CN1062886C - Porcelain-like paint - Google Patents
Porcelain-like paint Download PDFInfo
- Publication number
- CN1062886C CN1062886C CN97105882A CN97105882A CN1062886C CN 1062886 C CN1062886 C CN 1062886C CN 97105882 A CN97105882 A CN 97105882A CN 97105882 A CN97105882 A CN 97105882A CN 1062886 C CN1062886 C CN 1062886C
- Authority
- CN
- China
- Prior art keywords
- portions
- paint
- powder
- prescription
- weight part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a ceramic-like paint prepared from paint and liquid adhesive, wherein the paint comprises components according to the following weight percentage: 15 to 20 portions of calcium hydroxide, 25 to 30 portions of calcium carbonate and 3 to 5 portions of barite powder, and the liquid adhesive comprises components according to the following weight percentage: 5 to 8 portions of polyvinyl alcohol, 0.2 to 0.5 portion of sodium hexametaphosphate, 0.5 to 1.0 portion of glycol, 0.4 to 0.8 portion of dibutyl phthalate and 90 to 110 portions of water. The ceramic-like paint has the advantages of high hardness of a coated and decorated surface, strong water resistance, smooth and fine handle of the coated surface, whiteness and brightness as that of porcelain tiles, no toxicity or odor, ventilation, moisture prevention, no shedding, no powder shedding, no peeling or cracking, no mildew deterioration with black spots, scientific formula and easy application.
Description
The invention belongs to a kind of building coating, particularly a kind of porcelain-imitated coating.
On construction market, mostly adopt at present and scrape the Da Bai finishing, back metope surface peeling, shedding, peeling be full of cracks, moldy metamorphism go out a series of product quality problems such as blackspot but ubiquity makes moist, trace it to its cause is that chalk powder and Mierocrystalline cellulose cause, because of chalk powder is that the expander raw material is met the continuation expansion of moist back, the industrial chemicals of cellulose-based easy mildew bacterium, thereby the back moldy metamorphism that makes moist goes out blackspot.
The purpose of this invention is to provide a kind of porcelain-imitated coating, cover with paint, lacquer, colour wash, etc. the surface hardness height, water resistance is strong, the smooth feel exquisiteness of the face that is coated with, the similar ceramic tile of pure white light, nonpoisonous and tasteless ventilative protection against the tide does not come off, the be full of cracks of shedding, peeling, moldy metamorphism does not go out blackspot, and scientific formulation is easy to construction.
The objective of the invention is to be achieved through the following technical solutions: it is made up of powder and glue, it is characterized in that:
The prescription of powder and weight part ratio are for example following:
Calcium hydroxide 15-20
Lime carbonate 25-30
Ground barium sulfate 3-5
The prescription of glue and weight part ratio are for example following:
Polyvinyl alcohol 5-8
Sodium hexametaphosphate 99 0.2-0.5
Ethylene glycol 0.5-1.0
Dibutyl phthalate 0.4-0.8
Water 90-110
Can add pigment in the above-mentioned powder formulation, its weight part is 0.1-0.8;
Can add whitening agent in the above-mentioned glue formula, its weight part is 0.1 5-0.2.
Technological process is as follows:
1, glue making processes: earlier quantitative water is added in the reactor, heat temperature raising to 28-35 degree starts stirrer and slowly adds quantitative polyvinyl alcohol; When temperature rises to 90-100 ℃, stop to heat up, proceed insulated and stirred; Treat that polyvinyl alcohol all stops heating after the dissolving, drop into quantitative whitening agent, stirred 10-15 minute; Add the quantitative properties-correcting agent of forming by Sodium hexametaphosphate 99, ethylene glycol, dibutyl phthalate, continue then to stir and filtered in 10-15 minute; With the glue after filtering be released to deposit in the cooling pool stand-by.
