CN106088509A - A kind of multifunction flexible imitates stone material and preparation method thereof - Google Patents
A kind of multifunction flexible imitates stone material and preparation method thereof Download PDFInfo
- Publication number
- CN106088509A CN106088509A CN201610643560.8A CN201610643560A CN106088509A CN 106088509 A CN106088509 A CN 106088509A CN 201610643560 A CN201610643560 A CN 201610643560A CN 106088509 A CN106088509 A CN 106088509A
- Authority
- CN
- China
- Prior art keywords
- layer
- main sheet
- sheet material
- glazed
- imitates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of multifunction flexible and imitate stone material and preparation method thereof, belong to building and ornament materials.A kind of multifunction flexible imitates stone material, including the main sheet material layers of bottom, middle decorative layer, the glazed layer on top layer, sprays interface agent layer between decorative layer and main sheet material layers, glazed layer is coated on decorative layer, described main sheet material layers includes that matrix, base bottom are provided with fibrous layer, and centre is provided with grid cloth；Described decorative layer is enamelled coating, including granite enamelled coating, the colorful enamelled coating of water burnt-in sand, true mineral varnish layer, sliver true mineral varnish layer, stone similar paint layer or F-C paint layer；Described glazed layer is made up of resin, auxiliary agent, functional material, pigment mixing.Bottom of the present invention is provided with non-woven fabrics, can strengthen pliability and reinforcing, and centre is provided with grid cloth, can improve crack resistance, it is easier to cuts and installs；Decorative layer can improve the fidelity of imitative stone material；Glazed layer can improve hardness and cleanablity.
Description
Technical field
The invention belongs to building and ornament materials, relate to imitative stone material, be specifically related to a kind of multifunction flexible imitate stone material and
Preparation method.
Background technology
Lithotome, as a kind of ornament materials, has natural colored and the characteristic of natural lines, increasingly by people
Welcome, be widely used in elevation of building, the finishing of house hall.But, lithotome not only has from great, cuts and pacifies
The shortcoming of dress difficulty；And during as house decorative material, there is radioactivity, during as exterior decorative materials, there is reflected sunlight
Efficiency is low, the shortcoming that surface temperature is high.
Under the irradiation of sunlight, heat constantly accumulates on radiation exposed body surface, can make its surface temperature not
Raising, once temperature is too high brings problems and inconvenience will to commercial production and daily life, and needs to expend greatly disconnectedly
The energy of amount maintains the operation of the cooling refrigeration equipment such as spray equipment, air-conditioning, air conditioner and electric fan.Under many circumstances,
Refrigeration plant cannot be used to reduce indoor temperature, therefore, reduce body surface temperature and the heat conductivity of body of wall, be to reduce room
The effective way of interior ambient temperature.
In order to solve that lithotome has from great, cut and installation difficulty, the shortcoming that surface temperature is high, the present invention carries
A kind of multifunction flexible has been supplied to imitate stone material.
Summary of the invention
It is an object of the invention to provide a kind of multifunction flexible and imitate stone material.
It is a further object to provide multifunction flexible and imitate the preparation method of stone material.
The present invention is achieved by the following technical solutions:
A kind of multifunction flexible imitates stone material, including the main sheet material layers of bottom, middle decorative layer, the glazed layer on top layer, decorative layer with
Spraying interface agent layer between main sheet material layers, glazed layer is coated on decorative layer, and described main sheet material layers includes that matrix, base bottom are provided with
Fibrous layer, centre is provided with grid cloth；Described decorative layer is enamelled coating, including granite enamelled coating, the colorful enamelled coating of water burnt-in sand, true mineral varnish
Layer, sliver true mineral varnish layer, stone similar paint layer or F-C paint layer；Described glazed layer is by resin, auxiliary agent, functional material, pigment mixing
Composition.
Further, described main sheet material layers thickness is 10-30mm, and wherein the fiber layer thickness of bottom is 0.2-1.0mm, in
Between grid cloth thickness be 0.2-1.0mm.
Described fibrous layer is acid and alkali-resistance non-woven fabrics, including polypropylene, terylene, chinlon, viscose rayon, acrylon, polyethylene or chlorine
Synthetic fibre.
Described resin is organic siliconresin or fluorine modified resin, and described auxiliary agent includes levelling agent, defoamer, delustring
Agent, lubricant.
