CN105939976A - 玻璃组合物和使用该玻璃组合物的太阳能电池用电极组合物 - Google Patents
玻璃组合物和使用该玻璃组合物的太阳能电池用电极组合物 Download PDFInfo
- Publication number
- CN105939976A CN105939976A CN201580006166.7A CN201580006166A CN105939976A CN 105939976 A CN105939976 A CN 105939976A CN 201580006166 A CN201580006166 A CN 201580006166A CN 105939976 A CN105939976 A CN 105939976A
- Authority
- CN
- China
- Prior art keywords
- composition
- resin
- weight
- glass composition
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了玻璃组合物以及含其的太阳能电池用电极组合物。更具体地,提供了具有低玻璃化转变温度且显示出三个或更多个放热峰的玻璃组合物,以及使用其的太阳能电池用电极组合物,所述电极组合物实现低串联电阻以及高填充因子以提高能量转换效率。
Description
技术领域
本发明涉及用于提高电极和衬底之间的接触电阻且抑制pn结的分流的玻璃组合物,以及使用该玻璃组合物的太阳能电池用电极组合物。
背景技术
太阳能电池电极包含导电金属粉、玻璃粉、有机粘合剂、溶剂等作为主要成分。其中,玻璃粉在诱导电极材料和pn结结构的单元(cell)之间的接触电阻方面发挥非常重要的作用。
为了获得结晶态太阳能电池的优异的转换效率,必须改善在高烧结温度(700℃至900℃)下玻璃粉的活性。具有优异活性的玻璃粉增加n层表面上的Ag沉积物从而提高了接触电阻,导致串联电阻和填充因子的提高。因此可能制造高效太阳能电池。通过提高接触电阻,还可在如高薄层电阻(80Ω/□或更大)结构的高阻抗衬底内获得稳定的串联电阻。
然而,在700℃至900℃的高温下,普通的玻璃粉持续地引起扩散反应,导致分流现象,且因此在n层表面上的导电成分(Ag)到达p层。
为了防止该问题,韩国专利公开第10-2011-0105682号公开了使用结晶玻璃粉的组合物。根据该方法,结晶玻璃阻止了持续的扩散反应从而减少了分流现象,但在不同烧结温度下不易控制结晶化反应,从而导致烧结温度低余裕的问题。
此外,韩国专利公开第10-2010-0125273号公开了不含PbO的Bi基玻璃组合物。根据该方法,不包括快速反应的PbO成分以减少Ag沉积物,且因此难以获得优异的接触电阻。此外,由于高薄层电阻电池(80Ω/□或更大)的应用,串联电阻可提高。
美国专利公开第2011-0232746号公开了包含Pb-Te-B氧化物作为主要成分的薄膜糊料组合物。然而该方法由于玻璃形成体B2O3可引起玻璃熔体的流动性降低和衬底的可润湿性降低。
发明内容
技术问题
本发明的一个目标为提供玻璃组合物,其具有与电池的低的接触电阻,防止pn结结构的分流,具有低玻璃化温度,尤其是示出三个或更多放热峰。
本发明的另一个目标为提供太阳能电池用电极组合物,其通过使用所述玻璃组合物而显示出低串联电阻以及高填充因子,从而提高能量转换效率。
技术解决方案
本发明提供玻璃组合物,根据通过差示扫描量热法的测量,所述玻璃组合物在200℃至600℃的范围内示出三个或更多放热峰。
