CN106308229A - Antiviral mattress - Google Patents

Antiviral mattress Download PDF

Info

Publication number
CN106308229A
CN106308229A CN201610885736.0A CN201610885736A CN106308229A CN 106308229 A CN106308229 A CN 106308229A CN 201610885736 A CN201610885736 A CN 201610885736A CN 106308229 A CN106308229 A CN 106308229A
Authority
CN
China
Prior art keywords
antiviral
mattress
cloth
layer
hot melt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610885736.0A
Other languages
Chinese (zh)
Inventor
王宝林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Yu Wang Intelligent Technology Bed Co Ltd
Original Assignee
Qingdao Yu Wang Intelligent Technology Bed Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Yu Wang Intelligent Technology Bed Co Ltd filed Critical Qingdao Yu Wang Intelligent Technology Bed Co Ltd
Priority to CN201610885736.0A priority Critical patent/CN106308229A/en
Publication of CN106308229A publication Critical patent/CN106308229A/en
Pending legal-status Critical Current

Abstract

The invention relates to a manufacture technology of a functional Simmons mattress, and particularly relates to an antiviral mattress. The antiviral mattress comprises a piece of cloth in the upper layer, a liner layer in the middle and a piece of cloth in the lower layer, wherein both the cloth in the upper layer and the cloth in the lower layer are subjected to antiviral treatment, an antiviral liquid is sprayed to the cloth in the upper layer and the cloth in the lower layer by a nebulizer, then solidification is performed under ultraviolet ray, and finally drying is performed for 2-12 hours at 20-80 DEG C, and the spraying amount is 0.1-0.2g per square meter. According to the invention, a nano composite material is applied to the mattress, so that the mattress has the antiviral effect, and especially has a remarkable effect for the novel influenza virus H1N1, thus realizing the effects of being healthy and environmentally friendly, being capable of keeping the mattress clean and odorless for a long time, bringing innovative revolution for the industry of mattress, and filling up a domestic blank.