Further, above-mentioned multifunction flexible imitates the preparation method of stone material, and step is:
(1) being preheated by mould, matrix material, at 60-100 DEG C, is injected in mould by control temperature, when irrigating Modeling Material, in
Centre position tiling grid cloth, then proceedes to irrigate matrix material, and finally tile fibrous layer, compacting, supports 20-100 DEG C of temperature
Protect 1-10h, after the demoulding, form main sheet material layers；
(2) main sheet material layers maintenance 48-72h, cleans up surface, sprays interface agent layer, is dried, spraying and decorating layer；
(3) decorative layer is dried, sprays glazed layer material, and described glazed layer material is by resin, auxiliary agent, functional material, pigment
It is composited, after drying and get final product.
Described mould is ferrum, aluminum or silica gel mould.
Above-mentioned multifunction flexible imitates the preparation method of stone material, and step is:
(1) on fibrous layer, scratch matrix material, tiling grid cloth, then proceed to scratch matrix material, at 20 100 DEG C of drying rooms
Middle maintenance, during leather hard, is compacted with the mould being preheating to 50-100 DEG C, moulding, keeps pressure and temperature 5-10 minute,
Main sheet material layers is formed after the demoulding；
(2) main sheet material layers maintenance 48-72h, cleans up surface, sprays interface agent layer, is dried, spraying and decorating layer；
(3) decorative layer is dried, sprays glazed layer material, and described glazed layer material is by resin, auxiliary agent, functional material, pigment
It is composited, after drying and get final product.
Described mould is ferrum, aluminum or silica gel mould.
The present invention is provided with acid and alkali-resistance non-woven fabrics at the base bottom of main sheet material layers, and described non-woven fabrics is through high-temperature fusion, spray
Silk, paving guiding principle, the coiled material of hot pressing, include but not limited to polypropylene (PP), terylene (PET), chinlon (PA), viscose rayon, acrylon,
Polyethylene (HDPE), polyvinyl chloride fibre (PVC), be possible not only to strengthen the suppleness of imitative stone material, and matrix play the effect of reinforcing；At base
The centre position of body is fixed with grid cloth, and grid cloth and matrix are compacted into one, matrix plays the effect of cracking resistance；In main sheet material layers
Top layer spraying interfacial agents, this interfacial agents has the effect formed a connecting link, and makes main sheet material layers be combined with decorative layer more firm；Simultaneously
Closing salt, the precipitation of alkali in moulding layer, after being completely dried, spraying and decorating layer, decorative layer can be granite enamelled coating, water burnt-in sand
Colorful enamelled coating, true mineral varnish layer, sliver true mineral varnish layer, stone similar paint layer or F-C paint layer, thickness is 0.5-1.5mm, makes stone material reach
Fidelity true to nature；Spray glazed layer on decorative layer top layer, use organic siliconresin or fluorine modified resin, add auxiliary agent (levelling
Agent, defoamer, delustering agent, feel lubricant), functional material, transparent pigment are composited, and after solidification, on surface, formation has super
Strong self-cleaning glazed layer, this glazed layer not only hardness is to (more than 1H), and has preferable toughness, resistance to marring etc., shape
Become the glazed layer of similar ceramic tile surface.
Compared with prior art, bottom of the present invention is provided with non-woven fabrics, can strengthen pliability and reinforcing, and centre is provided with
Grid cloth, can improve crack resistance, it is easier to cuts and installs；Decorative layer can improve the fidelity of imitative stone material；Glazed layer can
To improve hardness and cleanablity.
Accompanying drawing explanation
Fig. 1 is the structural representation of invention；
In figure: the main sheet material layers of 1-, 2-decorative layer, 3-glazed layer, 4-grid cloth 5-fibrous layer.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1
Multifunction flexible as shown in Figure 1 imitates stone material, including the main sheet material layers 1 of bottom, middle decorative layer 2, the glazed layer on top layer
3, spray interfacial agents between wherein said decorative layer 2 and main sheet material layers 1, described glazed layer 3 is coated on decorative layer 2, described
Main sheet material layers 1 includes that matrix, base bottom are provided with fibrous layer 5, and centre is provided with grid cloth 4;
Described main sheet material layers 1 thickness is 10mm, and wherein fibrous layer 5 thickness of bottom is 0.5mm, and middle grid cloth 4 is
1.0mm, wherein fibrous layer is polypropylene (can also be terylene, chinlon, viscose rayon, acrylon, polyethylene or polyvinyl chloride fibre)；Decorative layer 2 is
Granite enamelled coating (can also be the colorful enamelled coating of water burnt-in sand, true mineral varnish layer, sliver true mineral varnish layer, stone similar paint layer or F-C paint layer),
Thickness is 1.5mm, and described resin is organic siliconresin, and described auxiliary agent includes levelling agent, defoamer, delustering agent, lubricant；
During preparation, step is:
(1) being preheated by irony mould, matrix material, at 60-80 DEG C, is injected in mould by control temperature, at perfusion Modeling Material
Time, in centre position tiling grid cloth, then proceed to irrigate matrix material, finally tile fibrous layer, and compacting, 20-50 DEG C of temperature
Degree maintenance 1h, forms main sheet material layers after the demoulding；
(2) main sheet material layers maintenance 72h, cleans up surface, sprays interface agent layer, is dried, spraying and decorating layer；
(3) decorative layer is dried, sprays glazed layer material, and described glazed layer material is by organic siliconresin, auxiliary agent, function material
Material, pigment are composited, after drying and get final product.
