CN105996156A - 一种草珊瑚裤袜及其生产工艺 - Google Patents
一种草珊瑚裤袜及其生产工艺 Download PDFInfo
- Publication number
- CN105996156A CN105996156A CN201610368864.8A CN201610368864A CN105996156A CN 105996156 A CN105996156 A CN 105996156A CN 201610368864 A CN201610368864 A CN 201610368864A CN 105996156 A CN105996156 A CN 105996156A
- Authority
- CN
- China
- Prior art keywords
- herba pileae
- pileae scriptae
- liquid
- panty hose
- herba
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种袜子，尤其是涉及一种草珊瑚裤袜及其生产工艺。草珊瑚裤袜，包括裤体和袜体，所述的裤体和袜体均由表纱和里纱编织而成，表纱和里纱均为草珊瑚纤维。本发明具有能够有效地杀灭细菌、抑制细菌滋生、保证内部环境干燥、避免皮肤干裂等有益效果。
Description
技术领域
本发明涉及一种袜子，尤其是涉及一种草珊瑚裤袜及其生产工艺。
背景技术
随着人们物质文化水平的提高，人们对纺织品的要求也在提高，不仅要求保暖、美观，而且更加注重舒适性和功能性。功能性纺织品成为纺织产业未来的发展趋向之一，将与细旦纤维纺织品、无纺布、复合材料、环保型材料等共同构成未来纺织品的大走势。现今科技的发展为功能性纺织品的开发提供了保证，同时也为纺织企业发展及产品结构调整，起到了较大的促进作用并提高了纺织品的附加值。研究和生产有益于人类生态和健康的功能性纺织产品，已经成为当今世界发展的潮流。现有的裤袜通常采用涤纶、氨纶等纤维材料作为纱线来编织袜子，当裤袜需要包覆整个下半身时，这类材料的裤袜透气性差，裤袜内部潮湿，容易滋生细菌，而这类裤袜的纱线与纱线之间的间隙容易作为细菌繁殖的温床。
发明内容
本发明主要是针对上述问题，提供一种能够有效地杀灭细菌、抑制细菌滋生、保证内部环境干燥、避免皮肤干裂的草珊瑚裤袜及其生产工艺。
本发明的目的主要是通过下述方案得以实现的：一种草珊瑚裤袜，包括裤体和袜体，所述的裤体和袜体均由表纱和里纱编织而成，表纱和里纱均为草珊瑚纤维。裤袜包括裤体和袜体，裤体包覆裆部和腿部，袜体包覆脚部，裤体和袜体均由表纱和里纱编织而成，而表纱和里纱均采用草珊瑚纤维。草珊瑚纤维主要含有草珊瑚内的金丝桃苷，金丝桃苷具有杀菌抑菌的作用，当表纱和里纱交织的间隙处滋生细菌时，金丝桃苷能够有效地杀灭细菌并抑制细菌再生。
一种上述草珊瑚裤袜的生产工艺，步骤如下：
编织：将草珊瑚纤维作为表纱和里纱，并通过织袜机编织成型，形成草珊瑚裤袜半成品。将已经制备完成的草珊瑚纤维作为表纱和里纱的主要原料，将表纱和里纱穿入织袜机进行编织，制得初步成型的草珊瑚裤袜半成品。
前整理：将草珊瑚裤袜半成品浸液处理。将草珊瑚裤袜半成品浸入配比好的整理液内，通过整理液内的化学成分对草珊瑚裤袜半成品做功能性整理。