所述玻璃组合物可包含PbO、TeO2和Li2O。玻璃组合物还可包括选自以下的一种或更多种金属氧化物:Na2O、K2O、Bi2O3和SiO2。在这种情况下,玻璃组合物可具有以下的金属氧化物组成:PbO、TeO2、Li2O和Bi2O3;PbO、TeO2、Li2O、Na2O和K2O;PbO、TeO2、Li2O、Na2O、K2O和SiO2;PbO、TeO2、Li2O、Na2O、K2O和Bi2O3;或PbO、TeO2、Li2O、Na2O、K2O、Bi2O3和SiO2。
此外,玻璃组合物可不包含金属成分或除了上述金属氧化物之外的金属氧化物,杂质除外。
在玻璃组合物中,基于玻璃组合物的总重量,可包含20重量%至70重量%的PbO、20重量%至70重量%的TeO2、以及0.1重量%至20重量%的Li2O。
此外,基于总共100重量份的PbO、TeO2和Li2O,另外包含的金属氧化物的量可为0.1重量份至30重量份。
所述玻璃组合物优选地具有200℃至400℃的玻璃化转变温度。
本发明还提供太阳能电池用电极组合物,其为包括导电颗粒、玻璃粉、粘合剂以及溶剂的糊料组合物,其中玻璃粉可包括上述玻璃组合物。
基于总的糊料组合物,玻璃粉可以以0.1重量%至20重量%的量包含。
导电颗粒可包括具有10nm至10μm的平均直径的Ag、Cu或Ni颗粒。
粘合剂可为选自以下的一种或更多种:纤维素衍生物,如甲基纤维素、乙基纤维素、硝化纤维素、羟基纤维素或纤维素乙酸酯;丙烯酸树脂;醇酸树脂;聚丙烯类树脂;聚氯乙烯类树脂;聚氨酯类树脂;环氧类树脂;有机硅类树脂;松香类树脂;萜烯类树脂;酚醛树脂;脂肪族石油树脂;丙烯酸酯类树脂;二甲苯类树脂;香豆酮茚类树脂(cumaronindene-basedresin);苯乙烯类树脂;二环戊二烯类树脂;聚丁烯类树脂;聚醚类树脂;脲类树脂;密胺类树脂;乙酸乙烯酯类树脂以及聚异丁基类树脂(polyisobutyl-based resin)。
溶剂为选自以下的一种或更多种:乙酸丁基卡必醇酯、丁基卡必醇、丙二醇单甲醚、二丙二醇单甲醚、丙二醇单甲醚丙酸酯、乙醚丙酸酯、丙二醇单甲醚乙酸酯、松油醇、TEXANOL酯醇(texanol,2,2,4-三甲基-1,3-戊二醇单异丁酸酯)、(二甲基氨基)甲醛、甲基乙基酮、γ-丁内酯和乳酸乙酯。
太阳能电池用电极组合物可用于在具有80Ω/□或更大的薄层电阻的衬底上形成前电极。
发明效果
根据本发明的玻璃组合物为具有低玻璃化转变温度(200℃至400℃)的结晶的玻璃粉。当包含该玻璃组合物的太阳能电池用电极组合物用于形成电极时,可获得低串联电阻和高填充因子从而提高能量转换效率。此外,本发明的玻璃组合物在预定的温度区间表现出三个或更多个放热峰,从而显示出与电池的低接触电阻。此外,在本发明中,示出三个或更多放热峰的玻璃组合物用于制造太阳能电池的前电极,从而抑制pn结的分流,即形成于n层上的导电成分渗入p层。而且,本发明具有提高烧结温度和时间的余裕的效果。
附图说明
图1示出通过差示扫描量热法(DSC)测量的实施例1的玻璃组合物的热分析结果。
图2示出通过差示扫描量热法(DSC)测量的实施例2的玻璃组合物的热分析结果。
图3示出通过差示扫描量热法(DSC)测量的实施例3的玻璃组合物的热分析结果。
图4示出通过差示扫描量热法(DSC)测量的比较例1的玻璃组合物的热分析结果。
图5示出通过TLM图案测量的实施例9和比较例6的接触电阻的测量结果。
图6示出通过CoreScan测试仪测量的实施例9和比较例6的接触电阻的测量结果。
