CN106120368A - Light sensation complexion changed uvioresistant fabrics and preparation method thereof - Google Patents
Light sensation complexion changed uvioresistant fabrics and preparation method thereof Download PDFInfo
- Publication number
- CN106120368A CN106120368A CN201610775908.9A CN201610775908A CN106120368A CN 106120368 A CN106120368 A CN 106120368A CN 201610775908 A CN201610775908 A CN 201610775908A CN 106120368 A CN106120368 A CN 106120368A
- Authority
- CN
- China
- Prior art keywords
- drying
- light sensation
- uvioresistant
- grey cloth
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of light sensation complexion changed uvioresistant fabrics and preparation method thereof, belong to Strand Feeding Technique field.The light sensation complexion changed uvioresistant fabrics of the present invention, it is followed successively by photosensitive color-changing layer and grey cloth layer from outer layer to internal layer, described photosensitive color-changing layer is fixed on described grey cloth layer surface, described photosensitive color-changing layer surface is provided with lines, the manufacture method of light sensation complexion changed uvioresistant fabrics, comprises the steps: to join cloth, desizing and washing, desizing and washing, dyes, is dehydrated and fixation, the anti-drying of sizing, drying, anti-ultraviolet radiation treatment and roller coating and drying;The light sensation complexion changed uvioresistant fabrics of the present invention meets the irradiation of different wave length ultraviolet can produce different colours, and can prevent ultraviolet direct irradiation skin, has again water-proof function.
Description
Technical field
The invention belongs to fabric technical field, be specifically related to a kind of light sensation complexion changed uvioresistant fabrics and preparation method thereof.
Background technology
The Main Function of ozone layer is exactly to absorb to have the ultraviolet of damaging effect, thus the biology on preserving our planet from
The radiation of ultraviolet.But, along with the frequent activities of mankind's activity, the dependency degree of the Nature being continuously increased, environment suffers entirely
Not some destruction, causes global environment constantly to deteriorate, and the ozone layer concentration in atmosphere is gradually lowered so that have harm to make
Ultraviolet be directly radiated earth's surface, this is biological on the whole world and environment creates the biggest impact.
The ultraviolet light of wavelength 200nm ~ 280nm is short wave ultraviolet, is called for short UVC, and wavelength is the ultraviolet of 280nm ~ 320nm
Line is ultraviolet B radiation, be called for short UVB, wavelength be the ultraviolet of 320nm ~ 400nm be long wave ultraviolet, be called for short UVA, these ultraviolets
Line has penetrance to human body skin, very harmful to human body.
Such as the Chinese patent of Application No. 201410645184.7, disclose a kind of anti-ultraviolet flashing fabric, including under
Cotton layer, wool layer and upper cotton layer, the surface of described upper cotton layer is covered with one layer of antistatic backing, the surface of described antistatic backing
Being provided with ultraviolet resistant layer, this ultraviolet resistant layer is the non-woven fabrics that an oxidized zinc processed, and this non-woven fabrics is adsorbed with ultra-fine
Zinc oxide particles, described basic unit is made up of fabric, and described fabric is interweaved by warp yarn and weft yams and constitutes, described
The section of warp yarn and weft yams is triangle, the ultraviolet resistant layer of this invention product for be adsorbed with super fine zinc oxide from
The non-woven fabrics of son, thus reach the effect of anti-ultraviolet, this is not suitable for using for relatively thin fabric, and flash function is predominantly
The section of warp thread and weft yarn is triangle, utilizes the effect that the refraction principle of prism is brought, same, this method for
The requirement of fabric is higher, it is impossible to be widely used on other kinds of fabric.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, it is provided that a kind of chance different wave length ultraviolet irradiates and can produce not
Same color, and ultraviolet direct irradiation skin can be prevented, there is again the light sensation complexion changed uvioresistant fabrics of anti-dial water function.
The present invention is achieved by the following technical solutions:
Light sensation complexion changed uvioresistant fabrics, is followed successively by photosensitive color-changing layer and grey cloth layer from outside to inside, and described photosensitive color-changing layer is fixed
In described grey cloth layer surface.
Further, described photosensitive color-changing layer surface is provided with lines.
