CN105970720A - Rosin sizing agent - Google Patents
Rosin sizing agent Download PDFInfo
- Publication number
- CN105970720A CN105970720A CN201610313828.1A CN201610313828A CN105970720A CN 105970720 A CN105970720 A CN 105970720A CN 201610313828 A CN201610313828 A CN 201610313828A CN 105970720 A CN105970720 A CN 105970720A
- Authority
- CN
- China
- Prior art keywords
- parts
- sizing agent
- rosin sizing
- rosin
- fatty acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention disclosed a rosin sizing agent, belonging to the technical field of rosin deep processing. The rosin sizing agent is prepared from the following raw materials in parts by weight: 100 parts of rosin, 15-20 parts of soybean oil fatty acid, 5-8 parts of phosphoryl trichloride, 1-2 parts of sodium acetate, 6-10 parts of polyethylene glycol, 0.1-0.2 part of sulfonated lignin, 15-25 parts of dimethyl silicone oil and 10-15 parts of deionized water with conductivity less than 5mu S/ cm. By adding the soybean oil fatty acid, the phosphoryl trichloride, the sodium acetate, the polyethylene glycol, the sulfonated lignin, the dimethyl silicone oil and the deionized water with conductivity less than 5mu S/cm into the rosin, the prepared rosin sizing agent has the advantage of being high in stability.
Description
Technical field
The invention belongs to Colophonium deep process technology field, particularly relate to a kind of rosin sizing agent.
Background technology
Sizing agent is the additive of a kind of papermaking, and it can give paper and the anti-ink of cardboard, water resistant, anti-emulsion, the performance such as anticorrosive to improve its smoothness, intensity and validity period.Sizing agent can be divided into internal sizing agent and Cypres, and wherein rosin sizing agent belongs to the one of paper making additive internal sizing agent.
The rosin sizing agent kind that existing market is sold is a lot, but it shows the defect that stability is poor, the shelf-life is too short mostly.
Summary of the invention
The technical problem to be solved is to provide a kind of rosin sizing agent, thus solves the problem that existing rosin sizing agent existence and stability energy is poor, the shelf-life is too short.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is:
It is prepared by the raw material of following weight portion:
Colophonium 100 parts, soy(a)-bean oil fatty acid 15 parts~20 parts, phosphorus oxychloride 5 parts~8 parts, sodium acetate 1 part~2 parts, Polyethylene Glycol 6 parts~10 parts, lignosulfonate 0.1 part~0.2 part, dimethyl-silicon 15 parts~25 parts and the electrical conductivity deionized water 10 parts~15 parts less than 5 μ S/cm.
In technique scheme, more specifically technical scheme is: Colophonium 100 parts, soy(a)-bean oil fatty acid 15 parts, phosphorus oxychloride 5 parts, sodium acetate 2 parts, Polyethylene Glycol 8 parts, lignosulfonate 0.15 part, dimethyl-silicon 20 parts and the electrical conductivity deionized water 15 parts less than 5 μ S/cm;
Further, Colophonium 100 parts, soy(a)-bean oil fatty acid 17 parts, phosphorus oxychloride 8 parts, sodium acetate 1 part, Polyethylene Glycol 10 parts, lignosulfonate 0.1 part, dimethyl-silicon 15 parts and the electrical conductivity deionized water 12 parts less than 5 μ S/cm;
Further, Colophonium 100 parts, soy(a)-bean oil fatty acid 20 parts, phosphorus oxychloride 6 parts, sodium acetate 1.5 parts, Polyethylene Glycol 6 parts, lignosulfonate 0.2 part, dimethyl-silicon 25 parts and the electrical conductivity deionized water 10 parts less than 5 μ S/cm.
Owing to using technique scheme, there is advantages that
The present invention is by adding soy(a)-bean oil fatty acid, phosphorus oxychloride, sodium acetate, Polyethylene Glycol, lignosulfonate, dimethyl-silicon and the electrical conductivity deionized water less than 5 μ S/cm in Colophonium, so that the product rosin sizing agent prepared has the advantage that stability is strong.
Detailed description of the invention
Below in conjunction with instantiation, the invention will be further described:
Embodiment 1
The preparation method of this rosin sizing agent is as follows:
Under stirring, first Colophonium 100 kg is added thermal melting, it is subsequently adding soy(a)-bean oil fatty acid 15 kg, phosphorus oxychloride 5kg, sodium acetate 2kg, Polyethylene Glycol 8kg, lignosulfonate 0.15kg, dimethyl-silicon 20kg and the electrical conductivity deionized water 15kg less than 5 μ S/cm, it is then heated to 80 DEG C, isothermal reaction 2 hours.
The rosin sizing agent good stability that the present embodiment prepares, can store 2 years when 40 DEG C.
Embodiment 2
This rosin sizing agent includes following preparation process:
Under stirring, first Colophonium 100 kg is added thermal melting, it is subsequently adding soy(a)-bean oil fatty acid 17 kg, phosphorus oxychloride 8kg, sodium acetate 1kg, Polyethylene Glycol 10kg, lignosulfonate 0.1kg, dimethyl-silicon 15kg and the electrical conductivity deionized water 12kg less than 5 μ S/cm, it is then heated to 65 DEG C, isothermal reaction 2 hours.
The rosin sizing agent good stability that the present embodiment prepares, can store 2 years when 40 DEG C.
Embodiment 3
This rosin sizing agent includes following preparation process:
Under stirring, first Colophonium 100 kg is added thermal melting, it is subsequently adding soy(a)-bean oil fatty acid 20 kg, phosphorus oxychloride 6kg, sodium acetate 1.5kg, Polyethylene Glycol 6kg, lignosulfonate 0.2kg, dimethyl-silicon 25kg and the electrical conductivity deionized water 10kg less than 5 μ S/cm, it is then heated to 60 DEG C, isothermal reaction 1 hour.
The rosin sizing agent good stability that the present embodiment prepares, can store 2 years when 40 DEG C.
Claims (4)
1. a rosin sizing agent, it is characterised in that prepared by the raw material of following weight portion:
Colophonium 100 parts, soy(a)-bean oil fatty acid 15 parts~20 parts, phosphorus oxychloride 5 parts~8 parts, sodium acetate 1 part~2 parts, Polyethylene Glycol 6 parts~10 parts, lignosulfonate 0.1 part~0.2 part, dimethicone 15 parts~25 parts and the electrical conductivity deionized water 10 parts~15 parts less than 5 μ S/cm.
Rosin sizing agent the most according to claim 1, it is characterised in that: Colophonium 100 parts, soy(a)-bean oil fatty acid 15 parts, phosphorus oxychloride 5 parts, sodium acetate 2 parts, Polyethylene Glycol 8 parts, lignosulfonate 0.15 part, dimethyl-silicon 20 parts and the electrical conductivity deionized water 15 parts less than 5 μ S/cm.
Rosin sizing agent the most according to claim 1, it is characterised in that: Colophonium 100 parts, soy(a)-bean oil fatty acid 17 parts, phosphorus oxychloride 8 parts, sodium acetate 1 part, Polyethylene Glycol 10 parts, lignosulfonate 0.1 part, dimethyl-silicon 15 parts and the electrical conductivity deionized water 12 parts less than 5 μ S/cm.
Rosin sizing agent the most according to claim 1, it is characterised in that: Colophonium 100 parts, soy(a)-bean oil fatty acid 20 parts, phosphorus oxychloride 6 parts, sodium acetate 1.5 parts, Polyethylene Glycol 6 parts, lignosulfonate 0.2 part, dimethyl-silicon 25 parts and the electrical conductivity deionized water 10 parts less than 5 μ S/cm.