后整理：对浸液处理后的草珊瑚裤袜半成品烘干定型。将前整理完成后的草珊瑚半成品烘干定型，制得草珊瑚裤袜的成品。
4）成品检验、包装入库。
本发明根据本发明中制备的草珊瑚纤维的特性，结合织袜机的性能，设计出符合本发明中草珊瑚纤维特性的上机组织。根据草珊瑚纤维的性能制定前整理的工艺，配比合理的整理液。
作为优选，步骤1）中草珊瑚纤维的制备方法如下：将聚酯切片、草珊瑚颗粒以及β-葡聚糖共混后通过熔融纺丝机进行纺丝，制成草珊瑚纤维，草珊瑚颗粒与β-葡聚糖的比例为15:2到14:3，草珊瑚颗粒占总体含量38-42wt%。
作为优选，所述的草珊瑚颗粒的制备方法如下：1）取洗净的草珊瑚原料粉碎，将粉碎后的草珊瑚原料过网筛，得到草珊瑚粒子，将草珊瑚粒子与乙醇混合，得到A液，草珊瑚粒子的质量为A液的10-15%；2） 取洗净的橄榄叶和芦荟打浆并过滤，在过滤后的液体内加入羧甲基纤维素钠搅拌均匀，得到B液；3）将A液和B液混合并搅拌均匀，A液和B液的混合比例为3:1，通过离心机离心，过滤残渣，制得C液；4）将C液经过100℃-120℃加热5分钟，再经过0.3Mpa-0.5Mpa加压3分钟后经过喷雾干燥后制得草珊瑚颗粒。
首先，制备草珊瑚颗粒，将聚酯切片、草珊瑚颗粒以及β-葡聚糖共混制备草珊瑚纤维。草珊瑚颗粒的制备方法是取草珊瑚 原料进行粉碎，通过小孔的网筛对粉碎的草珊瑚原料过滤，得到粉末状的草珊瑚粒子。再将草珊瑚粒子与乙醇混合，得到A液，草珊瑚中富含的金丝桃苷、芦丁以及莨菪亭等成分能够溶于乙醇，草珊瑚粒子的质量为A液的10-15%，保证草珊瑚粒子能够完全溶于A液中的乙醇内，并能够保证A液中草珊瑚粒子的浓度以及后续乙醇的可溶性，同时保证A液内富含了具有杀菌抑菌作用的金丝桃苷。但与此同时，A液中含有对皮肤具有刺激性的羟基大黄素。取洗净的橄榄叶和芦荟打浆并过滤，橄榄叶的成分具有抑菌作用，而且橄榄叶中富含裂环烯醚萜，裂环烯醚萜具有吸湿性，与此同时，芦荟打浆后，芦荟多糖，对人体皮肤又良好的滋润作用，利用芦荟独特的吸湿性配合裂环烯醚萜的吸湿性，进一步增强整个纤维的吸湿效果。将过滤后的液体加入羧甲基纤维素钠，得到B液。羧甲基纤维素钠能够将B液增稠，利用羧甲基纤维素钠的增稠效果保护B液内的裂环烯醚萜、氨基酸和活性酶等成分。将A液与B液混合并且搅拌均匀，A液和B液的混合比例为3:1，保证混合液中具有杀菌作用的A液成分比例更高，同时混合液中具有能够吸湿的B液中的成分。当A液和B液的成分混合后，利用橄榄叶中的抑菌成分进一步增强了A液中草珊瑚粒子中的抑菌成分的抑菌效果，同时提高了混合液吸湿性能。而且当A液和B液混合后，增稠过的B液能够增强整个混合液的粘稠度，A液中的羟基大黄素能够被B液中的羧甲基纤维素钠吸附，通过离心机离心后，吸附了羟基大黄素的羧甲基纤维素钠与乙醇混合液分离开，经过过滤后，能够将吸附了羟基大黄素的羧甲基纤维素钠等残渣过滤掉，得到C液，此时，C液中对皮肤有刺激性的羟基大黄素被分离过滤。将C液经过100℃-120℃加热5分钟，再经过0.3Mpa-0.5Mpa加压3分钟，通过高温高压使C液中的乙醇、水以及低沸点的残余成分蒸发，经过喷雾干燥后制得草珊瑚颗粒。草珊瑚颗粒富含草珊瑚成分、橄榄叶成分以及芦荟的主要成分，同时，增强了草珊瑚颗粒的抑菌性和吸湿性，消除了草珊瑚原料中对皮肤有刺激性的元素，使草珊瑚颗粒能够应用于纺织品上。