CN106238638A - 一种铬镍钼合金钢锻造的工艺方法 - Google Patents
一种铬镍钼合金钢锻造的工艺方法 Download PDFInfo
- Publication number
- CN106238638A CN106238638A CN201610603531.9A CN201610603531A CN106238638A CN 106238638 A CN106238638 A CN 106238638A CN 201610603531 A CN201610603531 A CN 201610603531A CN 106238638 A CN106238638 A CN 106238638A
- Authority
- CN
- China
- Prior art keywords
- chromium
- alloy steel
- forging
- heated
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种铬镍钼合金钢锻造的工艺方法,包括如下步骤:1)将铬镍钼合金钢在箱式加热炉中升温至180 ℃,进行保温20 min,喷涂润滑剂,喷涂后的毛坯在100 ℃环境中干燥15min;2)将铬镍钼合金钢和模具分别加热到1200 和1500 ℃,加热20 min,均热10 min;3)再将模具加热至950 ℃,将加热到950 ℃的铬镍钼合金钢放入模具型腔定位,保温10 min;4)采用空冷的锻造后处理。本发明提供的一种铬镍钼合金钢锻造的工艺方法,通过大量实验证明,采用该方法材料利用率为60%,可见,工艺的改进可大幅度地提高材料利用率,减少机加工工时,为满足航空航天等高科技领域对钛合金精锻件的需求奠定良好的基础。
Description
技术领域
本发明涉及钢材技术领域,尤其涉及一种铬镍钼合金钢锻造的工艺方法。
背景技术
钢铁工业从形成到现在得到了突飞猛进的发展,这些钢材中相当大的数量经过机械加工以零件的形式服务于各行各业的领域和场合。随着机械加工的切削速度越来越快,对钢的工艺也提出了更高的要求。
发明内容
为解决现有技术和实际情况中存在的上述问题,本发明提供了一种铬镍钼合金钢锻造的工艺方法,其特征在于,包括如下步骤:
1)将铬镍钼合金钢在箱式加热炉中升温至180 ℃,进行保温20 min,喷涂润滑剂,
喷涂后的毛坯在100 ℃环境中干燥15min ;
2)将铬镍钼合金钢和模具分别加热到1200 和1500 ℃,加热20 min,均热10 min;
3)再将模具加热至950 ℃,将加热到950 ℃的铬镍钼合金钢放入模具型腔定位,保温10 min;
4)采用空冷的锻造后处理。
有益效果:
本发明提供的一种铬镍钼合金钢锻造的工艺方法,通过大量实验证明,采用该方法材料利用率为60%,可见,工艺的改进可大幅度地提高材料利用率,减少机加工工时,为满足航空航天等高科技领域对钛合金精锻件的需求奠定良好的基础。
具体实施方式
下面详细介绍本发明技术方案。
一种铬镍钼合金钢锻造的工艺方法,其特征在于,包括如下步骤:
1)将铬镍钼合金钢在箱式加热炉中升温至180 ℃,进行保温20 min,喷涂润滑剂,
喷涂后的毛坯在100 ℃环境中干燥15min ;
2)将铬镍钼合金钢和模具分别加热到1200 和1500 ℃,加热20 min,均热10 min;
3)再将模具加热至950 ℃,将加热到950 ℃的铬镍钼合金钢放入模具型腔定位,保温10 min;
4)采用空冷的锻造后处理。
有益效果:
本发明提供的一种铬镍钼合金钢锻造的工艺方法,通过大量实验证明,采用该方法材料利用率为60%,可见,工艺的改进可大幅度地提高材料利用率,减少机加工工时,为满足航空航天等高科技领域对钛合金精锻件的需求奠定良好的基础。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (1)
1.一种铬镍钼合金钢锻造的工艺方法,其特征在于,包括如下步骤:
1)将铬镍钼合金钢在箱式加热炉中升温至180 ℃,进行保温20 min,喷涂润滑剂,
喷涂后的毛坯在100 ℃环境中干燥15min ;
2)将铬镍钼合金钢和模具分别加热到1200 和1500 ℃,加热20 min,均热10 min;
3)再将模具加热至950 ℃,将加热到950 ℃的铬镍钼合金钢放入模具型腔定位,保温10 min;
4)采用空冷的锻造后处理。