CN106012292A - Antibacterial waterproof polyvinyl alcohol nanofiber membrane - Google Patents
Antibacterial waterproof polyvinyl alcohol nanofiber membrane Download PDFInfo
- Publication number
- CN106012292A CN106012292A CN201610446112.9A CN201610446112A CN106012292A CN 106012292 A CN106012292 A CN 106012292A CN 201610446112 A CN201610446112 A CN 201610446112A CN 106012292 A CN106012292 A CN 106012292A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyvinyl alcohol
- water
- acid
- fibrous membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial waterproof polyvinyl alcohol nanofiber membrane. The antibacterial waterproof polyvinyl alcohol nanofiber membrane is prepared from polyvinyl alcohol, polystyrene, polyetherimide, polyethylene glycol, methyl alcohol, glucomannan, cinnamaldehyde, sepiolite, rectorite, modified montmorillonite, polydimethylsiloxane, tannin, phosphomolybdic acid, glycerol monooleate, triethyl citrate, polyacrylic acid, phthalic acid, amino acid, N-vinyl-2-pyrrolidone, poly(L-gamma-chloroethyl glutamate), soybean protein and water. The antibacterial waterproof polyvinyl alcohol nanofiber membrane has excellent water resistance, antibacterial property and antifouling property.
Description
Technical field
The present invention relates to technology field of membrane materials, particularly relate to a kind of antibacterial water-resistant polyvinyl alcohol nanofiber
Film.
Background technology
Polyvinyl alcohol is known and is because its nontoxic degradable so that its to environment almost without dirt
Dye, in addition, it is outstanding that it has the oil resistivity of uniqueness, wearability, solvent resistance, and film property etc.
Performance, be one of material that nano fibrous membrane is conventional.Although polyvinyl alcohol material processing is simple, environment friend
Good, excellent performance, but polyvinyl alcohol nanofiber membrane resistance to water is poor, and the existence of steam can make poly-second
Enol nano fibrous membrane water absorption and swelling even dissolves, and it is less desirable to add its antibiotic property, limits poly-
The application of vinyl alcohol nano fibrous membrane.
Summary of the invention
The technical problem existed based on background technology, the present invention proposes a kind of antibacterial water-resistant polyvinyl alcohol and receives
Rice fibrous membrane, it has the resistance to water of excellence, and antibiotic property and antifouling property are excellent.
The one antibacterial water-resistant polyvinyl alcohol nano fibrous membrane that the present invention proposes, its raw material includes by weight:
Polyvinyl alcohol 20-50 part, polystyrene 2-10 part, Polyetherimide 2-10 part, Polyethylene Glycol 1-3.5 part,
Methanol 2-5 part, glucomannan 2-5 part, cinnamic aldehyde 0.5-2 part, meerschaum 0.5-2 part, rectorite 0.5-2
Part, modified montmorillonoid 2-5 part, polydimethylsiloxane 0.1-1 part, tannin 0.1-0.5 part, phosphomolybdic acid 0.2-1.2
Part, glyceryl monooleate 0.5-1 part, triethyl citrate 0.3-2 part, polyacrylic acid 0.2-1.5 part, adjacent benzene
Dioctyl phthalate 0.1-0.8 part, aminoacid 0.5-2.5 part, NVP 0.5-2.5 part, poly-(L-r-
Chloroethyl glutamate) 0.3-2 part, soybean protein 0.3-2 part, water 50-100 part.
Preferably, its raw material includes by weight: polyvinyl alcohol 35-40 part, polystyrene 5.8-7 part, poly-
Etherimide 5-6 part, Polyethylene Glycol 1.8-2.3 part, methanol 3.2-4 part, glucomannan 3.8-4.2 part,
Cinnamic aldehyde 1-1.6 part, meerschaum 0.9-1.5 part, rectorite 1-1.5 part, modified montmorillonoid 3.2-4 part, poly-
Dimethyl siloxane 0.5-0.9 part, tannin 0.2-0.3 part, phosphomolybdic acid 0.5-1 part, glyceryl monooleate
0.6-0.8 part, triethyl citrate 1-1.5 part, polyacrylic acid 0.8-1.2 part, phthalic acid 0.5-0.7
Part, amino acid/11-2 parts, NVP 0.8-1.2 part, poly-(L-r-chloroethyl glutamic acid
Ester) 0.9-1.4 part, soybean protein 1-1.4 part, water 65-80 part.
