CN106167416A - 一种利用污泥的新型环保陶瓷材料 - Google Patents

一种利用污泥的新型环保陶瓷材料 Download PDF

Info

Publication number
CN106167416A
CN106167416A CN201610545127.0A CN201610545127A CN106167416A CN 106167416 A CN106167416 A CN 106167416A CN 201610545127 A CN201610545127 A CN 201610545127A CN 106167416 A CN106167416 A CN 106167416A
Authority
CN
China
Prior art keywords
parts
water
environmental protection
building block
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610545127.0A
Other languages
English (en)
Inventor
戚海冰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Province Nanning City Guierchuang Environmental Protection Technology Co Ltd
Original Assignee
Guangxi Province Nanning City Guierchuang Environmental Protection Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Province Nanning City Guierchuang Environmental Protection Technology Co Ltd filed Critical Guangxi Province Nanning City Guierchuang Environmental Protection Technology Co Ltd
Priority to CN201610545127.0A priority Critical patent/CN106167416A/zh
Publication of CN106167416A publication Critical patent/CN106167416A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种利用污泥的新型环保陶瓷材料，以重量份为单位，包括以下原料：干污泥48‑86份、农作物秸秆38‑50份、冰晶石12‑24份、方解石10‑22份、高岭土10‑16份、氧化锂8‑12份、氧化锡6‑10份、氧化钨6‑12份、二氧化铝4‑6份、玻璃纤维2‑3份、减水剂2‑3份、发泡剂0.6‑1.2份、发泡调节剂0.4‑1份、催化剂0.4‑0.6份、交联剂0.4‑0.6份、稳泡剂0.2‑0.4份、双氧水30‑40份、水380‑480份。本发明为污泥废料、农作物秸秆开辟了利用的领域，有效降低本制作陶瓷成本、节约能源消耗，实现了变废为宝。

