CN106193485A - A kind of building wall exempts from cracking resistance technique of plastering - Google Patents
A kind of building wall exempts from cracking resistance technique of plastering Download PDFInfo
- Publication number
- CN106193485A CN106193485A CN201610579432.1A CN201610579432A CN106193485A CN 106193485 A CN106193485 A CN 106193485A CN 201610579432 A CN201610579432 A CN 201610579432A CN 106193485 A CN106193485 A CN 106193485A
- Authority
- CN
- China
- Prior art keywords
- layer
- building
- coated
- plastering
- crack mastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of building wall exempts from cracking resistance technique of plastering, it is characterized in that, this technique be at the inner corner trim and external corner of building, block wall, concrete be respectively adopted different construction technologies from masonry seam crossing, in building inner corner trim (1) with external corner (2) outward, bottom anti-crack mastic layer (3) pastes angle respectively internal corner strip (4) and the external corner strip (5) that cross section is L-type is installed, be coated with outside internal corner strip and external corner strip and scrape top layer levelling anti-crack mastic layer (6)；The block wall that building block (7) is built by laying bricks or stones is coated with and scrapes jointing anti-crack mastic (11), be coated with successively on overall metope afterwards and scrape bottom anti-crack mastic layer (3) and top layer levelling anti-crack mastic layer (6)；The concrete (12) metope with building block (7) joint is directly coated with and scrapes the high-elastic putty layer of bottom (13), afterwards alkali resistant grid cloth (14) is pressed into the high-elastic putty layer of bottom, then scrapes the high-elastic putty layer in top layer (15) in the outer topcoating of alkali resistant grid cloth.The present invention can effectively solve described house wall surface quality problems.
Description
Technical field
The invention belongs to building wall construction technology technical field.
Background technology
Building engineering construction hands over room increasingly to trend towards paying well-decorated house at present, is constructing and is handing in room often due to room
The metope quality problems in room cause checking and accepting defective and handing over room difficulty.Owing to the metope of existing building is all to use manually to smear
Ash completes, and this coat of plaster is due to material and the deficiency of construction technology, and mass defect is more, such as the inner corner trim of metope, external corner not
Straight the most upright or external corner is damaged, inner corner trim cracking, metope occur hollowing, ftracture, come off, surface irregularity etc., concrete connects with masonry
Metope at seam is cracking, come off, and these quality problems are the most controversial, not only affects completion of works and checks and accepts, also shadow
Ring and use and sense organ.
Summary of the invention
The purpose of the present invention aims to solve the problem that the deficiencies in the prior art, it is provided that one can effectively solve described house wall surface quality
The building wall of problem exempts from cracking resistance technique of plastering.
For achieving the above object, the technical solution used in the present invention is as follows:
A kind of building wall exempts from cracking resistance technique of plastering, this technique be at the inner corner trim and external corner of building, block wall,
Concrete is respectively adopted different construction technologies from masonry seam crossing, specific as follows:
A. in building inner corner trim and outside external corner, scrape on the bottom anti-crack mastic layer on metope being coated with, respectively patch angle peace
Dress cross section is the internal corner strip of L-type and cross section is the external corner strip of L-type, is coated with and scrapes the levelling cracking resistance in top layer outside internal corner strip and external corner strip
Putty layer；
B. it is coated with on the block wall formed after concrete block masonry and scrapes jointing anti-crack mastic, be coated with successively on overall metope afterwards
Scrape bottom anti-crack mastic layer and top layer levelling anti-crack mastic layer；
C. directly it is coated with on the concrete metope with building block joint and scrapes the high-elastic putty layer of bottom, afterwards alkali resistant grid cloth is pressed into
The high-elastic putty layer of bottom, then scrape the high-elastic putty layer in top layer in the outer topcoating of alkali resistant grid cloth.
Internal corner strip described in present invention process and external corner strip use high density polyethylene (HDPE) to manufacture.Described building block is steam pressurized mixed
Solidifying earth building blocks.The specification of described alkali resistant grid cloth is 5 × 5mm, and width is 300mm.On the levelling anti-crack mastic layer of top layer or table
Finish coat is coated in floor height bullet putty layer.