图7示出通过扫描电子显微镜(SEM)测量的实施例9和比较例6的电极表面的测量结果。
具体实施方式
下文将更具体地描述本发明。
根据本发明的一个实施方案,提供由差示扫描量热法测量的在200℃至600℃范围内示出三个或更多放热峰的玻璃组合物。
本发明玻璃组合物包含PbO、TeO2和Li2O。此外本发明的玻璃组合物还包含选自以下的一种或更多种金属氧化物:Na2O、K2O、Bi2O3和SiO2。
就此而言,本发明中提到的玻璃组合物意指玻璃粉或玻璃熔块(frit),且为在太阳能电池用电极组合物中使用的组分。由于上述特定组合物,本发明的玻璃组合物的特征在于,根据通过差示扫描量热法(DSC)的测量,该玻璃组合物在200℃或更高的范围内示出三个或更多个放热峰。
特别地,根据本发明的玻璃组合物,其特征在于,根据通过差示扫描量热法的测量,该玻璃组合物在200℃至400℃的范围内示出一个或更多个放热峰。此外,根据通过差示扫描量热法的测量,本发明的玻璃组合物在400℃至600℃的范围内可示出两个或更多个放热峰,优选三个或更多个放热峰。最优选地,根据通过差示扫描量热法(DSC)的测量,本发明玻璃组合物在200℃至600℃的范围内或在400℃至600℃的范围内可示出四个至五个放热峰。
因此,与先前的组合物相比,本发明的玻璃组合物可防止pn结结构的分流。此外,根据本发明的玻璃组合物为具有200℃至400℃的玻璃化转变温度(Tg)的低温玻璃粉,其活性和流动性优异,且其易于控制结晶化反应。因此当玻璃组合物用于电极组合物时,n层表面上的Ag沉积物增加,从而提高了接触电阻,从而实现太阳能电池的高效率。
此外,与先前的组合物相比,本发明的玻璃组合物可显示出如前述温度范围内的低玻璃化转变温度。更优选地,本发明的玻璃组合物可具有200℃至300℃的玻璃化转变温度(Tg),其比先前的组合物的玻璃化转变温度更低。
就此而言,如果玻璃组合物的玻璃化转变温度高于400℃,由于Ag电极烧结过程期间的玻璃的高粘度,存在难以获得均匀的接触特性的问题。如果玻璃组合物的玻璃化转变温度低于200℃,存在过度烧结流动行为可导致电极图案周围的图案扩散的问题。尽管先前的玻璃组合物显示出低玻璃化转变温度,但该玻璃组合物的组成不满足本发明建议的特定主要成分和含量范围,因此可能不示出多重放热峰。
特别地,本发明的玻璃组合物为玻璃粉,所述玻璃粉示出如下特征:通过上述特定成分引发多级反应以在热分析中示出三个或更多个放热峰。因此,当使用烧结过程期间具有多重放热特性的本发明的玻璃聚合物时,可实现低接触电阻。
在制造太阳能电池电极的烧结过程的扩散反应中,多级控制是可能的,从而抑制分流现象,即n层表面上的导电成分(Ag)渗入p层。换言之,重要的是控制太阳能电池结构中的高温扩散性质,该太阳能电池结构具有低n层厚度和高薄层电阻。在本发明中,可通过控制玻璃粉的过分的流动行为来防止pn结结构的分流。因此,可能通过提高烧结余裕和高薄层电阻电池(80Ω/□或更大)结构中的稳定性以及提高接触电阻来实现结晶态太阳能电池的高效率。
本发明的玻璃组合物可不包含金属成分或除了上述的特定金属氧化物之外的金属氧化物。
因此本发明的玻璃组合物包含作为主要成分的基于PbO、TeO2和Li2O的化合物,尤其是,其不包含通常用于先前的玻璃组合物中的B2O3和P2O5成分。此外,即使本发明玻璃组合物仅包含TeO2以及Pb和Li的氧化物,其也带来如上的多重放热峰。