2, the making processes of coating: the glue that will be cooled to below 40 ℃ adds in the agitator by the prescription quantitative requirement, adds pigment and stirs 10-15 minute, and whitewash does not then add pigment; Adding quantitative calcium hydroxide by ratio requirement stirs; Add quantitative lime carbonate, ground barium sulfate by ratio requirement, continue to stir, treat that material is even, color and luster is consistent.
The present invention has following advantage: adopt Paris white to replace traditional chalk powder as additive, because this physique starting material coefficient of expansion is very little, meet moist back and form solid as cement, its hardness is tens times of traditional coating, after this physique raw material softens processing through scientific formula, whiteness is greater than 92%, therefore have cover with paint, lacquer, colour wash, etc. the surface hardness height, water resistance is strong, the face that is coated with is smooth, feel is fine and smooth, the similar ceramic tile of pure white light, nonpoisonous and tasteless, ventilative moistureproof advantage, has antistatic, fire resistance, be easy to constructing operation, wiper is effective.
Below provide specific embodiment.
Embodiment 1
The prescription and the weight part of powder are as follows:
Calcium hydroxide 18
Lime carbonate 30
Ground barium sulfate 3
Pigment 0.3
The prescription of glue and weight part ratio are for example down;
Polyvinyl alcohol 5
Sodium hexametaphosphate 99 0.25
Ethylene glycol 0.5
Dibutyl phthalate 0.5
Ultramarine 0.2
Water 100
1, makes glue; With heating to 30 degree in the quantitative pure water adding reactor, start stirrer and slowly add quantitative polyvinyl alcohol; When being raised to 95 ℃, temperature carried out insulated and stirred 30 minutes; Treat that polyvinyl alcohol all stops heating after the dissolving, drop into quantitative whitening agent ultramarine (with 0.5 kilogram of cold water ultramarine being converted into solution stirring and filtration in advance), stirred 10 minutes, add the properties-correcting agent of quantitatively forming then and continue to stir and filtered in 15 minutes by Sodium hexametaphosphate 99, ethylene glycol, dibutyl phthalate, with the glue after the filtration be released to deposit in the cooling pool stand-by.
2, make coating: will be cooled to glue below 40 ℃ and put into a mixing bowl by the prescription quantitative requirement and add pigment, stirred 10 minutes, and added quantitative calcium hydroxide, lime carbonate and ground barium sulfate then on request, continue to stir 15 minutes, make material even at last, the color and luster unanimity.
Embodiment 2
The prescription of powder and weight part ratio are for example following:
Calcium hydroxide 20
Lime carbonate 25
Ground barium sulfate 5
Pigment 0.5
The prescription of glue and weight part ratio are for example following:
Polyvinyl alcohol 8
Sodium hexametaphosphate 99 0.5
Ethylene glycol 1.0
Dibutyl phthalate 0.8
Ultramarine 0.16
Water 110
Production process is with embodiment 1.
Embodiment 3
The prescription of powder and weight part ratio are for example following:
Calcium hydroxide 15
Lime carbonate 28
Ground barium sulfate 4
The prescription of glue and weight part ratio are for example following:
Polyvinyl alcohol 7
Sodium hexametaphosphate 99 0.23
Ethylene glycol 0.8
Dibutyl phthalate 0.6
Ultramarine 0.18
Water 90
Production process is with embodiment 1.
Claims (3)
1, porcelain-imitated coating, it is made up of powder and glue, it is characterized in that:
The prescription of powder and weight part ratio are for example following:
Calcium hydroxide 15-20
Lime carbonate 25-30
Ground barium sulfate 3-5
The prescription of glue and weight part ratio are for example following:
Polyvinyl alcohol 5-8
Sodium hexametaphosphate 99 0.2-0.5
Ethylene glycol 0.5-1.0
Dibutyl phthalate 0.4-0.8
Water 90-110.
2, porcelain-imitated coating according to claim 1 is characterized in that: can add pigment in the prescription of powder, its weight part is 0.1-0.8.
3, porcelain-imitated coating according to claim 1 is characterized in that: can add whitening agent in the prescription of glue, its weight part is 0.15-0.2.