CN106042105A - Pine and bamboo particle recombination board and manufacturing method thereof - Google Patents

Pine and bamboo particle recombination board and manufacturing method thereof Download PDF

Info

Publication number
CN106042105A
CN106042105A CN201610560840.2A CN201610560840A CN106042105A CN 106042105 A CN106042105 A CN 106042105A CN 201610560840 A CN201610560840 A CN 201610560840A CN 106042105 A CN106042105 A CN 106042105A
Authority
CN
China
Prior art keywords
bamboo
netted
granule
pine
spongiosa
Prior art date
Application number
CN201610560840.2A
Other languages
Chinese (zh)
Inventor
曹淦钦
王海林
Original Assignee
江西达森家私有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 江西达森家私有限公司 filed Critical 江西达森家私有限公司
Priority to CN201610560840.2A priority Critical patent/CN106042105A/en
Publication of CN106042105A publication Critical patent/CN106042105A/en

Abstract

The invention belongs to the technical field of composite plates, and relates to a pine and bamboo particle recombination board and a manufacturing method thereof. The manufacturing method comprises the following steps: weaving bamboo skin strips in a staggering manner to form a bottom mesh grid and a surface mesh grid; placing a pine particle blended sizing material between the bottom mesh grid and the surface mesh grid in a filling manner, performing high-temperature and high-pressure treatment to obtain a pine and bamboo particle recombination board blank, grinding and polishing the bottom and the surface of the pine and bamboo particle recombination board blank, and cutting to obtain the pine and bamboo particle recombination board finished product. According to the pine and bamboo particle recombination board and the manufacturing method thereof, the problem that the conventional multilayer bonded board is easy to degum and open is thoroughly solved, and the surface bonding strength of the board is greatly enhanced.

