CN106215547A - Anion air purifying filtering material and preparation method thereof - Google Patents
Anion air purifying filtering material and preparation method thereof Download PDFInfo
- Publication number
- CN106215547A CN106215547A CN201610742321.8A CN201610742321A CN106215547A CN 106215547 A CN106215547 A CN 106215547A CN 201610742321 A CN201610742321 A CN 201610742321A CN 106215547 A CN106215547 A CN 106215547A
- Authority
- CN
- China
- Prior art keywords
- anion
- parts
- air purifying
- magnetic
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of anion air purifying filtering material and preparation method thereof, described anion air purifying filtering material is the lamination layer structure being made up of internal layer and outer layer, internal layer is substrate layer, and outer layer is latex functional layer, and described substrate layer is with spun-laced nonwoven fabric as base material;The component of described latex functional layer and weight portion composition are as follows: latex 60 70 parts, synthetic resin 15 20 parts, anion powder 5 10 parts, 20 30 parts of bamboo carbon fiber powder, diatom ooze 58 parts, 35 parts of the order mesoporous medium of magnetic.Magnetic ordered mesoporous carbon of the present invention or the order mesoporous nickel ferrite based magnetic loaded of magnetic possess huge specific surface area and abundant three dimensional pore structures, and high-specific surface area is conducive to the adsorption storage of anion powder and diatom ooze;Regular orderly open duct, the aperture of size adjustable are that anion generation provides path, and beneficially anion slowly persistently produces for a long time, improves the using effect of anion air purifying filtering material, extends its service life.
Description
Technical field
The present invention relates to a kind of anion air purifying filtering material and preparation method thereof.
Background technology
Along with expanding economy, the extensive application of indoor a large amount of new decorative materials, cause room air pollution further
Aggravation, adds people and also result in certain pollution at indoor life activity, and problem of indoor air quality becomes more to dash forward
Go out.The health of indoor air quality and human body has close relationship, the most especially with volatile organic matter compound (TVOC),
The pollutant such as PM2.5 are the most serious to the harm of human body.
Air filtration media of the prior art typically uses paper fiber, glass fibre, polymer fiber and activated carbon,
Wherein paper fiber is owing to papery is distinctive the most corrosion-resistant or not weatherability, causes its restricted lifetime;Glass fibre is under a cloud
It is carcinogen, is therefore not intended in air filter use, and activated carbon can only adsorb harmful gas and can not filter
PM2.5, so air filtration production is complex, cost remains high.
Anion air purifying filtering material is a kind of filtration for the unhealthy composition in air, by shunting certainly
So producing negative oxygen ion, reduce PM2.5 nuisance, existing air filtration apparatus is a lot, but is typically all for reducing PM2.5
Part is studied, relatively fewer for improving air quality.
Summary of the invention
It is an object of the invention to solve the deficiencies in the prior art, it is provided that a kind of anion air purifying filtering material.
Further object is that the preparation method that a kind of anion air purifying filtering material is provided.
The technical solution adopted for the present invention to solve the technical problems is:
Anion air purifying filtering material, described anion air purifying filtering material is to be made up of internal layer and outer layer
Lamination layer structure, internal layer is substrate layer, and outer layer is latex functional layer, and described substrate layer is with spun-laced nonwoven fabric as base material;Described breast
The component of glue functional layer and weight portion composition are as follows: latex 40-60 part, synthetic resin 10-30 part, anion powder 5-10 part, bamboo
Carbon fibe powder 20-40 part, diatom ooze 10-30 part, magnetic order mesoporous medium 3-8 part.
Preferably, the component of described latex functional layer and weight portion composition are as follows: latex 55 parts, and synthetic resin 18 parts is negative
7 parts of ion powder, 30 parts of bamboo carbon fiber powder, diatom ooze 15 parts, 5 parts of the order mesoporous medium of magnetic.
Preferably, the order mesoporous medium of described magnetic is magnetic ordered mesoporous carbon or the order mesoporous nickel ferrite based magnetic loaded of magnetic.
