CN106147494A - Copper sculpture epoxy acrylic anticorrosion water-soluble paint and preparation method thereof in a kind of purification air chamber - Google Patents
Copper sculpture epoxy acrylic anticorrosion water-soluble paint and preparation method thereof in a kind of purification air chamber Download PDFInfo
- Publication number
- CN106147494A CN106147494A CN201610524519.9A CN201610524519A CN106147494A CN 106147494 A CN106147494 A CN 106147494A CN 201610524519 A CN201610524519 A CN 201610524519A CN 106147494 A CN106147494 A CN 106147494A
- Authority
- CN
- China
- Prior art keywords
- water
- air chamber
- copper sculpture
- soluble paint
- alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses copper sculpture epoxy acrylic anticorrosion water-soluble paint in a kind of purification air chamber, it is to be prepared by the raw material of following weight parts: epoxy resin E 44 40 60, ethylene glycol monobutyl ether 10 15, n-butyl alcohol 15 25, eucalyptus oil 0.1 0.15, Fructus Citri Limoniae oil 0.1 0.2, methacrylic acid 68, styrene 46, butyl acrylate 35, benzoyl peroxide 0.5 1, N, N diformyl ethanol 46, titania nanotube 46, nanometer germanium 0.1 0.15, nano-tourmaline powder 0.3 0.5, phenylpropyl alcohol triazole 0.3 0.5, γ mercaptopropyltriethoxysilane 0.1 0.15, sodium alginate 0.3 0.5, water 100 120.The copper sculpture water paint of the present invention had both had excellent Corrosion Protection, mechanical performance and lasting effectiveness, also has the effect purifying air, is conducive to improving indoor environmental quality.
Description
Technical field
The present invention relates to copper sculpture technical field of coatings, particularly relate to a kind of purify copper sculpture epoxy in air chamber-
Acrylic acid anticorrosion water-soluble paint and preparation method thereof.
Background technology
Along with modern life level and the raising of aesthetic consciousness, this traditional arts and crafts of sculpture is more and more designed
Teacher and masses like.Wherein copper sculpture not only pattern is unique, and has the highest enjoying value, with the sculpture phase of other materials
Ratio, feature the most sturdy and durable, survivable, it is widely used.Copper sculpture without M R continually, but
Under conditions of air humidity is excessive, use can have a strong impact on the quality of copper sculpture.For reducing corrosion, extend the use of copper sculpture
In the life-span, the preventive measure being usually taken is that copper sculpture surface carries out protective treatment, wherein brushing paint be currently used relatively
For extensive, economical and practical method.
Along with the enhancing of environmental consciousness, traditional solvent-borne corrosion resistant coating is gradually eliminated, high-performance, oligosaprobic water-repellent preservation
Paint has become as development trend.More aqueous anticorrosion paint is applied mainly to have epoxy resin etc. at present.Document " acrylic acid-grafted changes
Property epoxy resin anticorrosion emulsion research " use acrylic acid epoxy resin is carried out graft modification, the emulsion obtained has epoxy concurrently
Resin and the advantage of acrylic resin, have good adhesive force and decay resistance.But, this method prepares the three of emulsion
The dimension network structure degree of cross linking is relatively low, and resistance to water is not enough, and the protection to matrix surface is inadequate, have impact on its antiseptic property, and cannot
The anticorrosion persistency that reply painting defect or breakdown of coating bring declines, and is further improved the most in actual applications.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of crosslinking degree height, good mechanical property, prevent
Protect performance and by force and there is copper sculpture epoxy-acrylic anticorrosion water-soluble paint and preparation thereof in excellent persistent purification air chamber
Method.
