of yellow glue mud, 0.32 part of copper sulphate, wood fibre
Plain 1.4 parts, 9 parts of ginger juice, 3.5 parts of lemon juice, 5 parts of plant ash, 22 parts of water.
The treatment fluid is prepared from the following raw materials by weight: 2.8 parts of sodium citrate, 4.5 parts of glacial acetic acid, fatty alcohol polyoxy
4.2 parts of vinethene, 40 parts of water.
Embodiment 3
A kind of processing method for the wicker promoting knitting yield rate, comprising the following steps:
(1), blade is removed after wicker harvesting, the sodium acetate solution immersion treatment for the use of mass fraction being 1.2% by wicker
0.6h, the potassium sulfate solution immersion treatment 1.2h for the use of mass fraction being then 2%；
(2), the wicker that step (1) is handled well is wrapped up using mixed soil, mixed soil is with a thickness of 1cm, then at 51 DEG C
1.2h is toasted, keeps toasting everywhere in baking process uniformly, rapidly by the willow for being wrapped in mixed soil after baking after the completion of baking
Item is put into immersion treatment 28min in the treatment fluid that temperature is 32 DEG C；
The mixed soil is mixed by following raw material by weight: 36 parts of yellow glue mud, 0.36 part of copper sulphate, wood fibre
Plain 1.3 parts, 10 parts of ginger juice, 3 parts of lemon juice, 5.2 parts of plant ash, 22 parts of water；
The treatment fluid is prepared from the following raw materials by weight: 2.8 parts of sodium citrate, 4.2 parts of glacial acetic acid, fatty alcohol polyoxy
4.25 parts of vinethene, 40 parts of water；
(3), being dried to moisture content after cleaning the wicker that step (2) is handled well at 44 DEG C is 36%, is woven.
Embodiment 4
A kind of processing method for the wicker promoting knitting yield rate, comprising the following steps:
(1), blade is removed after wicker harvesting, the sodium acetate solution immersion treatment for the use of mass fraction being 1.2% by wicker
0.8h, the potassium sulfate solution immersion treatment 1.2h for the use of mass fraction being then 2%；
(2), the wicker that step (1) is handled well is wrapped up using mixed soil, mixed soil is with a thickness of 1.5cm, then at 50 DEG C
Lower baking 1.6h keeps in baking process toasting everywhere uniformly, rapidly by the mixed soil that is wrapped in after baking after the completion of baking
Wicker is put into immersion treatment 25min in the treatment fluid that temperature is 32 DEG C；
The mixed soil is mixed by following raw material by weight: 36 parts of yellow glue mud, 0.34 part of copper sulphate, wood fibre
Plain 1.3 parts, 11 parts of ginger juice, 3.5 parts of lemon juice, 4.6 parts of plant ash, 25 parts of water；
The treatment fluid is prepared from the following raw materials by weight: 3 parts of sodium citrate, 3.6 parts of glacial acetic acid, fatty alcohol polyoxy second
3.8 parts of alkene ether, 40 parts of water；
(3), being dried to moisture content after cleaning the wicker that step (2) is handled well at 43 DEG C is 36%, is woven.
Comparative example 1
A kind of processing method for the wicker promoting knitting yield rate, comprising the following steps:
(1), blade is removed after wicker harvesting；
(2), the wicker that step (1) is handled well is wrapped up using mixed soil, mixed soil is with a thickness of 1.3cm, then at 51 DEG C
Lower baking 1.5h keeps in baking process toasting everywhere uniformly, rapidly by the mixed soil that is wrapped in after baking after the completion of baking
Wicker is put into immersion treatment 22min in the treatment fluid that temperature is 30 DEG C；
(3), being dried to moisture content after cleaning the wicker that step (2) is handled well at 44 DEG C is 38%, is woven.
The mixed soil is mixed by following raw material by weight: 38 parts of yellow glue mud, 0.32 part of copper sulphate, wood fibre
Plain 1.4 parts, 9 parts of ginger juice, 3.5 parts of lemon juice, 5 parts of plant ash, 22 parts of water.
The treatment fluid is prepared from the following raw materials by weight: 2.8 parts of sodium citrate, 4.5 parts of glacial acetic acid, fatty alcohol polyoxy
4.2 parts of vinethene, 40 parts of water.
Comparative example 2
A kind of processing method for the wicker promoting knitting yield rate, comprising the following steps:
(1), blade is removed after wicker harvesting, the sodium acetate solution immersion treatment for the use of mass fraction being 1.2% by wicker
0.75h, the potassium sulfate solution immersion treatment 1.2h for the use of mass fraction being then 2%；
(2), the wicker that step (1) is handled well is toasted at 51 DEG C 1.5h, kept toasting everywhere in baking process uniformly,
The wicker after baking is put into immersion treatment 22min in the treatment fluid that temperature is 30 DEG C rapidly after the completion of baking；
(3), being dried to moisture content after cleaning the wicker that step (2) is handled well at 44 DEG C is 38%, is woven.
The treatment fluid is prepared from the following raw materials by weight: 2.8 parts of sodium citrate, 4.5 parts of glacial acetic acid, fatty alcohol polyoxy
4.2 parts of vinethene, 40 parts of water.
Comparative example 3
A kind of processing method for the wicker promoting knitting yield rate, comprising the following steps:
(1), blade is removed after wicker harvesting, the sodium acetate solution immersion treatment for the use of mass fraction being 1.2% by wicker
0.75h, the potassium sulfate solution immersion treatment 1.2h for the use of mass fraction being then 2%；
(2), the wicker that step (1) is handled well is wrapped up using mixed soil, mixed soil is with a thickness of 1.3cm, then at 51 DEG C
Lower baking 1.5h keeps in baking process toasting everywhere uniformly；
(3), being dried to moisture content after cleaning the wicker that step (2) is handled well at 44 DEG C is 38%, is woven.
The mixed soil is mixed by following raw material by weight: 38 parts of yellow glue mud, 0.32 part of copper sulphate, wood fibre
Plain 1.4 parts, 9 parts of ginger juice, 3.5 parts of lemon juice, 5 parts of plant ash, 22 parts of water.
Using the wicker of the method for each embodiment and comparative example processing same batch, every kind of method handles 1000 wickers,
Wicker is complete before handling, and each group weaving manner is consistent, the yield rate of statistics each group braiding, the result is as follows:
Yield rate refer to braiding during certified products ratio, certified products be no cracking, nothing fracture, the complete finished product of shape；
Fracture rate refers to the ratio of wicker fracture during braiding.
Table 1 is the wicker cracking rate in the weaving process and yield rate of each group method processing:
| Processing mode | Fracture rate (%) | Yield rate (%) |
| Embodiment 1 | 0.3 | 98.7 |
| Embodiment 2 | 0.3 | 98.1 |
| Embodiment 3 | 0.6 | 97.7 |
| Comparative example 1 | 6.2 | 91.5 |
| Comparative example 2 | 5.4 | 91.3 |
| Comparative example 3 | 3.8 | 92.5 |
| Direct braiding is not handled | 8.7 | 90.4 |
As shown in Table 1, it is obviously improved using the yield rate of this method treated wicker establishment wicker products.
Claims (2)