CN105908520A - 一种保暖透气防钻绒服装面料 - Google Patents

一种保暖透气防钻绒服装面料 Download PDF

Info

Publication number
CN105908520A
CN105908520A CN201610492512.3A CN201610492512A CN105908520A CN 105908520 A CN105908520 A CN 105908520A CN 201610492512 A CN201610492512 A CN 201610492512A CN 105908520 A CN105908520 A CN 105908520A
Authority
CN
China
Prior art keywords
fabric
chiseling down
coating
fiber
fibers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201610492512.3A
Other languages
English (en)
Inventor
程飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Yundu Cotton Co Ltd
Original Assignee
Hefei Yundu Cotton Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Yundu Cotton Co Ltd filed Critical Hefei Yundu Cotton Co Ltd
Priority to CN201610492512.3A priority Critical patent/CN105908520A/zh
Publication of CN105908520A publication Critical patent/CN105908520A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种保暖透气防钻绒服装面料，包括基层面料和防钻绒涂层；所述基层面料是由经纱和纬纱交织而成的，所述经纱是由棉纤维和莫代尔纤维捻和而成的，所述纬纱是由抗菌导湿腈纶纤维和竹炭纤维捻和而成的，所述各纤维所占的质量百分比为：棉纤维45%‑50%、莫代尔纤维15%‑20%、抗菌导湿腈纶纤维25%‑30%、竹炭纤维10%‑15%；所述防钻绒涂层为有机硅高弹涂层。通过上述方式，本发明的面料质地细密紧致，具有良好的保暖性、防钻绒性及透气性，同时具有抑菌抗菌作用，且无毒、无害、环保又安全。

