CN106087409A - The clothing of adjustable dimension and technique thereof - Google Patents
The clothing of adjustable dimension and technique thereof Download PDFInfo
- Publication number
- CN106087409A CN106087409A CN201610387576.7A CN201610387576A CN106087409A CN 106087409 A CN106087409 A CN 106087409A CN 201610387576 A CN201610387576 A CN 201610387576A CN 106087409 A CN106087409 A CN 106087409A
- Authority
- CN
- China
- Prior art keywords
- sample
- wool
- fiber
- clothing
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to clothing and the technique thereof of adjustable dimension, in the clothing of this adjustable dimension, the shoulder of clothing is provided with telescopic band and fixing band, with fastener fastening quantity thus it is adjusted shoulder breadth by adjusting the part of taking on telescopic band and fixing band, just can regulate the length at hasp, so shoulder can be adjusted a comfortable size according to the situation of self, more Comfortable attractive when enabling a wearer to wear；Damaged products can be greatly reduced simultaneously, reduce balling-up, good springiness, stability is strong, and drying property can complete in the test short time simultaneously, and test result is the most timely, be conducive to enterprise that water absorption fabric is produced and technology g uarantee, method of testing is simple and practical, it is not necessary to configuring special detection equipment, testing cost is low.
Description
Technical field
The present invention relates to clothing and the technique thereof of adjustable dimension, belong to garment material technical field.
Background technology
At present, the dress ornament on market, there is relative model during the making of dress ornament, model defines the shoulder breadth of clothes, waist
Enclose, clothing height short.Different models has different sizes, but the size of model is but fixing.The bodily form of people has high short and stout
Thin, fat people typically can select the clothes of relatively large size to wear, and the shoulder breadth of clothes is to be suitable for but clothing body can be longer, wears
Seem short and small, it appears unsightly；When thin people wears clothes, when clothing body is suitable, shoulder breadth is relatively big, and clothes seems big, misfits,
Seem unsightly.
The blend fabric of different materials needs to make each component obtain essentially identical color, reduces aberration, just can obtain height
The product of quality.Dyeing to blended yarn weaved fabric at present, the method generally used is to dye fabric respectively, dyes identical dyeing
After dyed yarn, obtain the preferable blended yarn weaved fabric of homochromatism through blending；Or it is good that the repeatedly resisdye of blending grey cloth is obtained homochromatism
Blended yarn weaved fabric.No matter but use which kind of method, its process is the most complicated, and production cost is higher.
Simultaneously as wool fabric has water repellency, moisture content cannot be carried out inside fabric, and many major generals of water suction directly affect survey
The correctness of test result, so its drying property is not tested by conventional wool fabric, also cannot ensure wool fabric
Dehumidifying performance.
Summary of the invention
It is an object of the invention to overcome above-mentioned deficiency, it is provided that one is fit, attractive in appearance when wearing, dyeing can be shortened simultaneously
Time, reduce clothing and the technique thereof of the adjustable dimension of dyeing cost.
The object of the present invention is achieved like this:
A kind of clothing of adjustable dimension, it includes garment body, the shoulder of garment body is provided with telescopic band and fixing band,
Wherein telescopic band includes expansion strip, and expansion strip is provided with multiple part of taking, and fixing band includes fixed strip, fixed strip is provided with many
Individual fastener, described in take part and match with fastener.