当草珊瑚颗粒做成纤维而且保证草珊瑚颗粒占总体含量38-42wt%，即草珊瑚纤维中的草珊瑚颗粒含量占比在三分之一以上，提高草珊瑚纤维杀菌抑菌和吸湿的性能，利用制备好的草珊瑚纤维制成裤袜时，能够利用草珊瑚颗粒的抑菌杀菌性对吸附在裤袜上的细菌进行杀灭，同时抑制细菌再生。利用草珊瑚颗粒的吸湿性，能够将裤体内部尤其是裆部的湿气吸附在裤体上，再利用裤体自身的透气性将湿气排出，保证裤体内部环境的干燥性，在环境干燥的情况下能够进一步抑制细菌再生。但由于草珊瑚颗粒自身的吸湿性较强，使裤体内部环境干燥的情况下，容易造成皮肤脱水干燥甚至干裂。因此，再利用草珊瑚颗粒与聚酯切片共混制备纤维时，同时加入β-葡聚糖，而且保证草珊瑚颗粒与β-葡聚糖的比例为15:2到14:3，在这个比例下，草珊瑚颗粒的杀菌抑菌效果得到保证，同时对裤体内部环境吸湿效果得到保证，同时β-葡聚糖的含量也可以得到保证，当裤体的草珊瑚纤维与皮肤接触时，β-葡聚糖能够直接与皮肤基础，得到皮肤的吸收，β-葡聚糖不仅能够修复皮肤表面粘膜、使皮肤红润紧致，而且能够使皮肤细胞舒敏保湿。通过这种方式制备的草珊瑚纤维，不仅能够杀灭已生细菌、抑制细菌再生、对裤体内部环境吸湿起到裤体内部环境干燥的效果，进一步避免潮湿环境下的细菌滋生，而且能够通过与皮肤的接触使皮肤红润紧致、舒敏保湿。即穿着草珊瑚裤袜后，裤体与皮肤之间的环境得到很好的干燥，但又不会使皮肤脱水干裂。
作为优选，步骤2）浸液处理时，将草珊瑚裤袜半成品在室温下浸入整理液内，将整理液以5℃/min的速度升温至85℃，然后保温30min，再以5℃/min的速度降温至60℃，再保温30min，最终将保温完成后的草珊瑚裤袜半成品浸没在水中2分钟，完成浸液处理，整理液中含有以下成分：聚乙烯吡咯烷酮0.3g/L、硅酸钠0.5g/L、甲壳素1.5g/L、羟丙甲纤维素0.5/L。
利用草珊瑚纤维编织而成的草珊瑚裤袜半成品，草珊瑚纤维中的成分并不稳定，经过步骤2）的处理之后，能够进一步增强草珊瑚裤袜的杀菌效果，而且能够保护草珊瑚纤维中的成分流失，增强草珊瑚纤维的稳定性。首先，配比整理液，整理液中含有以下成分：聚乙烯吡咯烷酮0.3g/L、硅酸钠0.5g/L、甲壳素1.5g/L、羟丙甲纤维素0.5/L，其中聚乙烯吡咯烷酮具有较强的杀菌效果，利用前整理的方式，增强了最终成品的杀菌性能，对细菌和真菌均有效果。羟丙甲纤维素不仅能够作为增稠剂，而且能够作为稳定剂使草珊瑚裤袜半成品中的成分稳定。羟丙甲纤维素0.5/L的成分比例，避免整理液过于黏稠，保证整理液的均匀性，使聚乙烯吡咯烷酮以及草珊瑚纤维的成分能够得到附着和保留。在整理过程中，将整理液以5℃/min的速度升温至85℃，利用迅速升温的方式避免整理液挥发，在经过保温30min，使草珊瑚裤袜半成品以及整理液在85℃的温度下充分加热，整理液在受热后能够更加黏稠的吸附在草珊瑚裤袜半成品上与草珊瑚裤袜半成品充分作用。再以5℃/min的速度降温至60℃，即从85℃降至60℃时，草珊瑚半成品及整理液内的金丝桃苷、氨基酸、聚乙烯吡咯烷酮能够充分保留。最终将保温完成后的草珊瑚裤袜半成品浸没在水中2分钟，完成浸液处理，即草珊瑚裤袜半成品浸入水中之前的温度保留在60℃，浸入水中后迅速降温冷却，增强了整理液的吸附性和吸附效果，经过2分钟的冲洗后洗掉草珊瑚裤袜上的残留粘稠物，完成整理。