Preferably, its raw material includes by weight: polyvinyl alcohol 38 parts, polystyrene 6 parts, Polyetherimide
5.3 parts, Polyethylene Glycol 2 parts, methanol 3.5 parts, glucomannan 4 parts, cinnamic aldehyde 1.2 parts, meerschaum 1 part,
Rectorite 1.2 parts, modified montmorillonoid 3.6 parts, polydimethylsiloxane 0.65 part, tannin 0.25 part, phosphorus molybdenum
Acid 0.65 part, glyceryl monooleate 0.7 part, triethyl citrate 1.2 parts, polyacrylic acid 1 part, O-phthalic
Acid 0.55 part, amino acid/11 .3 part, NVP 1 part, poly-(L-r-chloroethyl glutamic acid
Ester) 1.2 parts, soybean protein 1.2 parts, 70 parts of water.
Preferably, described Polyethylene Glycol is Macrogol 600, polyethylene glycol-800, cetomacrogol 1000, gathers
One or more mixture in ethylene glycol 2000.
Preferably, the modifying agent that described modified montmorillonoid is used is 1, double (triethoxy the is silica-based) ethane of 2-,
The combination of the one or two kinds of in VTES is mixed with 17 fluorine decyl triethoxysilanes
Compound.
Preferably, described aminoacid is L-Histidine, 1B, L-arginine, Serine, L-Soviet Union
One or more mixture in propylhomoserin, Valine, L-glycine, L-Methionine.
Preferably, the average diameter of described antibacterial water-resistant polyvinyl alcohol nano fibrous membrane is 100-350nm, hole
Gap rate is 35-60%.
Antibacterial water-resistant polyvinyl alcohol nano fibrous membrane of the present invention can be according to conventional polyvinyl alcohol nano
The preparation technology of fibrous membrane is prepared from.
In the present invention antibacterial water-resistant polyvinyl alcohol nano fibrous membrane, with polyvinyl alcohol as major ingredient, add poly-
It is modified by styrene and Polyetherimide, can give the resistance to water that polyvinyl alcohol nanofiber membrane is excellent,
The stability making fibrous membrane is good, improves its mechanical performance simultaneously, make fibrous membrane can bear higher outside
Boundary's pressure, improve the microcellular structure of film simultaneously so as to get nano fibrous membrane surface finer and close, give
The combination property that fibrous membrane is excellent, wherein, in glucomannan and cinnamic aldehyde addition system, energy generation effect,
Make stress increase, thus cause the tensile strength of film to increase, with tannin, phosphomolybdic acid, aminoacid, N-ethylene
Base-2-Pyrrolidone gives, after coordinating, the antibiotic property that fibrous membrane is excellent, and makes the film smooth surface obtained, diameter
Less and be evenly distributed, and intensity and toughness high.
Detailed description of the invention
Below, by specific embodiment, technical scheme is described in detail.
Embodiment 1
The one antibacterial water-resistant polyvinyl alcohol nano fibrous membrane that the present invention proposes, its raw material includes by weight:
Polyvinyl alcohol 50 parts, polystyrene 2 parts, Polyetherimide 10 parts, Polyethylene Glycol 1 part, methanol 5 parts, Portugal are sweet
Dew polysaccharide 2 parts, cinnamic aldehyde 2 parts, meerschaum 0.5 part, rectorite 2 parts, modified montmorillonoid 2 parts, poly dimethyl
Siloxanes 1 part, tannin 0.1 part, phosphomolybdic acid 1.2 parts, glyceryl monooleate 0.5 part, triethyl citrate 2 parts,
Polyacrylic acid 0.2 part, phthalic acid 0.8 part, 0.5 part of aminoacid, NVP 2.5 parts,
Poly-(L-r-chloroethyl glutamate) 0.3 part, soybean protein 2 parts, 50 parts of water.
Embodiment 2
The one antibacterial water-resistant polyvinyl alcohol nano fibrous membrane that the present invention proposes, its raw material includes by weight:
Polyvinyl alcohol 20 parts, polystyrene 10 parts, Polyetherimide 2 parts, Polyethylene Glycol 3.5 parts, methanol 2 parts, Portugal
Mannan 5 parts, cinnamic aldehyde 0.5 part, meerschaum 2 parts, rectorite 0.5 part, modified montmorillonoid 5 parts, poly-two
Methylsiloxane 0.1 part, tannin 0.5 part, phosphomolybdic acid 0.2 part, glyceryl monooleate 1 part, Fructus Citri Limoniae triethylenetetraminehexaacetic acid
Ester 0.3 part, polyacrylic acid 1.5 parts, phthalic acid 0.1 part, 2.5 parts of aminoacid, N-vinyl-2-pyrroles
Alkanone 0.5 part, poly-(L-r-chloroethyl glutamate) 2 parts, soybean protein 0.3 part, 100 parts of water.