就此而言,当B2O3包含于玻璃组合物中时,如上所述,可降低熔体的流动性和衬底的可润湿性。此外,当P2O5包含于玻璃组合物中时,Tg增加从而导致熔体流动性和衬底可润湿性降低,且P2O5作为杂质显著增加了接触电阻(Rc)。而且,如果不使用Pb、Te和Li成分中的任一个,由于烧结过程期间n层表面被玻璃熔体持续刻蚀造成导电成分(Ag)到达p层,导致分流现象。
在本发明中,基于玻璃组合物的总重量,三种主要成分的含量可优选为20重量%至70重量%的PbO、20重量%至70重量%的TeO2、以及0.1重量%至20重量%的Li2O。
此外,玻璃组合物包含作为任选添加剂成分的金属氧化物,如Na2O,从而期望形成低玻璃化转变温度和提高Ag电极和减反射层之间活性的协同效应,以形成均匀的接触电阻。例如,如上所述,连同上述三种主要成分,本发明的玻璃组合物还可包含选自Na2O、K2O、Bi2O3和SiO2的一种或更多种金属氧化物。此外,当金属氧化物还用于玻璃组合物中时,基于总共100重量份的三种主要成分PbO、TeO2和Li2O,金属氧化物的量可适当地控制在0.1重量份至30重量份的范围内。
优选地,本发明的玻璃组合物包含以下组合物:PbO、TeO2、Li2O、和Bi2O3;PbO、TeO2、Li2O、Na2O、和K2O;PbO、TeO2、Li2O、Na2O、K2O、和SiO2;PbO、TeO2、Li2O、Na2O、K2O、和Bi2O3;或者PbO、TeO2、Li2O、Na2O、K2O、Bi2O3、和SiO2。如上所述,玻璃组合物可不包含金属成分或除了上述金属氧化物以外的金属氧化物,杂质除外。即本发明玻璃组合物仅包含上述成分。
另一方面,如果PbO成分的含量低于20重量%,存在衬底的可润湿性降低以及减反射层未渗透的问题。如果PbO成分的含量高于70重量%,存在难以玻璃化的问题。此外如果TeO2成分的含量低于20重量%,存在不能对多级反应进行控制,发生分流,以及因此n层表面上的导电成分(Ag)到达p层的问题。如果TeO2成分的含量高于70重量%,存在难以玻璃化的问题。此外,如果Li2O成分的含量低于0.1重量%,存在粘附性降低的问题。如果Li2O成分的含量高于20重量%,存在热膨胀系数增大从而在表面上产生微裂纹的问题。
如果金属化合物的含量高于30重量份,Na2O或K2O提高了碱含量,且因此难以玻璃化,而Bi2O3或SiO2提高玻璃化转变为温度,且因此难以降低烧结过程期间玻璃的高温粘度,从而降低衬底的可润湿性。
根据本发明的另一方面,提供了太阳能电池用电极组合物,其为包含导电颗粒、玻璃粉、粘合剂和溶剂的糊料组合物,其中玻璃粉可包含上述玻璃组合物。
根据本发明,具有上述低接触电阻、在预定的温度范围内有三个或更多个放热峰以及防止pn结结构的分流的特性的玻璃组合物包含于太阳能电池用电极组合物中,以获得太阳能电池的高填充因子和低串联电阻,从而提高能量转换效率。
就此而言,根据本发明的电极组合物优选用于制造太阳能电池的前电极。此外,本发明的电极组合物可用以制造具有低薄层电阻的常用衬底,其还可用来制造高薄层电阻结构的太阳能电池,太阳能电池包含具有80Ω/□或更大的薄层电阻的衬底。因此,本发明的太阳能电池用电极组合物可最优选用于在具有80Ω/□或更大的薄层电阻的衬底上形成前电极。
同时,本发明太阳能电池用电极组合物,基于全部糊料组合物,玻璃粉的含量可优选为0.1重量%至20重量%,且更优选为0.5重量%至5重量%。
导电颗粒可包含具有10nm至10μm的平均粒径的Ag、Cu或Ni颗粒,且优选Ag颗粒。就此而言,Ag颗粒可为球形颗粒、非球形颗粒以及薄片状颗粒中的任一种,但形状上无特别限制,且根据需要这些Ag颗粒可以其混合物的形式使用。基于全部糊料组合物,导电颗粒的含量可为45重量%至95重量%。
