CN106084461A - A kind of method that high-polarity polypropylene resin material is prepared in Rhizoma Seu Herba Bergeniae modification - Google Patents
A kind of method that high-polarity polypropylene resin material is prepared in Rhizoma Seu Herba Bergeniae modification Download PDFInfo
- Publication number
- CN106084461A CN106084461A CN201610477144.5A CN201610477144A CN106084461A CN 106084461 A CN106084461 A CN 106084461A CN 201610477144 A CN201610477144 A CN 201610477144A CN 106084461 A CN106084461 A CN 106084461A
- Authority
- CN
- China
- Prior art keywords
- prepared
- seu herba
- rhizoma seu
- herba bergeniae
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method that high-polarity polypropylene resin material is prepared in Rhizoma Seu Herba Bergeniae modification, belong to polyacrylic resin material preparing technical field.The present invention takes the mixing such as peptone, potassium phosphate, Selective agar medium is prepared after high temperature sterilize, inoculation Flavobacterium cultivate Flavobacterium cultivate bacterium colony standby, collection Rhizoma Seu Herba Bergeniae leaf is milled after sieving and is obtained mixed serum, mix high temperature sterilize with acrylic resin, magnesium sulfate etc. and obtain Rhizoma Seu Herba Bergeniae resin mixture liquor, inoculation Flavobacterium cultivate bacterium colony ferment mixed liquor, through being evaporated to dryness, prepare high-polarity polypropylene resin material with hydraulic giant rinsing, drying.The invention has the beneficial effects as follows: preparation process of the present invention is simple, surface can be high, reaches 38.3 × 10‑5~39.2 × 10‑5N is high with the adhesion strength of coating;Products obtained therefrom is good with the polar polymer compatibility, easily infiltrates bonding after using, and paintability improves 20~25%.
Description
Technical field
The present invention relates to a kind of method that high-polarity polypropylene resin material is prepared in Rhizoma Seu Herba Bergeniae modification, belong to acrylic resin
Technical field of material.
Background technology
Polypropylene, is a kind of thermoplastic resin prepared by propylene polymerization.The highly crystallized in compound with regular structure, thus molten
Point may be up to 167 DEG C.Heat-resisting, corrosion-resistant, the sterilization of goods used vapour is its outstanding advantages.Density is little, is the lightest general plastic
Material.Shortcoming is that low-temperature impact resistance is poor, and electrostatic degree is high, contacts the most aging with copper, and dyeability, printing and adhesion are poor.Poly-third
Alkene is polymer nontoxic, that odorless, tasteless milky are highly crystalline, and density only has 0.90~0.91g/cm3, it is the most all moulding
One of kind the lightest in material.It is particularly stable to water, and the water absorption rate in water is only 0.01%, molecular weight about 80,000~150,000.
Good moldability, but because shrinkage factor is big (being 1%~2.5%).Thick article easily caves in, part higher to some dimensional accuracies, is difficult to
In reaching requirement.Therefore needing it modified, the method to its modification has blending and modifying and cross-linking modified method at present, and PA, ABS etc. are firm
Property polymer and PP intensity and the rigidity that then can toughness reinforcing while ensure material is blended.But due to this kind of rigid polymer
Being all polar polymer, and PP material is non-polar material, surface can be low so that it is both compatibilitys are poor, is difficult to infiltration, bonding
With printing, paintability is poor.Polyacrylic cross-linking modified during degraded and cross-linking reaction exist simultaneously, use crosslinking with radiation time
Cross-linking efficiency ratio is relatively low, and is typically all when using chemical crosslinking and promotes to hand over the cross-linking system that helps of unsaturated bond by addition
Connection reaction.
