CN106118414A - 一种环保聚氨酯型粉末涂料 - Google Patents
一种环保聚氨酯型粉末涂料 Download PDFInfo
- Publication number
- CN106118414A CN106118414A CN201610481795.1A CN201610481795A CN106118414A CN 106118414 A CN106118414 A CN 106118414A CN 201610481795 A CN201610481795 A CN 201610481795A CN 106118414 A CN106118414 A CN 106118414A
- Authority
- CN
- China
- Prior art keywords
- environment
- powdery paints
- agent
- polyurethane type
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保聚氨酯型粉末涂料,所述环保聚氨酯型粉末涂料以重量为单位,包括以下原料:基体树脂82‑95份、颜填料36‑48份、固化剂10‑16份、脱气剂3‑5份、分散剂1‑2份、垂纹剂0.4‑0.8份、增韧剂0.3‑0.6份、增光剂0.3‑0.5份、润湿剂0.2‑0.4份、防腐剂0.2‑0.4份、抗氧剂0.2‑0.3份、光稳定剂0.2‑0.3份,所述环保聚氨酯型粉末涂料是经过原料混合、熔解、压片、制粒、粉碎制得的。本发明的环保聚氨酯型粉末涂料具有耐候性,可以遮挡紫外线光对银粉的直射,具有较强的耐腐蚀性,长时间在阳光下不会粉化变黑,广泛应用于护栏、门业、铝型材等户外金属表面涂装。
Description
【技术领域】
本发明属于涂料制备技术领,具体涉及一种环保聚氨酯型粉末涂料。
【背景技术】
粉末涂料是一种以石油化工原料为主而延生出来的新型环保材料,主要由低分子量树脂、助剂、填料等,在一定的条件下制备、喷涂、烘烤而形成具有一定的外观、光泽、颜色,并在物件表面起到防腐和装饰作用的涂膜。粉末涂料在实际应用过程中,如户外大门、阳台护栏等。经过一段时间,涂膜将会发生一定程度变化,如光泽下降、颜色变暗或冷白、涂层表面出现锈点、裂纹等,特别是垂纹银色粉末涂料,由于其主要颜料是铝粉,而铝偏偏又是一种很活跃,耐候性差,易腐蚀的材料,在阳光下一般2-3个月内就会粉化变黑,因此只能用于户内。
【发明内容】
本发明提供一种环保聚氨酯型粉末涂料,以解决现有垂纹银色粉末涂料耐候性差、易腐蚀等问题。本发明的环保聚氨酯型粉末涂料具有耐候性,可以遮挡紫外线光对银粉的直射,具有较强的耐腐蚀性,长时间在阳光下不会粉化变黑,广泛应用于护栏、门业、铝型材等户外金属表面涂装。
为解决以上技术问题,本发明采用以下技术方案:
一种环保聚氨酯型粉末涂料,以重量为单位,包括以下原料:基体树脂82-95份、颜填料36-48份、固化剂10-16份、脱气剂3-5份、分散剂1-2份、垂纹剂0.4-0.8份、增韧剂0.3-0.6份、增光剂0.3-0.5份、润湿剂0.2-0.4份、防腐剂0.2-0.4份、抗氧剂0.2-0.3份、光稳定剂0.2-0.3份;所述分散剂为分散剂CP-8131;所述垂纹剂为垂纹剂HM-15;所述润湿剂为润湿剂CF-10;所述防腐剂为防腐剂JLB50;所述抗氧剂为抗氧剂626;所述光稳定剂为光稳定剂HS-3203;所述环保聚氨酯型粉末涂料的制备方法,包括以下步骤:
S1:将基体树脂、颜填料、固化剂、脱气剂、分散剂、垂纹剂、增韧剂、增光剂、润湿剂、防腐剂、抗氧剂、光稳定剂放入混料缸预混合4-6min,得到均匀混合物;
S2:将步骤S1制得的均匀混合物通过挤出机在110-114℃下熔融挤出,并通过压片破碎机制片,冷却后制得片体;
S3:将步骤S2制得的片体采用切刀剪切,制得切粒;
