CN106221486A - A kind of coating of vehicle steering gearshift plectrum - Google Patents

A kind of coating of vehicle steering gearshift plectrum Download PDF

Info

Publication number
CN106221486A
CN106221486A CN201610668841.9A CN201610668841A CN106221486A CN 106221486 A CN106221486 A CN 106221486A CN 201610668841 A CN201610668841 A CN 201610668841A CN 106221486 A CN106221486 A CN 106221486A
Authority
CN
China
Prior art keywords
parts
part
minutes
coating
material
Prior art date
Application number
CN201610668841.9A
Other languages
Chinese (zh)
Inventor
王贤敏
商则志
付波
印体斌
熊德建
付磊
印超
熊伟光
Original Assignee
蚌埠金光车轮有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 蚌埠金光车轮有限公司 filed Critical 蚌埠金光车轮有限公司
Priority to CN201610668841.9A priority Critical patent/CN106221486A/en
Publication of CN106221486A publication Critical patent/CN106221486A/en

Abstract

A kind of coating of vehicle steering gearshift plectrum, relate to auto parts and components processing renovation technique field, it is characterized in that: be made up of following weight portion, 9 parts of amino resins, polybutylene terephthalate (PBT) 2 parts, 9 parts of age resistor, diethylenetriamines 1 part, methylimidazole 2 parts, charcoal powder 1 part, 0.5 part of asbestos, citric acid 1.5 parts, conch meal 2 parts, octylisothiazolinone 2 parts, 1 part of flint clay powder, 4 parts of aluminum argentum powder, polypropylene glycerol aether 1 part, lauric acid 2 parts, alcohol ester 12 coalescents 1 part, auxiliary agent 3 parts.The inventive method is reasonable, easy to operate, reasonable mixture ratio.

Description

A kind of coating of vehicle steering gearshift plectrum

Technical field:

The present invention relates to auto parts and components processing renovation technique field, be specifically related to a kind of vehicle steering gearshift plectrum and use Coating.

Background technology:

Gearshift plectrum is as one gear shift device efficiently, it is possible to largely promote the operability of driving.Gearshift is dialled Sheet is normally at steering wheel rear.When handling gearshift plectrum, driver is general only need to push D, S or stick shift pattern by gear. Utilizing gearshift plectrum, driver's both hands just can complete a liter downshift operation without departing from steering wheel.

Because gearshift plectrum is located on rear side of steering wheel, so changing easily, efficiency is high.In a lot of rallys, field Match in even F1 race and all have employed this device.

And plectrum of shifting gears also have on automobile application very extensively, many people are using, and often due to long Time uses and is easily caused the coating shedding of outside, cracking, so easily by exposed for inside outside, the time for a long time after, be one The biggest individual damage.

Summary of the invention:

The technical problem to be solved be to overcome existing technological deficiency provide a kind of method rationally, operation side Just, the coating of a kind of vehicle steering gearshift plectrum of reasonable mixture ratio.

The technical problem to be solved uses following technical scheme to realize:

A kind of coating of vehicle steering gearshift plectrum, it is characterised in that: it is made up of following weight portion,

9 parts of amino resins, polybutylene terephthalate (PBT) 2 parts, 9 parts of age resistor, diethylenetriamines 1 part, dimethyl Imidazoles 2 parts, charcoal powder 1 part, 0.5 part of asbestos, citric acid 1.5 parts, conch meal 2 parts, octylisothiazolinone 2 parts, flint clay powder 1 Part, 4 parts of aluminum argentum powder, polypropylene glycerol aether 1 part, lauric acid 2 parts, alcohol ester 12 coalescents 1 part, auxiliary agent 3 parts;

Including following preparation process,

Above-mentioned material is put in milling apparatus by I, conventionally grinds 35 minutes, is subsequently adding material gross weight The deionized water of 1/20, mix and blend 25 minutes;

II will grind after material be placed in the sealed environment of 5-11 DEG C standing 60 minutes;

Mixture in II is put into high-temperature heating 30 minutes in the smelting furnace of 100 DEG C by III, then takes out after 5 minutes and puts into shake Swing concussion mixing 10 minutes in equipment, be subsequently adding 1/50 distilled water of material gross weight, continue concussion 10 minutes;

IV will stand after material put in high-speed mixing equipment the rotating speed dispersed with stirring according to 1400-1700 rev/min 60-75 minute, then compound is put in ball mill and carry out spheroidal graphite process in a conventional manner;

Described auxiliary agent is made up of the material of following weight portion,

Concha Arcae 1 part, Radix Cynanchi Atrati 1 part, Endoconcha Sepiae 2 parts, Flos Campsis 3 parts, Rhizoma Curcumae 3 parts, Hirudo 2 parts, Semen Sterculiae Lychnophorae 4 parts, the four seasons Green grass or young crops 4 parts, Folium Isatidis 5 parts, Spora Lygodii 5 parts;

Preparation method: above-mentioned material is placed in sealing container airtight 3 hours, is placed under high light sudden and violent after then taking out Shine 24 hours.