粘合剂可为疏水性粘合剂和亲水性粘合剂中的任一种,且粘合剂可为选自以下的一种或更多种:纤维素衍生物,如甲基纤维素、乙基纤维素、硝化纤维素、羟基纤维素或纤维素乙酸酯;丙烯酸树脂;醇酸树脂;聚丙烯类树脂;聚氯乙烯类树脂;聚氨酯类树脂;环氧类树脂;有机硅类树脂;松香类树脂;萜烯类树脂;酚醛树脂;脂肪族石油树脂;丙烯酸酯类树脂;二甲苯类树脂;香豆酮茚类树脂;苯乙烯类树脂;二环戊二烯类树脂;聚丁烯类树脂;聚醚类树脂;脲类树脂;密胺类树脂;乙酸乙烯酯类树脂以及聚异丁基类树脂。基于全部糊料组合物,粘合剂的含量可为0.1重量%至10重量%。
溶剂可为疏水性溶剂和亲水性溶剂中的任一种,且溶剂可选自以下的一种或更多种:乙酸丁基卡必醇酯、丁基卡必醇、丙二醇单甲醚、二丙二醇单甲醚、丙二醇单甲醚丙酸酯、乙醚丙酸酯、丙二醇单甲醚乙酸酯、松油醇、TEXANOL酯醇、(二甲基氨基)甲醛、甲基乙基酮、γ-丁内酯以及乳酸乙酯。溶剂可以足够溶解粘合剂的量来使用,且其范围无特别限制。例如,基于全部糊料组合物,溶剂含量可为1重量%至40重量%。
根据需要,本发明的太阳能电池用电极组合物还可包含添加剂,且例如可使用消泡剂、分散剂、塑化剂等。基于100重量份的太阳能电池用电极组合物,添加剂的含量可为0.01重量份至10重量份。
本发明的太阳能电池用电极组合物可用以制造前电极,且除了使用本发明的电极组合物和具有高薄层电阻的衬底外,对于制造方法无特别限制。因此在本发明中,可根据本领域中公知的方法制造太阳能电池。
例如,将常规Ag糊料组合物印刷于硅衬底上,然后干燥以形成Ag背电极。将Al糊料组合物印刷在该Ag背电极的一部分之上交叠的区域内,然后干燥以形成Al电极。随后,可将本发明的太阳能电池用电极组合物印刷于硅衬底的整个表面上,然后干燥以形成用于太阳能电池的前电极。就此而言,可使用指形线和汇流条图案形成前电极。
此外,在本发明中,用于形成前电极和背电极的各自的糊料组合物为通过使用常规方法涂布于衬底上的,所述方法如丝网印刷、刮涂(doctorblade)、喷墨印刷或凹版印刷。涂布电极组合物之后,对用于干燥和烧结的温度也无特别限制。
本发明中所用衬底可为包含于硅太阳能电池中的前电极中使用的硅衬底,且衬底可具有80Ω/□或更大的薄层电阻。
电极组合物的干燥可在150℃至350℃的温度下进行1分钟至30分钟,且烧结可在750℃至950℃的最高温度下进行数秒至5分钟。
此外,可与本领域公知的发射层、减反射层等一起,提供本发明太阳能电池。
下文,将参考下列实施例和比较例更具体地描述本发明。然而这些实施例仅用于说明目的,且本发明无意于限于这些实施例。
[实施例1至6和比较例1至5]
根据依照下列表1和表2的组合物和含量,制备实施例和比较例的玻璃组合物。
[表1]
成分 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 |
PbO(重量%) | 46.9 | 37.43 | 44.97 | 59.26 | 47.71 | 65.96 |
TeO2(重量%) | 49.0 | 58.83 | 54.29 | 36.5 | 50.4 | 30.85 |
Li2O(重量%) | 4.1 | 3.74 | 0.74 | 4.24 | 1.89 | 3.19 |
总计 | 100 | 100 | 100 | 100 | 100 | 100 |
Na2O(重量份) | - | 2.67 | - | 3.7 | 1.78 | 1.59 |
K2O(重量份) | - | 2.14 | - | 2.11 | 2.11 | 2.66 |