Using present invention process, workmen is when carrying out wall covering construction, and the metope for different parts uses not
Same construction technology.One is to be installed on the inner corner trim of building entity, external corner, internal corner strip, external corner strip in conjunction with manufacturing internal corner strip
Preferable tension, bending resistance, resistance to compression and the impact resistance being had with the high density polyethylene (HDPE) of external corner strip, and stronger acidproof
Caustic corrosion ability, can effectively solve inner corner trim, external corner the most straight, the quality problems such as lines bending, allows inner corner trim, external corner be straight, line
Bar is straight.And when accidentally colliding external corner after being conducive in other follow-up finishings or coming into operation, can effectively reduce brokenly
Damage, reach the purpose of finished product protection.Owing to the inner corner trim of building mostly is in the formation of bi-material junction, (such as concrete and building block are even
Meet place), easily ftractureing in this position, utilizes it elastic after application internal corner strip, problem that is that can effectively solve inner corner trim cracking.Two is to get rid of
Abandon the block wall coat of plaster of prior art, be directly coated with on masonry surface and scrape anti-crack mastic, use anti-crack mastic order to build
Surface jointing and local are made up a deficiency, are coated with and scrape bottom anti-crack mastic layer, top layer levelling anti-crack mastic layer, use " double faced adhesive tape " mechanism,
Realize bonding interface and surface is levelling.Owing to anti-crack mastic granule is trickle, under dampness, there is the plasticity of superelevation, can be very
Good and autoclave aerated concrete building block engages, and forms an entirety, its surface again can good bonding surface layer, have two-way
Affinity and levelling ability, can be prevented effectively from the generation of hollowing, cracking, obscission, efficiently solves asking of existing coat of plaster
Topic, just can carry out the construction of finish coat after 72 hours.Three is to use high-elastic putty to be directly coated with the wall scraped at concrete Yu building block seam crossing
On face, and special press-in alkali resistant grid cloth in the middle of high-elastic putty layer, form cracking resistance reinforcing strip.Owing to high-elastic putty has superpower
Anti-cracking performance, can overcome the disadvantages that because building shrinks uneven and features such as the irregular Dynamic Crack that produces, be equipped with grid cloth
Can resist and alleviate the generation of structural cracks, use the flexible break resistant scheme of " flexible gradual change successively discharges stress ", high-elastic greasy
Son and alkali resistant grid cloth are integrated, and form cracking resistance reinforcing strip, efficiently solve concrete and the quality problems of building block seam crossing cracking.
Present invention process, for the construction features of building wall different parts, uses different construction works targetedly
Skill, scientific and reasonable, can effectively solve house wall surface quality problems.
Accompanying drawing explanation
Fig. 1 is the process structure schematic diagram at building inner corner trim and external corner；
Fig. 2 is the process structure schematic diagram on block wall；
Fig. 3 is the process structure schematic diagram at concrete Yu building block joint.
Detailed description of the invention
Below in conjunction with the accompanying drawings and present invention process is further elaborated by embodiment.
A kind of building wall exempts from cracking resistance technique of plastering, this technique be at the inner corner trim and external corner of building, block wall,
Concrete is respectively adopted different construction technologies from masonry seam crossing.
Building wall as shown in Figure 1 exempts from straight negative and positive corner structure of plastering, and is in the inner corner trim 1 of building and external corner 2
Outward, scraping on the bottom anti-crack mastic layer 3 on metope being coated with, patch angle is provided with internal corner strip 4 that cross section is L-type and transversal respectively
Face is the external corner strip 5 of L-type, and top layer levelling anti-crack mastic layer 6 is coated outside internal corner strip 4 and external corner strip 5.Internal corner strip and external corner strip
Employing high density polyethylene (HDPE) is manufactured.
Construction procedure is as follows:
A. being coated with by ready anti-crack mastic first pass scrapes on the metope that building block 7, concrete 8 are built into, and forms wall surface bottom layer
Anti-crack mastic layer 3；
B. internal corner strip 4 is fixed on building block 7 with putty and in inner corner trim that concrete 8 is constituted, internal corner strip patch angle is installed, its right angle with
Inner corner trim is in the same direction；Being fixed with putty by external corner strip 5, and paste angle and be wrapped in outside external corner, its right angle is with external corner in the same direction；
C. carry out inner corner trim, the repairing of external corner and putty according to the location of internal corner strip, external corner strip to make up a deficiency, at internal corner strip 4 and sun
The outer painting of angle bead 5 scrapes top layer levelling anti-crack mastic layer 6；
D. polishing spary finish coat 9 can just be carried out after requiring to have carried out putty construction according to construction drawing.