It is furthermore preferred that the order mesoporous medium of described magnetic is the order mesoporous nickel ferrite based magnetic loaded of magnetic, its preparation method is as follows:
1) by Ni (NO3)2·6H2O and Fe (NO3)3·9H2O is dissolved in methanol, and appropriate porous silicon KIT-6 is put into Sheng
Have in the polytetrafluoroethylcontainer container of normal hexane, be sufficiently stirred for;
2) by solution 1) raw material be added dropwise over step 2) in, the mixed solution formed is sufficiently stirred for, and adds in 50-60 DEG C
Hot 8-12h;
3) step 2) gained solid calcination 4-5h at 250-280 DEG C;
4) by step 3) gained solid is cooled to room temperature, in the polished round-bottomed flask being transferred to fill NaOH solution,
Centrifugal recovery after return stirring 24-36h under 40-50 DEG C of water bath condition;
5) by step 4) gained solid cleans to neutrality repeatedly with ethanol and deionized water respectively, vacuum dried i.e.
Can.
Magnetic ordered mesoporous carbon of the present invention or the order mesoporous nickel ferrite based magnetic loaded of magnetic possess huge specific surface area and
Abundant three dimensional pore structures, high-specific surface area is conducive to the adsorption storage of anion powder and diatom ooze;Regular orderly opening
Property duct, the aperture of size adjustable be that anion produces and provides path, beneficially anion slowly persistently produces for a long time, carries
The using effect of high-negative ion air purification filter material, extends its service life.
Preferably, described synthetic resin is any one in commercial resins for universal use, such as polyethylene, polypropylene, polychlorostyrene second
Alkene, polystyrene and ABS.
A kind of preparation method of anion air purifying filtering material, preparation method is as follows:
(1) the latex functional layer component of formula ratio is sufficiently stirred for by blender, the micro-frequency of emulsion high temperature after stirring
10-30min, is placed in impregnation glue groove standby;
The micro-frequency of high temperature refers to, under 110-130 DEG C of high temperature, process through stable frequency of vibration, such as 10-
200Hz, so that slurry is full and uniform.
(2) by machine on spun-laced nonwoven fabric base material, spun-laced nonwoven fabric and emulsion is made fully to infiltrate, at impregnation process by impregnation
The micro-frequency of middle high temperature, so that base material is uniformly starched, is formed two-in-one material of main part by slurry base material by extruding, and material of main part is producing
Through hot extrusion on line, stentering forming, subsequently enter (a kind of work that can produce heat-flash gas impact air-flow of hot-air pump negative pressure cabin
Storehouse), heat-flash gas impact air-flow upper and lower in storehouse run through, hit logical material of main part, form some micropores, be distributed in each portion of material
Point, form negative ion air purifying material semi-finished product;
(3) semi-finished product pass through shear history, are excised by redundance, after storing solidification cooling, enter Product checking.
The invention has the beneficial effects as follows: the anion air purifying filtering material of the present invention can be effectively isolated in air
PM2.5 material, isolation simultaneously volatilization negative oxygen ion and, improve air quality.
Detailed description of the invention
Below by specific embodiment, technical scheme is described in further detail.
Embodiment 1:
Anion air purifying filtering material, described anion air purifying filtering material is to be made up of internal layer and outer layer
Lamination layer structure, internal layer is substrate layer, and outer layer is latex functional layer, and described substrate layer is with spun-laced nonwoven fabric as base material;Described breast
The component of glue functional layer and weight portion composition are as follows: latex 40 parts, synthetic resin 10 parts, anion powder 5 parts, bamboo carbon fiber powder 20
Part, diatom ooze 10 parts, 3 parts of the order mesoporous medium of magnetic, the order mesoporous medium of described magnetic is magnetic ordered mesoporous carbon, described conjunction
Resin is any one in commercial resins for universal use, such as polyethylene.