Description

Pine bamboo granule recombination plates and manufacture method thereof
Technical field
The invention belongs to composite plate technical field, be specifically related to a kind of pine bamboo granule recombination plates and manufacture method thereof.
Background technology
The south China miscellaneous material aboundresources of pine, especially Pinus massoniana Lamb.Owing to Pinus massoniana Lamb footpath material furuncle scar is many, bending big, texture Staggered difficulty of drawing materials, so causing the waste of utilization rate of raw materials low-resource big.All kinds of bamboo canes, Garcinia mangostana the main place of production also in south Side, but because deep development is inadequate, the utilization rate of bamboo is the lowest.
CN204869124U provides a kind of full bamboo and bamboo wood laminated particle-board, it is characterised in that this laminated particle-board includes Top layer and sandwich layer, top layer is divided into upper epidermis and layer, upper epidermis to use full bamboo or bamboo wood compos-ite fine particles glue mixing pressure with layer System forms, and sandwich layer is clipped between upper epidermis and layer, and sandwich layer uses full bamboo or bamboo wood to be combined coarse grain glue mixing compacting and forms.This is special Although profit can utilize Song Hezhu, but bamboo and wood bond after being all broken into granule, do not make full use of bamboo toughness and intensity.
CN 102773888 A discloses a kind of thin bamboo strips used for weaving plywood and the fast preparation method of laminated timber, and its method is: will execute Thin bamboo strips used for weaving after glue is put in hot press with orthogonal to mating formation into thin bamboo strips used for weaving plywood or forward mating formation into thin bamboo strips used for weaving laminated board, uses height Temperature, high pressure realize the solidification of adhesive in sheet material, and then high-pressure molding forms plate product;After continue, not reducing in hot press Under conditions of hot pressing temperature, implement the stress-relief process of more than three sections, make hot press inner plate surface pressure drop to zero from high pressure;Panel Interior steam discharges in order;Finally take out finished product.This patent takes full advantage of the performance of thin bamboo strips used for weaving, but cannot utilize Masson Pine grain.
CN102398287B discloses a kind of method for producing bamboo-wood composite board, the thin bamboo strips used for weaving bar that drying is obtained by it through applying glue, Hot pressing, cooling prepare dash board, and through applying glue, hot pressing, cooling, wood granule is prepared central layer, central layer, dash board are carried out applying glue, hot pressing, Cool down to obtain bamboo grove composite plate.There is easy degumming, problem easy to open in this bamboo grove composite plate, the combination between central layer and dash board is not Enough firm.
Summary of the invention
In order to improve the utilization rate of spongiosa granule and bamboo, obtain tensile property good, the bamboo-wood plyboard that anti-pressure ability is strong, this Invention provides a kind of pine bamboo granule recombination plates manufacture method, the loose bamboo granule recombination plates prepared, and thoroughly solves multilamellar The easy degumming of pressing, opening problem, greatly improve the face bond strength of sheet material.Use spongiosa granule and bamboo matter grid recombination form The loose bamboo granule recombination plates produced, can improve pine bamboo former material utilization rate, reduces pine bamboo resource waste.Due to formula simple material Being easy to get, physical and chemical index is easily-controllable and sexual valence is high, and value-added space is more suitable for greatly batch production.
The present invention is realized by following technical proposals.
A kind of pine bamboo granule recombination plates manufacture method, it is characterised in that: thin bamboo strips used for weaving strand weaving is reticulated bottom sieve frame and Netted lattice;Spongiosa granule mixes and stirs sizing material and is filled between netted bottom sieve frame and netted lattice, obtains pine after high temperature high pressure process Bamboo granule recombination plates blank, then the end and the face of pine bamboo granule recombination plates blank are carried out sanding and polishing, cut after obtain Song Zhu Granule recombination plates finished product.
Further preferably, spongiosa granule is mixed and stirred and is filled between netted bottom sieve frame and netted lattice without urea formaldehyde glue, netted Defining spongiosa particle board core between bottom sieve frame and netted lattice, spongiosa granule also fills up the mesh at netted bottom sieve frame Yu netted lattice In.
Further preferably, first the bamboo of length 2500mm is peeled into 0.3mm book sheet, the most again by the bamboo matter book of 0.3mm Sheet is divided into wide 3mm strip thin bamboo strips used for weaving strand stand-by.
Further preferably, the width of thin bamboo strips used for weaving strand is 2-5mm, and thin bamboo strips used for weaving strand is woven into netted bottom sieve frame and the net of netted lattice Hole size is: the length of side of 2-5mm × 2-5mm, preferably mesh is equal to the width of thin bamboo strips used for weaving strand.