Description

一种利用污泥的新型环保陶瓷材料
技术领域
本发明属于陶瓷材料制备技术领域，具体涉及一种利用污泥的新型环保陶瓷材料。
背景技术
长期以来陶瓷器皿深受广大人民群众所喜欢，他们具有很多优点：第一、热稳定性好，传热慢；第二、化学稳定性好；第三、易于洗涤和保持洁净；第四、吸水率低。目前，陶瓷产品的价格较高，制作陶瓷的原料也比较缺乏，需要寻找新的原料。
在我们的社会上又另外存在着一种大量增加着的还没有得到有效利用的废料—污泥，据2010年发布的“第一次全国污染源普查公报”指出：我国污水处理厂污水年实际处理量为210.31亿吨，“十一五”期间，我国新增污水处理能力超过5000万吨每日，全国污水处理率由2005年的52%提高到75%以上。目前我国每年产生的干污泥为900万吨，并且每年以10%以上的速度递增。虽然污泥是较好的农业肥料，其中氮、磷、钾含量远高于农家肥，但污泥还有寄生虫，病菌等，臭味问题尤其突出，如果用污泥肥田肥林，农民无法忍受其气味，不愿意接受。况且农业生产有季节性，污泥堆肥受到季节和销售半径的明显影响，即使没有臭味等问题农林业利用也无法全部消纳城市产出的污泥。所以到现在以上还没有给污泥找到出路，仍然处于废料的地位，在2011年3月28日得科技日报上发表了“污水处理了，污泥咋办？”的文章，呼吁社会各界来关心污泥处理的问题，摆在我们面前的问题是如何将污泥在陶瓷上得到利用。
发明内容
本发明要解决的技术问题是提供一种利用污泥的新型环保陶瓷材料，以解决现有陶瓷产品价格较高，制作陶瓷的原料也比较缺乏；以及污泥如何有效利用等问题。采用本发明的利用污泥的新型环保陶瓷材料制成的陶瓷击穿强度好；本发明为污泥废料、农作物秸秆开辟了利用的领域，有效降低本制作陶瓷成本、节约能源消耗，实现了变废为宝。
为了解决以上技术问题，本发明采用以下技术方案：
一种利用污泥的新型环保陶瓷材料，以重量份为单位，包括以下原料：干污泥48-86份、农作物秸秆38-50份、冰晶石12-24份、方解石10-22份、高岭土10-16份、氧化锂8-12份、氧化锡6-10份、氧化钨6-12份、二氧化铝4-6份、玻璃纤维2-3份、减水剂2-3份、发泡剂0.6-1.2份、发泡调节剂0.4-1份、催化剂0.4-0.6份、交联剂0.4-0.6份、稳泡剂0.2-0.4份、双氧水30-40份、水380-480份。上述原料中的污泥可以是生活污水处理中得到的污泥，也可以是工业污水处理中得到的污泥或者生活和工业混合污水处理中得到的污泥，污泥中含有机物和重金属，污泥需要通过预处理，即除水，除臭，除有机物和分离重金属。
所述利用污泥的新型环保陶瓷材料的制备方法，包括以下步骤：
S1：将干污泥、农作物秸秆、冰晶石、方解石、高岭土、氧化锂、氧化锡、氧化钨、二氧化铝、玻璃纤维放入粉碎机中，在转速为400-800r/min下粉碎2-3h，制得复合粉体；
S2：将步骤S1制得的复合粉体放入球磨机中，在转速为500-600r/min下球磨处理1-2h后过200-300目筛子，制得粉末；
S3：将步骤S2制得的粉末和减水剂、发泡剂、发泡调节剂、催化剂、交联剂、稳泡剂、双氧水、水在温度为，转速为100-120r/min下搅拌4-5h，制得浆料；
S4：将步骤S3制得的浆料在真空度为0.85-0.95下，抽真空15-20min，制得毛坯件；
S5：将步骤S4制得的毛坯件在60-70℃下进行微波处理，处理时间为10-20min，随后在1250-1300℃下进行烧结，烧结时间为20-25h，制得利用污泥的新型环保陶瓷材料。
进一步地，所述干污泥的含水量≤10%。
进一步地，所述农作物秸秆粉末的粒径≤300μm，水分含量≤14%。
进一步地，所述农作物包括玉米、水稻中的一种或多种。
进一步地，所述减水剂为聚羧酸减水剂。
进一步地，所述发泡剂为偶氮二甲酰胺。
进一步地，所述发泡调节剂为丙烯酸酯类发泡调节剂。
进一步地，所述催化剂包括辛酸亚锡、三乙烯二胺·六水中的一种或两种。
进一步地，所述交联剂为过氧化二异丙苯。
进一步地，所述稳泡剂为硅酮酰胺。
本发明具有以下有益效果：
（1）本发明为污泥废料、农作物秸秆开辟了利用的领域，有效降低本制作陶瓷成本、节约能源消耗，实现了变废为宝；
（2）创造了经济价值，使原来一文不值的废物变成了陶瓷的重要材料；
（3）采用本发明的利用污泥的新型环保陶瓷材料制成的陶瓷击穿强度为6.52-6.56KV/mm，具备良好抗冲击能力，其他性能也良好。
具体实施方式
为便于更好地理解本发明，通过以下实例加以说明，这些实例属于本发明的保护范围，但不限制本发明的保护范围。
在实施例中，所述利用污泥的新型环保陶瓷材料，以重量份为单位，包括以下原料：干污泥48-86份、农作物秸秆38-50份、冰晶石12-24份、方解石10-22份、高岭土10-16份、氧化锂8-12份、氧化锡6-10份、氧化钨6-12份、二氧化铝4-6份、玻璃纤维2-3份、减水剂2-3份、发泡剂0.6-1.2份、发泡调节剂0.4-1份、催化剂0.4-0.6份、交联剂0.4-0.6份、稳泡剂0.2-0.4份、双氧水30-40份、水380-480份。
所述干污泥的含水量≤10%。
所述农作物秸秆粉末的粒径≤300μm，水分含量≤14%。
所述农作物包括玉米、水稻中的一种或多种。
所述减水剂为聚羧酸减水剂。
所述发泡剂为偶氮二甲酰胺。
所述发泡调节剂为丙烯酸酯类发泡调节剂。
所述催化剂包括辛酸亚锡、三乙烯二胺·六水中的一种或两种。
所述交联剂为过氧化二异丙苯。
所述稳泡剂为硅酮酰胺。
所述利用污泥的新型环保陶瓷材料的制备方法，包括以下步骤：
S1：将干污泥、农作物秸秆、冰晶石、方解石、高岭土、氧化锂、氧化锡、氧化钨、二氧化铝、玻璃纤维放入粉碎机中，在转速为400-800r/min下粉碎2-3h，制得复合粉体；
S2：将步骤S1制得的复合粉体放入球磨机中，在转速为500-600r/min下球磨处理1-2h后过200-300目筛子，制得粉末；