S4:将步骤S3制得的切粒粉碎后过150-200目筛子,制得环保聚氨酯型粉末涂料。
进一步地,所述基体树脂为聚氨树脂。
进一步地,所述颜填料为金属颜料和体质颜料。
进一步地,所述金属颜料为银粉。
进一步地,所述体质颜料为膨润土。
进一步地,所述固化剂为多异氰酸酯。
进一步地,所述脱气剂为酰胺蜡。
进一步地,所述增韧剂为乙烯-醋酸乙烯酯共聚物。
进一步地,所述增光剂为增光剂HR908。
本发明具有以下有益效果:
(1)本发明的环保聚氨酯型粉末涂料耐冲击性为85-100kg/cm,抗弯曲性为1.5-1.7mm,附着力为100%,抗老化实验中,变色≤2级,失光≤2级,无粉化、起泡、开裂、剥落等异常现象;
(2)本发明的环保聚氨酯型粉末涂料具有耐候性,可以遮挡紫外线光对银粉的直射,具有较强的耐腐蚀性,长时间在阳光下不会粉化变黑,广泛应用于护栏、门业、铝型材等户外金属表面涂装。
【具体实施方式】
为便于更好地理解本发明,通过以下实施例加以说明,这些实施例属于本发明的保护范围,但不限制本发明的保护范围。
在实施例中,所述环保聚氨酯型粉末涂料,以重量为单位,包括以下原料:基体树脂82-95份、颜填料36-48份、固化剂10-16份、脱气剂3-5份、分散剂1-2份、垂纹剂0.4-0.8份、增韧剂0.3-0.6份、增光剂0.3-0.5份、润湿剂0.2-0.4份、防腐剂0.2-0.4份、抗氧剂0.2-0.3份、光稳定剂0.2-0.3份;所述基体树脂为聚氨树脂;所述颜填料为金属颜料和体质颜料;所述金属颜料为银粉;所述体质颜料为膨润土;所述固化剂为多异氰酸酯;所述脱气剂为酰胺蜡;所述分散剂为分散剂CP-8131;所述垂纹剂为垂纹剂HM-15;所述增韧剂为乙烯-醋酸乙烯酯共聚物;所述增光剂为增光剂HR908;所述润湿剂为润湿剂CF-10;所述防腐剂为防腐剂JLB50;所述抗氧剂为抗氧剂626;所述光稳定剂为光稳定剂HS-3203。
所述环保聚氨酯型粉末涂料的制备方法,包括以下步骤:
S1:将基体树脂、颜填料、固化剂、脱气剂、分散剂、垂纹剂、增韧剂、增光剂、润湿剂、防腐剂、抗氧剂、光稳定剂放入混料缸预混合4-6min,得到均匀混合物;
S2:将步骤S1制得的均匀混合物通过挤出机在110-114℃下熔融挤出,并通过压片破碎机制片,冷却后制得片体;
S3:将步骤S2制得的片体采用切刀剪切,制得切粒;
S4:将步骤S3制得的切粒粉碎后过150-200目筛子,制得环保聚氨酯型粉末涂料。
实施例1
一种环保聚氨酯型粉末涂料,以重量为单位,包括以下原料:基体树脂90份、颜填料42份、固化剂15份、脱气剂5份、分散剂1.5份、垂纹剂0.6份、增韧剂0.5份、增光剂0.4份、润湿剂0.3份、防腐剂0.3份、抗氧剂0.2份、光稳定剂0.2份;所述基体树脂为聚氨树脂;所述颜填料为金属颜料和体质颜料;所述金属颜料为银粉;所述体质颜料为膨润土;所述固化剂为多异氰酸酯;所述脱气剂为酰胺蜡;所述分散剂为分散剂CP-8131;所述垂纹剂为垂纹剂HM-15;所述增韧剂为乙烯-醋酸乙烯酯共聚物;所述增光剂为增光剂HR908;所述润湿剂为润湿剂CF-10;所述防腐剂为防腐剂JLB50;所述抗氧剂为抗氧剂626;所述光稳定剂为光稳定剂HS-3203。
所述环保聚氨酯型粉末涂料的制备方法,包括以下步骤:
S1:将基体树脂、颜填料、固化剂、脱气剂、分散剂、垂纹剂、增韧剂、增光剂、润湿剂、防腐剂、抗氧剂、光稳定剂放入混料缸预混合4min,得到均匀混合物;
S2:将步骤S1制得的均匀混合物通过挤出机在110℃下熔融挤出,并通过压片破碎机制片,冷却后制得片体;
S3:将步骤S2制得的片体采用切刀剪切,制得切粒;
S4:将步骤S3制得的切粒粉碎后过150目筛子,制得环保聚氨酯型粉末涂料。
实施例2