Further preferably, the distance between described netted bottom sieve frame and netted lattice is 10-25mm, most preferably 18mm.
Further preferably, epidermis and pine miscellaneous footpath material, the brush wood rotary-cut in corrupt source will be removed or smash into diameter 1-2mm's to pieces Spongiosa granule, spongiosa granule drying again, defat, bleaching.
Further preferably, a diameter of 1-2mm of described spongiosa granule.
Pine bamboo granule recombination plates of the present invention, is first that pine bamboo raw material resources is widely distributed and utilization rate is low, Song Zhu The characteristic of former material is the most rationally applied to provide space for deep development.Song Zhu restructuring be by the toughness of bamboo, pull resistance with And hygroscopicity, anti-ultraviolet property are tight with the material of pine, nail-holding ability is strong, the constitutionally stable advantage of corruption wear-resisting, anti-integrates one Rise, create the board had complementary advantages and establish one's own system, contribute for the energy-conserving and environment-protective utilization of resources.Pine bamboo granule restructuring The performance of plate feature is as follows;
1. the netted bottom sieve frame of (2450*1250*0.3) mm become by thin bamboo strips used for weaving strand weaving takes full advantage of bamboo fiber Tensile property.Netted bottom sieve frame after applying glue is compressed on the end dough-making powder of spongiosa particle board core, it is possible to quiet by transverse and longitudinal direction Bent pressure is distributed on every thin bamboo strips used for weaving strand uniformly, greatly improves pine bamboo granule recombination board anti-pressure ability.
2. through knitting device and stay the netted bottom sieve frame of (3*3) mm to be compressed on spongiosa particle board core thin bamboo strips used for weaving strand, spongiosa granule Also filling up in the netted bottom sieve frame mesh with netted lattice, bamboo chip transverse and longitudinal multilamellar pressing method more existing than market is more firm. Thoroughly solve the easy degumming of multilamellar pressing, opening problem, greatly improve the face bond strength of sheet material.
3. the spongiosa granule of diameter (1-2) mm is more smaller than traditional particieboard granule, just smaller due to granule, and distribution of particles is Evenly, more highdensity sheet material could be suppressed under not changing existing equipment pressure state.
4., due to the raising of panel density, improve pine the front nail-holding ability of bamboo granule recombination board, side the most well Nail-holding ability.
5. the tow sides of pine bamboo granule recombination plates are bamboo fiber and are wrapped up its any surface finish former, wear-resisting, sense of touch temperature Moisten fine and smooth.
---distribution is, and------nail-holding ability is big---facet is smooth---, and sense of touch is gentle, is high for-high density for the least granule The ideal chose of end furniture woods.
7. pine bamboo granule recombination plates is selected without urea formaldehyde glue, has not only protected without aldehyde, but also can improve water resistance.To guarantee that sheet material reaches To E0 level environmental protection standard, meet house decoration needs.
Accompanying drawing explanation
Fig. 1 is thin bamboo strips used for weaving strand schematic diagram.
Fig. 2 is the braiding schematic diagram of netted bottom sieve frame and netted lattice.
Fig. 3 is the schematic diagram of pine bamboo granule recombination plates.
In figure: 1. thin bamboo strips used for weaving strand, 2. mesh, the most netted lattice, the most netted bottom sieve frame, 5. spongiosa particle board core.
Detailed description of the invention
It is further elucidated with the present invention below in conjunction with the accompanying drawings with preferred embodiment.
Embodiment 1
Step one: with reference to Fig. 1, is first peeled into the thick book sheet of 0.3mm, the most again by 0.3mm by the bamboo of length 2500mm Bamboo matter book sheet be divided into wide 3mm strip thin bamboo strips used for weaving strand 1 stand-by.
Step 2: with reference to Fig. 2, becomes the netted bottom sieve frame of (2450*1250*0.3) mm 4 and netted by thin bamboo strips used for weaving strand 1 weaving Face lattice 3 are stand-by, and mesh size is: 3mm × 3mm.
Step 3: epidermis and the corrupt pine miscellaneous footpath material in source, brush wood rotary-cut will be removed or smash into the spongiosa of diameter 1-2mm to pieces Granule, spongiosa granule drying again, defat, bleaching.Spongiosa granule is mixed and stirred without urea formaldehyde glue be filled in netted bottom sieve frame 4 with Between netted lattice 3, defining spongiosa particle board core 5 between netted bottom sieve frame 4 and netted lattice 3, spongiosa granule also fills up at net Shape bottom sieve frame 4, with in the mesh of netted lattice 3, obtains the loose bamboo granule recombination plates hair that thickness is 18.2mm after high temperature high pressure process Base, then the end and the face of pine bamboo granule recombination plates blank are carried out sanding and polishing, cut after obtain (2440*1220*18) mm pine Bamboo granule recombination plates finished product, with reference to Fig. 3.Spongiosa granule is mixed and stirred without urea formaldehyde glue be filled in netted bottom sieve frame and netted lattice it Between, while defining spongiosa particle board core between netted bottom sieve frame and netted lattice, spongiosa granule also fill up netted bottom sieve frame with Play netted bottom sieve frame and netted lattice positioning action in the mesh of netted lattice.Five uniform faces of thin bamboo strips used for weaving are embedded in and glue Spongiosa granule in play dispersed quiet bent pressure effect.