The present invention is achieved by the following technical solutions:
Copper sculpture epoxy-acrylic anticorrosion water-soluble paint in a kind of purification air chamber, it is to be prepared by the raw material of following weight parts:
Epoxy resin E-44 40-60, ethylene glycol monobutyl ether 10-15, n-butyl alcohol 15-25, eucalyptus oil 0.1-0.15, Fructus Citri Limoniae oil
0.1-0.2, methacrylic acid 6-8, styrene 4-6, butyl acrylate 3-5, benzoyl peroxide 0.5-1, N, N-diformyl
Ethanol 4-6, titania nanotube 4-6, nanometer germanium 0.1-0.15, nano-tourmaline powder 0.3-0.5, phenylpropyl alcohol triazole 0.3-
0.5, gamma-mercaptopropyltriethoxysilane 0.1-0.15, sodium alginate 0.3-0.5, water 100-120;
Described titania nanotube is to use hydrothermal synthesis method to prepare, and caliber is 5-25nm, and pipe range is 500-1000nm.
A kind of purify the preparation method of copper sculpture epoxy-acrylic anticorrosion water-soluble paint in air chamber, comprise the following steps:
(1) titania nanotube is mixed with dehydrated alcohol by solid-liquid weight ratio 1:10-1:15 it is uniformly dispersed, be subsequently adding eucalyptus globulus
Leaf oil, Fructus Citri Limoniae oil, phenylpropyl alcohol triazole and gamma-mercaptopropyltriethoxysilane stirring 6-12h, do gained solid vacuum after being centrifuged
Dry, obtain Modified Titanium nanotube;
(2) by the Modified Titanium nanotube in (1), nanometer germanium, nano-tourmaline powder, N, the mixing dispersion of N-diformyl second alcohol and water
Uniformly, obtain component A, the mixing of epoxy resin E-44, ethylene glycol monobutyl ether and n-butyl alcohol is warming up to 105-110 DEG C, the most slowly
Dropping methacrylic acid, styrene, butyl acrylate and the mixed solution of benzoyl peroxide, and anti-in 115-120 DEG C of insulation
Answer 2-4h, obtain B component, by uniform in 80-85 DEG C of mixing high-speed stirred to component A and B component, then anti-in 50-60 DEG C of insulation
Answer 1-1.5h, obtain complex emulsions;
(3) grind uniformly after the complex emulsions in (2) being mixed with remaining raw material, copper sculpture ring in air chamber must be purified
Oxygen-acrylic acid anticorrosion water-soluble paint.
The invention have the advantage that
The present invention first with titania nanotube to eucalyptus oil, Fructus Citri Limoniae oil, phenylpropyl alcohol triazole and γ-mercapto propyl-triethoxysilicane
Alkane loads, and then carries out emulsion polymerization with epoxy resin and acrylate and obtains complex emulsions, can effectively promote
The tridimensional network crosslinking degree of film, promotes the barrier propterty to matrix, can improve again the mechanical performance of film and stablize
Property, and due to the load to composite corrosion inhibitor, the Copper substrate of paint film defect or breakage can be played good anticorrosion
Effect, improves the persistency of surfacecti proteon.Meanwhile, by remaining raw material add with compounding so as to get copper sculpture water paint
Comprehensive, lasting protection can be provided for matrix surface, have excellent Corrosion Protection, mechanical performance and lasting effectiveness concurrently, also
There is the effect purifying air, be conducive to improving indoor environmental quality.
Detailed description of the invention
Copper sculpture epoxy-acrylic anticorrosion water-soluble paint in a kind of purification air chamber, the component by following weight (kg) is former
Material is prepared from:
Epoxy resin E-44 40, ethylene glycol monobutyl ether 10, n-butyl alcohol 15, eucalyptus oil 0.1, Fructus Citri Limoniae oil 0.1, methacrylic acid 6,
Styrene 4, butyl acrylate 3, benzoyl peroxide 0.5, N, N-diformyl ethanol 4, titania nanotube 4, nanometer germanium
0.1, nano-tourmaline powder 0.3, phenylpropyl alcohol triazole 0.3, gamma-mercaptopropyltriethoxysilane 0.1, sodium alginate 0.3, water 100;
Described titania nanotube is to use hydrothermal synthesis method to prepare, and caliber is 5nm, and pipe range is 500nm.