The invention have the benefit that I material cost is the highest, overweight financial burden will not be brought to enterprise;

II material is the most nontoxic, brings body harm will not to Producer, user;

III manufacture method is simple, technique is convenient, and volume production is convenient.

Detailed description of the invention:

For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, enter below One step illustrates the present invention.

A kind of coating of vehicle steering gearshift plectrum, it is characterised in that: it is made up of following weight portion,

9 parts of amino resins, polybutylene terephthalate (PBT) 2 parts, 9 parts of age resistor, diethylenetriamines 1 part, dimethyl Imidazoles 2 parts, charcoal powder 1 part, 0.5 part of asbestos, citric acid 1.5 parts, conch meal 2 parts, octylisothiazolinone 2 parts, flint clay powder 1 Part, 4 parts of aluminum argentum powder, polypropylene glycerol aether 1 part, lauric acid 2 parts, alcohol ester 12 coalescents 1 part, auxiliary agent 3 parts;

Including following preparation process,

Above-mentioned material is put in milling apparatus by I, conventionally grinds 35 minutes, is subsequently adding material gross weight The deionized water of 1/20, mix and blend 25 minutes;

II will grind after material be placed in the sealed environment of 5-11 DEG C standing 60 minutes;

Mixture in II is put into high-temperature heating 30 minutes in the smelting furnace of 100 DEG C by III, then takes out after 5 minutes and puts into shake Swing concussion mixing 10 minutes in equipment, be subsequently adding 1/50 distilled water of material gross weight, continue concussion 10 minutes;

IV will stand after material put in high-speed mixing equipment the rotating speed dispersed with stirring according to 1400-1700 rev/min 60-75 minute, then compound is put in ball mill and carry out spheroidal graphite process in a conventional manner;

Described auxiliary agent is made up of the material of following weight portion,

Concha Arcae 1 part, Radix Cynanchi Atrati 1 part, Endoconcha Sepiae 2 parts, Flos Campsis 3 parts, Rhizoma Curcumae 3 parts, Hirudo 2 parts, Semen Sterculiae Lychnophorae 4 parts, the four seasons Green grass or young crops 4 parts, Folium Isatidis 5 parts, Spora Lygodii 5 parts;

Preparation method: above-mentioned material is placed in sealing container airtight 3 hours, is placed under high light sudden and violent after then taking out Shine 24 hours.

The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and Equivalent defines.

Claims (3)

1. the coating of a vehicle steering gearshift plectrum, it is characterised in that: it is made up of following weight portion,
9 parts of amino resins, polybutylene terephthalate (PBT) 2 parts, 9 parts of age resistor, diethylenetriamines 1 part, methylimidazole 2 Part, charcoal powder 1 part, 0.5 part of asbestos, citric acid 1.5 parts, conch meal 2 parts, octylisothiazolinone 2 parts, 1 part of flint clay powder, aluminum 4 parts of argentum powder, polypropylene glycerol aether 1 part, lauric acid 2 parts, alcohol ester 12 coalescents 1 part, auxiliary agent 3 parts.
The coating of a kind of vehicle steering the most according to claim 1 gearshift plectrum, it is characterised in that: include following system Standby step,
Above-mentioned material is put in milling apparatus by I, conventionally grinds 35 minutes, is subsequently adding material gross weight 1/20 Deionized water, mix and blend 25 minutes;
II will grind after material be placed in the sealed environment of 5-11 DEG C standing 60 minutes;
Mixture in II is put into high-temperature heating 30 minutes in the smelting furnace of 100 DEG C by III, then takes out after 5 minutes and puts into concussion and set Standby middle concussion mixing 10 minutes, is subsequently adding 1/50 distilled water of material gross weight, continues concussion 10 minutes;
IV will stand after material put in high-speed mixing equipment rotating speed dispersed with stirring 60-75 according to 1400-1700 rev/min Minute, then compound is put in ball mill and carry out spheroidal graphite process in a conventional manner.
A kind of vehicle steering the most according to claim 1 gearshift plectrum coating, it is characterised in that: described auxiliary agent by The material of following weight portion is made,
Concha Arcae 1 part, Radix Cynanchi Atrati 1 part, Endoconcha Sepiae 2 parts, Flos Campsis 3 parts, Rhizoma Curcumae 3 parts, Hirudo 2 parts, Semen Sterculiae Lychnophorae 4 parts, Ilex purpurea Hassk.[I.chinensis Sims 4 Part, Folium Isatidis 5 parts, Spora Lygodii 5 parts;
Preparation method: above-mentioned material is placed in sealing container airtight 3 hours, is placed on after then taking out under high light and is exposed to the sun 24 Individual hour.
CN201610668841.9A 2016-08-12 2016-08-12 A kind of coating of vehicle steering gearshift plectrum CN106221486A (en)