Specifically comprising the following steps that of the technique of the clothing of a kind of adjustable dimension
1) selecting wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, described wool fiber is ultra-fine by rabbit fur fibre, beautiful promise
Wool fiber, Angora goat wool fibre and the four kinds of fiber blend braidings of mercerized wool fiber form, described blending rabbit sheep
In wool fibre fabric, percentage by weight shared by each composition is respectively as follows: described rabbit fur fibre and accounts for 18%-22%, the described beautiful ultra-fine sheep of promise
Wool fibre accounts for 15%-19%, and described Angora goat wool fibre accounts for 26%-30%, and described mercerized wool fiber accounts for 29%-41%, to sheep
Wool fibre, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and soft treatment, and anti pilling processes to be selected
Phosphate ester antimony oxide mixture is wool fiber weight as anti pilling agent, phosphate ester antimony oxide amount of mixture
1.5-4%, ferment treatment system uses protease to process, and protease consumption is the 0.1-0.2% of wool fiber weight, at softness
The softening agent that reason is selected is water-soluble organic silicon softening agent, and water-soluble organic silicon softening agent consumption is the 6-of wool fiber weight
8%；
2) fabric again by base inspection → mending → reinspection → tape edge → prewashing → fulling → fine purifiation → dehydration → decatizing → porcupine roller
Fluffing → cropping → raising teasel → wet brush → drying and shaping → hot light；
3) through washing, soap, obtain homochromy blended yarn weaved fabric；
4) drying property of wool fabric is tested:
Step one: lead at 40cm and take two pieces of the sample of 10cm × 20cm on the woolen sample of width as test sample；
Step 2: being placed on by sample in washing appearance device, addition 300ml tetrachloroethylene, as Dry Cleaners, is put into dry-cleaning after sealing
In instrument, take out after dry-cleaning 30min, then repeated washing twice.
Step 3: the loose wool yarn of sample selvedge after cracking-off dry-cleaning, is flat on temperature 20 ± 2 DEG C by sample, and humidity 65 ±
In the environment of 3%, it is put on balance after balancing 12 hours and weighs, claim to obtain the front weight of sample leaching；
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent in 499.5ml distilled water
FFA), the sample after dry-cleaning is placed in beaker fully moisture absorption 1 minute；
Step 5: be two to be hung on airer for clothes by the folding along its length of the sample after moisture absorption, is placed in the airer for clothes hanging with sample
Temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, measures sample weight after 30 minutes, until
Till sample recovers the front weight of leaching；
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.
Compared with prior art, the invention has the beneficial effects as follows:
In the clothing of this adjustable dimension and technique thereof, the shoulder of clothing is provided with telescopic band and fixing band, by adjust telescopic band and
Part of taking on fixing band with fastener fastening quantity thus is adjusted shoulder breadth, it is possible to the length at regulation hasp, such shoulder
A comfortable size can be adjusted, more Comfortable attractive when enabling a wearer to wear according to the situation of self；Face can be made
Material dyes simultaneously, shortens the time of dyeing, reduces dyeing cost；Can be complete in the drying property test short time simultaneously
Becoming, test result is quickly timely, and water absorption fabric is produced and technology g uarantee by beneficially enterprise, and method of testing is simple and practical, no
Needing to configure special detection equipment, testing cost is low.
Detailed description of the invention
The present invention relates to the clothing of a kind of adjustable dimension, it includes garment body, and the shoulder of garment body is provided with
Telescopic band and fixing band, wherein telescopic band includes expansion strip, and expansion strip is provided with multiple part of taking, and fixing band includes fixed strip,
Be provided with multiple fastener on fixed strip, described in take part and match with fastener.
Take part by adjustment and with fastener fastening quantity thus be adjusted shoulder breadth, it is possible to the length at regulation hasp, this
Sample shoulder can be adjusted a comfortable size according to the situation of self, more Comfortable attractive when enabling a wearer to wear.
Specifically comprising the following steps that of the technique of the clothing of a kind of adjustable dimension
1) selecting wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, described wool fiber is ultra-fine by rabbit fur fibre, beautiful promise
Wool fiber, Angora goat wool fibre and the four kinds of fiber blend braidings of mercerized wool fiber form, described blending rabbit sheep
In wool fibre fabric, percentage by weight shared by each composition is respectively as follows: described rabbit fur fibre and accounts for 18%-22%, the described beautiful ultra-fine sheep of promise
Wool fibre accounts for 15%-19%, and described Angora goat wool fibre accounts for 26%-30%, and described mercerized wool fiber accounts for 29%-41%, to sheep
Wool fibre, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and soft treatment, and anti pilling processes to be selected
Phosphate ester antimony oxide mixture is wool fiber weight as anti pilling agent, phosphate ester antimony oxide amount of mixture
1.5-4%, ferment treatment system uses protease to process, and protease consumption is the 0.1-0.2% of wool fiber weight, at softness
The softening agent that reason is selected is water-soluble organic silicon softening agent, and water-soluble organic silicon softening agent consumption is the 6-of wool fiber weight
8%；
2) fabric again by base inspection → mending → reinspection → tape edge → prewashing → fulling → fine purifiation → dehydration → decatizing → porcupine roller
Fluffing → cropping → raising teasel → wet brush → drying and shaping → hot light；
3) through washing, soap, obtain homochromy blended yarn weaved fabric；
4) drying property of wool fabric is tested:
Step one: lead at 40cm and take two pieces of the sample of 10cm × 20cm on the woolen sample of width as test sample；
Step 2: being placed on by sample in washing appearance device, addition 300ml tetrachloroethylene, as Dry Cleaners, is put into dry-cleaning after sealing
In instrument, take out after dry-cleaning 30min, then repeated washing twice.