The preparation method of anion air purifying filtering material, preparation method is as follows:
(1) the latex functional layer component of formula ratio is sufficiently stirred for by blender, the micro-frequency of emulsion high temperature after stirring
10min, is placed in impregnation glue groove standby;
The micro-frequency of high temperature refers to, under 110 DEG C of high temperature, process through stable frequency of vibration, such as 100Hz, so that slurry
Expect full and uniform;
(2) by machine on spun-laced nonwoven fabric base material, spun-laced nonwoven fabric and emulsion is made fully to infiltrate, at impregnation process by impregnation
The micro-frequency of middle high temperature, so that base material is uniformly starched, is formed two-in-one material of main part by slurry base material by extruding, and material of main part is producing
Through hot extrusion on line, stentering forming, (one can produce heat-flash (150 DEG C) gas impact air-flow to subsequently enter hot-air pump negative pressure cabin
Working bin), heat-flash gas impact air-flow upper and lower in storehouse run through, hit logical material of main part, form some micropores, be distributed in material
Material each several part, forms negative ion air purifying material semi-finished product;
(3) semi-finished product pass through shear history, are excised by redundance, after storing solidification cooling, enter Product checking.
Embodiment 2:
Anion air purifying filtering material, described anion air purifying filtering material is to be made up of internal layer and outer layer
Lamination layer structure, internal layer is substrate layer, and outer layer is latex functional layer, and described substrate layer is with spun-laced nonwoven fabric as base material;Described breast
The component of glue functional layer and weight portion composition are as follows: latex 60 parts, synthetic resin 30 parts, anion powder 10 parts, bamboo carbon fiber powder
40 parts, diatom ooze 30 parts, 8 parts of the order mesoporous medium of magnetic, the order mesoporous medium of described magnetic is magnetic ordered mesoporous carbon, described
Synthetic resin is any one in commercial resins for universal use, such as polypropylene.
The preparation method of anion air purifying filtering material, preparation method is as follows:
(1) the latex functional layer component of formula ratio is sufficiently stirred for by blender, the micro-frequency of emulsion high temperature after stirring
30min, is placed in impregnation glue groove standby;
The micro-frequency of high temperature refers to, under 130 DEG C of high temperature, process through stable frequency of vibration, such as 40Hz, so that slurry
Expect full and uniform;
(2) by machine on spun-laced nonwoven fabric base material, spun-laced nonwoven fabric and emulsion is made fully to infiltrate, at impregnation process by impregnation
The micro-frequency of middle high temperature, so that base material is uniformly starched, is formed two-in-one material of main part by slurry base material by extruding, and material of main part is producing
Through hot extrusion on line, stentering forming, (one can produce heat-flash (180 DEG C) gas impact air-flow to subsequently enter hot-air pump negative pressure cabin
Working bin), heat-flash gas impact air-flow upper and lower in storehouse run through, hit logical material of main part, form some micropores, be distributed in material
Material each several part, forms negative ion air purifying material semi-finished product;
(3) semi-finished product pass through shear history, are excised by redundance, after storing solidification cooling, enter Product checking.
Embodiment 3:
Anion air purifying filtering material, described anion air purifying filtering material is to be made up of internal layer and outer layer
Lamination layer structure, internal layer is substrate layer, and outer layer is latex functional layer, and described substrate layer is with spun-laced nonwoven fabric as base material;Described breast
The component of glue functional layer and weight portion composition are as follows: latex 55 parts, synthetic resin 18 parts, anion powder 7 parts, bamboo carbon fiber powder 30
Part, diatom ooze 15 parts, 5 parts of the order mesoporous medium of magnetic, the order mesoporous medium of described magnetic is the order mesoporous nickel ferrite based magnetic loaded of magnetic, institute
Stating synthetic resin is any one in commercial resins for universal use, such as polrvinyl chloride.