Embodiment 3
The one antibacterial water-resistant polyvinyl alcohol nano fibrous membrane that the present invention proposes, its raw material includes by weight:
Polyvinyl alcohol 35 parts, polystyrene 7 parts, Polyetherimide 5 parts, Macrogol 600 2.3 parts, methanol 3.2
Part, glucomannan 4.2 parts, cinnamic aldehyde 1 part, meerschaum 1.5 parts, rectorite 1 part, modified montmorillonoid 4 parts,
Polydimethylsiloxane 0.5 part, tannin 0.3 part, phosphomolybdic acid 0.5 part, glyceryl monooleate 0.8 part, Fructus Citri Limoniae
Triethylenetetraminehexaacetic acid ester 1 part, polyacrylic acid 1.2 parts, phthalic acid 0.5 part, L-Histidine 2 parts, N-vinyl-2-
Ketopyrrolidine 0.8 part, poly-(L-r-chloroethyl glutamate) 1.4 parts, soybean protein 1 part, 80 parts of water;
Wherein, the modifying agent that described modified montmorillonoid is used is 1,2-double (triethoxy is silica-based) ethane, second
Thiazolinyl triethoxysilane, 17 fluorine decyl triethoxysilanes are by weight the mixture for 4:6:1;
The average diameter of described antibacterial water-resistant polyvinyl alcohol nano fibrous membrane is 350nm, and porosity is 35%.
Embodiment 4
The one antibacterial water-resistant polyvinyl alcohol nano fibrous membrane that the present invention proposes, its raw material includes by weight:
Polyvinyl alcohol 40 parts, polystyrene 5.8 parts, Polyetherimide 6 parts, polyethylene glycol-800 0.3 part, poly-second two
Alcohol 1,000 0.5 parts, Macrogol 2000 1 part, methanol 4 parts, glucomannan 3.8 parts, cinnamic aldehyde 1.6 parts,
Meerschaum 0.9 part, rectorite 1.5 parts, modified montmorillonoid 3.2 parts, polydimethylsiloxane 0.9 part, tannin
0.2 part, phosphomolybdic acid 1 part, glyceryl monooleate 0.6 part, triethyl citrate 1.5 parts, polyacrylic acid 0.8 part,
Phthalic acid 0.7 part, 1B 0.3 part, L-arginine 0.3 part, Serine 0.4 part, N-ethylene
Base-2-Pyrrolidone 1.2 parts, poly-(L-r-chloroethyl glutamate) 0.9 part, soybean protein 1.4 parts, water 65
Part;
Wherein, the modifying agent that described modified montmorillonoid is used is VTES and 17 fluorine last of the ten Heavenly stems
Ethyl triethoxy silicane alkane is by weight the mixture for 5:2;
The average diameter of described antibacterial water-resistant polyvinyl alcohol nano fibrous membrane is 100nm, and porosity is 60%.
Embodiment 5
The one antibacterial water-resistant polyvinyl alcohol nano fibrous membrane that the present invention proposes, its raw material includes by weight:
Polyvinyl alcohol 38 parts, polystyrene 6 parts, Polyetherimide 5.3 parts, Macrogol 600 0.4 part, poly-second two
Alcohol 800 0.2 parts, cetomacrogol 1000 0.4 part, Macrogol 2000 1 part, methanol 3.5 parts, Portugal's manna
Polysaccharide 4 parts, cinnamic aldehyde 1.2 parts, meerschaum 1 part, rectorite 1.2 parts, modified montmorillonoid 3.6 parts, poly-diformazan
Radical siloxane 0.65 part, tannin 0.25 part, phosphomolybdic acid 0.65 part, glyceryl monooleate 0.7 part, citric acid three
Ethyl ester 1.2 parts, polyacrylic acid 1 part, phthalic acid 0.55 part, L-Histidine 0.3 part, 1B 0.2
Part, L-arginine 0.1 part, Serine 0.1 part, L-threonine 0.2 part, Valine 0.2 part, L-are sweet
Propylhomoserin 0.1 part, L-Methionine 0.1 part, NVP 1 part, poly-(L-r-chloroethyl glutamic acid
Ester) 1.2 parts, soybean protein 1.2 parts, 70 parts of water;
Wherein, the modifying agent that described modified montmorillonoid is used is 1, double (triethoxy the is silica-based) ethane and ten of 2-
Seven fluorine decyl triethoxysilanes are by weight the mixture for 3:2;
The average diameter of described antibacterial water-resistant polyvinyl alcohol nano fibrous membrane is 300nm, and porosity is 45%.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention not office
Being limited to this, any those familiar with the art is in the technical scope that the invention discloses, according to this
The technical scheme of invention and inventive concept thereof in addition equivalent or change, all should contain the protection in the present invention
Within the scope of.