一种环保聚氨酯型粉末涂料,以重量为单位,包括以下原料:基体树脂82份、颜填料36份、固化剂10份、脱气剂3份、分散剂1份、垂纹剂0.4份、增韧剂0.3份、增光剂0.3份、润湿剂0.2份、防腐剂0.2份、抗氧剂0.2份、光稳定剂0.2份;所述基体树脂为聚氨树脂;所述颜填料为金属颜料和体质颜料;所述金属颜料为银粉;所述体质颜料为膨润土;所述固化剂为多异氰酸酯;所述脱气剂为酰胺蜡;所述分散剂为分散剂CP-8131;所述垂纹剂为垂纹剂HM-15;所述增韧剂为乙烯-醋酸乙烯酯共聚物;所述增光剂为增光剂HR908;所述润湿剂为润湿剂CF-10;所述防腐剂为防腐剂JLB50;所述抗氧剂为抗氧剂626;所述光稳定剂为光稳定剂HS-3203。
所述环保聚氨酯型粉末涂料的制备方法,包括以下步骤:
S1:将基体树脂、颜填料、固化剂、脱气剂、分散剂、垂纹剂、增韧剂、增光剂、润湿剂、防腐剂、抗氧剂、光稳定剂放入混料缸预混合6min,得到均匀混合物;
S2:将步骤S1制得的均匀混合物通过挤出机在114℃下熔融挤出,并通过压片破碎机制片,冷却后制得片体;
S3:将步骤S2制得的片体采用切刀剪切,制得切粒;
S4:将步骤S3制得的切粒粉碎后过200目筛子,制得环保聚氨酯型粉末涂料。
实施例3
一种环保聚氨酯型粉末涂料,以重量为单位,包括以下原料:基体树脂95份、颜填料48份、固化剂16份、脱气剂5份、分散剂2份、垂纹剂-0.8份、增韧剂0.6份、增光剂0.5份、润湿剂0.4份、防腐剂0.4份、抗氧剂0.3份、光稳定剂0.3份;所述基体树脂为聚氨树脂;所述颜填料为金属颜料和体质颜料;所述金属颜料为银粉;所述体质颜料为膨润土;所述固化剂为多异氰酸酯;所述脱气剂为酰胺蜡;所述分散剂为分散剂CP-8131;所述垂纹剂为垂纹剂HM-15;所述增韧剂为乙烯-醋酸乙烯酯共聚物;所述增光剂为增光剂HR908;所述润湿剂为润湿剂CF-10;所述防腐剂为防腐剂JLB50;所述抗氧剂为抗氧剂626;所述光稳定剂为光稳定剂HS-3203。
所述环保聚氨酯型粉末涂料的制备方法,包括以下步骤:
S1:将基体树脂、颜填料、固化剂、脱气剂、分散剂、垂纹剂、增韧剂、增光剂、润湿剂、防腐剂、抗氧剂、光稳定剂放入混料缸预混合5min,得到均匀混合物;
S2:将步骤S1制得的均匀混合物通过挤出机在112℃下熔融挤出,并通过压片破碎机制片,冷却后制得片体;
S3:将步骤S2制得的片体采用切刀剪切,制得切粒;
S4:将步骤S3制得的切粒粉碎后过180目筛子,制得环保聚氨酯型粉末涂料。
实施例4
一种环保聚氨酯型粉末涂料,以重量为单位,包括以下原料:基体树脂90份、颜填料40份、固化剂14份、脱气剂4份、分散剂1份、垂纹剂0.5份、增韧剂0.3份、增光剂0.3份、润湿剂0.2份、防腐剂0.2份、抗氧剂0.2份、光稳定剂0.2份;所述基体树脂为聚氨树脂;所述颜填料为金属颜料和体质颜料;所述金属颜料为银粉;所述体质颜料为膨润土;所述固化剂为多异氰酸酯;所述脱气剂为酰胺蜡;所述分散剂为分散剂CP-8131;所述垂纹剂为垂纹剂HM-15;所述增韧剂为乙烯-醋酸乙烯酯共聚物;所述增光剂为增光剂HR908;所述润湿剂为润湿剂CF-10;所述防腐剂为防腐剂JLB50;所述抗氧剂为抗氧剂626;所述光稳定剂为光稳定剂HS-3203。
所述环保聚氨酯型粉末涂料的制备方法,包括以下步骤:
S1:将基体树脂、颜填料、固化剂、脱气剂、分散剂、垂纹剂、增韧剂、增光剂、润湿剂、防腐剂、抗氧剂、光稳定剂放入混料缸预混合4min,得到均匀混合物;
S2:将步骤S1制得的均匀混合物通过挤出机在110℃下熔融挤出,并通过压片破碎机制片,冷却后制得片体;
S3:将步骤S2制得的片体采用切刀剪切,制得切粒;
S4:将步骤S3制得的切粒粉碎后过200目筛子,制得环保聚氨酯型粉末涂料。
实施例5