Bi2O3(重量份) | - | - | 5.82 | - | 7.58 | 1.1 |
SiO2(重量份) | - | 2.14 | - | - | 1.1 |
[表2]
成分 | 比较例1 | 比较例2 | 比较例3 | 比较例4 | 比较例5 |
PbO(重量%) | 73.18 | 48.01 | 95.54 | - | 75 |
TeO2(重量%) | 24.61 | 51.5 | - | 85.71 | 25 |
Li2O(重量%) | 2.21 | 0.49 | 4.46 | 14.29 | - |
总计 | 100 | 100 | 100 | 100 | 100 |
Na2O(重量份) | 1.17 | - | 1.79 | - | - |
K2O(重量份) | 2.34 | - | - | 4.29 | 1.88 |
Bi2O3(重量份) | - | 7.6 | 50 | - | - |
B2O3(重量份) | 0.39 | 0.55 | - | - | - |
TiO2(重量份) | - | 2.6 | - | 6 | 1.88 |
Al2O3(重量份) | 5.34 | - | - | 3.71 | 6.25 |
CuO(重量份) | 0.26 | - | - | - | - |
P2O5(重量份) | 14.44 | - | - | - | - |
SiO2(重量份) | 5.86 | - | 5.86 | 15.14 | 2.3 |
[实施例7至9和比较例6至7]
根据依照下列表3(单位:重量%)的组合物和含量,制备包含导电颗粒、玻璃粉和溶解有粘合剂的溶剂的导电糊料。
详细地,使用PLM混合器将玻璃组合物中的每一种与媒质(vehicle)(粘合剂以及溶解该粘合剂的溶剂)混合,然后向其中加入导电颗粒(Ag),随后进行二次PLM混合。通过混合获得各个糊料通过使用三辊轧机揉制,最后制备了用于太阳能电池电极的糊料。
[表3]
[实验例1]
相对于实施例1至实施例3以及比较例1和比较例2的玻璃组合物,用差示扫描量热法(DSC)测量玻璃化转变温度(Tg)和放热峰。结果在表4中给出。此外,在图1至图4中给出实施例1至实施例3以及比较例1的差示扫描量热法结果。
[表4]
[实验例2]
根据常规方法使用实施例9和比较例6的导电糊料制造太阳能电池。
用于印刷电极的硅晶片为具有90Ω/□的薄层电阻的高薄层电阻单元,且将用于Ag背电极的糊料印刷于硅衬底上,然后干燥以形成Ag背电极。接下来,将用于Al背电极的糊料丝网印刷以与Ag背电极的一部分交叠,然后干燥。各个糊料在170℃的温度下干燥。
通过丝网印刷将实施例和比较例的糊料印刷于硅晶片的整个表面上,随后进行干燥过程。就此而言,用于印刷的掩模为具有47μm的总厚度的360目网,且通过使用具有40μm宽度的指形线和具有1.5mm宽度的汇流条将图案形成于前电极上。在170℃下干燥后,进行烧结以制造太阳能电池,并如下评估其性能。
(1)接触电阻
使用TLM图案和CoreScan测试仪来评估接触电阻。结果在图3和图4中给出。
(2)测试电极表面上的Ag沉积物产物
在通过将电极图案浸入30%氢氟酸溶液中数秒至3分钟来刻蚀形成于电池表面的电极图案之后,通过扫描电子显微镜(SEM)观察形成于n层表面的Ag沉积物。
(3)电学特性
通过使用太阳光模拟器评估太阳能电池衬底的电学特性(曲线I至V),且结果在表5中给出。
[表5]
实施例9 | 比较例6 | |
串联电阻(mΩ) | 1.52 | 4.24 |