The manufacture method of light sensation complexion changed uvioresistant fabrics, comprises the steps:
Step one, joins cloth:
Grey cloth debatching joining cloth to cloth car, wherein, described grey cloth is the superfine denier fabric of 20D/12F;
Step 2, desizing and washing:
Described grey cloth is carried out desizing and washing, obtains washer wrinkle fabric;
Step 3, dyeing:
Gained washer wrinkle fabric in step 2 is imported dye vat dye, obtain stained clot-h;
Step 4, dehydration and fixation:
Carry out being dehydrated and fixation treatment by step 3 gained uvioresistant grey cloth, obtain fixation grey cloth;
Step 5, anti-drying of shaping:
The anti-drying that carries out step 4 gained fixation grey cloth shaping processes, anti-drying cloth of must shaping, wherein, and the anti-drying of described sizing
In processing procedure, fixation anti-drying auxiliary agent includes following composition: dryingagent, isopropanol and glacial acetic acid, shaping, anti-drying processes
Time, it being sequentially added into dryingagent 18 ~ 23g/L, isopropanol 4 ~ 6g/L and glacial acetic acid 0.4 ~ 0.6g/L according to watermeter, regulation pH is extremely
5.5 ~ 6.5, the time of padding is 30 ~ 40min;
Step 6, dries:
Anti-drying cloth of being shaped by step 5 gained imports drying chamber dries, and obtains drying grey cloth, wherein, dry temperature be 150 ~
170 DEG C, selvage guide vehicle speed is 30m/min.
Step 7, anti-ultraviolet radiation treatment:
Gained in step 6 is dried in grey cloth imports anti-ultraviolet radiation treatment cylinder and carries out anti-ultraviolet radiation treatment, obtain uvioresistant base
Cloth, wherein, uvioresistant auxiliary agent includes the UV absorbent 2 ~ 4g/L according to watermeter, during anti-ultraviolet radiation treatment, adjusts
Joint pH to 4 ~ 5, temperature is 85 ~ 95 DEG C, constant temperature 30 ~ 40min;
Step 8, roller coating and drying:
Step 7 gained uvioresistant grey cloth is carried out roller coating and drying, obtains light sensation complexion changed uvioresistant fabrics, wherein, during roller coating
Using the 80 mesh rollers being carved with decorative pattern, rolling coating agent includes the following component according to mass fraction meter: PU 90 ~ 110 parts, light sensation
Agent 5 ~ 10 parts, 2 ~ 5 parts of surfactant, 2 ~ 4 parts of firming agent, catalyst 1 ~ 2 part, in described drying course, first with 115 ~ 125 DEG C
Dry 3 ~ 5min, finally dry 2 ~ 4min with 145 ~ 155 DEG C and dry 2 ~ 4min.
Further, described step 5 is shaped in anti-dial water treatment procedure, when anti-drying of shaping processes, according to watermeter
Being sequentially added into dryingagent 20g/L, isopropanol 5g/L and glacial acetic acid 0.5g/L, regulate pH to 6.0, the time of padding is 30min.
Further, in described step 6 drying course, drying temperature is 160 DEG C.
Further, during described step 7 anti-ultraviolet radiation treatment, uvioresistant auxiliary agent includes ultraviolet (UV) resistant agent, anti-purple
In outside line processing procedure, adding ultraviolet (UV) resistant agent 3g/L according to watermeter, regulate pH to 4.5, temperature is 90 DEG C, constant temperature
30min。
Further, during described step 8 roller coating, rolling coating agent includes the following component according to following mass fraction meter:
PU 100 parts, light sensation agent 8 parts, 3 parts of surfactant, 3 parts of firming agent, catalyst 1 part, in described drying course, first with 120 DEG C
Dry 3min, finally dry 2min with 150 DEG C.
Beneficial effects of the present invention is embodied in:
Compared with prior art, the light sensation complexion changed uvioresistant fabrics of the present invention is by the way of cylinder roller coating so that fabric table
Mask has decorative pattern attractive in appearance and a pattern, meanwhile, by roller coating operation, by PU, light sensation agent, surfactant, firming agent and
Catalyst together roller coating is to web surface, in conjunction with the decorative pattern of web surface so that fabric produces when running into the ultraviolet of different wave length
Different color changes, i.e. meets wavelength and is respectively 290nm ~ 400nm, 270nm ~ 370nm, 280nm ~ 390nm and 290nm ~ 390nm
Ultraviolet time, the color of web surface complexion changed respectively is redness, yellow, blueness and purple;And, the light sensation complexion changed of the present invention
Uvioresistant fabrics also have passed through anti-drying and processes, and has anti-drying characteristic.
Detailed description of the invention
Raw material of the present invention is commercially available product;
Wherein, PU is purchased from Taiwan Gao Ding Chemical Co., Ltd., and model is NC-5056;
Light sensation agent is purchased from E.I.Du Pont Company, and model is AF-123;
UV absorbent is purchased from Changzhou Mei Sheng biomaterial company limited;
Dryingagent is fluorinated work (Chinese) company limited purchased from great Jin, and model is TG-420;
Surfactant is water-proofing agent, and purchased from De Bao Chemical Co., Ltd., model is TC-565;
Firming agent is Bridge Erector, and purchased from De Bao Chemical Co., Ltd., model is 6535;
Catalyst is purchased from De Bao Chemical Co., Ltd., and model is 558.