Summary of the invention
The technical problem to be solved: prepare polyacrylic resin material for blending modification method, due to polypropylene
Material is non-polar material, and surface can be low so that poor with PA, ABS compatibility, is difficult to infiltration, bonds and print, paintability
The drawback of difference, it is provided that one takes the mixing such as peptone, potassium phosphate, prepares Selective agar medium after high temperature sterilize, the yellow bar of inoculation
Bacterium cultivate Flavobacterium cultivate bacterium colony standby, gather Rhizoma Seu Herba Bergeniae leaf mill sieve after mixed serum, with acrylic resin, sulphuric acid
The mixing high temperature sterilize such as magnesium obtains Rhizoma Seu Herba Bergeniae resin mixture liquor, inoculation Flavobacterium cultivate bacterium colony fermentation mixed liquor, through evaporating
To dry, the method preparing high-polarity polypropylene resin material with hydraulic giant rinsing, drying.The present invention decomposes Rhizoma Seu Herba Bergeniae by Flavobacterium
Organic substance in liquid, by compound Bergeninum uniform load highly polar in Rhizoma Seu Herba Bergeniae to polypropylene material surface, is effectively improved it
Polar intensity, preparation process of the present invention is simple, and surface polarity can be high, the problem efficiently solving polarity of polypropylene difference, and gained produces
Product easily infiltrate bonding, and paintability is good.
For solving above-mentioned technical problem, the present invention uses the technical scheme as described below to be:
(1) count by weight, weigh respectively 65~85 parts of deionized waters, 5~10 parts of peptones, 5~10 parts of glucoses, 2~7
Part potassium phosphate and 3~8 parts of magnesium sulfate are placed in culture dish, and stirring mixing is placed in high temperature sterilize at 100~105 DEG C and processes, with
Rear standing cooling is prepared into Selective agar medium;
(2) by Flavobacterium that strain number is 209202 by inoculum concentration 10%, it is seeded on the Selective agar medium of above-mentioned preparation, controls
Cultivation temperature 37~38 DEG C, be placed in 200~250r/min shaking tables shaken cultivation 2~3 days, be prepared into Flavobacterium and cultivate bacterium
Fall, standby;
(3) gather Rhizoma Seu Herba Bergeniae leaf, cleaned to dry and be placed in mortar, it milled and crosses 60~80 mesh sieves, being prepared into rock
Chinese cabbage mixed serum, then count by weight, weigh 40~55 part 20~40 mesh acrylic resins, 35~40 parts of above-mentioned systems respectively
Standby Rhizoma Seu Herba Bergeniae mixed serum, 5~10 parts of potassium phosphates and 5~10 parts of magnesium sulfate are placed in culture dish, high at 100~105 DEG C
Temperature sterilization treatment 10~15min, is prepared into Rhizoma Seu Herba Bergeniae resin mixture liquor;
(4) by inoculum concentration 10%, the Flavobacterium that step (2) is cultivated is seeded in the Rhizoma Seu Herba Bergeniae resin mixture liquor of above-mentioned preparation, control
Cultivation temperature 37 processed~38 DEG C, be placed in 200~250r/min shaking tables shaken cultivation 5~7 days, collect and obtaining fermentation mixing
Liquid;
(5) the fermentation mixed liquor of above-mentioned preparation is placed in rotary evaporated to dryness at 65~80 DEG C, is prepared into dry mixed modification tree
Fat, then dry mixed modification resin is placed on 50~60 eye mesh screens, it is rinsed with the hydraulic giant of 50mm diameter, controls hydraulic giant stream
Speed is 10~15m/s, to be rinsed to resin surface without Rhizoma Seu Herba Bergeniae leaf residue after, be placed at 65~80 DEG C be dried 6~8h, i.e.
A kind of high-polarity polypropylene resin material can be prepared into.
The high-polarity polypropylene resin material vicat softening temperature that the present invention prepares is 148~150 DEG C, hot torsion temperature
100 DEG C, shrinkage factor is 1.2~1.3%, and hot strength is 75~85MPa, and bending strength is 80~122MPa, and bending modulus is
3000~3700MPa, heat resisting temperature is 135~145 DEG C.
The present invention is compared with additive method, and Advantageous Effects is:
(1) preparation process of the present invention is simple, and surface can be high, reaches 38.3 × 10-5~39.2 × 10-5N is strong with the bonding of coating
Degree height;
(2) products obtained therefrom is good with the polar polymer compatibility, easily infiltrates bonding after using, and paintability improves 20~25%.