因此，本发明的一种草珊瑚裤袜及其生产工艺具备下述优点：1、裤体和袜体均由表纱和里纱编织而成，而表纱和里纱均采用草珊瑚纤维，草珊瑚纤维主要含有草珊瑚内的金丝桃苷，金丝桃苷具有杀菌抑菌的作用，当表纱和里纱交织的间隙处滋生细菌时，金丝桃苷能够有效地杀灭细菌并抑制细菌再生；2、通过这种方式制备的草珊瑚纤维，不仅能够杀灭已生细菌、抑制细菌再生、对裤体内部环境吸湿起到裤体内部环境干燥的效果，进一步避免潮湿环境下的细菌滋生，而且能够通过与皮肤的接触使皮肤红润紧致、舒敏保湿，即穿着草珊瑚裤袜后，裤体与皮肤之间的环境得到很好的干燥，但又不会使皮肤脱水干裂。
附图说明
附图1是本发明的一种结构示意图。
图示说明：1-裤体，2-袜体。
具体实施方式
下面通过实施例，并结合附图，对本发明的技术方案作进一步具体的说明。
实施例1：如图1所示，一种草珊瑚裤袜，包括裤体1和袜体2，裤体和袜体均由表纱和里纱编织而成，表纱和里纱均为草珊瑚纤维。
上述草珊瑚裤袜的生产工艺，其特征在于，步骤如下：
1）编织：将草珊瑚纤维作为表纱和里纱，并通过织袜机编织成型，形成草珊瑚裤袜半成品；
2）前整理：将草珊瑚裤袜半成品浸液处理；
3）后整理：对浸液处理后的草珊瑚裤袜半成品烘干定型；
4）成品检验、包装入库。
步骤1）中草珊瑚纤维的制备方法如下：将聚酯切片、草珊瑚颗粒以及β-葡聚糖共混后通过熔融纺丝机进行纺丝，制成草珊瑚纤维，草珊瑚颗粒与β-葡聚糖的比例为15:2到14:3，草珊瑚颗粒占总体含量38-42wt%。
草珊瑚颗粒的制备方法如下：1）取洗净的草珊瑚原料粉碎，将粉碎后的草珊瑚原料过网筛，得到草珊瑚粒子，将草珊瑚粒子与乙醇混合，得到A液，草珊瑚粒子的质量为A液的10-15%；2） 取洗净的橄榄叶和芦荟打浆并过滤，在过滤后的液体内加入羧甲基纤维素钠搅拌均匀，得到B液；3）将A液和B液混合并搅拌均匀，A液和B液的混合比例为3:1，通过离心机离心，过滤残渣，制得C液；4）将C液经过100℃-120℃加热5分钟，再经过0.3Mpa-0.5Mpa加压3分钟后经过喷雾干燥后制得草珊瑚颗粒。
步骤2）浸液处理时，将草珊瑚裤袜半成品在室温下浸入整理液内，将整理液以5℃/min的速度升温至85℃，然后保温30min，再以5℃/min的速度降温至60℃，再保温30min，最终将保温完成后的草珊瑚裤袜半成品浸没在水中2分钟，完成浸液处理，整理液中含有以下成分：聚乙烯吡咯烷酮0.3g/L、硅酸钠0.5g/L、甲壳素1.5g/L、羟丙甲纤维素0.5/L。
步骤3）烘干定型是由蒸汽定型机完成，蒸汽压力为0.8Mpa-1Mpa，定型时间为25-40秒。
裤袜包括裤体和袜体，裤体包覆裆部和腿部，袜体包覆脚部，裤体和袜体均由表纱和里纱编织而成，而表纱和里纱均采用草珊瑚纤维。草珊瑚纤维主要含有草珊瑚内的金丝桃苷，金丝桃苷具有杀菌抑菌的作用，当表纱和里纱交织的间隙处滋生细菌时，金丝桃苷能够有效地杀灭细菌并抑制细菌再生。本发明根据本发明中制备的草珊瑚纤维的特性，结合织袜机的性能，设计出符合本发明中草珊瑚纤维特性的上机组织。根据草珊瑚纤维的性能制定前整理的工艺，配比合理的整理液。
