CN106085238B - A kind of steel surface processing agent with self-repair function - Google Patents
A kind of steel surface processing agent with self-repair function Download PDFInfo
- Publication number
- CN106085238B CN106085238B CN201610376496.1A CN201610376496A CN106085238B CN 106085238 B CN106085238 B CN 106085238B CN 201610376496 A CN201610376496 A CN 201610376496A CN 106085238 B CN106085238 B CN 106085238B
- Authority
- CN
- China
- Prior art keywords
- agent
- steel surface
- base resin
- water
- self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of steel surface processing agent with self-repair function, and mass percent shared by its constituent and each composition is respectively：Carrier water-base resin：30 45%, anti-wear agent：2 5%, sealer：3 5%, conditioning agent：4 10%, acid pickling promotor：2 4%, inorganic particle：3 6%, stabilizer：3 5%, remaining is deionized water；Carrier water-base resin is the mixture of water-base resin, lubricating oil and dilval powder, and passes through activation process.The present invention has significant repair for the impaired surface like steel of friction, and the steel surface after reparation still has outstanding wearability；It can effectively remove that oxide, scavenging period that steel surface may contain are short, product is environmentally friendly simultaneously, and can make steel surface that there is outstanding anti-corrosion effect.
Description
Technical field
The invention belongs to steel surface processing technology field, and in particular at a kind of steel surface with self-repair function
Manage agent.
Background technology
Wearing down with loss for material is a common phenomenon on engineering goods, especially after steel surface wears extremely
Easily cause that the operation of whole plant equipment is not smooth or even can not run, once and the contact surface of steel be damaged, cause its by
Damage part gets rusty easily, and removes the operation that can equally influence whole plant equipment not in time.
Therefore, it is people in the art to develop a kind of inorganic agent for being used to be damaged steel surface processing for problem above
Member institute urgent need to solve the problem.
The content of the invention
To solve the above problems, the invention discloses a kind of steel surface processing agent with self-repair function.
In order to achieve the above object, the present invention provides following technical scheme：
Mass percent shared by a kind of steel surface processing agent with self-repair function, its constituent and each composition
Respectively：Carrier water-base resin：30-45%, anti-wear agent：2-5%, sealer：3-5%, conditioning agent：4-10%, acid pickling promotor：2-
4%th, inorganic particle：3-6%, stabilizer：3-5%, remaining be deionized water；Carrier water-base resin be water-base resin, lubricating oil and
The mixture of dilval powder, and pass through activation process.
Preferably, water-base resin, lubricating oil and dilval powder account for the white difference of carrier water-base resin gross mass
Respectively：35-52%、30-50%、8-18%.
Preferably, the method for activation process is：It is cooled to after contacting 2-3h using polyvinylpyrrolidone steam
Room temperature.
Preferably, anti-wear agent is crystalline flake graphite.
Preferably, sealer is concentration 10-20% sealer.
Preferably, conditioning agent is pH value conditioning agent and defoamer.
Preferably, mass percent shared by the constituent of inorganic particle and each composition is：TiO2：40-58%、
Al2O3：30-45%、SiO2：8-20%.
Preferably, stabilizer is sorbester p18 or Tween 80.
The invention provides a kind of steel surface processing agent with self-repair function, by carrier water-base resin, anti-wear agent,
Sealer, conditioning agent, acid pickling promotor, inorganic particle, stabilizer and deionized water composition.Wherein carrier water-base resin conduct
The carrier of other compositions in the present invention, by water-base resin, lubricating oil and dilval powder, carried based on water-base resin
Body, mix with lubricating oil, there is significant lubricant effect for some steel surfaces being among friction, while be also mixed with
Dilval powder, for playing certain filling effect to the impaired part that rubs；The addition of anti-wear agent causes painting of the present invention
Certain abrasion resistant effect can be played when being put on steel surface；The addition of sealer causes the present invention to have very high anti-corrosion
And extremely strong adhesive force；Conditioning agent is made up of pH value conditioning agent and defoamer, is respectively used to adjust the pH value of steel surface
And the defoaming in processing procedure；The addition of acid pickling promotor, which not only allows the invention to effectively to remove steel surface, to be difficult to clearly
The oxide skin removed, greatly shortens processing time；The corrosion rate of steel surface can be substantially reduced, while smog can be suppressed
Produce, substantially improve processing environment；The addition of inorganic particle can play certain modifying function；Stabilizer selection is sorbester p18
Or one kind in Tween 80, stabilizer during each composition mixing in the present invention can either be ensured, while can also ensure this hair
The stabilizer of bright finished product, reduce finished surface tension force, prevent light, thermal decomposition.
The present invention has significant repair compared with prior art, for the impaired surface like steel that rubs, and repaiies
Steel surface after multiple still has outstanding wearability；Can effectively remove simultaneously oxide that steel surface may contain,
Scavenging period is short, product is environmentally friendly, and steel surface can be made to have outstanding anti-corrosion effect.
Embodiment
Technical scheme provided by the invention is described in detail below with reference to specific embodiment, it should be understood that following specific
Embodiment is only illustrative of the invention and is not intended to limit the scope of the invention.