The preparation method of anion air purifying filtering material, preparation method is as follows:
(1) the latex functional layer component of formula ratio is sufficiently stirred for by blender, the micro-frequency of emulsion high temperature after stirring
20min, is placed in impregnation glue groove standby;
The micro-frequency of high temperature refers to, under 120 DEG C of high temperature, process through stable frequency of vibration, such as 20Hz, so that slurry
Expect full and uniform;
(2) by machine on spun-laced nonwoven fabric base material, spun-laced nonwoven fabric and emulsion is made fully to infiltrate, at impregnation process by impregnation
The micro-frequency of middle high temperature, so that base material is uniformly starched, is formed two-in-one material of main part by slurry base material by extruding, and material of main part is producing
Through hot extrusion on line, stentering forming, (one can produce heat-flash (160 DEG C) gas impact air-flow to subsequently enter hot-air pump negative pressure cabin
Working bin), heat-flash gas impact air-flow upper and lower in storehouse run through, hit logical material of main part, form some micropores, be distributed in material
Material each several part, forms negative ion air purifying material semi-finished product;
(3) semi-finished product pass through shear history, are excised by redundance, after storing solidification cooling, enter Product checking.
Magnetic ordered mesoporous carbon of the present invention or the order mesoporous nickel ferrite based magnetic loaded of magnetic possess huge specific surface area and
Abundant three dimensional pore structures, high-specific surface area is conducive to the adsorption storage of anion powder and diatom ooze;Regular orderly opening
Property duct, the aperture of size adjustable be that anion produces and provides path, beneficially anion slowly persistently produces for a long time, carries
The using effect of high-negative ion air purification filter material, extends its service life.
The anion air purifying filtering material of the present invention can be effectively isolated the PM2.5 material in air, in isolation simultaneously
Volatilization negative oxygen ion and, improve air quality.
Embodiment described above is the one preferably scheme of the present invention, not makees the present invention any pro forma
Limit, on the premise of without departing from the technical scheme described in claim, also have other variant and remodeling.
Claims (5)
1. anion air purifying filtering material, it is characterised in that: described anion air purifying filtering material be by internal layer and
The lamination layer structure that outer layer is constituted, internal layer is substrate layer, and outer layer is latex functional layer, and described substrate layer is with spun-laced nonwoven fabric as base
Material;The component of described latex functional layer and weight portion composition are as follows: latex 40-60 part, synthetic resin 10-30 part, anion powder
5-10 part, bamboo carbon fiber powder 20-40 part, diatom ooze 10-30 part, magnetic order mesoporous medium 3-8 part.
Anion air purifying filtering material the most according to claim 1, it is characterised in that: the group of described latex functional layer
Divide and weight portion composition is as follows: latex 55 parts, synthetic resin 18 parts, anion powder 7 parts, 30 parts of bamboo carbon fiber powder, diatom ooze 15
Part, 5 parts of the order mesoporous medium of magnetic.
Anion air purifying filtering material the most according to claim 1 and 2, it is characterised in that: described magnetic is situated between in order
Hole medium is magnetic ordered mesoporous carbon or the order mesoporous nickel ferrite based magnetic loaded of magnetic.
Anion air purifying filtering material the most according to claim 1 and 2, it is characterised in that: described synthetic resin is
Any one in commercial resins for universal use.
5. a preparation method for the anion air purifying filtering material described in claim 1-4 any one, its feature exists
In: preparation method is as follows:
(1) the latex functional layer component of formula ratio is sufficiently stirred for by blender, the emulsion high temperature micro-frequency 10-after stirring
30min, is placed in impregnation glue groove standby;
(2) by machine on spun-laced nonwoven fabric base material, spun-laced nonwoven fabric and emulsion is made fully to infiltrate by impregnation, high in impregnation process
The micro-frequency of temperature, so that base material is uniformly starched, is formed two-in-one material of main part by slurry base material by extruding, and material of main part is on a production line
Through hot extrusion, stentering forming, subsequently enter hot-air pump negative pressure cabin, heat-flash gas impact air-flow upper and lower in storehouse run through, hit
Logical material of main part, forms some micropores, is distributed in material each several part, forms negative ion air purifying material semi-finished product;
(3) semi-finished product pass through shear history, are excised by redundance, after storing solidification cooling, enter Product checking.