首先，制备草珊瑚颗粒，将聚酯切片、草珊瑚颗粒以及β-葡聚糖共混制备草珊瑚纤维。草珊瑚颗粒的制备方法是取草珊瑚 原料进行粉碎，通过小孔的网筛对粉碎的草珊瑚原料过滤，得到粉末状的草珊瑚粒子。再将草珊瑚粒子与乙醇混合，得到A液，草珊瑚中富含的金丝桃苷、芦丁以及莨菪亭等成分能够溶于乙醇，草珊瑚粒子的质量为A液的10-15%，保证草珊瑚粒子能够完全溶于A液中的乙醇内，并能够保证A液中草珊瑚粒子的浓度以及后续乙醇的可溶性，同时保证A液内富含了具有杀菌抑菌作用的金丝桃苷。但与此同时，A液中含有对皮肤具有刺激性的羟基大黄素。取洗净的橄榄叶和芦荟打浆并过滤，橄榄叶的成分具有抑菌作用，而且橄榄叶中富含裂环烯醚萜，裂环烯醚萜具有吸湿性，与此同时，芦荟打浆后，芦荟多糖，对人体皮肤又良好的滋润作用，利用芦荟独特的吸湿性配合裂环烯醚萜的吸湿性，进一步增强整个纤维的吸湿效果。将过滤后的液体加入羧甲基纤维素钠，得到B液。羧甲基纤维素钠能够将B液增稠，利用羧甲基纤维素钠的增稠效果保护B液内的裂环烯醚萜、氨基酸和活性酶等成分。将A液与B液混合并且搅拌均匀，A液和B液的混合比例为3:1，保证混合液中具有杀菌作用的A液成分比例更高，同时混合液中具有能够吸湿的B液中的成分。当A液和B液的成分混合后，利用橄榄叶中的抑菌成分进一步增强了A液中草珊瑚粒子中的抑菌成分的抑菌效果，同时提高了混合液吸湿性能。而且当A液和B液混合后，增稠过的B液能够增强整个混合液的粘稠度，A液中的羟基大黄素能够被B液中的羧甲基纤维素钠吸附，通过离心机离心后，吸附了羟基大黄素的羧甲基纤维素钠与乙醇混合液分离开，经过过滤后，能够将吸附了羟基大黄素的羧甲基纤维素钠等残渣过滤掉，得到C液，此时，C液中对皮肤有刺激性的羟基大黄素被分离过滤。将C液经过100℃-120℃加热5分钟，再经过0.3Mpa-0.5Mpa加压3分钟，通过高温高压使C液中的乙醇、水以及低沸点的残余成分蒸发，经过喷雾干燥后制得草珊瑚颗粒。草珊瑚颗粒富含草珊瑚成分、橄榄叶成分以及芦荟的主要成分，同时，增强了草珊瑚颗粒的抑菌性和吸湿性，消除了草珊瑚原料中对皮肤有刺激性的元素，使草珊瑚颗粒能够应用于纺织品上。当草珊瑚颗粒做成纤维而且保证草珊瑚颗粒占总体含量38-42wt%，即草珊瑚纤维中的草珊瑚颗粒含量占比在三分之一以上，提高草珊瑚纤维杀菌抑菌和吸湿的性能，利用制备好的草珊瑚纤维制成裤袜时，能够利用草珊瑚颗粒的抑菌杀菌性对吸附在裤袜上的细菌进行杀灭，同时抑制细菌再生。利用草珊瑚颗粒的吸湿性，能够将裤体内部尤其是裆部的湿气吸附在裤体上，再利用裤体自身的透气性将湿气排出，保证裤体内部环境的干燥性，在环境干燥的情况下能够进一步抑制细菌再生。但由于草珊瑚颗粒自身的吸湿性较强，使裤体内部环境干燥的情况下，容易造成皮肤脱水干燥甚至干裂。因此，再利用草珊瑚颗粒与聚酯切片共混制备纤维时，同时加入β-葡聚糖，而且保证草珊瑚颗粒与β-葡聚糖的比例为15:2到14:3，在这个比例下，草珊瑚颗粒的杀菌抑菌效果得到保证，同时对裤体内部环境吸湿效果得到保证，同时β-葡聚糖的含量也可以得到保证，当裤体的草珊瑚纤维与皮肤接触时，β-葡聚糖能够直接与皮肤基础，得到皮肤的吸收，β-葡聚糖不仅能够修复皮肤表面粘膜、使皮肤红润紧致，而且能够使皮肤细胞舒敏保湿。通过这种方式制备的草珊瑚纤维，不仅能够杀灭已生细菌、抑制细菌再生、对裤体内部环境吸湿起到裤体内部环境干燥的效果，进一步避免潮湿环境下的细菌滋生，而且能够通过与皮肤的接触使皮肤红润紧致、舒敏保湿。即穿着草珊瑚裤袜后，裤体与皮肤之间的环境得到很好的干燥，但又不会使皮肤脱水干裂。首先，配比整理液，整理液中含有以下成分：聚乙烯吡咯烷酮0.3g/L、硅酸钠0.5g/L、甲壳素1.5g/L、羟丙甲纤维素0.5/L，其中聚乙烯吡咯烷酮具有较强的杀菌效果，利用前整理的方式，增强了最终成品的杀菌性能，对细菌和真菌均有效果。