A kind of purify the preparation method of copper sculpture epoxy-acrylic anticorrosion water-soluble paint in air chamber, comprise the following steps:
(1) titania nanotube mixed with dehydrated alcohol by solid-liquid weight ratio 1:10 be uniformly dispersed, be subsequently adding eucalyptus oil,
Fructus Citri Limoniae oil, phenylpropyl alcohol triazole and gamma-mercaptopropyltriethoxysilane stirring 6h, be vacuum dried gained solid after being centrifuged, must change
Property titanium nanotube;
(2) by the Modified Titanium nanotube in (1), nanometer germanium, nano-tourmaline powder, N, the mixing dispersion of N-diformyl second alcohol and water
Uniformly, obtain component A, the mixing of epoxy resin E-44, ethylene glycol monobutyl ether and n-butyl alcohol is warming up to 105 DEG C, is then slowly added dropwise
The mixed solution of methacrylic acid, styrene, butyl acrylate and benzoyl peroxide, and in 115 DEG C of insulation reaction 2h, obtain B
Component, by uniform in 80 DEG C of mixing high-speed stirred to component A and B component, then in 50 DEG C of insulation reaction 1h, obtains complex emulsions;
(3) grind uniformly after the complex emulsions in (2) being mixed with remaining raw material, copper sculpture ring in air chamber must be purified
Oxygen-acrylic acid anticorrosion water-soluble paint.
Outward appearance: flat smooth, transparent;
Adhesive force: 1 grade;
Resistance to water: 1500h is unchanged;
Salt fog resistance: 1000h is unchanged.
Claims (2)
1. copper sculpture epoxy-acrylic anticorrosion water-soluble paint in a purification air chamber, it is characterised in that it is by following weight
The raw material of part prepares:
Epoxy resin E-44 40-60, ethylene glycol monobutyl ether 10-15, n-butyl alcohol 15-25, eucalyptus oil 0.1-0.15, Fructus Citri Limoniae oil
0.1-0.2, methacrylic acid 6-8, styrene 4-6, butyl acrylate 3-5, benzoyl peroxide 0.5-1, N, N-diformyl
Ethanol 4-6, titania nanotube 4-6, nanometer germanium 0.1-0.15, nano-tourmaline powder 0.3-0.5, phenylpropyl alcohol triazole 0.3-
0.5, gamma-mercaptopropyltriethoxysilane 0.1-0.15, sodium alginate 0.3-0.5, water 100-120;
Described titania nanotube is to use hydrothermal synthesis method to prepare, and caliber is 5-25nm, and pipe range is 500-1000nm.
The most according to claim 1 a kind of purify the preparation of copper sculpture epoxy-acrylic anticorrosion water-soluble paint in air chamber
Method, it is characterised in that comprise the following steps:
(1) titania nanotube is mixed with dehydrated alcohol by solid-liquid weight ratio 1:10-1:15 it is uniformly dispersed, be subsequently adding eucalyptus globulus
Leaf oil, Fructus Citri Limoniae oil, phenylpropyl alcohol triazole and gamma-mercaptopropyltriethoxysilane stirring 6-12h, do gained solid vacuum after being centrifuged
Dry, obtain Modified Titanium nanotube;
(2) by the Modified Titanium nanotube in (1), nanometer germanium, nano-tourmaline powder, N, the mixing dispersion of N-diformyl second alcohol and water
Uniformly, obtain component A, the mixing of epoxy resin E-44, ethylene glycol monobutyl ether and n-butyl alcohol is warming up to 105-110 DEG C, the most slowly
Dropping methacrylic acid, styrene, butyl acrylate and the mixed solution of benzoyl peroxide, and anti-in 115-120 DEG C of insulation
Answer 2-4h, obtain B component, by uniform in 80-85 DEG C of mixing high-speed stirred to component A and B component, then anti-in 50-60 DEG C of insulation
Answer 1-1.5h, obtain complex emulsions;
(3) grind uniformly after the complex emulsions in (2) being mixed with remaining raw material, copper sculpture ring in air chamber must be purified
Oxygen-acrylic acid anticorrosion water-soluble paint.