CN106193505A - Non-woven fabrics plate structure and formula thereof and processing technique - Google Patents
Non-woven fabrics plate structure and formula thereof and processing technique Download PDFInfo
- Publication number
- CN106193505A CN106193505A CN201610516469.XA CN201610516469A CN106193505A CN 106193505 A CN106193505 A CN 106193505A CN 201610516469 A CN201610516469 A CN 201610516469A CN 106193505 A CN106193505 A CN 106193505A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- fabric
- glass
- fiber
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of non-woven fabrics plate structure, including middle material (3), it is characterised in that: the top of described middle material (3) is sequentially provided with glass-fiber-fabric one (4) and non-woven fabrics (5);The lower section of middle material (3) sequentially glass-fiber-fabric two (2) and 9g/m2 non-woven fabrics (1).Beneficial effects of the present invention: this floor by rational formula and processing technique, sheet metal thickness error is decreased to ± 0.3mm within, convenient use and the later stage carries out deep processing, be suitable for promoting the use of.
Description
Technical field
The present invention relates to a kind of non-woven fabrics plate structure, be specifically related to a kind of non-woven fabrics plate structure and formula thereof and processing work
Skill, belongs to board technology field.
Background technology
Sheet material is commonly made to the flattened rectangular constructional material plate of normal size, makees the component on wall, ceiling or floor.Also
The metallic plate refer to forging, rolling or casting more.It is divided into thin plate, middle plate, slab, special heavy plate, is commonly made to normal size
Flattened rectangular constructional material plate.
It is a kind of ecological fire preventing trim panel as Patent publication No CN104131668A discloses the present invention, distinguishes from the bottom to top
Including initial bed, the middle bed of material, fiberglass layer, nonwoven layers and internal decorative layer;Initial bed, the middle bed of material, fiberglass layer, nonwoven layers and interior trim
The exposed face of layer is coated with waterproof sealing layer;Wherein initial bed is to be enclosed with the PVC board of non-woven fabrics or be enclosed with non-woven fabrics
TOB ceramic plate, internal decorative layer is that PVC board forms with aluminium foil hot pressing.It is good that the present invention has fire retardant effect;Soundproof effect is good;Insulation
Excellent performance and the strong feature of weatherability.
And for example Patent publication No CN101337366A discloses the production method of a kind of nano crystal-sand floor, and it produces step
Suddenly include Wooden slice by conventional technique, select plate and fluting, also include floor base material being processed by shot blasting and comprising 2
Road aqueous, environmental protective priming paint, 3 road wear-resistant primer, 9 road elastic primers, 17 road multiple mutual formula infiltration lacquer paintings of 3 road scratch-resistant finish paints are coated with
Coating process;The present invention uses the 17 multiple mutual formula infiltration technologies in road of 3+2+9+3, and uses the interactive mode of nano-titanium paint molecule to ooze
Thoroughly technology, makes paint molecule the most fully penetrate in wood molecule, through multiple tracks super abrasive priming paint, hardening primer through levelling
With several solidification and sanding, floor is made to possess superpower hardness and wear-resistant, scratch-resistant, the excellent properties of antioxidation xanthochromia, its paint
Face adhesive force, pliability, floor scratch resistance are considerably beyond common process floor.
Existing sheet metal thickness error is bigger, it has not been convenient to use and the later stage carries out deep processing.
Summary of the invention
Instant invention overcomes the problem that prior art exists, it is proposed that a kind of non-woven fabrics plate structure and formula thereof and processing
Technique, this floor is by rational formula and processing technique, and sheet metal thickness error reduces, within ± 0.3, convenient use and later stage
Carry out deep processing, it is also possible to according to customer requirement, spread one layer of prime cement at orlop, make surface more attractive in appearance.
The concrete technical scheme of the present invention is as follows: non-woven fabrics plate structure, including middle material (3), it is characterised in that: in described
The top of layered material (3) is sequentially provided with glass-fiber-fabric one (4) and non-woven fabrics (5);The lower section of middle material (3) sequentially glass-fiber-fabric two (2) and
9g/m2Non-woven fabrics (1);
The formula of described middle material (3) is:
Light calcined magnesia: 100 parts;
Magnesium sulfate heptahydrate: 40-80 part;
Water: 60-100 part;
Wood flour: 20-60 part;
Other inserts: 4-40 part;
Modifying agent: 1-5 part;
Pigment: 1-10 part;
Preferentially, other inserts described are the one in perlite, gangue, flyash, quartz sand, rice husk, straw
Or it is two or more.