Embodiment 2
Multifunction flexible as shown in Figure 1 imitates stone material, including the main sheet material layers 1 of bottom, middle decorative layer 2, the glazed layer on top layer
3, spray interfacial agents between wherein said decorative layer 2 and main sheet material layers 1, described glazed layer 3 is coated on decorative layer 2, described
Main sheet material layers 1 includes that matrix, base bottom are provided with fibrous layer 5, and centre is provided with grid cloth 4;
Described main sheet material layers 1 thickness is 20mm, and wherein fibrous layer 5 thickness of bottom is 1mm, and middle grid cloth 4 is 0.2mm,
Wherein fibrous layer is terylene (can also be chinlon, viscose rayon, acrylon, polyethylene or polyvinyl chloride fibre)；Decorative layer 2 is the true mineral varnish of sliver
Layer (can also be the colorful enamelled coating of water burnt-in sand, true mineral varnish layer, stone similar paint layer or F-C paint layer), thickness is 1.2mm, described tree
Fat is fluorine modified resin, and described auxiliary agent includes levelling agent, defoamer, delustering agent, lubricant；
During preparation, step is:
(1) being preheated by silica gel mould, matrix material, at 70-90 DEG C, is injected in mould by control temperature, at perfusion Modeling Material
Time, in centre position tiling grid cloth, then proceed to irrigate matrix material, finally tile fibrous layer, and compacting, 40-80 DEG C of temperature
Degree maintenance 3h, forms main sheet material layers after the demoulding；
(2) main sheet material layers maintenance 65h, cleans up surface, sprays interface agent layer, is dried, spraying and decorating layer；
(3) decorative layer is dried, sprays glazed layer material, and described glazed layer material is by fluorine modified resin, auxiliary agent, function material
Material, pigment are composited, after drying and get final product.
Embodiment 3
Multifunction flexible as shown in Figure 1 imitates stone material, including the main sheet material layers 1 of bottom, middle decorative layer 2, the glazed layer on top layer
3, spray interfacial agents between wherein said decorative layer 2 and main sheet material layers 1, described glazed layer 3 is coated on decorative layer 2, described
Main sheet material layers 1 includes that matrix, base bottom are provided with fibrous layer 5, and centre is provided with grid cloth 4;
Described main sheet material layers 1 thickness is 30mm, and wherein fibrous layer 5 thickness of bottom is 0.2mm, and middle grid cloth 4 is
0.4mm, wherein fibrous layer is polyethylene (can also be chinlon, viscose rayon, acrylon or polyvinyl chloride fibre)；Decorative layer 2 is F-C paint layer
(can also be the colorful enamelled coating of water burnt-in sand, true mineral varnish layer or stone similar paint layer), thickness be 0.8mm, and described resin is fluorine richness tree
Fat, described auxiliary agent includes levelling agent, defoamer, delustering agent, lubricant；
During preparation, step is:
(1) being preheated by aluminum matter mould, matrix material, at 80-100 DEG C, is injected in mould by control temperature, at perfusion Modeling Material
Time, in centre position tiling grid cloth, then proceed to irrigate matrix material, finally tile fibrous layer, and compacting, 70-100 DEG C of temperature
Degree maintenance 5h, forms main sheet material layers after the demoulding；
(2) main sheet material layers maintenance 55h, cleans up surface, sprays interface agent layer, is dried, spraying and decorating layer；
(3) decorative layer is dried, sprays glazed layer material, and described glazed layer material is by fluorine modified resin, auxiliary agent, function material
Material, pigment are composited, after drying and get final product.