Embodiment 1
Light sensation complexion changed uvioresistant fabrics, is followed successively by photosensitive color-changing layer and grey cloth layer from outside to inside, and described photosensitive color-changing layer is fixed
In described grey cloth layer surface, described photosensitive color-changing layer surface is provided with lines.
The manufacture method of described light sensation complexion changed uvioresistant fabrics, comprises the steps:
Step one, joins cloth:
Grey cloth debatching joining cloth to cloth car, wherein, described grey cloth is the superfine denier fabric of 20D/12F.
Step 2, desizing and washing:
Described grey cloth is carried out desizing and washing, obtains washer wrinkle fabric.
Step 3, dyeing:
Gained washer wrinkle fabric in step 2 is imported dye vat dye, obtain stained clot-h.
Step 4, dehydration and fixation:
Carry out being dehydrated and fixation treatment by step 3 gained uvioresistant grey cloth, obtain fixation grey cloth.
Step 5, anti-drying of shaping:
The anti-drying that carries out step 4 gained fixation grey cloth shaping processes, anti-drying cloth of must shaping, wherein, and the anti-drying of described sizing
In processing procedure, fixation anti-drying auxiliary agent includes following composition: dryingagent, isopropanol and glacial acetic acid, shaping, anti-drying processes
Time, it is sequentially added into dryingagent 18g/L, isopropanol 4g/L and glacial acetic acid 0.4g/L according to watermeter, regulates pH to 5.5, when padding
Between be 35min.
Step 6, dries:
Anti-drying cloth of being shaped by step 5 gained imports drying chamber dries, and obtains drying grey cloth, and wherein, drying temperature is 150
DEG C, selvage guide vehicle speed is 30m/min.
Step 7, anti-ultraviolet radiation treatment:
Gained in step 6 is dried in grey cloth imports anti-ultraviolet radiation treatment cylinder and carries out anti-ultraviolet radiation treatment, obtain uvioresistant base
Cloth, wherein, uvioresistant auxiliary agent includes UV absorbent 2g/L according to watermeter, during anti-ultraviolet radiation treatment, regulation
PH to 4, temperature is 85 DEG C, constant temperature 35min.
Step 8, roller coating and drying:
Step 7 gained uvioresistant grey cloth is carried out roller coating and drying, obtains light sensation complexion changed uvioresistant fabrics, wherein, during roller coating
Using the 80 mesh rollers being carved with decorative pattern, rolling coating agent includes the following component according to mass fraction meter: PU 90 parts, light sensation agent 5
Part, 2 parts of surfactant, 2 parts of firming agent, catalyst 1 part, in described drying course, first dry 4min with 115 DEG C, finally with
Dry 3min for 145 DEG C.
Embodiment 2
Light sensation complexion changed uvioresistant fabrics, is followed successively by photosensitive color-changing layer and grey cloth layer from outside to inside, and described photosensitive color-changing layer is fixed
In described grey cloth layer surface, described photosensitive color-changing layer surface is provided with lines.
The manufacture method of light sensation complexion changed uvioresistant fabrics, comprises the steps:
Step one, joins cloth:
Grey cloth debatching joining cloth to cloth car, wherein, described grey cloth is the superfine denier fabric of 20D/12F.
Step 2, desizing and washing:
Described grey cloth is carried out desizing and washing, obtains washer wrinkle fabric.
Step 3, dyeing:
Gained washer wrinkle fabric in step 2 is imported dye vat dye, obtain stained clot-h.
Step 4, dehydration and fixation:
Carry out being dehydrated and fixation treatment by step 3 gained uvioresistant grey cloth, obtain fixation grey cloth.
Step 5, anti-drying of shaping:
The anti-drying that carries out step 4 gained fixation grey cloth shaping processes, anti-drying cloth of must shaping, wherein, and the anti-drying of described sizing
In processing procedure, fixation anti-drying auxiliary agent includes following composition: dryingagent, isopropanol and glacial acetic acid, shaping, anti-drying processes
Time, it is sequentially added into dryingagent 20g/L, isopropanol 5g/L and glacial acetic acid 0.5g/L according to watermeter, regulates pH to 6.0, when padding
Between be 30min.
Step 6, dries:
Anti-drying cloth of being shaped by step 5 gained imports drying chamber dries, and obtains drying grey cloth, and wherein, drying temperature is 160
DEG C, selvage guide vehicle speed is 30m/min.