Preferentially, the one during described pigment is iron oxide yellow, iron oxide red, iron oxide green, iron oxide blue, carbon black.
Described 9g/m2Non-woven fabrics (1) is provided with bottom pulp layer further below.The formula of described bottom pulp layer is
Light calcined magnesia: 100 parts;
Magnesium chloride: 50-80 part;
Water: 40-70 part;
Pulvis Talci: 30-70 part;
Latex powder: 5-10 part;
Modifying agent: 3-6 part;
Pigment 2-10 part;
The preparation technology of described bottom pulp layer is as follows:
1) magnesium chloride and water are added together in proportion it are stirred, until magnesium chloride is completely dissolved;
2) it is proportionally added in agitator tank stirring by magnesium chloride solution and modifying agent;
3) it is proportionally added in agitator tank stirring by pigment, light calcined magnesia, Pulvis Talci and latex powder, has prepared
Become.
Preferentially, the preparation technology of described middle material (6) is as follows:
1) Magnesium sulfate heptahydrate and water are added together in proportion it are stirred, until Magnesium sulfate heptahydrate is completely dissolved;
2) it is proportionally added in agitator tank stirring by Magnesium sulfate heptahydrate solution and modifying agent;
3) it is proportionally added into light calcined magnesia in agitator tank stirring;
4) it is proportionally added in agitator tank stirring by pigment, wood flour and other inserts;
5) adding foaming agent according to density requirements, stir, preparation completes.
The present invention also provides for a kind of non-woven fabrics board machining process, it is characterised in that: comprise the following steps,
Concrete board making process:
1) PVC or ABS template is prepared;
2) mould oil of uniform brushing thin layer in template;
3) one layer of 9g/m is laid2Non-woven fabrics (1), glass-fiber-fabric two (2) are as lower nonwoven fabric layer and lower floor's glass layer of cloth;
4) dispensing of the middle bed of material (4) is lowered on the good glass-fiber-fabric of roll-in two (2), adjusts middle material pressure roller and template
Between distance i.e. sheet metal thickness, the bed of material (3) in laying again by roll-in mode;By 1 layer of glass-fiber-fabric while the laying of middle material
One (4) by middle material pressure roller together with middle bed of material roll-in;
5) by non-woven fabrics (5) roll-in on glass-fiber-fabric one (4);
6) after laying, after cutting, enter cage car, push curing room and carry out maintenance;
7) care environments temperature is at about 20-40 DEG C;Maintenance 12-16 hour afterwards can the demoulding;
8) after the demoulding, sheet material keeps flat and carries out secondary temperature elevation, ensures that sheet material board body temperature is less than 50 in temperature-rise period
℃;Riser cooling to be carried out when arriving marginal value, must take blowing mode to lower the temperature if desired;
9) after riser is rested 5-7 days, when detecting its moisture content to less than 10%, i.e. cut, pack after terminating.
Beneficial effects of the present invention: this floor is reduced by rational formula and processing technique, sheet metal thickness error, ±
Within 0.3, convenient use carries out deep processing with the later stage, is suitable for promoting the use of.
Accompanying drawing explanation
Fig. 1 is non-woven fabrics plate structure schematic diagram.
Detailed description of the invention
Embodiment 1
As it can be seen, this enforcement processing nonwoven fabrics plate structure, including middle material 3, the top of described middle material 3 is sequentially provided with
Glass-fiber-fabric 1 and non-woven fabrics 5;Sequentially glass-fiber-fabric 22 and 9g/m, the lower section of middle material 32Non-woven fabrics 1;
The formula of described middle material 3 is:
Light calcined magnesia: 100 parts;
Magnesium sulfate heptahydrate: 40 parts;
Water: 60 parts;
Wood flour: 20 parts;
Other inserts: 4 parts;
Modifying agent: 1 part;
Pigment: 1 part;
Other inserts are one or more in perlite, gangue, flyash, quartz sand, rice husk, straw.