Detailed description of the invention
Count the most by weight, weigh 65~85 portions of deionized waters, 5~10 portions of peptones, 5~10 portions of Fructus Vitis viniferaes respectively
Sugar, 2~7 parts of potassium phosphates and 3~8 parts of magnesium sulfate are placed in culture dish, and stirring mixing is placed in high temperature sterilize at 100~105 DEG C
Process, stand cooling subsequently and be prepared into Selective agar medium;Then by Flavobacterium that strain number is 209202 by inoculum concentration 10%, connect
Plant to the Selective agar medium of above-mentioned preparation, control cultivation temperature 37~38 DEG C, be placed in 200~250r/min shaking tables and shake
Swing cultivation 2~3 days, be prepared into Flavobacterium and cultivate bacterium colony, standby;Gather Rhizoma Seu Herba Bergeniae leaf, cleaned to dry and be placed in mortar,
It milled and crosses 60~80 mesh sieves, being prepared into Rhizoma Seu Herba Bergeniae mixed serum, then count by weight, weighing 40~55 part 20 respectively
~40 mesh acrylic resins, the Rhizoma Seu Herba Bergeniae mixed serum of 35~40 parts of above-mentioned preparations, 5~10 parts of potassium phosphates and 5~10 parts of sulphuric acid
Magnesium is placed in culture dish, and at 100~105 DEG C, high temperature sterilize processes 10~15min, is prepared into Rhizoma Seu Herba Bergeniae resin mixture liquor;Press
Inoculum concentration 10%, is seeded to the Flavobacterium of cultivation in the Rhizoma Seu Herba Bergeniae resin mixture liquor of above-mentioned preparation, controls cultivation temperature 37~38
DEG C, it is placed in 200~250r/min shaking tables shaken cultivation 5~7 days, collects and to obtain fermentation mixed liquor;Finally by above-mentioned preparation
Fermentation mixed liquor be placed in rotary evaporated to dryness at 65~80 DEG C, be prepared into dry mixed modification resin, then dry mixed changed
Property resin be placed on 50~60 eye mesh screens, be rinsed with the hydraulic giant of 50mm diameter, control hydraulic giant flow velocity be 10~15m/s, treat
Rinse to resin surface without Rhizoma Seu Herba Bergeniae leaf residue after, be placed at 65~80 DEG C be dried 6~8h, a kind of high pole can be prepared into
Property polyacrylic resin material.
Example 1
Count the most by weight, weigh 65 parts of deionized waters, 10 parts of peptones, 10 parts of glucoses, 7 parts of potassium phosphates and 8 respectively
Part magnesium sulfate is placed in culture dish, and stirring mixing is placed in high temperature sterilize at 100 DEG C and processes, and stands cooling subsequently and is prepared into selection
Culture medium;Then by Flavobacterium that strain number is 209202 by inoculum concentration 10%, it is seeded on the Selective agar medium of above-mentioned preparation,
Control cultivation temperature 37 DEG C, be placed on shaken cultivation 2 days in 200r/min shaking table, be prepared into Flavobacterium and cultivate bacterium colony, standby;
Gather Rhizoma Seu Herba Bergeniae leaf, cleaned to dry and be placed in mortar, it is milled and crosses 60 mesh sieves, be prepared into Rhizoma Seu Herba Bergeniae and mix and starch
Liquid, then count by weight, weigh respectively 40 part of 20 mesh acrylic resin, the Rhizoma Seu Herba Bergeniae mixed serum of 40 parts of above-mentioned preparations, 10
Part potassium phosphate and 10 parts of magnesium sulfate are placed in culture dish, and at 100 DEG C, high temperature sterilize processes 10min, is prepared into Rhizoma Seu Herba Bergeniae resin
Mixed liquor;By inoculum concentration 10%, the Flavobacterium of cultivation is seeded in the Rhizoma Seu Herba Bergeniae resin mixture liquor of above-mentioned preparation, controls to cultivate
Temperature 37 DEG C, is placed on shaken cultivation 5 days in 200r/min shaking table, collects to obtain fermentation mixed liquor;Finally by above-mentioned preparation
Fermentation mixed liquor is placed in rotary evaporated to dryness at 65 DEG C, is prepared into dry mixed modification resin, then by dry mixed modification resin
Being placed on 50 eye mesh screens, be rinsed with the hydraulic giant of 50mm diameter, controlling hydraulic giant flow velocity is 10m/s, to be rinsed to resin surface
After the residue of leaf without Rhizoma Seu Herba Bergeniae, it is placed at 65 DEG C and is dried 6h, a kind of high-polarity polypropylene resin material can be prepared into.This
Bright preparation process is simple, and surface can be high, reaches 38.3 dyne/cm2, high with the adhesion strength of coating;Products obtained therefrom gathers with polarity
The compound compatibility is good, easily infiltrates bonding after using, and paintability improves 20%;The high-polarity polypropylene resin material dimension prepared
Card softening temperature is 148 DEG C, hot torsion temperature 100 DEG C, and shrinkage factor is 1.2%, and hot strength is 75MPa, and bending strength is
80MPa, bending modulus is 3000MPa, and heat resisting temperature is 135 DEG C.