Embodiment 4
Multifunction flexible as shown in Figure 1 imitates stone material, including the main sheet material layers 1 of bottom, middle decorative layer 2, the glazed layer on top layer
3, spray interfacial agents between wherein said decorative layer 2 and main sheet material layers 1, described glazed layer 3 is coated on decorative layer 2, described
Main sheet material layers 1 includes that matrix, base bottom are provided with fibrous layer 5, and centre is provided with grid cloth 4;
Described main sheet material layers 1 thickness is 18mm, and wherein fibrous layer 5 thickness of bottom is 0.7mm, and middle grid cloth 4 is
0.8mm, wherein fibrous layer is viscose rayon (can also be terylene, chinlon, acrylon, polyethylene or polyvinyl chloride fibre)；Decorative layer 2 is water bag
The colorful enamelled coating of sand (can also true mineral varnish layer, sliver true mineral varnish layer, stone similar paint layer or F-C paint layer), thickness is 0.5mm, described
Resin be organic siliconresin, described auxiliary agent includes levelling agent, defoamer, delustering agent, lubricant；
During preparation, step is:
(1) being preheated by irony mould, matrix material, at 70-85 DEG C, is injected in mould by control temperature, at perfusion Modeling Material
Time, in centre position tiling grid cloth, then proceed to irrigate matrix material, finally tile fibrous layer, and compacting, 50-80 DEG C of temperature
Degree maintenance 10h, forms main sheet material layers after the demoulding；
(2) main sheet material layers maintenance 48h, cleans up surface, sprays interface agent layer, is dried, spraying and decorating layer；
(3) decorative layer is dried, sprays glazed layer material, and described glazed layer material is by organic siliconresin, auxiliary agent, function material
Material, pigment are composited, after drying and get final product.
Claims (8)
1. multifunction flexible imitates a stone material, including the main sheet material layers of bottom, middle decorative layer, the glazed layer on top layer, decorative layer
And spraying interface agent layer between main sheet material layers, glazed layer is coated on decorative layer, it is characterised in that
Described main sheet material layers includes that matrix, base bottom are provided with fibrous layer, and centre is provided with grid cloth；
Described decorative layer is enamelled coating, including granite enamelled coating, the colorful enamelled coating of water burnt-in sand, true mineral varnish layer, sliver true mineral varnish layer, imitates
Mineral varnish layer or F-C paint layer；
Described glazed layer is made up of resin, auxiliary agent, functional material, pigment mixing.
Multifunction flexible the most according to claim 1 imitates stone material, it is characterised in that described main sheet material layers thickness is 10-
30mm, wherein the fiber layer thickness of bottom is 0.2-1.0mm, and middle grid cloth thickness is 0.2-1.0mm.
Multifunction flexible the most according to claim 1 and 2 imitates stone material, it is characterised in that described fibrous layer is acid and alkali-resistance
Non-woven fabrics, including polypropylene, terylene, chinlon, viscose rayon, acrylon, polyethylene or polyvinyl chloride fibre.
Multifunction flexible the most according to claim 1 and 2 imitates stone material, it is characterised in that described resin is organosilicon tree
Fat or fluorine modified resin, described auxiliary agent includes levelling agent, defoamer, delustering agent, lubricant.
5. the multifunction flexible described in claim 1 imitates the preparation method of stone material, and step is:
(1) being preheated by mould, matrix material, at 60-100 DEG C, is injected in mould by control temperature, when irrigating Modeling Material, in
Centre position tiling grid cloth, then proceedes to irrigate matrix material, and finally tile fibrous layer, compacting, supports 20-100 DEG C of temperature
Protect 1-10h, after the demoulding, form main sheet material layers；
(2) main sheet material layers maintenance 48-72h, cleans up surface, sprays interface agent layer, is dried, spraying and decorating layer；
(3) decorative layer is dried, sprays glazed layer material, and described glazed layer material is by resin, auxiliary agent, functional material, pigment
It is composited, after drying and get final product.
Multifunction flexible the most according to claim 5 imitates the preparation method of stone material, it is characterised in that described mould is
Ferrum, aluminum or silica gel mould.
7. the multifunction flexible described in claim 1 imitates the preparation method of stone material, and step is:
(1) on fibrous layer, scratch matrix material, tiling grid cloth, then proceed to scratch matrix material, at 20 100 DEG C of drying rooms
Middle maintenance, during leather hard, is compacted with the mould being preheating to 50-100 DEG C, moulding, keeps pressure and temperature 5-10 minute,
Main sheet material layers is formed after the demoulding；
(2) main sheet material layers maintenance 48-72h, cleans up surface, sprays interface agent layer, is dried, spraying and decorating layer；
(3) decorative layer is dried, sprays glazed layer material, and described glazed layer material is by resin, auxiliary agent, functional material, pigment
It is composited, after drying and get final product.
Multifunction flexible the most according to claim 7 imitates the preparation method of stone material, it is characterised in that described mould is
Ferrum, aluminum or silica gel mould.