Description

A kind of antiviral mattress
Technical field
The present invention relates to the manufacturing technology of a kind of function mattress, specifically a kind of antiviral mattress.
Background technology
At present, all mattresses that family uses, from using beginning just empty by human body and outside in mattress inside and surface thereof The antibacterial of the band of gas, acarid, virus, abnormal flavour invade, and use central mattress to clean for many years, it is impossible to remove these antibacterials, demodicid mite Worm, virus, abnormal flavour, used for a long time more and more.Furthermore, virus is the big problem of mattress inevitable, is polluted by virus Mattress, healthy to user produces serious threat.
Summary of the invention
The technical assignment of the present invention is for the deficiencies in the prior art, it is provided that a kind of antiviral mattress.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of antiviral mattress, including upper strata cloth, middle bladder layer and the cloth of lower floor, described upper strata cloth and Lower layer mix feeding all does antiviral and processes, and is sprayed on upper strata cloth and lower layer mix feeding by atomizer by antiviral liquid, then Solidify under ultraviolet light, last 20-80 DEG C dry 2-12 hour, spraying quantity be every square of 0.1-0.2g.
As preferably, bladder layer of the present invention includes hot melt catalyst non-woven fabrics, bamboo carbon fibre hot melting wool, hot melt felt, bed Net, spring core, bed net, hot melt felt, bamboo carbon fibre hot melting wool.
As preferably, described antiviral liquid includes the mixed sols of nano titanium oxide and nanometer silver.Nanometer titanium dioxide Titanium and nano silver colloidal sol preparation process comprise: titanium tetrachloride is added in aqueous hydrochloric acid solution at 0~5 DEG C by (1);(2) to step (1) add ammonia spirit in, make whole solution form titanium hydroxide colloid, regulate the scope that its pH value is 7 to 12;(3) to hydrogen Adding hydrogen peroxide in titanium oxide colloid, form mixed solution, now the solid weight of titanium dioxide is 0.01% with the ratio of water To 2%, the mole ratio of hydrogen peroxide and titanium is between 2 to 1 to 5 to 1;(4) silver nitrate is added in B solution, now silver nitrate Ratio is the 0.01% to 10% of the solid weight of titanium dioxide;And B solution heats in the range of 60 to 100 DEG C, until glue Body complete hydrolysis disappears, and can form the TiO 2 sol of stable transparent, and the mole ratio of titanium dioxide/hydrogen peroxide is 1/2 Between 1/10.
As preferably, described nano titanium oxide and nanometer silver part by weight are 1-9: 0.01-1.
As preferably, the present invention also comprises the application at anti-virus aspect of the above-mentioned antiviral mattress.
As preferably, the present invention also comprises the application in anti-H1NI virus of the above-mentioned antiviral mattress.
The present invention is by nanocomposite applications to mattress so that mattress has the effect of antiviral, especially to newly Type influenza virus H1N1 has significant effect, it is achieved the effect of health environment-friendly, can the tasteless mattress of long-lasting cleanliness, to bed Pad industry brings innovation revolution, has filled up domestic blank.The present invention uses eleventh floor concrete structure, it is thus achieved that antiviral mattress, if Meter novelty, scientific and reasonable, using effect is good, has good promotional value, has huge market economy prospect.
Accompanying drawing explanation
Fig. 1 is section structure schematic diagram of the present invention.
Detailed description of the invention
In order to make the purpose of the present invention, technical scheme and advantage clearer, below in conjunction with specific embodiment to this Invention is further elaborated.
A kind of antiviral mattress, its structure as described in Figure 1, the most successively: ground floor cloth 1, second layer hot melt Catalyst non-woven fabrics 2, third layer bamboo carbon fibre hot melting wool 3, the 4th layer of hot melt felt 4, layer 5 bed net 5, layer 6 spring core 6, the Seven layers of bed net 7, the 8th layer of hot melt felt 8, the 9th layer of bamboo carbon fibre hot melting wool 9, the tenth layer of hot melt catalyst non-woven fabrics 10, eleventh floor Cloth 11.
Above-mentioned ground floor cloth 1 and eleventh floor cloth 11 are various cotton or cashmere cloth, and upper strata cloth and Lower layer mix feeding all does antiviral and processes, and is sprayed on upper strata cloth and lower layer mix feeding by atomizer by antiviral liquid, then Solidifying under ultraviolet light, last 60 DEG C are dried 3 hours, and spraying quantity is every square of 0.1-0.2g.Antiviral liquid includes nanometer Titanium dioxide and the mixed sols of nanometer silver.Nano titanium oxide and nano silver colloidal sol preparation process comprise: (1) is by titanium tetrachloride Add in aqueous hydrochloric acid solution at 0~5 DEG C;(2) in step (1), add ammonia spirit, make whole solution form titanium hydroxide Colloid, regulates the scope that its pH value is 7 to 12;(3) in titanium hydroxide colloid, add hydrogen peroxide, form mixed solution, now The solid weight of titanium dioxide and the ratio of water are 0.01% to 2%, and the mole ratio of hydrogen peroxide and titanium is between 2 to 1 to 5 to 1; (4) add silver nitrate in B solution, now the ratio of silver nitrate be titanium dioxide solid weight 0.01% to 10%;And B Solution heats in the range of 60 to 100 DEG C, until colloid complete hydrolysis disappears, the titanium dioxide that can form stable transparent is molten Glue, the mole ratio of titanium dioxide/hydrogen peroxide is between 1/2 to 1/10.
Catalyst in above-mentioned hot melt catalyst non-woven fabrics is the one that di(2-ethylhexyl)phosphate titanium oxide combination product works under low-light Low-light catalyst.Low-light catalyst liquid nano is di(2-ethylhexyl)phosphate titanium oxide combination product liquid nano.
The bamboo carbon fibre hot melting wool thickness of above-mentioned third layer and the 9th layer is 5mm-30mm, and bamboo carbon fibre hot melting wool is floss The soft thermal fusing surface of shape.
The manufacturing process of the above-mentioned described second layer and the tenth layer of hot melt catalyst non-woven fabrics is: by low-light catalyst liquid and heat Melten gel mix homogeneously, is then spread evenly across on non-woven fabrics, and described PUR refers to 120 DEG C of environment-friendlyadhesive adhesive melted.
Above-mentioned 4th layer and the hot melt felt thickness of the 8th layer are 20mm-50mm, and hot melt felt uses hard hot melt felt
The antiviral detection of above antiviral mattress is as follows:
Experiment material
The source of Strain
A influenza virus H1N1, coming from U.S.'s pathology can ability test Strain
Host cell
Mdck cell strain, preserves and research and development centre purchased from living resources.
Nano composite material is the colloidal sol of nano titanium oxide and nanometer silver, self-control.
Test method
(1) cell is cultivated
Cell strain knot is incubated in 24 hole culture dishs.With minimum essential medium (MEM)+8%fetal Bovine serum, 36 DEG C, 5%CO2Cultivate 48 hours full up to growing.Abandon culture fluid, with phosphate buffer Saline (PBS) rinse 2 times standby.
(2) virus preparation
By virus inoculation in the culture dish containing cell strain, with MEM+2ug/mg trypsin, 36 DEG C, 5%CO2Cultivate To 48 hours, cellulation pathological changes, strike off cell, centrifugal 6000rpm, 2 minutes, Aspirate supernatant was viral suspension, will 120ul viral suspension adds 1080ul MEM, carries out the dilution of continuous ten times.120ul diluent is added 1080ul MEM, Carry out the dilution of continuous ten times.As shown in table 1:
Table 1
Virus TDID50 test
Matched group
The cell strain of 24 hole culture dishs, the first hole, hurdle 4 is not inoculated as cell strain QC, and 2-6 hurdle A influenza virus connects respectively Plant 101Again, 102Again, 103Again, 104Again, 105The viral suspension 200ul of dilution again.
Experimental group
100ul viral suspension is added 400ulMEM, carries out the dilution of 5 times.50ul diluent is added 450ulMEM, Carry out the dilution of continuous 10 times.Preparing 1.25% disinfectant (75ul disinfectant+5952ulMEM), above-mentioned each diluent adds 450ul.It addition, one 1.25% disinfectant 450ul of preparation adds MEM450ul, without virus, it is the poison of nano composite material Property test.As shown in table 2 below:
Table 2
Above-mentioned room temperature shines UV mono-hour.
The cell strain of 24 hole culture dishs, the first hole, hurdle 4 inoculation nano composite material toxotest, remaining 5 hurdle is inoculated respectively 101Again, 102Again, 103Again, 104Again, 105The viral suspension of dilution is in 0.625% nano composite material effect afterproduct again 200ul。
Experimental group and matched group all with 36 DEG C, 5%CO2Infecting one hour, period, shake in every 20 minutes mixes once, MEM (+trypsin), 36 DEG C, 5%CO is added with every hole2Cultivate to 5 days, every day observation of cell pathological changes hole count.Add 4% Formaldehyde 1ml, room temperature stands one hour, rinses with tap water and adds 0.5%crystal violet 2 times 1ml.Room temperature stands 5 minutes.
Experimental result
Anti-A type influenza effect such as table 3 below
Table 3
Calculate and suppress virus usefulness:
Influenza virus suppression percentage ratio=[1-10?(-(5.1-3.2))] * 100=98.74.
As can be seen here, the colloidal sol of the nano composite material nano titanium oxide in this experiment and nanometer silver has anti-H1N1's Effect, its effect is notable.
Although above the preferred embodiment of the present invention being described, but the invention is not limited in above-mentioned concrete reality Executing mode, above-mentioned detailed description of the invention is only schematically, is not restrictive, and those of ordinary skill in the art exists Under the enlightenment of the present invention, in the case of without departing from present inventive concept and scope of the claimed protection, it is also possible to make a lot Form, within these belong to protection scope of the present invention.

