CN106012182A - Antibacterial towel and making method thereof - Google Patents
Antibacterial towel and making method thereof Download PDFInfo
- Publication number
- CN106012182A CN106012182A CN201610462924.2A CN201610462924A CN106012182A CN 106012182 A CN106012182 A CN 106012182A CN 201610462924 A CN201610462924 A CN 201610462924A CN 106012182 A CN106012182 A CN 106012182A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- towel
- minutes
- manufacture method
- antibacterial towel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial towel. The antibacterial towel is formed by blending and weaving polyester and cotton fibers containing a silver-ion antibacterial agent. The invention further discloses a making method of the antibacterial towel. The method comprises steps as follows: mixing of raw materials containing the silver-ion antibacterial agent; warping; sizing; weaving; desizing and degreasing; bleaching; after-finishing; fabric forming; slitting; serging; packaging. During weaving of the anti-bacterial towel, the raw materials with the silver-ion antibacterial agent added are adopted, and the antibacterial agent is inlaid in the raw materials, so that the antibacterial towel has the permanent sterilizing effect without damaging the fiber raw materials.
Description
Technical field
The application belongs to functional fiber material manufacturing technology field, particularly relate to a kind of antibacterial towel and
Its manufacture method.
Background technology
Fibre is varied in actual life, the fibre that wherein towel is common in being life.
The Fiber Materials of towel is the most varied, common are cotton textiles, viscose rayon, tencel, Modal fibre
Deng.The fibres such as towel in use can grow a lot of antibacterial, will be to raw as processed not in time
Live and bring inconvenience, not only result in textile and stink, cause towel to destroy, and easily make
Become cross infection, pathophoresis and human injury, therefore, the fibres such as towel are carried out antimicrobial treatment
Particularly important.
The towel that water absorption is the strongest, the most easily grows along with antibacterial equally, produces variable color, mouldy, change
Taste, the existing general antibacterial that adds when Final finishing, but it is washable, wear no resistance, it is impossible to meet client
Demand.
Summary of the invention
It is an object of the invention to provide a kind of antibacterial towel and preparation method thereof, to overcome in prior art
Deficiency.
For achieving the above object, the present invention provides following technical scheme:
The open a kind of antibacterial towel of the embodiment of the present application, by the polyster fibre containing silver ion antimicrobial agent and cotton
Fiber blend weaving forms.
Accordingly, disclosed herein as well is the manufacture method of a kind of antibacterial towel, including step: mixing contains
There is the raw material-warping-starching-weaving-desizing defat-bleaching-Final finishing-one-tenth cloth of silver ion antimicrobial agent-cut-lock
Limit-packaging.
Preferably, in the manufacture method of above-mentioned antibacterial towel, the formula of described desizing defat meets:
Amylase 8 g/L, Sal 20g/L, penetrating agent 8gL.
Preferably, in the manufacture method of above-mentioned antibacterial towel, the condition of described desizing defat meets:
Hot water wash temperature 40 DEG C；Prick enzyme liquid temp 50 DEG C.
Preferably, in the manufacture method of above-mentioned antibacterial towel, the formula of described bleaching meets: insurance
Powder 6g/L, soda 6g/L, refining agent 8g/L.
Preferably, in the manufacture method of above-mentioned antibacterial towel, the condition of described bleaching meets: bleaching
Temperature 70 C, temperature retention time 30min.
Preferably, in the manufacture method of above-mentioned antibacterial towel, described Final finishing include deoxidation-dyeing-
Soft-drying is washed-added to soap boiling-ferment, and described deoxygenation step is the bath raio according to 1: 10, and grey cloth is first 1g/L's
Citric acid body lotion circulates 10 minutes at 50 DEG C, is subsequently adding deoxygenase, grey cloth circulation in 40 DEG C of water
20 minutes, deoxygenase concentration 0.12ml/L；Described staining procedure is the bath raio according to 1: 10, in dye liquor 150%
The red mass content of 3BS 0.2%, Matrii Sulfas Exsiccatus 15g/L, soda 10g/L, grey cloth dye at a temperature of 60 DEG C
Color 30 minutes；Described soap boiling step is the bath raio according to 1: 10, at 95 DEG C in 0.13g/L detergent solution
Lower circulation 15 minutes；Described ferment wash step for according to 1: 10 bath raio, containing 0.33g/L citric acid and
In the solution of 1.5ml/L cellulase, circulate 30 minutes at 50 DEG C；Described add soft step for according to 1: 10
Bath raio, softening agent 4ml/L in solution, circulates 20 minutes at 40 DEG C.
Compared with prior art, it is an advantage of the current invention that:
The present invention, when weaving, uses the antibacterial raw material adding silver ion, and this antibacterial is embedded in raw material
In, there is bactericidal effect that is permanent and that do not damage fibrous raw material.
Accompanying drawing explanation
In order to be illustrated more clearly that the embodiment of the present application or technical scheme of the prior art, below will be to reality
Execute the required accompanying drawing used in example or description of the prior art to be briefly described, it should be apparent that below,
Accompanying drawing in description is only some embodiments described in the application, for those of ordinary skill in the art
From the point of view of, on the premise of not paying creative work, it is also possible to obtain other accompanying drawing according to these accompanying drawings.
Fig. 1 show the manufacture method schematic flow sheet of antibacterial towel in the specific embodiment of the invention.