Description

一种保暖透气防钻绒服装面料
技术领域
本发明涉及服装面料领域，特别是涉及一种保暖透气防钻绒服装面料。
背景技术
目前，适用于羽绒产品的纺织面料主要有棉织物和化学纤维织物，棉织面料具有良好的吸湿性、透气性，穿着柔软舒适，保暖性好，但是易褶皱，缩水率大；化学纤维面料手感柔软，光泽好，颜色鲜艳，但是透气性和舒适性差，并且羽绒产品的纺织面料还需具有一定的防钻绒性能，需要面料具有高密性，这就造成面料地质较硬、透气性能差，故现有的羽绒产品的纺织面料很难同时具有防钻绒性、透气性及良好的保暖舒适性。
发明内容
本发明主要解决的技术问题是提供一种保暖透气防钻绒服装面料，具有良好的保暖性、防钻绒性及透气性，同时具有抑菌抗菌作用，且无毒、无害、环保又安全。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种保暖透气防钻绒服装面料，包括基层面料和和防钻绒涂层，所述防钻绒涂层是通过真空喷涂工艺成型于所述基础面料上的；所述基层面料为纺织物，是由经纱和纬纱交织而成的，所述经纱是由棉纤维和莫代尔纤维捻和而成的，所述纬纱是由抗菌导湿腈纶纤维和竹炭纤维捻和而成的，所述各纤维所占的质量百分比为：棉纤维45%-50%、莫代尔纤维15%-20%、抗菌导湿腈纶纤维25%-30%、竹炭纤维10%-15%，所述经纱的线密度为12tex，所述纬纱的线密度为10tex，并且所述基层面料的厚度为0.3-0.5mm；所述防钻绒涂层为有机硅高弹涂层，所述防钻绒涂层的厚度为5-6μm。
在本发明一个较佳实施例中，所述面料的纱支数为60S。
在本发明一个较佳实施例中，所述面料的纱支密度为300T。
在本发明一个较佳实施例中，所述棉纤维为木棉纤维。
本发明的有益效果是：基层面料采用具有柔软性好、吸湿性强、保暖性好的棉纤维；具有干爽、透气、保暖作用的莫代尔纤维；具有发射远红外线、蓄热保暖作用的竹炭纤维；具有吸(导)湿、抗菌和抗静电的功能的抗菌导湿腈纶纤维以及具有抑菌抗菌、发射远红外线、蓄热保暖的作用的竹炭纤维交织而成；并且在基层面料上涂覆一层有机硅高弹涂层，使面料具有良好的保暖性、防钻绒性及透气性，同时具有抑菌抗菌作用，且无毒、无害、环保又安全。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括：
一种保暖透气防钻绒服装面料，包括基层面料和和防钻绒涂层，所述防钻绒涂层是通过真空喷涂工艺成型于所述基础面料上的；所述基层面料为纺织物，是由经纱和纬纱交织而成的，所述经纱是由棉纤维和莫代尔纤维捻和而成的，所述纬纱是由抗菌导湿腈纶纤维和竹炭纤维捻和而成的，所述各纤维所占的质量百分比为：棉纤维45%-50%、莫代尔纤维15%-20%、抗菌导湿腈纶纤维25%-30%、竹炭纤维10%-15%，所述经纱的线密度为12tex，所述纬纱的线密度为10tex，并且所述基层面料的厚度为0.3-0.5mm；所述防钻绒涂层为有机硅高弹涂层，又叫纸感涂层，具有很强的回弹性、抗皱性，并能增加面料的牢度性、延长面料的使用寿命，所述防钻绒涂层的厚度为5-6μm，涂层厚度低，不影响面料的透气性。
其中，所述面料的纱支数为60S，纱支密度高，均匀度好，面料具有良好的舒适性。
所述面料的纱支密度为300T，面料具有高密性，能有效防止钻绒现象。
所述棉纤维为木棉纤维，具有柔软性好、吸湿性强、保暖性好的特点。
本发明面料选用的成分及性能如下：
莫代尔纤维：具有干爽、透气、保暖作用，并且可以进行生物降解，具有良好的环保性能。
抗菌导湿腈纶纤维：具有吸(导)湿、抗菌和抗静电的功能。
竹炭纤维：具有抑菌抗菌、发射远红外线、蓄热保暖的作用。
实施例一：
一种保暖透气防钻绒服装面料，包括基层面料和和防钻绒涂层，所述防钻绒涂层是通过真空喷涂工艺成型于所述基础面料上的；所述基层面料为纺织物，是由经纱和纬纱交织而成的，所述经纱是由木棉纤维和莫代尔纤维捻和而成的，所述纬纱是由抗菌导湿腈纶纤维和竹炭纤维捻和而成的，所述各纤维所占的质量百分比为：木棉纤维45%、莫代尔纤维20%、抗菌导湿腈纶纤维25%、竹炭纤维10%，所述经纱的线密度为12tex，所述纬纱的线密度为10tex，并且所述基层面料的厚度为0.3mm；所述防钻绒涂层为有机硅高弹涂层，所述防钻绒涂层的厚度为5μm。
其中，所述面料的纱支数为60S。
所述面料的纱支密度为300T。
实施例二：
一种保暖透气防钻绒服装面料，包括基层面料和和防钻绒涂层，所述防钻绒涂层是通过真空喷涂工艺成型于所述基础面料上的；所述基层面料为纺织物，是由经纱和纬纱交织而成的，所述经纱是由木棉纤维和莫代尔纤维捻和而成的，所述纬纱是由抗菌导湿腈纶纤维和竹炭纤维捻和而成的，所述各纤维所占的质量百分比为：棉纤维45%、莫代尔纤维15%、抗菌导湿腈纶纤维25%、竹炭纤维15%，所述经纱的线密度为12tex，所述纬纱的线密度为10tex，并且所述基层面料的厚度为0.5mm；所述防钻绒涂层为有机硅高弹涂层，所述防钻绒涂层的厚度为6μm。
其中，所述面料的纱支数为60S。
所述面料的纱支密度为300T。
本发明揭示了一种保暖透气防钻绒服装面料，基层面料采用具有柔软性好、吸湿性强、保暖性好的棉纤维；具有干爽、透气、保暖作用的莫代尔纤维；具有发射远红外线、蓄热保暖作用的竹炭纤维；具有吸(导)湿、抗菌和抗静电的功能的抗菌导湿腈纶纤维以及具有抑菌抗菌、发射远红外线、蓄热保暖的作用的竹炭纤维交织而成；并且在基层面料上涂覆一层有机硅高弹涂层，使面料具有良好的保暖性、防钻绒性及透气性，同时具有抑菌抗菌作用，且无毒、无害、环保又安全。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (4)

1.一种保暖透气防钻绒服装面料，其特征在于，包括基层面料和和防钻绒涂层，所述防钻绒涂层是通过真空喷涂工艺成型于所述基础面料上的；所述基层面料为纺织物，是由经纱和纬纱交织而成的，所述经纱是由棉纤维和莫代尔纤维捻和而成的，所述纬纱是由抗菌导湿腈纶纤维和竹炭纤维捻和而成的，所述各纤维所占的质量百分比为：棉纤维45%-50%、莫代尔纤维15%-20%、抗菌导湿腈纶纤维25%-30%、竹炭纤维10%-15%，所述经纱的线密度为12tex，所述纬纱的线密度为10tex，并且所述基层面料的厚度为0.3-0.5mm；所述防钻绒涂层为有机硅高弹涂层，所述防钻绒涂层的厚度为5-6μm。
2.根据权利要求1所述的保暖透气防钻绒服装面料，其特征在于，所述面料的纱支数为60S。
3.根据权利要求1所述的保暖透气防钻绒服装面料，其特征在于，所述面料的纱支密度为300T。
4.根据权利要求1所述的保暖透气防钻绒服装面料，其特征在于，所述棉纤维为木棉纤维。
CN201610492512.3A 2016-06-29 2016-06-29 一种保暖透气防钻绒服装面料 Withdrawn CN105908520A (zh)