Claims (6)

1. an antiviral mattress, it is characterised in that: include upper strata cloth, middle bladder layer and the cloth of lower floor, described Upper strata cloth and lower layer mix feeding all do antiviral and process, and by atomizer, antiviral liquid is sprayed on upper strata cloth and lower floor's cloth On material, solidify the most under ultraviolet light, last 20-80 DEG C dry 2-12 hour, spraying quantity be every square of 0.1-0.2g.
A kind of antiviral mattress the most according to claim 1, it is characterised in that: described bladder layer includes hot melt catalyst nonwoven Cloth, bamboo carbon fibre hot melting wool, hot melt felt, bed net, spring core, bed net, hot melt felt, bamboo carbon fibre hot melting wool.
A kind of antiviral mattress the most according to claim 1, it is characterised in that: described antiviral liquid includes nano-silica Change titanium and the mixed sols of nanometer silver.
A kind of antiviral mattress the most according to claim 3, it is characterised in that: described nano titanium oxide and nanometer silver weight Amount ratio is 1-9: 0.01-1.
5. comprise a kind of antiviral mattress as claimed in claim 1 application at anti-virus aspect.
6. comprise a kind of antiviral mattress as claimed in claim 1 application in anti-H1NI virus.
CN201610885736.0A 2016-10-11 2016-10-11 Antiviral mattress Pending CN106308229A (en)