CN106283138A - 镍钼合金电刷镀液及其电刷镀工艺 - Google Patents
镍钼合金电刷镀液及其电刷镀工艺 Download PDFInfo
- Publication number
- CN106283138A CN106283138A CN201610803725.3A CN201610803725A CN106283138A CN 106283138 A CN106283138 A CN 106283138A CN 201610803725 A CN201610803725 A CN 201610803725A CN 106283138 A CN106283138 A CN 106283138A
- Authority
- CN
- China
- Prior art keywords
- nickel
- brush plating
- molybdenum alloy
- alloy electric
- electric brush
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种镀层光亮致密、硬度高、耐磨性好、耐腐蚀性强的镍钼合金电刷镀液及工艺。镍钼合金电刷镀液主要由硫酸镍、钼酸钠、冰醋酸、柠檬酸、柠檬酸钠、硫酸钠和十二烷基硫酸钠配制而成。本发明镀液稳定可靠,电刷镀工艺简单,所获镀层光亮致密,硬度高,耐磨、耐腐蚀性好。
Description
技术领域
本发明属于电刷镀技术领域,具体涉及镍钼合金电刷镀液及其电刷镀工艺。
背景技术
在金属零件表面电刷镀铁、镍、铬等金属,能够延长零件的使用寿命,可用于零件的修复和表面强化。电刷镀镍钨、镍钴等合金镀层比电刷镀镍等单一金属镀层,性能更优越,应用更广泛。镍钼合金具有较高的强度以及优良的耐磨和耐腐蚀性,是极好的代镀铬材料,研究镍钼合金电刷镀液及其电刷镀工艺,使其应用于零部件再制造(修复),具有商业价值。
发明内容
本发明所要解决的技术问题在于提供一种镀层光亮致密、硬度高、耐磨性好、耐腐蚀性强的镍钼合金电刷镀液及其电刷镀工艺。
为解决上述技术问题,本发明所采用的技术方案为:
一种镍钼合金电刷镀液,由主盐、配合剂、缓冲剂、导电盐和添加剂组成。
前面所述的镍钼合金电刷镀液,优选的在于,所述主盐为:硫酸镍、钼酸钠。
前面所述的镍钼合金电刷镀液,优选的在于,所述配合剂为:柠檬酸、柠檬酸钠。
前面所述的镍钼合金电刷镀液,优选的在于,所述缓冲剂为:冰醋酸。
前面所述的镍钼合金电刷镀液,优选的在于,所述导电盐为:硫酸钠。
前面所述的镍钼合金电刷镀液,优选的在于,所述添加剂为:十二烷基硫酸钠。
前面所述的镍钼合金电刷镀液,优选的在于,组分及含量为:
NiSO4·6H2O 420~430g/L
Na2MoO4·2H2O 25~28g/L
CH3COOH 18~22mL/L
C6H8O7 35~38g/L
C6H5Na3O7·2H2O35~38g/L
Na2SO4·10H2O 18~22g/L
C12H25SO4Na 0.08~0.12g/L。
前面所述的镍钼合金电刷镀液,优选的在于,pH为:2~3。
本发明还提供了利用所述的镍钼合金电刷镀液的电刷镀工艺,参数控制为:工作电压12~16V,电极相对速度8~20m/min。
本发明所提供的镍钼合金电刷镀工艺,制备的镀层具有出光快、整平性好及硬度高、耐磨性好、耐腐蚀性强的优势。