Pigment is the one in iron oxide yellow, iron oxide red, iron oxide green, iron oxide blue, carbon black.
The preparation technology of middle material 6 is as follows:
1) Magnesium sulfate heptahydrate and water are added together in proportion it are stirred, until Magnesium sulfate heptahydrate is completely dissolved;
2) it is proportionally added in agitator tank stirring by Magnesium sulfate heptahydrate solution and modifying agent;
3) it is proportionally added into light calcined magnesia in agitator tank stirring;
4) it is proportionally added in agitator tank stirring by pigment, wood flour and other inserts;
5) adding foaming agent according to density requirements, stir, preparation completes.
The present invention also provides for a kind of non-woven fabrics board machining process, comprises the following steps,
Concrete board making process:
1) PVC or ABS template is prepared;
2) mould oil of uniform brushing thin layer in template;
3) one layer of 9g/m is laid2Non-woven fabrics 1, glass-fiber-fabric 22 are as lower nonwoven fabric layer and lower floor's glass layer of cloth;
4) dispensing of the middle bed of material 3 is lowered on the good glass-fiber-fabric of roll-in 22, adjusts between middle material pressure roller and template
Distance i.e. sheet metal thickness, the bed of material 3 in laying again by roll-in mode;During 1 layer of glass-fiber-fabric 1 is passed through while laying by middle material
Material pressure roller is together with middle bed of material roll-in;
5) by non-woven fabrics 5 roll-in on glass-fiber-fabric 1;
6) after laying, after cutting, enter cage car, push curing room and carry out maintenance;
7) care environments temperature is at about 20 DEG C;Maintenance 12 hours afterwards can the demoulding;
8) after the demoulding, sheet material keeps flat and carries out secondary temperature elevation, ensures that sheet material board body temperature is less than 50 in temperature-rise period
℃;Riser cooling to be carried out when arriving marginal value, must take blowing mode to lower the temperature if desired;
9) after riser is rested 5 days, when detecting its moisture content to less than 10%, i.e. cut, pack after terminating.
Embodiment 2
As it can be seen, this enforcement processing nonwoven fabrics plate structure, including middle material 3, the top of described middle material 3 is sequentially provided with
Glass-fiber-fabric 1 and non-woven fabrics 5;Sequentially glass-fiber-fabric 22 and 9g/m, the lower section of middle material 32Non-woven fabrics 1;
Described 9g/m2Non-woven fabrics 1 is provided with bottom pulp layer further below.The formula of described bottom pulp layer is
Light calcined magnesia: 100 parts;
Magnesium chloride: 50-80 part;
Water: 40-70 part;
Pulvis Talci: 30-70 part;
Latex powder: 5-10 part;
Modifying agent: 3-6 part;
Pigment 2-10 part;
The preparation technology of described bottom pulp layer is as follows:
1) magnesium chloride and water are added together in proportion it are stirred, until magnesium chloride is completely dissolved;
2) it is proportionally added in agitator tank stirring by magnesium chloride solution and modifying agent;
3) it is proportionally added in agitator tank stirring by pigment, light calcined magnesia, Pulvis Talci and latex powder, has prepared
Become.
The formula of described middle material 3 is:
Light calcined magnesia: 100 parts;
Magnesium sulfate heptahydrate: 60 parts;
Water: 75 parts;
Wood flour: 40 parts;
Other inserts: 24 parts;
Modifying agent: 3 parts;
Pigment: 5 parts;
Other inserts are one or more in perlite, gangue, flyash, quartz sand, rice husk, straw.
Pigment is the one in iron oxide yellow, iron oxide red, iron oxide green, iron oxide blue, carbon black.
The preparation technology of middle material 6 is as follows:
1) Magnesium sulfate heptahydrate and water are added together in proportion it are stirred, until Magnesium sulfate heptahydrate is completely dissolved;
2) it is proportionally added in agitator tank stirring by Magnesium sulfate heptahydrate solution and modifying agent;
3) it is proportionally added into light calcined magnesia in agitator tank stirring;
4) it is proportionally added in agitator tank stirring by pigment, wood flour and other inserts;
5) adding foaming agent according to density requirements, stir, preparation completes.