Step 7, anti-ultraviolet radiation treatment:
Gained in step 6 is dried in grey cloth imports anti-ultraviolet radiation treatment cylinder and carries out anti-ultraviolet radiation treatment, obtain uvioresistant base
Cloth, wherein, uvioresistant auxiliary agent includes ultraviolet (UV) resistant agent 3g/L according to watermeter, anti-ultraviolet radiation treatment during, regulation
PH to 4.5, temperature is 90 DEG C, constant temperature 30min.
Step 8, roller coating and drying:
Step 7 gained uvioresistant grey cloth is carried out roller coating and drying, obtains light sensation complexion changed uvioresistant fabrics, wherein, during roller coating
Using the 80 mesh rollers being carved with decorative pattern, rolling coating agent includes the following component according to mass fraction meter: PU 100 parts, light sensation agent 8
Part, 3 parts of surfactant, 3 parts of firming agent, catalyst 1 part, in described drying course, first dry 3min with 120 DEG C, finally with
Dry 2min for 150 DEG C.
Embodiment 3
Light sensation complexion changed uvioresistant fabrics, is followed successively by photosensitive color-changing layer and grey cloth layer from outside to inside, and described photosensitive color-changing layer is fixed
In described grey cloth layer surface, described photosensitive color-changing layer surface is provided with lines.
The manufacture method of light sensation complexion changed uvioresistant fabrics, it is characterised in that comprise the steps:
Step one, joins cloth:
Grey cloth debatching joining cloth to cloth car, wherein, described grey cloth is the superfine denier fabric of 20D/12F;
Step 2, desizing and washing:
Described grey cloth is carried out desizing and washing, obtains washer wrinkle fabric;
Step 3, dyeing:
Gained washer wrinkle fabric in step 2 is imported dye vat dye, obtain stained clot-h;
Step 4, dehydration and fixation:
Carry out being dehydrated and fixation treatment by step 3 gained uvioresistant grey cloth, obtain fixation grey cloth;
Step 5, anti-drying of shaping:
The anti-drying that carries out step 4 gained fixation grey cloth shaping processes, anti-drying cloth of must shaping, wherein, and the anti-drying of described sizing
In processing procedure, fixation anti-drying auxiliary agent includes following composition: dryingagent, isopropanol and glacial acetic acid, shaping, anti-drying processes
Time, it is sequentially added into dryingagent 23g/L, isopropanol 6g/L and glacial acetic acid 0.6g/L according to watermeter, regulates pH to 6.5, when padding
Between be 40min.
Step 6, dries:
Anti-drying cloth of being shaped by step 5 gained imports drying chamber dries, and obtains drying grey cloth, and wherein, drying temperature is 170
DEG C, selvage guide vehicle speed is 30m/min.
Step 7, anti-ultraviolet radiation treatment:
Gained in step 6 is dried in grey cloth imports anti-ultraviolet radiation treatment cylinder and carries out anti-ultraviolet radiation treatment, obtain uvioresistant base
Cloth, wherein, uvioresistant auxiliary agent includes UV absorbent 4g/L according to watermeter, during anti-ultraviolet radiation treatment, regulation
PH to 5, temperature is 95 DEG C, constant temperature 40min;
Step 8, roller coating and drying:
Step 7 gained uvioresistant grey cloth is carried out roller coating and drying, obtains light sensation complexion changed uvioresistant fabrics, wherein, during roller coating
Using the 80 mesh rollers being carved with decorative pattern, rolling coating agent includes the following component according to mass fraction meter: PU 110 parts, light sensation agent 10
Part, 5 parts of surfactant, 4 parts of firming agent, catalyst 2 parts, in described drying course, first dry 5min with 125 DEG C, finally with
Dry 4min for 155 DEG C.
The light sensation complexion changed uvioresistant fabrics prepared the present invention according to embodiment 1 to 3 carries out photosensitive color-changing detection, result
As follows:
Table 1 test result
Ultraviolet wavelength | Embodiment 1 | Embodiment 2 | Embodiment 3 |
270nm~370nm | Yellow | Yellow | Yellow |
280nm—390nm | Blue | Blue | Blue |
290nm—390nm | Purple | Purple | Purple |
290nm---400nm | Red | Red | Red |
By the test result of table 1 it can be seen that the light sensation complexion changed uvioresistant fabrics produced according to the inventive method, running into ripple
During the ultraviolet of a length of 270nm ~ 370nm, fabric manifests yellow, and when wavelength is the ultraviolet of 280nm 390nm, fabric manifests
Blueness, when wavelength is the ultraviolet of 290nm 390nm, fabric manifests purple, when wavelength is the ultraviolet of 290nm---400nm,
Fabric manifests redness.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (8)
1. light sensation complexion changed uvioresistant fabrics, it is characterised in that be followed successively by photosensitive color-changing layer and grey cloth layer, described light from outside to inside
Sense photochromic layer is fixed on described grey cloth layer surface.