Embodiment 2
Step one: first the bamboo of length 2500mm is peeled into the thick book sheet of 0.2mm, the most again by the bamboo matter book of 0.2mm Sheet is divided into wide 2mm strip thin bamboo strips used for weaving strand 1 stand-by.
Step 2: become the netted bottom sieve frame of (2450*1250*0.3) mm 4 and netted lattice 3 to treat thin bamboo strips used for weaving strand 1 weaving With, mesh 2 size is: 3mm × 3mm.
Step 3: spongiosa granule is mixed and stirred and is filled between netted bottom sieve frame 4 and netted lattice 3 without urea formaldehyde glue, described net Distance between shape bottom sieve frame 4 and netted lattice 3 is 10mm, obtains pine bamboo granule recombination plates blank after high temperature high pressure process, then The end and the face of pine bamboo granule recombination plates blank are carried out sanding and polishing, cut after obtain pine bamboo granule recombination plates finished product.
Embodiment 3
Step one: first the bamboo of length 2500mm is peeled into the thick book sheet of 0.4mm, the most again by the bamboo matter book of 0.4mm Sheet is divided into wide 4mm strip thin bamboo strips used for weaving strand 1 stand-by.
Step 2: (netted bottom sieve frame 4 and netted lattice 3 are stand-by, and mesh 2 size is: 5mm by thin bamboo strips used for weaving strand 1 weaving one-tenth ×5mm。
Step 3: spongiosa granule is mixed and stirred and is filled between netted bottom sieve frame 4 and netted lattice 3 without urea formaldehyde glue, described net Distance between shape bottom sieve frame 4 and netted lattice 3 is 25mm, obtains pine bamboo granule recombination plates blank after high temperature high pressure process, then The end and the face of pine bamboo granule recombination plates blank are carried out sanding and polishing, cut after obtain pine bamboo granule recombination plates finished product.
Embodiment 4
Step one: the bamboo of length 2500mm being first peeled into 0.3mm thick, book sheet wide for 4mm, the most again by 0.3mm's Bamboo matter book sheet is divided into wide 4mm strip thin bamboo strips used for weaving strand 1 stand-by.
Step 2: thin bamboo strips used for weaving strand 1 weaving reticulating bottom sieve frame 4 and netted lattice 3 are stand-by, mesh 2 size is: 4mm ×3mm。
Step 3: spongiosa granule is mixed and stirred and is filled between netted bottom sieve frame 4 and netted lattice 3 without urea formaldehyde glue, described net Distance between shape bottom sieve frame 4 and netted lattice 3 is 18mm, obtains pine bamboo granule recombination plates blank after high temperature high pressure process, then The end and the face of pine bamboo granule recombination plates blank are carried out sanding and polishing, cut after obtain pine bamboo granule recombination plates finished product.
Plain particles plate is analyzed with pine bamboo granule recombination plates physical property, result such as following table:
Pine bamboo granule recombination plates feature performance is as follows;
1. the netted bottom sieve frame become by thin bamboo strips used for weaving strand weaving takes full advantage of the tensile property of bamboo fiber.After applying glue Netted bottom sieve frame be compressed on the end dough-making powder of spongiosa particle board core, it is possible to the quiet bent pressure on transverse and longitudinal direction is distributed to uniformly On every thin bamboo strips used for weaving strand, greatly improve pine bamboo granule recombination board anti-pressure ability.
2. through knitting device and staying netted bottom sieve frame to be compressed on spongiosa particle board core thin bamboo strips used for weaving strand, spongiosa granule also fills up Netted bottom sieve frame is with in the mesh of netted lattice, and bamboo chip transverse and longitudinal multilamellar pressing method more existing than market is more firm.Thoroughly solve The easy degumming of multilamellar pressing, opening problem, greatly improve the face bond strength of sheet material.
3. the spongiosa granule of diameter is more smaller than traditional particieboard granule, just smaller due to granule, distribution of particles the most evenly, More highdensity sheet material could be suppressed under not changing existing equipment pressure state.
4., due to the raising of panel density, improve pine the front nail-holding ability of bamboo granule recombination board, side the most well Nail-holding ability.
5. the tow sides of pine bamboo granule recombination plates are bamboo fiber and are wrapped up its any surface finish former, wear-resisting, sense of touch temperature Moisten fine and smooth.
---distribution is, and------nail-holding ability is big---facet is smooth---, and sense of touch is gentle, is high for-high density for the least granule The ideal chose of end furniture woods.
7. pine bamboo granule recombination plates is selected without urea formaldehyde glue, has not only protected without aldehyde, but also can improve water resistance.To guarantee that sheet material reaches To E0 level environmental protection standard, meet house decoration needs.

