CN106221565A - A kind of preparation method of the reinforcing agent for strengthening chromium-free fingerprint-resistant plate powder coating adhesive force - Google Patents
A kind of preparation method of the reinforcing agent for strengthening chromium-free fingerprint-resistant plate powder coating adhesive force Download PDFInfo
- Publication number
- CN106221565A CN106221565A CN201610742735.0A CN201610742735A CN106221565A CN 106221565 A CN106221565 A CN 106221565A CN 201610742735 A CN201610742735 A CN 201610742735A CN 106221565 A CN106221565 A CN 106221565A
- Authority
- CN
- China
- Prior art keywords
- pure water
- stirring mixing
- reinforcing agent
- preparation
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to fingerprint-proof plate powder coating process technical field, be specifically related to the preparation method of a kind of reinforcing agent for strengthening chromium-free fingerprint-resistant plate powder coating adhesive force.Reinforcing agent is by 3 glycidyl ether propyl-triethoxysilicanes 0.001~10 parts, wetting agent 0.002~5 parts and complements to the pure water of 100 parts and makes.3 glycidyl ether propyl-triethoxysilicanes are added to the pure water of half amount, stirring mixing 1~20min;Being subsequently added into second half pure water, then stirring mixing 1~20min, be eventually adding wetting agent, stirring mixing 1~30min obtains reinforcing agent.The present invention solves the problem that chromium-free fingerprint-resistant plate coating powder paint adhesion is the best, and the reinforcing agent of employing is remarkably improved the adhesive force of powder coating, then improves the quality of production efficiency and product.
Description
Technical field
The present invention relates to fingerprint-proof plate powder coating process technical field, be specifically related to a kind of for strengthening the resistance to finger of Chrome-free
The preparation method of the reinforcing agent of card powder coating adhesive force.
Background technology
Powder spray (application) is the surface of powder paint to workpiece with powder spraying apparatus (static plastic spraying machine), quiet
Under electro ultrafiltration, powder can be adsorbed in surface of the work uniformly, forms the coating of powdery;Powdery coating is solid through high-temperature baking levelling
Change, become the final coating of effect different (the variety classes effect of powdery paints);The spraying effect of powder spray is strong at machinery
Degree, adhesive force, the aspect such as corrosion-resistant, ageing-resistant are better than lacquer spraying technique, and cost is also under the spraying paint of same effect.
At present, in the course of processing of chromium-free fingerprint-resistant plate, because there is one layer of resinous coat on chromium-free fingerprint-resistant plate surface, repaste
Dress powdery paints, adhesive force is the best, thus causes chromium-free fingerprint-resistant plate powder coating layer fastness poor, easily peels off.
Summary of the invention
It is an object of the invention to provide a kind of reinforcing agent for strengthening chromium-free fingerprint-resistant plate powder coating adhesive force
Preparation method, the reinforcing agent of preparation is remarkably improved the adhesive force of powder coating.
For achieving the above object, present invention employs techniques below scheme:
A kind of technique strengthening chromium-free fingerprint-resistant plate powder coating adhesive force, step is as follows:
1., defat: workpiece enters degreasing bath and carries out defat, and skimming temp is 45~70 DEG C, and the time is 1~10min, basicity
It is 5~15pt;
2., washing: the workpiece of defat enters clear water reserviors washing, and temperature is room temperature, and washing time is 1~10min;
3., adhesive promoter processes: through water washed workpiece, soaking, spray or brushing reinforcing agent, treatment temperature is room
Temperature, the process time is 1~10min;
4., dry: the workpiece through washing enters drying chamber and dries, and heating zone air themperature is 150~190 DEG C,
Heat preservation zone air themperature is 170~210 DEG C, and drying time is 5~25min;
5., powder paint: spraying indoor air velocity is 0.4m/s, indoor illumination intensity 600Lx, construction Control of Voltage 60~
80KV, for powder pressure 0.1~0.5Mpa, the powder outlet quantity of electrostatic hand gun is 50~200g/min, automatic electrostatic gun
Powder outlet quantity is 50~150g/min, the distance 150~220mm of Spray gun nozzle to workpiece;
6., solidify: using the black brilliant pipe Far-infrared electric heater radiation of pottery to heat, workpiece surface temperature is 150~180 DEG C,
Temperature retention time 5~15min.