Light sensation complexion changed uvioresistant fabrics the most according to claim 1, it is characterised in that described photosensitive color-changing layer surface sets
There is lines.
3. the manufacture method of the light sensation complexion changed uvioresistant fabrics described in claim 1, it is characterised in that comprise the steps:
Step one, joins cloth:
Grey cloth debatching joining cloth to cloth car, wherein, described grey cloth is the superfine denier fabric of 20D/12F;
Step 2, desizing and washing:
Described grey cloth is carried out desizing and washing, obtains washer wrinkle fabric;
Step 3, dyeing:
Gained washer wrinkle fabric in step 2 is imported dye vat dye, obtain stained clot-h;
Step 4, dehydration and fixation:
Carry out being dehydrated and fixation treatment by step 3 gained uvioresistant grey cloth, obtain fixation grey cloth;
Step 5, anti-drying of shaping:
The anti-drying that carries out step 4 gained fixation grey cloth shaping processes, anti-drying cloth of must shaping, wherein, and the anti-drying of described sizing
In processing procedure, fixation anti-drying auxiliary agent includes following composition: dryingagent, isopropanol and glacial acetic acid, shaping, anti-drying processes
Time, it being sequentially added into dryingagent 18 ~ 23g/L, isopropanol 4 ~ 6g/L and glacial acetic acid 0.4 ~ 0.6g/L according to watermeter, regulation pH is extremely
5.5 ~ 6.5, the time of padding is 30 ~ 40min;
Step 6, dries:
Anti-drying cloth of being shaped by step 5 gained imports drying chamber dries, and obtains drying grey cloth, wherein, dry temperature be 150 ~
170 DEG C, selvage guide vehicle speed is 30m/min.
4. step 7, anti-ultraviolet radiation treatment:
Gained in step 6 is dried in grey cloth imports anti-ultraviolet radiation treatment cylinder and carries out anti-ultraviolet radiation treatment, obtain uvioresistant base
Cloth, wherein, uvioresistant auxiliary agent includes the UV absorbent 2 ~ 4g/L according to watermeter, during anti-ultraviolet radiation treatment, adjusts
Joint pH to 4 ~ 5, temperature is 85 ~ 95 DEG C, constant temperature 30 ~ 40min;
Step 8, roller coating and drying:
Step 7 gained uvioresistant grey cloth is carried out roller coating and drying, obtains light sensation complexion changed uvioresistant fabrics, wherein, during roller coating
Using the 80 mesh rollers being carved with decorative pattern, rolling coating agent includes the following component according to mass fraction meter: PU 90 ~ 110 parts, light sensation
Agent 5 ~ 10 parts, 2 ~ 5 parts of surfactant, 2 ~ 4 parts of firming agent, catalyst 1 ~ 2 part, in described drying course, first with 115 ~ 125 DEG C
Dry 3 ~ 5min, finally dry 2 ~ 4min with 145 ~ 155 DEG C.
The manufacture method of light sensation complexion changed uvioresistant fabrics the most according to claim 3, it is characterised in that described step 5
Shape in anti-dial water treatment procedure, when anti-drying of shaping processes, be sequentially added into dryingagent 20g/L, isopropanol according to watermeter
5g/L and glacial acetic acid 0.5g/L, regulates pH to 6.0, and the time of padding is 30min.
The manufacture method of light sensation complexion changed uvioresistant fabrics the most according to claim 3, it is characterised in that described step 6
In drying course, drying temperature is 160 DEG C.
The manufacture method of light sensation complexion changed uvioresistant fabrics the most according to claim 3, it is characterised in that described step 7
During anti-ultraviolet radiation treatment, adding ultraviolet (UV) resistant agent 3g/L according to watermeter, regulate pH to 4.5, temperature is 90 DEG C, constant temperature
30min。
The manufacture method of light sensation complexion changed uvioresistant fabrics the most according to claim 3, it is characterised in that described step 8
During roller coating, rolling coating agent includes the following component according to following mass fraction meter: PU 100 parts, light sensation agent 8 parts, surface activity
Agent 3 parts, 3 parts of firming agent, catalyst 1 part, in described drying course, first dry 3min with 120 DEG C, finally with 150 DEG C of drying
2min。