Claims (10)

1. a loose bamboo granule recombination plates, it is characterised in that: include that thin bamboo strips used for weaving strand weaving reticulates bottom sieve frame and netted lattice, It it is spongiosa particle board core between netted bottom sieve frame and netted lattice;Spongiosa granule mixes and stirs sizing material and is filled in netted bottom sieve frame and netted lattice Between formed spongiosa particle board core, obtain after high temperature high pressure process pine bamboo granule recombination plates blank, then by pine bamboo granule restructuring The end of plate blank and face carry out sanding and polishing, cut after obtain pine bamboo granule recombination plates finished product.
2. a loose bamboo granule recombination plates manufacture method, it is characterised in that: thin bamboo strips used for weaving strand weaving is reticulated bottom sieve frame and net Shape face lattice;Spongiosa granule mixes and stirs sizing material and is filled between netted bottom sieve frame and netted lattice, obtains Song Zhu after high temperature high pressure process Granule recombination plates blank, then the end and the face of pine bamboo granule recombination plates blank are carried out sanding and polishing, cut after obtain pine bamboo Grain recombination plates finished product.
Pine bamboo granule recombination plates manufacture method the most according to claim 2, it is characterised in that: spongiosa granule is mixed and stirred without aldehyde Resin glue is filled between netted bottom sieve frame and netted lattice, defines spongiosa particle board core between netted bottom sieve frame and netted lattice Meanwhile, spongiosa granule also fills up to play in the netted bottom sieve frame mesh with netted lattice and is made with netted lattice location by netted bottom sieve frame With.
Pine bamboo granule recombination plates manufacture method the most according to claim 3, it is characterised in that: the length of side of mesh is equal to thin bamboo strips used for weaving The width of strand.
Pine bamboo granule recombination plates manufacture method the most according to claim 2, it is characterised in that: first by the bamboo of length 2500mm Son is peeled into 0.3mm book sheet, and the bamboo matter book sheet of 0.3mm is divided into wide 3mm strip thin bamboo strips used for weaving strand stand-by more again.
Pine bamboo granule recombination plates manufacture method the most according to claim 2, it is characterised in that: the width of thin bamboo strips used for weaving strand is 3mm, thin bamboo strips used for weaving strand is woven into the mesh size of netted bottom sieve frame and netted lattice and is: 3mm × 3mm.
Pine bamboo granule recombination plates manufacture method the most according to claim 2, it is characterised in that: described netted bottom sieve frame and netted Distance between the lattice of face is 10-25mm.
Pine bamboo granule recombination plates manufacture method the most according to claim 2, it is characterised in that: described netted bottom sieve frame and netted Distance between the lattice of face is 18mm.
Pine bamboo granule recombination plates manufacture method the most according to claim 2, it is characterised in that: epidermis and corrupt source will be removed Pine miscellaneous footpath material, brush wood rotary-cut or smash into the spongiosa granule of diameter 1-2mm to pieces, at spongiosa granule drying again, defat, bleaching Reason.
Pine bamboo granule recombination plates manufacture method the most according to claim 2, it is characterised in that: described spongiosa granule straight Footpath is 1-2mm.
CN201610560840.2A 2016-07-15 2016-07-15 Pine and bamboo particle recombination board and manufacturing method thereof CN106042105A (en)