The present invention also provides for a kind of non-woven fabrics board machining process, comprises the following steps,
Concrete board making process:
1) PVC or ABS template is prepared;
2) mould oil of uniform brushing thin layer in template;
3) prime cement starts to put down from blender, directly under in template, lay one layer of 9g/m2Non-woven fabrics 1, glass-fiber-fabric two
2 as lower nonwoven fabric layer and lower floor's glass layer of cloth;
4) dispensing of the middle bed of material 3 is lowered on the good glass-fiber-fabric of roll-in 22, adjusts between middle material pressure roller and template
Distance i.e. sheet metal thickness, the bed of material 3 in laying again by roll-in mode;During 1 layer of glass-fiber-fabric 1 is passed through while laying by middle material
Material pressure roller is together with middle bed of material roll-in;
5) by non-woven fabrics 5 roll-in on glass-fiber-fabric 1;
6) after laying, after cutting, enter cage car, push curing room and carry out maintenance;
7) care environments temperature is at about 30 DEG C;Maintenance 14 hours afterwards can the demoulding;
8) after the demoulding, sheet material keeps flat and carries out secondary temperature elevation, ensures that sheet material board body temperature is less than 50 in temperature-rise period
℃;Riser cooling to be carried out when arriving marginal value, must take blowing mode to lower the temperature if desired;
9) after riser is rested 6 days, when detecting its moisture content to less than 10%, i.e. cut, pack after terminating.
Embodiment 3
As it can be seen, this enforcement processing nonwoven fabrics plate structure, including middle material 3, the top of described middle material (3) sequentially sets
There are glass-fiber-fabric 1 and non-woven fabrics 5;Sequentially glass-fiber-fabric 22 and 9g/m, the lower section of middle material 32Non-woven fabrics 1;
The formula of described middle material 3 is:
Light calcined magnesia: 100 parts;
Magnesium sulfate heptahydrate: 80 parts;
Water: 100 parts;
Wood flour: 60 parts;
Other inserts: 40 parts;
Modifying agent: 5 parts;
Pigment: 10 parts;
Other inserts are one or more in perlite, gangue, flyash, quartz sand, rice husk, straw.
Pigment is the one in iron oxide yellow, iron oxide red, iron oxide green, iron oxide blue, carbon black.
The preparation technology of middle material 6 is as follows:
1) Magnesium sulfate heptahydrate and water are added together in proportion it are stirred, until Magnesium sulfate heptahydrate is completely dissolved;
2) it is proportionally added in agitator tank stirring by Magnesium sulfate heptahydrate solution and modifying agent;
3) it is proportionally added into light calcined magnesia in agitator tank stirring;
4) it is proportionally added in agitator tank stirring by pigment, wood flour and other inserts;
5) adding foaming agent according to density requirements, stir, preparation completes.
The present invention also provides for a kind of non-woven fabrics board machining process, comprises the following steps,
Concrete board making process:
1) PVC or ABS template is prepared;
2) mould oil of uniform brushing thin layer in template;
3) one layer of 9g/m is laid2Non-woven fabrics 1, glass-fiber-fabric 22 are as lower nonwoven fabric layer and lower floor's glass layer of cloth;
4) dispensing of the middle bed of material 3 is lowered on the good glass-fiber-fabric of roll-in 22, adjusts between middle material pressure roller and template
Distance i.e. sheet metal thickness, the bed of material 3 in laying again by roll-in mode;During 1 layer of glass-fiber-fabric 1 is passed through while laying by middle material
Material pressure roller is together with middle bed of material roll-in;
5) by non-woven fabrics 5 roll-in on glass-fiber-fabric 1;
6) after laying, after cutting, enter cage car, push curing room and carry out maintenance;
7) care environments temperature is at about 35 DEG C;Maintenance 16 hours afterwards can the demoulding;
8) after the demoulding, sheet material keeps flat and carries out secondary temperature elevation, ensures that sheet material board body temperature is less than 50 in temperature-rise period
℃;Riser cooling to be carried out when arriving marginal value, must take blowing mode to lower the temperature if desired;
9) after riser is rested 7 days, when detecting its moisture content to less than 10%, i.e. cut, pack after terminating.