短路电流(A) | 8.672 | 8.665 |
开路电压(V) | 0.625 | 0.624 |
填充因子(%) | 79.22 | 74.31 |
能量转换效率(%) | 17.64 | 16.51 |
图5和图6的结果显示,与比较例相比,本发明的实施例中接触电阻得到极大改善。在图7中,实施例9的电极的n层表面上的Ag沉积物增加,表明接触电阻的提高,与图5和图6一样。然而,比较例6的电极表面上产生少量Ag沉积物,因此接触电阻高从而使电池性能恶化。
表5的结果显示,尽管高薄层电阻(90Ω/□或更大)结构中衬底的高电阻,实施例9具有相对于比较例6而言更低的串联电阻和更高的填充因子,从而改善了能量转换效率。
Claims (14)
1.一种玻璃组合物,根据通过差示扫描量热法的测量,其在200℃到600℃的范围内示出三个或更多个放热峰。
2.根据权利要求1所述的玻璃组合物,包含PbO、TeO2和Li2O。
3.根据权利要求1所述的玻璃组合物,还包含选自Na2O、K2O、Bi2O3和SiO2中的一种或更多种金属氧化物。
4.根据权利要求3所述的玻璃组合物,包括下列金属氧化物组合物:
PbO、TeO2、Li2O和Bi2O3;
PbO、TeO2、Li2O、Na2O和K2O;
PbO、TeO2、Li2O、Na2O、K2O和SiO2;
PbO、TeO2、Li2O、Na2O、K2O和Bi2O3;以及
PbO、TeO2、Li2O、Na2O、K2O、Bi2O3和SiO2。
5.根据权利要求1所述的玻璃组合物,不包含金属成分或除了根据权利要求2或4所述的金属氧化物之外的金属氧化物。
6.根据权利要求1或2所述的玻璃组合物,基于所述玻璃组合物的总重量,其包含20重量%至70重量%的PbO、20重量%至70重量%的TeO2,和0.1重量%至20重量%的Li2O。
7.根据权利要求3所述的玻璃组合物,其中基于总共100重量份的PbO、TeO2和Li2O,所述金属氧化物的含量为0.1重量份至30重量份。
8.根据权利要求1所述的玻璃组合物,其中玻璃化转变温度(Tg)为200℃至400℃。
9.一种太阳能电池用电极组合物,其为包含导电颗粒、玻璃粉、粘合剂以及溶剂的糊料组合物,其中所述玻璃粉包含根据权利要求1所述的玻璃组合物。
10.根据权利要求9所述的电极组合物,其中基于全部所述糊料组合物,所述玻璃粉的含量为0.1重量%至20重量%。
11.根据权利要求9所述的太阳能电池用电极组合物,其中所述导电颗粒包含平均直径为10nm至10μm的Ag、Cu或Ni颗粒。
12.根据权利要求9所述的太阳能电池用电极组合物,其中所述粘合剂为选自以下的一种或更多种:纤维素衍生物,如甲基纤维素、乙基纤维素、硝化纤维素、羟基纤维素或纤维素乙酸酯;丙烯酸树脂;醇酸树脂;聚丙烯类树脂;聚氯乙烯类树脂;聚氨酯类树脂;环氧类树脂;有机硅类树脂;松香类树脂;萜烯类树脂;酚醛树脂;脂肪族石油树脂;丙烯酸酯类树脂;二甲苯类树脂;香豆酮茚类树脂;苯乙烯类树脂;二环戊二烯类树脂;聚丁烯类树脂;聚醚类树脂;脲类树脂;密胺类树脂;乙酸乙烯酯类树脂和聚异丁基类树脂。
13.根据权利要求9所述的太阳能电池用电极组合物,其中所述溶剂为选自以下的一种或更多种:乙酸丁基卡必醇酯、丁基卡必醇、丙二醇单甲醚、二丙二醇单甲醚、丙二醇单甲醚丙酸酯、乙醚丙酸酯、丙二醇单甲醚乙酸酯、松油醇、TEXANOL酯醇、(二甲基氨基)甲醛、甲基乙基酮、γ-丁内酯和乳酸乙酯。
14.根据权利要求9所述的太阳能电池用电极组合物,其被用于在具有80Ω/□或更大的薄层电阻的衬底上形成前电极。