本发明公开了一种镀层光亮致密、硬度高、耐磨性好、耐腐蚀性强的镍钼合金电刷镀液及工艺。镍钼合金电刷镀液主要由硫酸镍、钼酸钠、冰醋酸、柠檬酸、柠檬酸钠、硫酸钠和十二烷基硫酸钠配制而成。钢零件表面电刷镀镍钼合金工艺流程为:电净→水冲→2号活化液活化→水冲→3号活化液活化→水冲→刷镀特殊镍→刷镀镍钼合金。本发明镀液稳定可靠,电刷镀工艺简单,所获镀层光亮致密,硬度高,耐磨、耐腐蚀性好。
具体实施方式
下面结合实施例对本发明作进一步描述,但保护范围不被此限制。
实施例1 一种镍钼合金电刷镀液,组分及含量为:硫酸镍435g,钼酸钠25g,冰醋酸20mL,柠檬酸35g,柠檬酸钠35g,硫酸钠20g,十二烷基硫酸钠0.1g。配制方法为:第一步,将钼酸钠、柠檬酸置于容器中,加蒸馏水加热搅拌使其溶解;第二步,将硫酸镍、冰醋酸、柠檬酸钠、硫酸钠置于另一容器中,加蒸馏水加热搅拌使其溶解;第三步,将第一步的溶液倒入第二步的溶液中,同时加入十二烷基硫酸钠并搅拌至全部溶解;第四步,溶液放置室温后,用蒸馏水稀释到1L。
利用本发明对45号钢轴的外表面进行电刷镀。钢零件表面电刷镀镍钼合金工艺流程:电净→水冲→2号活化液活化→水冲→3号活化液活化→水冲→刷镀特殊镍→刷镀镍钼合金。电刷镀镍钼合金工艺参数:工作电压14V,电极相对速度11m/min。
测试结论:镀层质量稳定、结晶致密、光洁度髙,镀层与基体的附着力强,镀层硬度高,耐磨性好,耐腐蚀性强。
实施例2 一种镍钼合金电刷镀液,组分及含量为:
NiSO4·6H2O 420g/L
Na2MoO4·2H2O 25g/L
CH3COOH 18mL/L
C6H8O7 35g/L
C6H5Na3O7·2H2O35g/L
Na2SO4·10H2O 18g/L
C12H25SO4Na 0.08g/L
实施例3 一种镍钼合金电刷镀液,组分及含量为:
NiSO4·6H2O 430g/L
Na2MoO4·2H2O 28g/L
CH3COOH 22mL/L
C6H8O7 38g/L
C6H5Na3O7·2H2O38g/L
Na2SO4·10H2O 22g/L
C12H25SO4Na 0.12g/L
实施例2和实施例3的镍钼合金的电刷镀液配制方法、电刷镀工艺流程、电刷镀工艺参数、测试结论等与实施例1相似。
以上各实施例只是对本发明做进一步说明,并非用以限制本发明专利,凡为本发明的等效实施,均应包含于本发明专利的权利要求范围之内。
Claims (9)
1.一种镍钼合金电刷镀液,其特征在于,由主盐、配合剂、缓冲剂、导电盐和添加剂组成。
2.根据权利要求1所述的镍钼合金电刷镀液,其特征在于,所述主盐为:硫酸镍、钼酸钠。
3.根据权利要求1所述的镍钼合金电刷镀液,其特征在于,所述配合剂为:柠檬酸、柠檬酸钠。
4.根据权利要求1所述的镍钼合金电刷镀液,其特征在于,所述缓冲剂为:冰醋酸。
5.根据权利要求1所述的镍钼合金电刷镀液,其特征在于,所述导电盐为:硫酸钠。
6.根据权利要求1所述的镍钼合金电刷镀液,其特征在于,所述添加剂为:十二烷基硫酸钠。
7.一种镍钼合金电刷镀液,其特征在于:组分及含量为:
NiSO4·6H2O 420~430g/L
Na2MoO4·2H2O 25~28g/L
CH3COOH 18~22mL/L
C6H8O7 35~38g/L
C6H5Na3O7·2H2O 35~38g/L
Na2SO4·10H2O 18~22g/L
C12H25SO4Na 0.08~0.12g/L。
8.根据权利要求1-7所述的镍钼合金电刷镀液,其特征在于, pH为:2~3。
9.根据权利要求1-7所述的镍钼合金电刷镀液的电刷镀工艺,其特征在于,参数控制为:工作电压12~16V,电极相对速度8~20m/min。