一种环保聚氨酯型粉末涂料,以重量为单位,包括以下原料:基体树脂92份、颜填料45份、固化剂16份、脱气剂5份、分散剂2份、垂纹剂0.7份、增韧剂0.5份、增光剂0.4份、润湿剂0.4份、防腐剂0.4份、抗氧剂0.3份、光稳定剂0.3份;所述基体树脂为聚氨树脂;所述颜填料为金属颜料和体质颜料;所述金属颜料为银粉;所述体质颜料为膨润土;所述固化剂为多异氰酸酯;所述脱气剂为酰胺蜡;所述分散剂为分散剂CP-8131;所述垂纹剂为垂纹剂HM-15;所述增韧剂为乙烯-醋酸乙烯酯共聚物;所述增光剂为增光剂HR908;所述润湿剂为润湿剂CF-10;所述防腐剂为防腐剂JLB50;所述抗氧剂为抗氧剂626;所述光稳定剂为光稳定剂HS-3203。
所述环保聚氨酯型粉末涂料的制备方法,包括以下步骤:
S1:将基体树脂、颜填料、固化剂、脱气剂、分散剂、垂纹剂、增韧剂、增光剂、润湿剂、防腐剂、抗氧剂、光稳定剂放入混料缸预混合5min,得到均匀混合物;
S2:将步骤S1制得的均匀混合物通过挤出机在114℃下熔融挤出,并通过压片破碎机制片,冷却后制得片体;
S3:将步骤S2制得的片体采用切刀剪切,制得切粒;
S4:将步骤S3制得的切粒粉碎后过160目筛子,制得环保聚氨酯型粉末涂料。
检测实施例1-5制得的环保聚氨酯型粉末涂料的性能指标,采用以下实验。
对实施例1-5制得的环保聚氨酯型粉末涂料用喷涂机喷涂到0.2mm的马口铁板及0.5mm的冷轧铁板上,烘烤固化得到50-70μm的均匀涂膜,然后对该涂膜进行下列性能检测,具体测试结果及指标如下表所示。
由上表可知:本发明的环保聚氨酯型粉末涂料耐冲击性为85-100kg/cm,抗弯曲性为1.5-1.7mm,附着力为100%,抗老化实验中,变色≤2级,失光≤2级,无粉化、起泡、开裂、剥落等异常现象,说明本发明的环保聚氨酯型粉末涂料性能优。
以上内容不能认定本发明的具体实施只局限于这些说明,对于本发明所属技术领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干简单推演或替换,都应当视为属于本发明由所提交的权利要求书确定的专利保护范围。
Claims (9)
1.一种环保聚氨酯型粉末涂料,其特征在于,以重量为单位,包括以下原料:基体树脂82-95份、颜填料36-48份、固化剂10-16份、脱气剂3-5份、分散剂1-2份、垂纹剂0.4-0.8份、增韧剂0.3-0.6份、增光剂0.3-0.5份、润湿剂0.2-0.4份、防腐剂0.2-0.4份、抗氧剂0.2-0.3份、光稳定剂0.2-0.3份;所述分散剂为分散剂CP-8131;所述垂纹剂为垂纹剂HM-15;所述润湿剂为润湿剂CF-10;所述防腐剂为防腐剂JLB50;所述抗氧剂为抗氧剂626 ;所述光稳定剂为光稳定剂HS-3203;所述环保聚氨酯型粉末涂料的制备方法,包括以下步骤:
S1:将基体树脂、颜填料、固化剂、脱气剂、分散剂、垂纹剂、增韧剂、增光剂、润湿剂、防腐剂、抗氧剂、光稳定剂放入混料缸预混合4-6min,得到均匀混合物;
S2:将步骤S1制得的均匀混合物通过挤出机在110-114℃下熔融挤出,并通过压片破碎机制片,冷却后制得片体;
S3:将步骤S2制得的片体采用切刀剪切,制得切粒;
S4:将步骤S3制得的切粒粉碎后过150-200目筛子,制得环保聚氨酯型粉末涂料。
2.根据权利要求1所述环保聚氨酯型粉末涂料,其特征在于,所述基体树脂为聚氨树脂。
3.根据权利要求1所述环保聚氨酯型粉末涂料,其特征在于,所述颜填料为金属颜料和体质颜料。
4.根据权利要求3所述环保聚氨酯型粉末涂料,其特征在于,所述金属颜料为银粉。
5.根据权利要求3所述环保聚氨酯型粉末涂料,其特征在于,所述体质颜料为膨润土。
6.根据权利要求1所述环保聚氨酯型粉末涂料,其特征在于,所述固化剂为多异氰酸酯。
7.根据权利要求1所述环保聚氨酯型粉末涂料,其特征在于,所述脱气剂为酰胺蜡。
8.根据权利要求1所述环保聚氨酯型粉末涂料,其特征在于,所述增韧剂为乙烯-醋酸乙烯酯共聚物。
9.根据权利要求1所述环保聚氨酯型粉末涂料,其特征在于,所述增光剂为增光剂HR908。