Claims (7)
1. non-woven fabrics plate structure, including middle material (3), it is characterised in that: the top of described middle material (3) is sequentially provided with glass-fiber-fabric
One (4) and non-woven fabrics (5);The lower section of middle material (3) sequentially glass-fiber-fabric two (2) and 9g/m2Non-woven fabrics (1);
The formula of described middle material (3) is:
Light calcined magnesia: 100 parts;
Magnesium sulfate heptahydrate: 40-80 part;
Water: 60-100 part;
Wood flour: 20-60 part;
Other inserts: 4-40 part;
Modifying agent: 1-5 part;
Pigment: 1-10 part.
Non-woven fabrics plate structure the most according to claim 1, it is characterised in that: other inserts described are perlite, bastard coal
One or more in stone, flyash, quartz sand, rice husk, straw.
Non-woven fabrics plate structure the most according to claim 1, it is characterised in that: described pigment be iron oxide yellow, iron oxide red,
One in iron oxide green, iron oxide blue, carbon black.
4. according to the non-woven fabrics plate structure described in any one in claim 1-3, it is characterised in that: described 9g/m2Non-woven fabrics
(1) being provided with bottom pulp layer further below, after adding bottom pulp layer, plate surface is more attractive in appearance, can increase and decrease according to customer requirement.
Non-woven fabrics plate structure the most according to claim 4, it is characterised in that: the formula of described bottom pulp layer is
Light calcined magnesia: 100 parts;
Magnesium chloride: 50-80 part;
Water: 40-70 part;
Pulvis Talci: 30-70 part;
Latex powder: 5-10 part;
Modifying agent: 3-6 part;
Pigment 2-10 part;
The preparation technology of described bottom pulp layer is as follows:
1) magnesium chloride and water are added together in proportion it are stirred, until magnesium chloride is completely dissolved;
2) it is proportionally added in agitator tank stirring by magnesium chloride solution and modifying agent;
3) being proportionally added in agitator tank stirring by pigment, light calcined magnesia, Pulvis Talci and latex powder, preparation completes.
Non-woven fabrics plate structure the most according to claim 1, it is characterised in that: the preparation technology of described middle material (6) is as follows:
1) Magnesium sulfate heptahydrate and water are added together in proportion it are stirred, until Magnesium sulfate heptahydrate is completely dissolved;
2) it is proportionally added in agitator tank stirring by Magnesium sulfate heptahydrate solution and modifying agent;
3) it is proportionally added into light calcined magnesia in agitator tank stirring;
4) it is proportionally added in agitator tank stirring by pigment, wood flour and other inserts;
5) adding foaming agent according to density requirements, stir, preparation completes.
7. non-woven fabrics board machining process, it is characterised in that: comprise the following steps,
Concrete board making process:
1) PVC or ABS template is prepared;
2) mould oil of uniform brushing thin layer in template;
3) one layer of 9g/m is laid2Non-woven fabrics (1), glass-fiber-fabric two (2) are as lower nonwoven fabric layer and lower floor's glass layer of cloth;
4) dispensing of the middle bed of material (3) is lowered on the good glass-fiber-fabric of roll-in two (2), adjusts between middle material pressure roller and template
Distance i.e. sheet metal thickness, the bed of material (3) in laying again by roll-in mode;By 1 layer of glass-fiber-fabric one (4) while the laying of middle material
By middle material pressure roller together with middle bed of material roll-in;
5) by non-woven fabrics (5) roll-in on glass-fiber-fabric one (4);
6) after laying, after cutting, enter cage car, push curing room and carry out maintenance;
7) care environments temperature is at about 20-40 DEG C;Maintenance 12-16 hour afterwards can the demoulding;
8) after the demoulding, sheet material keeps flat and carries out secondary temperature elevation, ensures that sheet material board body temperature is less than 50 DEG C in temperature-rise period;Arrive
Reach riser cooling to be carried out during marginal value, blowing mode must be taked if desired to lower the temperature;
9) after riser is rested 5-7 days, when detecting its moisture content to less than 10%, i.e. cut, pack after terminating.