羟丙甲纤维素不仅能够作为增稠剂，而且能够作为稳定剂使草珊瑚裤袜半成品中的成分稳定。羟丙甲纤维素0.5/L的成分比例，避免整理液过于黏稠，保证整理液的均匀性，使聚乙烯吡咯烷酮以及草珊瑚纤维的成分能够得到附着和保留。在整理过程中，将整理液以5℃/min的速度升温至85℃，利用迅速升温的方式避免整理液挥发，在经过保温30min，使草珊瑚裤袜半成品以及整理液在85℃的温度下充分加热，整理液在受热后能够更加黏稠的吸附在草珊瑚裤袜半成品上与草珊瑚裤袜半成品充分作用。再以5℃/min的速度降温至60℃，即从85℃降至60℃时，草珊瑚半成品及整理液内的金丝桃苷、氨基酸、聚乙烯吡咯烷酮能够充分保留。最终将保温完成后的草珊瑚裤袜半成品浸没在水中2分钟，完成浸液处理，即草珊瑚裤袜半成品浸入水中之前的温度保留在60℃，浸入水中后迅速降温冷却，增强了整理液的吸附性和吸附效果，经过2分钟的冲洗后洗掉草珊瑚裤袜上的残留粘稠物，完成整理。
应理解，该实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的范围。
Claims (6)
1.一种草珊瑚裤袜，包括裤体和袜体，其特征在于，所述的裤体和袜体均由表纱和里纱编织而成，表纱和里纱均为草珊瑚纤维。
2.一种根据权利要求1所述的草珊瑚裤袜的生产工艺，其特征在于，步骤如下：
编织：将草珊瑚纤维作为表纱和里纱，并通过织袜机编织成型，形成草珊瑚裤袜半成品；
前整理：将草珊瑚裤袜半成品浸液处理；
后整理：对浸液处理后的草珊瑚裤袜半成品烘干定型；
成品检验、包装入库。
3.根据权利要求2所述的草珊瑚裤袜的生产工艺，其特征在于，步骤1）中草珊瑚纤维的制备方法如下：将聚酯切片、草珊瑚颗粒以及β-葡聚糖共混后通过熔融纺丝机进行纺丝，制成草珊瑚纤维，草珊瑚颗粒与β-葡聚糖的比例为15:2到14:3，草珊瑚颗粒占总体含量38-42wt%。
4.根据权利要求3所述的草珊瑚裤袜的生产工艺，其特征在于，所述的草珊瑚颗粒的制备方法如下：1）取洗净的草珊瑚原料粉碎，将粉碎后的草珊瑚原料过网筛，得到草珊瑚粒子，将草珊瑚粒子与乙醇混合，得到A液，草珊瑚粒子的质量为A液的10-15%；2） 取洗净的橄榄叶和芦荟打浆并过滤，在过滤后的液体内加入羧甲基纤维素钠搅拌均匀，得到B液；3）将A液和B液混合并搅拌均匀，A液和B液的混合比例为3:1，通过离心机离心，过滤残渣，制得C液；4）将C液经过100℃-120℃加热5分钟，再经过0.3Mpa-0.5Mpa加压3分钟后经过喷雾干燥后制得草珊瑚颗粒。
5.根据权利要求2所述的草珊瑚裤袜的生产工艺，其特征在于，步骤2）浸液处理时，将草珊瑚裤袜半成品在室温下浸入整理液内，将整理液以5℃/min的速度升温至85℃，然后保温30min，再以5℃/min的速度降温至60℃，再保温30min，最终将保温完成后的草珊瑚裤袜半成品浸没在水中2分钟，完成浸液处理，整理液中含有以下成分：聚乙烯吡咯烷酮0.3g/L、硅酸钠0.5g/L、甲壳素1.5g/L、羟丙甲纤维素0.5/L。
6.根据权利要求1或2或3所述的草珊瑚裤袜的生产工艺，其特征在于，步骤3）烘干定型是由蒸汽定型机完成，蒸汽压力为0.8Mpa-1Mpa，定型时间为25-40秒。