Embodiment 1：
The present invention is a kind of steel surface processing agent with self-repair function, matter shared by its constituent and each composition
Measuring percentage is respectively：Carrier water-base resin：30%th, anti-wear agent：2%th, sealer：3%th, conditioning agent：4%th, acid pickling promotor：2%、
Inorganic particle：3%th, stabilizer：3%th, remaining is deionized water.
Carrier water-base resin be water-base resin, lubricating oil and dilval powder mixture, water-base resin, lubricating oil
And dilval powder accounts for the white of carrier water-base resin gross mass and is respectively respectively：35%、50%、15%；And at overactivation
Reason；The method of activation process is：Room temperature is cooled to after contacting 2-3h using polyvinylpyrrolidone steam.
Anti-wear agent is crystalline flake graphite.
Sealer is the sealer of concentration 10%.
Conditioning agent is pH value conditioning agent and defoamer.
Mass percent shared by the constituent of inorganic particle and each composition is：TiO2：40%、Al2O3：45%、SiO2：
15%。
Stabilizer is sorbester p18.
Embodiment 2：
The present invention is a kind of steel surface processing agent with self-repair function, matter shared by its constituent and each composition
Measuring percentage is respectively：Carrier water-base resin：45%th, anti-wear agent：5%th, sealer：5%th, conditioning agent：10%th, acid pickling promotor：4%、
Inorganic particle：6%th, stabilizer：5%th, remaining is deionized water.
Carrier water-base resin be water-base resin, lubricating oil and dilval powder mixture, water-base resin, lubricating oil
And dilval powder accounts for the white of carrier water-base resin gross mass and is respectively respectively：52%、30%、18%；And at overactivation
Reason；The method of activation process is：Room temperature is cooled to after contacting 3h using polyvinylpyrrolidone steam.
Anti-wear agent is crystalline flake graphite.
Sealer is the sealer of concentration 20%.
Conditioning agent is pH value conditioning agent and defoamer.
Mass percent shared by the constituent of inorganic particle and each composition is：TiO2：58%、Al2O3：30%、SiO2：
12%。
Stabilizer is Tween 80.
Embodiment 3：
The present invention is a kind of steel surface processing agent with self-repair function, matter shared by its constituent and each composition
Measuring percentage is respectively：Carrier water-base resin：40%th, anti-wear agent：3%th, sealer：4%th, conditioning agent：7%th, acid pickling promotor：3%、
Inorganic particle：5%th, stabilizer：4%th, remaining is deionized water.
Carrier water-base resin be water-base resin, lubricating oil and dilval powder mixture, water-base resin, lubricating oil
And dilval powder accounts for the white of carrier water-base resin gross mass and is respectively respectively：45%、45%、10%；And at overactivation
Reason；The method of activation process is：Room temperature is cooled to after contacting 3h using polyvinylpyrrolidone steam.
Anti-wear agent is crystalline flake graphite.
Sealer is the sealer of concentration 20%.
Conditioning agent is pH value conditioning agent and defoamer.
Mass percent shared by the constituent of inorganic particle and each composition is：TiO2：50%、Al2O3：37%、SiO2：
13%。
Stabilizer is Tween 80.
Steel surface is handled by the steel surface processing agent in three above embodiment, found impaired to rubbing
Steel be respectively provided with it is certain repair planarization effects, and the reparation planarization effects of embodiment 3 are optimal, while the cleaning of embodiment 3 is resistance to
Erosion effect is preferably also.
It is last it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention and non-limiting technical side
Case, it will be understood by those within the art that, technical scheme is modified for those or equivalent substitution, and
The objective and scope of the technical program are not departed from, all should be covered among scope of the presently claimed invention.
Claims (5)
- A kind of 1. steel surface processing agent with self-repair function, it is characterised in that：Shared by its constituent and each composition Mass percent is respectively：Carrier water-base resin：30-45%, anti-wear agent：2-5%, sealer：3-5%, conditioning agent：4-10%, acid Wash accelerator：2-4%, inorganic particle：3-6%, stabilizer：3-5%, remaining be deionized water；The carrier water-base resin is water-based The mixture of resin, lubricating oil and dilval powder, and pass through activation process；The water-base resin, lubricating oil and The percentage that dilval powder accounts for carrier water-base resin gross mass is respectively：35-52%、30-50%、8-18%；At the activation The method of reason is：Room temperature is cooled to after contacting 2-3h using polyvinylpyrrolidone steam；The conditioning agent is adjusted for pH value Save agent and defoamer.
- A kind of 2. steel surface processing agent with self-repair function according to claim 1, it is characterised in that：It is described resistance to Grinding agent is crystalline flake graphite.
- A kind of 3. steel surface processing agent with self-repair function according to claim 1, it is characterised in that：The envelope Close the sealer that agent is concentration 10-20%.
- A kind of 4. steel surface processing agent with self-repair function according to claim 1, it is characterised in that：The nothing Mass percent shared by the constituent of machine powder and each composition is：TiO2：40-58%、Al2O3：30-45%、SiO2：8- 20%。
- A kind of 5. steel surface processing agent with self-repair function according to claim 1, it is characterised in that：It is described steady It is sorbester p18 or Tween 80 to determine agent.