Detailed description of the invention
The present invention is described further by the following example: according to following embodiment, can be more preferably geographical
Solve the present invention.But, as it will be easily appreciated by one skilled in the art that the concrete material described by embodiment
Ratio, process conditions and result thereof are merely to illustrate the present invention, and should be also without limitation on claims
The present invention described in detail by.
The open a kind of antibacterial towel of the present embodiment, by the polyster fibre containing silver ion antimicrobial agent and cotton fiber
Hybrid woven forms.
Shown in Fig. 1, the manufacture method of antibacterial towel, including step: mixing is containing silver-ion antibiotic
Raw material-warping-starching-the weaving of agent-desizing defat-bleaching-Final finishing-one-tenth cloth-cut-lockstitch a border-pack.
Wherein:
The formula of desizing defat meets: amylase 8 g/L, Sal 20g/L, penetrating agent 8gL.
The condition of desizing defat meets: hot water wash temperature 40 DEG C；Prick enzyme liquid temp 50 DEG C.
The formula of bleaching meets: sodium hydrosulfite 6g/L, soda 6g/L, refining agent 8g/L.
The condition of bleaching meets: bleaching temperature 70 DEG C, temperature retention time 30min.
Final finishing includes that soft-drying is washed-added to deoxidation-dyeing-soap boiling-ferment, and described deoxygenation step is according to 1: 10
Bath raio, grey cloth first in the citric acid body lotion of 1g/L 50 DEG C circulate 10 minutes, be subsequently adding de-
Oxygenase, in 40 DEG C of water, grey cloth circulates 20 minutes, deoxygenase concentration 0.12ml/L；Described staining procedure is
According to the bath raio of 1: 10, in dye liquor, the red mass content of 150%3BS 0.2%, Matrii Sulfas Exsiccatus 15g/L, pure
Alkali 10g/L, piece dyeing finishing 30 minutes at a temperature of 60 DEG C；Described soap boiling step is the bath raio according to 1: 10,
0.13g/L detergent solution circulates 15 minutes at 95 DEG C；Described ferment washes step for according to 1: 10
Bath raio, in the solution containing 0.33g/L citric acid and 1.5ml/L cellulase, 50 DEG C circulate 30 points
Clock；Described to add soft step be the bath raio according to 1: 10, softening agent 4ml/L in solution, circulates at 40 DEG C
20 minutes.
The present invention, when weaving, uses the antibacterial raw material adding silver ion, and this antibacterial is embedded in raw material
In, there is bactericidal effect that is permanent and that do not damage fibrous raw material.
Finally, in addition it is also necessary to explanation, term " includes ", " comprising " or its any other variant are intended to
Comprising of nonexcludability, so that include the process of a series of key element, method, article or equipment not
Only include those key elements, but also include other key elements being not expressly set out, or also include for this
The key element that the process of kind, method, article or equipment are intrinsic.
Claims (7)
1. an antibacterial towel, by the polyster fibre containing silver ion antimicrobial agent and cotton fiber hybrid woven
Become.
2. the manufacture method of an antibacterial towel, it is characterised in that include step: mixing is containing silver ion
Raw material-warping-starching-the weaving of antibacterial-desizing defat-bleaching-Final finishing-one-tenth cloth-cut-lockstitch a border-pack.
The manufacture method of antibacterial towel the most according to claim 2, it is characterised in that: described desizing
The formula of defat meets: amylase 8 g/L, Sal 20g/L, penetrating agent 8gL.
The manufacture method of antibacterial towel the most according to claim 2, it is characterised in that: described desizing
The condition of defat meets: hot water wash temperature 40 DEG C；Prick enzyme liquid temp 50 DEG C.
The manufacture method of antibacterial towel the most according to claim 2, it is characterised in that: described bleaching
Formula meet: sodium hydrosulfite 6g/L, soda 6g/L, refining agent 8g/L.
The manufacture method of antibacterial towel the most according to claim 2, it is characterised in that: described bleaching
Condition meet: bleaching temperature 70 DEG C, temperature retention time 30min.
The manufacture method of antibacterial towel the most according to claim 2, it is characterised in that: whole after described
Reason includes that soft-drying is washed-added to deoxidation-dyeing-soap boiling-ferment, and described deoxygenation step is the bath raio according to 1: 10,
First grey cloth circulates 10 minutes at 50 DEG C in the citric acid body lotion of 1g/L, is subsequently adding deoxygenase,
In 40 DEG C of water, grey cloth circulates 20 minutes, deoxygenase concentration 0.12ml/L；Described staining procedure is according to 1: 10
Bath raio, the red mass content of 150%3BS 0.2% in dye liquor, Matrii Sulfas Exsiccatus 15g/L, soda 10g/L,
Piece dyeing finishing 30 minutes at a temperature of 60 DEG C；Described soap boiling step is the bath raio according to 1: 10, at 0.13g/L
Detergent solution circulates 15 minutes at 95 DEG C；It is the bath raio according to 1: 10 that described ferment washes step,
In solution containing 0.33g/L citric acid and 1.5ml/L cellulase, circulate 30 minutes at 50 DEG C；Described add
Soft step is the bath raio according to 1: 10, softening agent 4ml/L in solution, circulates 20 minutes at 40 DEG C.