Described step 3. in the preparation method of reinforcing agent be:
1. it is made up of the raw material of following weight portion:
3-glycidyl ether propyl-triethoxysilicane 0.001~10 parts
Wetting agent 0.002~5 parts
Pure water complements to 100 parts;
2. preparation method:
3-glycidyl ether propyl-triethoxysilicane is added to the pure water of half amount, stirring mixing 1~20min;
Being subsequently added into second half pure water, then stirring mixing 1~20min, be eventually adding wetting agent, stirring mixing 1~30min obtains
Reinforcing agent.
Preferably, described step 3. in the preparation method of reinforcing agent be:
1. it is made up of the raw material of following weight portion:
3-glycidyl ether propyl-triethoxysilicane 0.005~5 parts
Wetting agent 0.005~1 part
Pure water complements to 100 parts;
2. preparation method:
3-glycidyl ether propyl-triethoxysilicane is added to the pure water of half amount, stirring mixing 5~15min;
Being subsequently added into second half pure water, then stirring mixing 5~10min, be eventually adding wetting agent, stirring mixing 5~20min obtains
Reinforcing agent.
It is further preferred that described step 3. in the preparation method of reinforcing agent be:
1. it is made up of the raw material of following weight portion:
3-glycidyl ether propyl-triethoxysilicane 0.01~3 parts
Wetting agent 0.02~0.2 part
Pure water complements to 100 parts;
2. preparation method:
3-glycidyl ether propyl-triethoxysilicane is added to the pure water of half amount, stirring mixing 10min;Then
Adding second half pure water, then stirring mixing 8min, be eventually adding wetting agent, stirring mixing 15min obtains reinforcing agent.
Described wetting agent is isomery ten polyoxyethylenated alcohol or alkylphenol polyoxyethylene.
Beneficial effects of the present invention shows:
The present invention solves the problem that chromium-free fingerprint-resistant plate coating powder paint adhesion is the best, and the reinforcing agent of employing can show
Write the adhesive force improving powder coating, then improve the quality of production efficiency and product.
Detailed description of the invention
Below with reference to embodiment, the present invention is described in detail.But, embodiment content is only to this
Bright example and explanation, described specific embodiment is done various repairing by affiliated those skilled in the art
Change or supplement or use similar mode to substitute, without departing from the design of invention or surmount defined in the claims
Scope, all should belong to protection scope of the present invention.
Embodiment 1
A kind of technique strengthening chromium-free fingerprint-resistant plate powder coating adhesive force, step is as follows:
1., defat: workpiece enters degreasing bath and carries out defat, and skimming temp is 50 DEG C, and the time is 5min, and basicity is 10pt.
2., washing: the workpiece of defat enters clear water reserviors washing, and temperature is room temperature, and washing time is 5min.
3., adhesive promoter processes: through water washed workpiece, soaking, spray or brushing reinforcing agent, treatment temperature is room
Temperature, the process time is 5min.The preparation method of reinforcing agent is: added by 2.5 parts of 3-glycidyl ether propyl-triethoxysilicanes
To the pure water of half amount, stirring mixing 10min.Being subsequently added into second half pure water, then stirring mixing 10min, finally adds
Entering 0.2 part of isomery ten polyoxyethylenated alcohol, stirring mixing 15min obtains reinforcing agent.
4., dry: the workpiece through washing enters drying chamber and dries, and heating zone air themperature is 160 DEG C, heat preservation zone
Air themperature is 200 DEG C, and drying time is 15min.