S3：将步骤S2制得的粉末和减水剂、发泡剂、发泡调节剂、催化剂、交联剂、稳泡剂、双氧水、水在温度为，转速为100-120r/min下搅拌4-5h，制得浆料；
S4：将步骤S3制得的浆料在真空度为0.85-0.95下，抽真空15-20min，制得毛坯件；
S5：将步骤S4制得的毛坯件在60-70℃下进行微波处理，处理时间为10-20min，随后在1250-1300℃下进行烧结，烧结时间为20-25h，制得利用污泥的新型环保陶瓷材料。
下面通过更具体实施例对本发明进行说明。
实施例1
一种利用污泥的新型环保陶瓷材料，以重量份为单位，包括以下原料：干污泥66份、农作物秸秆43份、冰晶石18份、方解石16份、高岭土14份、氧化锂10份、氧化锡8份、氧化钨8份、二氧化铝5份、玻璃纤维3份、减水剂3份、发泡剂0.9份、发泡调节剂0.8份、催化剂0.5份、交联剂0.5份、稳泡剂0.3份、双氧水35份、水450份。
所述干污泥的含水量为10%。
所述农作物秸秆粉末的粒径≤300μm，水分含量≤14%，所述农作物为玉米。
所述减水剂为聚羧酸减水剂。
所述发泡剂为偶氮二甲酰胺。
所述发泡调节剂为丙烯酸酯类发泡调节剂。
所述催化剂为辛酸亚锡。
所述交联剂为过氧化二异丙苯。
所述稳泡剂为硅酮酰胺。
所述利用污泥的新型环保陶瓷材料的制备方法，包括以下步骤：
S1：将干污泥、农作物秸秆、冰晶石、方解石、高岭土、氧化锂、氧化锡、氧化钨、二氧化铝、玻璃纤维放入粉碎机中，在转速为600r/min下粉碎2.5h，制得复合粉体；
S2：将步骤S1制得的复合粉体放入球磨机中，在转速为550r/min下球磨处理1.5h后过250目筛子，制得粉末；
S3：将步骤S2制得的粉末和减水剂、发泡剂、发泡调节剂、催化剂、交联剂、稳泡剂、双氧水、水在温度为，转速为120r/min下搅拌4h，制得浆料；
S4：将步骤S3制得的浆料在真空度为0.9下，抽真空18min，制得毛坯件；
S5：将步骤S4制得的毛坯件在65℃下进行微波处理，处理时间为15min，随后在1280℃下进行烧结，烧结时间为23h，制得利用污泥的新型环保陶瓷材料。
实施例2
一种利用污泥的新型环保陶瓷材料，以重量份为单位，包括以下原料：干污泥48份、农作物秸秆38份、冰晶石12份、方解石10份、高岭土10份、氧化锂8份、氧化锡6份、氧化钨6份、二氧化铝4份、玻璃纤维2份、减水剂2份、发泡剂0.6份、发泡调节剂0.4份、催化剂0.4份、交联剂0.4份、稳泡剂0.2份、双氧水30份、水380份。
所述干污泥的含水量为7%。
所述农作物秸秆粉末的粒径≤300μm，水分含量≤14%，所述农作物为水稻。
所述减水剂为聚羧酸减水剂。
所述发泡剂为偶氮二甲酰胺。
所述发泡调节剂为丙烯酸酯类发泡调节剂。
所述催化剂为三乙烯二胺·六水。
所述交联剂为过氧化二异丙苯。
所述稳泡剂为硅酮酰胺。
所述利用污泥的新型环保陶瓷材料的制备方法，包括以下步骤：
S1：将干污泥、农作物秸秆、冰晶石、方解石、高岭土、氧化锂、氧化锡、氧化钨、二氧化铝、玻璃纤维放入粉碎机中，在转速为400r/min下粉碎3h，制得复合粉体；
S2：将步骤S1制得的复合粉体放入球磨机中，在转速为500r/min下球磨处理2h后过200目筛子，制得粉末；
S3：将步骤S2制得的粉末和减水剂、发泡剂、发泡调节剂、催化剂、交联剂、稳泡剂、双氧水、水在温度为，转速为100r/min下搅拌5h，制得浆料；
S4：将步骤S3制得的浆料在真空度为0.85下，抽真空20min，制得毛坯件；
S5：将步骤S4制得的毛坯件在60℃下进行微波处理，处理时间为20min，随后在1250℃下进行烧结，烧结时间为25h，制得利用污泥的新型环保陶瓷材料。
实施例3
一种利用污泥的新型环保陶瓷材料，以重量份为单位，包括以下原料：干污泥86份、农作物秸秆50份、冰晶石24份、方解石22份、高岭土16份、氧化锂12份、氧化锡10份、氧化钨12份、二氧化铝6份、玻璃纤维3份、减水剂3份、发泡剂1.2份、发泡调节剂1份、催化剂0.6份、交联剂0.6份、稳泡剂0.4份、双氧水40份、水480份。
所述干污泥的含水量为6%。
所述农作物秸秆粉末的粒径≤300μm，水分含量≤14%，所述农作物为玉米、水稻。
所述减水剂为聚羧酸减水剂。
所述发泡剂为偶氮二甲酰胺。
所述发泡调节剂为丙烯酸酯类发泡调节剂。
所述催化剂为辛酸亚锡、三乙烯二胺·六水。
所述交联剂为过氧化二异丙苯。
所述稳泡剂为硅酮酰胺。
所述利用污泥的新型环保陶瓷材料的制备方法，包括以下步骤：
S1：将干污泥、农作物秸秆、冰晶石、方解石、高岭土、氧化锂、氧化锡、氧化钨、二氧化铝、玻璃纤维放入粉碎机中，在转速为800r/min下粉碎2h，制得复合粉体；
S2：将步骤S1制得的复合粉体放入球磨机中，在转速为600r/min下球磨处理1h后过300目筛子，制得粉末；
S3：将步骤S2制得的粉末和减水剂、发泡剂、发泡调节剂、催化剂、交联剂、稳泡剂、双氧水、水在温度为，转速为120r/min下搅拌4h，制得浆料；
S4：将步骤S3制得的浆料在真空度为0.95下，抽真空15min，制得毛坯件；
S5：将步骤S4制得的毛坯件在70℃下进行微波处理，处理时间为10min，随后在1300℃下进行烧结，烧结时间为20h，制得利用污泥的新型环保陶瓷材料。
采用实施例1-3的利用污泥的新型环保陶瓷材料制作陶瓷并进行性能检测，结果如下表所示：
实施例 密度，g/cm3 熔点，℃ 介电常数 击穿强度，KV/mm
1 3.87 2045 9.76 6.54
2 3.83 2041 9.74 6.52
3 3.85 2054 9.75 6.56
由上表可知，由本发明实施例1-3的利用污泥的新型环保陶瓷材料制成的陶瓷击穿强度为6.52-6.56KV/mm，具备良好抗冲击能力，同时其他性能也良好。
以上内容不能认定本发明的具体实施只局限于这些说明，对于本发明所属技术领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干简单推演或替换，都应当视为属于本发明由所提交的权利要求书确定的专利保护范围。