Step 3: the loose wool yarn of sample selvedge after cracking-off dry-cleaning, is flat on temperature 20 ± 2 DEG C by sample, and humidity 65 ±
In the environment of 3%, it is put on balance after balancing 12 hours and weighs, claim to obtain the front weight of sample leaching；
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent in 499.5ml distilled water
FFA), the sample after dry-cleaning is placed in beaker fully moisture absorption 1 minute；
Step 5: be two to be hung on airer for clothes by the folding along its length of the sample after moisture absorption, is placed in the airer for clothes hanging with sample
Temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, measures sample weight after 30 minutes, until
Till sample recovers the front weight of leaching；
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.
Claims (2)
1. the clothing of an adjustable dimension, it is characterised in that: it includes garment body, the shoulder of garment body is provided with and stretches
Contracting band and fixing band, wherein telescopic band includes expansion strip, and expansion strip is provided with multiple part of taking, and fixing band includes fixed strip, Gu
Determine on bar, to be provided with multiple fastener, described in take part and match with fastener.
The technique of the clothing of a kind of adjustable dimension the most according to claim 1, it is characterised in that:
Specifically comprising the following steps that of drying process
1) selecting wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, described wool fiber is ultra-fine by rabbit fur fibre, beautiful promise
Wool fiber, Angora goat wool fibre and the four kinds of fiber blend braidings of mercerized wool fiber form, described blending rabbit sheep
In wool fibre fabric, percentage by weight shared by each composition is respectively as follows: described rabbit fur fibre and accounts for 18%-22%, the described beautiful ultra-fine sheep of promise
Wool fibre accounts for 15%-19%, and described Angora goat wool fibre accounts for 26%-30%, and described mercerized wool fiber accounts for 29%-41%, to sheep
Wool fibre, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and soft treatment, and anti pilling processes to be selected
Phosphate ester antimony oxide mixture is wool fiber weight as anti pilling agent, phosphate ester antimony oxide amount of mixture
1.5-4%, ferment treatment system uses protease to process, and protease consumption is the 0.1-0.2% of wool fiber weight, at softness
The softening agent that reason is selected is water-soluble organic silicon softening agent, and water-soluble organic silicon softening agent consumption is the 6-of wool fiber weight
8%；
2) fabric again by base inspection → mending → reinspection → tape edge → prewashing → fulling → fine purifiation → dehydration → decatizing → porcupine roller
Fluffing → cropping → raising teasel → wet brush → drying and shaping → hot light；
3) through washing, soap, obtain homochromy blended yarn weaved fabric；
4) drying property of wool fabric is tested:
Step one: lead at 40cm and take two pieces of the sample of 10cm × 20cm on the woolen sample of width as test sample；
Step 2: being placed on by sample in washing appearance device, addition 300ml tetrachloroethylene, as Dry Cleaners, is put into dry-cleaning after sealing
In instrument, take out after dry-cleaning 30min, then repeated washing twice.
Step 3: the wool yarn that after cracking-off dry-cleaning, sample selvedge is loose, is flat on temperature 20 ± 2 DEG C by sample, humidity 65 ± 3%
Under environment, it is put on balance after balancing 12 hours and weighs, claim to obtain the front weight of sample leaching；
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent in 499.5ml distilled water
FFA), the sample after dry-cleaning is placed in beaker fully moisture absorption 1 minute；
Step 5: be two to be hung on airer for clothes by the folding along its length of the sample after moisture absorption, is placed in the airer for clothes hanging with sample
Temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, measures sample weight after 30 minutes, until
Till sample recovers the front weight of leaching；
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.