5., powder paint: spraying indoor air velocity is 0.4m/s, indoor illumination intensity 600Lx, and construction Control of Voltage exists
70KV, for powder pressure 0.4Mpa, the powder outlet quantity of electrostatic hand gun is 150g/min, and the powder outlet quantity of automatic electrostatic gun is
150g/min, distance 180mm of Spray gun nozzle to workpiece.
6., solidification: using the black brilliant pipe Far-infrared electric heater radiation heating of pottery, workpiece surface temperature is 160 DEG C, during insulation
Between 10min.
Embodiment 2
A kind of technique strengthening chromium-free fingerprint-resistant plate powder coating adhesive force, step is as follows:
1., defat: workpiece enters degreasing bath and carries out defat, and skimming temp is 55 DEG C, and the time is 3min, and basicity is 8pt.
2., washing: the workpiece of defat enters clear water reserviors washing, and temperature is room temperature, and washing time is 6min.
3., adhesive promoter processes: through water washed workpiece, soaking, spray or brushing reinforcing agent, treatment temperature is room
Temperature, the process time is 4min.The preparation method of reinforcing agent is: added by 0.05 part of 3-glycidyl ether propyl-triethoxysilicane
To the pure water of half amount, stirring mixing 8min.Being subsequently added into second half pure water, then stirring mixing 8min, is eventually adding
0.1 part of alkylphenol polyoxyethylene, stirring mixing 10min obtains reinforcing agent.
4., dry: the workpiece through washing enters drying chamber and dries, and heating zone air themperature is 170 DEG C, heat preservation zone
Air themperature is 210 DEG C, and drying time is 25min.
5., powder paint: spraying indoor air velocity is 0.4m/s, indoor illumination intensity 600Lx, and construction Control of Voltage exists
65KV, for powder pressure 0.45Mpa, the powder outlet quantity of electrostatic hand gun is 200g/min, and the powder outlet quantity of automatic electrostatic gun is
100g/min, distance 200mm of Spray gun nozzle to workpiece.
6., solidification: using the black brilliant pipe Far-infrared electric heater radiation heating of pottery, workpiece surface temperature is 160 DEG C, during insulation
Between 10min.
Claims (3)
1. the preparation method being used for strengthening the reinforcing agent of chromium-free fingerprint-resistant plate powder coating adhesive force, it is characterised in that:
1. it is made up of the raw material of following weight portion:
3-glycidyl ether propyl-triethoxysilicane 0.001~10 parts
Wetting agent 0.002~5 parts
Pure water complements to 100 parts;
2. preparation method:
3-glycidyl ether propyl-triethoxysilicane is added to the pure water of half amount, stirring mixing 1~20min;Then
Adding second half pure water, then stirring mixing 1~20min, be eventually adding wetting agent, stirring mixing 1~30min is strengthened
Agent.
2. the preparation method of the reinforcing agent for strengthening chromium-free fingerprint-resistant plate powder coating adhesive force as claimed in claim 1,
It is characterized in that:
1. it is made up of the raw material of following weight portion:
3-glycidyl ether propyl-triethoxysilicane 0.005~5 parts
Wetting agent 0.005~1 part
Pure water complements to 100 parts;
2. preparation method:
3-glycidyl ether propyl-triethoxysilicane is added to the pure water of half amount, stirring mixing 5~15min;Then
Adding second half pure water, then stirring mixing 5~10min, be eventually adding wetting agent, stirring mixing 5~20min is strengthened
Agent.
3. the preparation method of the reinforcing agent for strengthening chromium-free fingerprint-resistant plate powder coating adhesive force as claimed in claim 2,
It is characterized in that:
1. it is made up of the raw material of following weight portion:
3-glycidyl ether propyl-triethoxysilicane 0.01~3 parts
Wetting agent 0.02~0.2 part
Pure water complements to 100 parts;
2. preparation method:
3-glycidyl ether propyl-triethoxysilicane is added to the pure water of half amount, stirring mixing 10min;It is subsequently added into
Second half pure water, then stirring mixing 8min, be eventually adding wetting agent, and stirring mixing 15min obtains reinforcing agent.