Claims (7)
1. an antibacterial water-resistant polyvinyl alcohol nano fibrous membrane, it is characterised in that its raw material wraps by weight
Include: polyvinyl alcohol 20-50 part, polystyrene 2-10 part, Polyetherimide 2-10 part, Polyethylene Glycol 1-3.5
Part, methanol 2-5 part, glucomannan 2-5 part, cinnamic aldehyde 0.5-2 part, meerschaum 0.5-2 part, rectorite
0.5-2 part, modified montmorillonoid 2-5 part, polydimethylsiloxane 0.1-1 part, tannin 0.1-0.5 part, phosphorus molybdenum
Acid 0.2-1.2 part, glyceryl monooleate 0.5-1 part, triethyl citrate 0.3-2 part, polyacrylic acid 0.2-1.5
Part, phthalic acid 0.1-0.8 part, aminoacid 0.5-2.5 part, NVP 0.5-2.5
Part, poly-(L-r-chloroethyl glutamate) 0.3-2 part, soybean protein 0.3-2 part, water 50-100 part.
The most antibacterial water-resistant polyvinyl alcohol nano fibrous membrane, it is characterised in that its
Raw material includes by weight: polyvinyl alcohol 35-40 part, polystyrene 5.8-7 part, Polyetherimide 5-6 part,
Polyethylene Glycol 1.8-2.3 part, methanol 3.2-4 part, glucomannan 3.8-4.2 part, cinnamic aldehyde 1-1.6 part,
Meerschaum 0.9-1.5 part, rectorite 1-1.5 part, modified montmorillonoid 3.2-4 part, polydimethylsiloxane
0.5-0.9 part, tannin 0.2-0.3 part, phosphomolybdic acid 0.5-1 part, glyceryl monooleate 0.6-0.8 part, Fructus Citri Limoniae
Triethylenetetraminehexaacetic acid ester 1-1.5 part, polyacrylic acid 0.8-1.2 part, phthalic acid 0.5-0.7 part, amino acid/11-2 parts,
NVP 0.8-1.2 part, poly-(L-r-chloroethyl glutamate) 0.9-1.4 part, Semen sojae atricolor egg
White 1-1.4 part, water 65-80 part.
Antibacterial water-resistant polyvinyl alcohol nano fibrous membrane the most according to claim 1 or claim 2, it is characterised in that
Its raw material includes by weight: polyvinyl alcohol 38 parts, polystyrene 6 parts, Polyetherimide 5.3 parts, poly-second
Glycol 2 parts, methanol 3.5 parts, glucomannan 4 parts, cinnamic aldehyde 1.2 parts, meerschaum 1 part, rectorite 1.2
Part, modified montmorillonoid 3.6 parts, polydimethylsiloxane 0.65 part, tannin 0.25 part, phosphomolybdic acid 0.65 part,
Glyceryl monooleate 0.7 part, triethyl citrate 1.2 parts, polyacrylic acid 1 part, phthalic acid 0.55 part,
Amino acid/11 .3 part, NVP 1 part, poly-(L-r-chloroethyl glutamate) 1.2 parts, big
Soybean protein 1.2 parts, 70 parts of water.
4., according to water-resistant polyvinyl alcohol nano fibrous membrane antibacterial according to any one of claim 1-3, it is special
Levying and be, described Polyethylene Glycol is Macrogol 600, polyethylene glycol-800, cetomacrogol 1000, poly-second two
One or more mixture in alcohol 2000.
5., according to water-resistant polyvinyl alcohol nano fibrous membrane antibacterial according to any one of claim 1-4, it is special
Levying and be, the modifying agent that described modified montmorillonoid is used is 1,2-double (triethoxy is silica-based) ethane, ethylene
The combination of the one or two kinds of in ethyl triethoxy silicane alkane and the mixture of 17 fluorine decyl triethoxysilanes.
6., according to water-resistant polyvinyl alcohol nano fibrous membrane antibacterial according to any one of claim 1-5, it is special
Levy and be, described aminoacid be L-Histidine, 1B, L-arginine, Serine, L-threonine,
One or more mixture in Valine, L-glycine, L-Methionine.
7., according to water-resistant polyvinyl alcohol nano fibrous membrane antibacterial according to any one of claim 1-6, it is special
Levying and be, the average diameter of described antibacterial water-resistant polyvinyl alcohol nano fibrous membrane is 100-350nm, porosity
For 35-60%.