According to the actual requirements, can repaste outside top layer levelling anti-crack mastic layer 6 and scrape third layer anti-crack mastic layer 10, also
It is exactly at internal corner strip 4 and external corner strip 5 outer painting two-layer anti-crack mastic layer.
Cracking resistance as shown in Figure 2 and anti-hollowing exempt from block wall structure of plastering, be primarily adapted for use in steam-pressing aero-concrete
Building block 7 is built by laying bricks or stones on the large area metope of formation, is included on autoclave aerated concrete building block metope local and makes up a deficiency the jointing that painting is scraped
Anti-crack mastic 11, it is coated with, on overall metope, bottom anti-crack mastic layer 3 and top layer levelling anti-crack mastic layer 6 basis scraped successively afterwards
Construction requirement, also can be coated with on top layer levelling anti-crack mastic layer 6 and scrape finish coat 9.
The body of wall of concrete as shown in Figure 3 and masonry seam crossing exempts from cracking structure of plastering, and is included in concrete 12 and masonry 7 joint
Metope on be directly coated with scrape the high-elastic putty layer of bottom 13, the alkali resistant grid cloth 14 of the press-in high-elastic putty layer of bottom, be coated with and scrape anti-
The high-elastic putty layer in top layer 15 outside alkali grid cloth.The specification of alkali resistant grid cloth 14 determines according to practice of construction situation, typically selects
Select specification 5 × 5mm, the grid cloth of width 300mm.According to construction requirement, can be coated with in the high-elastic putty layer in top layer 15 and scrape finish coat
9.After the high-elastic putty layer in top layer is coated with and has scraped 48 hours, generally just can carry out the construction of finish coat.
The most various anti-crack mastic of various materials used by the present invention, high-elastic putty, high density polyethylene (HDPE), alkali resistant grid cloth,
Autoclave aerated concrete building blocks etc. all can use existing building construction material, directly can purchase from market.It is cheap, it is easy to
Buy.Constructing operation of the present invention is easy, can reduce wet trade, saves labour force, saves duration and management cost, can effectively promote
Construction quality.
Claims (6)
1. a building wall exempts from cracking resistance technique of plastering, it is characterised in that this technique be at the inner corner trim and external corner of building,
Block wall, concrete are respectively adopted different construction technologies from masonry seam crossing, specific as follows:
A. in building inner corner trim (1) with external corner (2) outward, scrape on bottom anti-crack mastic layer (3) on metope being coated with, paste respectively
The internal corner strip (4) and external corner strip (5) that cross section is L-type that cross section is L-type is installed at angle, at internal corner strip (4) and external corner strip (5) outward
Top layer levelling anti-crack mastic layer (6) is scraped in painting；
B. it is coated with on the block wall formed after building block (7) is built by laying bricks or stones and scrapes jointing anti-crack mastic (11), depend on overall metope afterwards
Bottom anti-crack mastic layer (3) and top layer levelling anti-crack mastic layer (6) are scraped in secondary painting；
C. directly it is coated with on the concrete (12) metope with building block (7) joint and scrapes the high-elastic putty layer of bottom (13), afterwards by alkali resistant net
Ge Bu (14) is pressed into the high-elastic putty layer of bottom, then scrapes the high-elastic putty layer in top layer (15) in the outer topcoating of alkali resistant grid cloth.
A kind of building wall the most according to claim 1 exempts from cracking resistance technique of plastering, it is characterised in that described internal corner strip and
External corner strip uses high density polyethylene (HDPE) to manufacture.
A kind of building wall the most according to claim 1 exempts from cracking resistance technique of plastering, it is characterised in that levelling anti-on top layer
Finish coat (9) is coated on crack putty layer (6).
4. exempt from, according to a kind of building wall described in claim 1 or 3, cracking resistance technique of plastering, it is characterised in that described building block
(7) it is autoclave aerated concrete building block.
A kind of building wall the most according to claim 1 exempts from cracking resistance technique of plastering, it is characterised in that described alkali resistant grid
The specification of cloth (14) is 5 × 5mm, and width is 300mm.
The most according to claim 1 or 5, a kind of building wall exempts from cracking resistance technique of plastering, it is characterised in that high on top layer
Play and finish coat (9) is coated in putty layer (15).