Example 2
Count the most by weight, weigh 75 parts of deionized waters, 8 parts of peptones, 7 parts of glucoses, 5 parts of potassium phosphates and 5 parts respectively
Magnesium sulfate is placed in culture dish, and stirring mixing is placed in high temperature sterilize at 103 DEG C and processes, and stands cooling subsequently and is prepared into selection training
Support base;Then by Flavobacterium that strain number is 209202 by inoculum concentration 10%, it is seeded on the Selective agar medium of above-mentioned preparation, control
Cultivation temperature processed 38 DEG C, is placed on shaken cultivation 3 days in 225r/min shaking table, is prepared into Flavobacterium and cultivates bacterium colony, standby;Adopt
Collection Rhizoma Seu Herba Bergeniae leaf, is cleaned to dry and is placed in mortar, mill it and cross 70 mesh sieves, being prepared into Rhizoma Seu Herba Bergeniae mixed serum,
Count the most by weight, weigh 47 part of 30 mesh acrylic resin, the Rhizoma Seu Herba Bergeniae mixed serum of 38 parts of above-mentioned preparations, 7 parts of phosphorus respectively
Acid potassium and 8 parts of magnesium sulfate are placed in culture dish, and at 103 DEG C, high temperature sterilize processes 13min, is prepared into Rhizoma Seu Herba Bergeniae mixed with resin
Liquid;By inoculum concentration 10%, the Flavobacterium of cultivation is seeded in the Rhizoma Seu Herba Bergeniae resin mixture liquor of above-mentioned preparation, controls cultivation temperature
38 DEG C, it is placed on shaken cultivation 6 days in 225r/min shaking table, collects to obtain fermentation mixed liquor;Finally by the fermentation of above-mentioned preparation
Mixed liquor is placed in rotary evaporated to dryness at 72 DEG C, is prepared into dry mixed modification resin, then is placed in by dry mixed modification resin
On 55 eye mesh screens, be rinsed with the hydraulic giant of 50mm diameter, control hydraulic giant flow velocity be 13m/s, to be rinsed to resin surface without rock
After Chinese cabbage leaf residue, it is placed at 72 DEG C and is dried 7h, a kind of high-polarity polypropylene resin material can be prepared into.System of the present invention
Standby step is simple, and surface can be high, reaches 38.7 dyne/cm2, high with the adhesion strength of coating;Products obtained therefrom and polar polymer
The compatibility is good, easily infiltrates bonding after using, and paintability improves 23%;The high-polarity polypropylene resin material dimension card prepared is soft
Changing temperature is 149 DEG C, hot torsion temperature 100 DEG C, and shrinkage factor is 1.3%, and hot strength is 80MPa, and bending strength is 101MPa,
Bending modulus is 3350MPa, and heat resisting temperature is 140 DEG C.