Claims (10)

1.一种利用污泥的新型环保陶瓷材料，其特征在于，以重量份为单位，包括以下原料：干污泥48-86份、农作物秸秆38-50份、冰晶石12-24份、方解石10-22份、高岭土10-16份、氧化锂8-12份、氧化锡6-10份、氧化钨6-12份、二氧化铝4-6份、玻璃纤维2-3份、减水剂2-3份、发泡剂0.6-1.2份、发泡调节剂0.4-1份、催化剂0.4-0.6份、交联剂0.4-0.6份、稳泡剂0.2-0.4份、双氧水30-40份、水380-480份；
所述利用污泥的新型环保陶瓷材料的制备方法，包括以下步骤：
S1：将干污泥、农作物秸秆、冰晶石、方解石、高岭土、氧化锂、氧化锡、氧化钨、二氧化铝、玻璃纤维放入粉碎机中，在转速为400-800r/min下粉碎2-3h，制得复合粉体；
S2：将步骤S1制得的复合粉体放入球磨机中，在转速为500-600r/min下球磨处理1-2h后过200-300目筛子，制得粉末；
S3：将步骤S2制得的粉末和减水剂、发泡剂、发泡调节剂、催化剂、交联剂、稳泡剂、双氧水、水在温度为，转速为100-120r/min下搅拌4-5h，制得浆料；
S4：将步骤S3制得的浆料在真空度为0.85-0.95下，抽真空15-20min，制得毛坯件；
S5：将步骤S4制得的毛坯件在60-70℃下进行微波处理，处理时间为10-20min，随后在1250-1300℃下进行烧结，烧结时间为20-25h，制得利用污泥的新型环保陶瓷材料。
2.根据权利要求1所述的用于制作环保砌块的材料，其特征在于，所述干污泥的含水量≤10%。
3.根据权利要求1所述的用于制作环保砌块的材料，其特征在于，所述农作物秸秆粉末的粒径≤300μm，水分含量≤14%。
4.根据权利要求3所述的用于制作环保砌块的材料，其特征在于，所述农作物包括玉米、水稻中的一种或多种。
5.根据权利要求1所述的用于制作环保砌块的材料，其特征在于，所述减水剂为聚羧酸减水剂。
6.根据权利要求1所述的用于制作环保砌块的材料，其特征在于，所述发泡剂为偶氮二甲酰胺。
7.根据权利要求1所述的用于制作环保砌块的材料，其特征在于，所述发泡调节剂为丙烯酸酯类发泡调节剂。
8.根据权利要求1所述的用于制作环保砌块的材料，其特征在于，所述催化剂包括辛酸亚锡、三乙烯二胺·六水中的一种或两种。
9.根据权利要求1所述的用于制作环保砌块的材料，其特征在于，所述交联剂为过氧化二异丙苯。
10.根据权利要求1所述的用于制作环保砌块的材料，其特征在于，所述稳泡剂为硅酮酰胺。
CN201610545127.0A 2016-07-12 2016-07-12 一种利用污泥的新型环保陶瓷材料 Pending CN106167416A (zh)