Example 3
Count the most by weight, weigh 85 parts of deionized waters, 5 parts of peptones, 5 parts of glucoses, 2 parts of potassium phosphates and 3 parts respectively
Magnesium sulfate is placed in culture dish, and stirring mixing is placed in high temperature sterilize at 105 DEG C and processes, and stands cooling subsequently and is prepared into selection training
Support base;Then by Flavobacterium that strain number is 209202 by inoculum concentration 10%, it is seeded on the Selective agar medium of above-mentioned preparation, control
Cultivation temperature processed 38 DEG C, is placed on shaken cultivation 3 days in 250r/min shaking table, is prepared into Flavobacterium and cultivates bacterium colony, standby;Adopt
Collection Rhizoma Seu Herba Bergeniae leaf, is cleaned to dry and is placed in mortar, mill it and cross 80 mesh sieves, being prepared into Rhizoma Seu Herba Bergeniae mixed serum,
Count the most by weight, weigh 55 part of 40 mesh acrylic resin, the Rhizoma Seu Herba Bergeniae mixed serum of 35 parts of above-mentioned preparations, 5 parts of phosphorus respectively
Acid potassium and 5 parts of magnesium sulfate are placed in culture dish, and at 105 DEG C, high temperature sterilize processes 15min, is prepared into Rhizoma Seu Herba Bergeniae mixed with resin
Liquid;By inoculum concentration 10%, the Flavobacterium of cultivation is seeded in the Rhizoma Seu Herba Bergeniae resin mixture liquor of above-mentioned preparation, controls cultivation temperature
38 DEG C, it is placed on shaken cultivation 7 days in 250r/min shaking table, collects to obtain fermentation mixed liquor;Finally by the fermentation of above-mentioned preparation
Mixed liquor is placed in rotary evaporated to dryness at 80 DEG C, is prepared into dry mixed modification resin, then is placed in by dry mixed modification resin
On 60 eye mesh screens, be rinsed with the hydraulic giant of 50mm diameter, control hydraulic giant flow velocity be 15m/s, to be rinsed to resin surface without rock
After Chinese cabbage leaf residue, it is placed at 80 DEG C and is dried 8h, a kind of high-polarity polypropylene resin material can be prepared into.System of the present invention
Standby step is simple, and surface can be high, reaches 39.2 dyne/cm2, high with the adhesion strength of coating;Products obtained therefrom and polar polymer
The compatibility is good, easily infiltrates bonding after using, and paintability improves 25%;The high-polarity polypropylene resin material dimension card prepared is soft
Changing temperature is 150 DEG C, hot torsion temperature 100 DEG C, and shrinkage factor is 1.3%, and hot strength is 85MPa, and bending strength is 122MPa,
Bending modulus is 3700MPa, and heat resisting temperature is 145 DEG C.
Claims (1)
1. the method that high-polarity polypropylene resin material is prepared in a Rhizoma Seu Herba Bergeniae modification, it is characterised in that concrete preparation process is:
(1) count by weight, weigh respectively 65~85 parts of deionized waters, 5~10 parts of peptones, 5~10 parts of glucoses, 2~7
Part potassium phosphate and 3~8 parts of magnesium sulfate are placed in culture dish, and stirring mixing is placed in high temperature sterilize at 100~105 DEG C and processes, with
Rear standing cooling is prepared into Selective agar medium;
(2) by Flavobacterium that strain number is 209202 by inoculum concentration 10%, it is seeded on the Selective agar medium of above-mentioned preparation, controls
Cultivation temperature 37~38 DEG C, be placed in 200~250r/min shaking tables shaken cultivation 2~3 days, be prepared into Flavobacterium and cultivate bacterium
Fall, standby;
(3) gather Rhizoma Seu Herba Bergeniae leaf, cleaned to dry and be placed in mortar, it milled and crosses 60~80 mesh sieves, being prepared into rock
Chinese cabbage mixed serum, then count by weight, weigh 40~55 part 20~40 mesh acrylic resins, 35~40 parts of above-mentioned systems respectively
Standby Rhizoma Seu Herba Bergeniae mixed serum, 5~10 parts of potassium phosphates and 5~10 parts of magnesium sulfate are placed in culture dish, high at 100~105 DEG C
Temperature sterilization treatment 10~15min, is prepared into Rhizoma Seu Herba Bergeniae resin mixture liquor;
(4) by inoculum concentration 10%, the Flavobacterium that step (2) is cultivated is seeded in the Rhizoma Seu Herba Bergeniae resin mixture liquor of above-mentioned preparation, control
Cultivation temperature 37 processed~38 DEG C, be placed in 200~250r/min shaking tables shaken cultivation 5~7 days, collect and obtaining fermentation mixing
Liquid;
(5) the fermentation mixed liquor of above-mentioned preparation is placed in rotary evaporated to dryness at 65~80 DEG C, is prepared into dry mixed modification tree
Fat, then dry mixed modification resin is placed on 50~60 eye mesh screens, it is rinsed with the hydraulic giant of 50mm diameter, controls hydraulic giant stream
Speed is 10~15m/s, to be rinsed to resin surface without Rhizoma Seu Herba Bergeniae leaf residue after, be placed at 65~80 DEG C be dried 6~8h, i.e.
A kind of high-polarity polypropylene resin material can be prepared into.