CN105887278A - Fiberglass cloth special for thermoplastic fiberglass reinforced PP composites - Google Patents
Fiberglass cloth special for thermoplastic fiberglass reinforced PP composites Download PDFInfo
- Publication number
- CN105887278A CN105887278A CN201610330241.1A CN201610330241A CN105887278A CN 105887278 A CN105887278 A CN 105887278A CN 201610330241 A CN201610330241 A CN 201610330241A CN 105887278 A CN105887278 A CN 105887278A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fiberglass
- glass
- fibre
- alkali
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of fiber cloth, in particular to fiberglass cloth special for thermoplastic fiberglass reinforced PP composites. A production process of the fiberglass cloth includes preparation of blended fiber yarn, preparation of the fiberglass cloth, and posttreatment; the step of preparation of the blended fiber yarn includes adding a PP yarn unreeling on a coil base special for an alkali-free fiberglass melting furnace drawing line, and designing yarn count according to the proportion of fiberglass: PP fiber=6:4 in the process of twistless fiberglass roving. Production cost is lowered, the production process is simplified, product strength is enhanced, and the fiberglass cloth is suitable for large-scale production.
Description
Technical field
The present invention relates to fiber cloth technical field, be specifically related to a kind of thermoplastic glass fiber reinforced PP and be combined
Material special glass fiber cloth.
Background technology
Thermoplastic refers to that material has thermoplastic, the characteristic of hardening by cooling characteristic, with thermosetting material
Material compare temperature time variance soft so that flowing, cool down hardening, this process is reversible, can be repeated,
Therefore there is the effect of recycling.Wherein thermoplastic glass fiber reinforced PP is Application comparison material widely
Material.
Conventional thermoplastic glass fiber reinforced PP composite is thermoplastic glass fiber to be chopped into
0.2-7mm, a kind of composite being evenly distributed in PP matrix.Its production technology is divided into granulation and becomes
Two processes of type, granulation is to heat mixed according to a certain percentage with PP particle after thermoplastic glass fiber's chopped
After conjunction, through die extrusion material strip after plasticating further more cooled, be dried be then cut into pellet.Shaping
Technique is injection technique, is that after being melted by granule heating, importing is expelled in die cavity the cooling through a period of time,
Making material be cooled to glassy state in the case of keeping mold cavity shapes, then goods are taken out in die sinking.
Through the thermoplastic glass fiber reinforced PP composite that above-mentioned technique produces, although the purposes ratio of goods
Wide, but it is the highest to there is intensity, the defect that production efficiency is relatively low and relatively costly, pushing away to product
Wide application brings adverse influence, particularly under the background that goods maximize day by day and structure complicates,
The intensity of goods is proposed higher requirement.
Summary of the invention
Present invention aims to defect and the deficiency of prior art, it is provided that a kind of reasonable in design, system
Make convenient thermoplastic glass fiber reinforced PP composite special glass fiber cloth, reduce production cost,
Simplify production technology, improve product strength, be suitable for large-scale production.
For achieving the above object, the technical solution used in the present invention is:
Its Making programme is as follows:
One, the preparation of blend fibre yarn: increase on the alkali-free glass fibre special table of pool kiln wiredrawing production line
Add PP yarn reeling-up reeling-out device, during drawing woven glass roving fabric, by glass fibre: PP fiber
=6: 4 (fluctuation ± 10% up and down) Proportionality design yarn number, by non-twist with alkali-free glass fibre thermoplasticity for PP yarn
Rove rolling together is molded, and then obtains required alkali-free glass fibre after drying and shaping fine with PP yarn blending
Dimension yarn, the technique of this blend fibre yarn is as follows: total yarn number is 800 ± 40tex, glass fibre: PP fiber
=6: 4 (fluctuations ± 10% up and down), winding ratio is 7.2, and package is 17 ± 1.0kg, oil content (glass
Fiber) it is 0.55 ± 0.15%；
Two, the preparation of glass fabric: above-mentioned blend fibre yarn is placed on warping creel, all yarns
Gluing with adhesive tape after discharge is good, be wound in warp beam, the fabric width of warp beam is 2220 ± 10mm, warp beam is pressed
Gaiting successively according to being organized as 2/2 or 1/3 twill, plug in reed, upper shaft, weave cotton cloth, its weaving process is nominal
Total amount is 510 ± 25g/m2, it is 800 ± 40tex through yarn number number, weft yarn number is 800 ± 40tex, warp
Close * filling density is 3.2*3.2 root/cm, and deviation range is ± 10%, rolls up a length of 100 ± 1m；
Three, postorder processes: according to required shape, the above-mentioned fiber cloth woven is carried out cutting, according to mould
The shape of tool is laid in a mold, i.e. available required goods after heating and melting.
After using above-mentioned technique, present invention have the beneficial effect that a kind of thermoplastic glass of the present invention is fine
Dimension strengthens PP composite special glass fiber cloth, reduces production cost, simplifies moulding process, improves
Production efficiency, it is also possible to avoid because injection moulding is because pressure is irregular or material flowing difference is easily generated defect system
The possibility of product.
Detailed description of the invention
Detailed description of the invention one:
This detailed description of the invention the technical scheme is that its Making programme is as follows:
One, the preparation of blend fibre yarn: increase on the alkali-free glass fibre special table of pool kiln wiredrawing production line
Add PP yarn reeling-up reeling-out device, during drawing woven glass roving fabric, by glass fibre: PP fiber
=6: 4 (fluctuation ± 10% up and down) Proportionality design yarn number, by non-twist with alkali-free glass fibre thermoplasticity for PP yarn
Rove rolling together is molded, and then obtains required alkali-free glass fibre after drying and shaping fine with PP yarn blending
Dimension yarn, the technique of this blend fibre yarn is as follows: total yarn number is 800 ± 40tex, glass fibre: PP fiber
=6: 4 (fluctuations ± 10% up and down), winding ratio is 7.2, and package is 17 ± 1.0kg, oil content (glass
Fiber) it is 0.55 ± 0.15%；
Two, the preparation of glass fabric: above-mentioned blend fibre yarn is placed on warping creel, all yarns
Gluing with adhesive tape after discharge is good, be wound in warp beam, the fabric width of warp beam is 2220 ± 10mm, warp beam is pressed
Gaiting successively according to being organized as 2/2 or 1/3 twill, plug in reed, upper shaft, weave cotton cloth, its weaving process is nominal
Total amount is 510 ± 25g/m2, it is 800 ± 40tex through yarn number number, weft yarn number is 800 ± 40tex, warp
Close * filling density is 3.2*3.2 root/cm, and deviation range is ± 10%, rolls up a length of 100 ± 1m；
Three, postorder processes: according to required shape, the above-mentioned fiber cloth woven is carried out cutting, according to mould
The shape of tool is laid in a mold, i.e. available required goods after heating and melting.
After using above-mentioned technique, present invention have the beneficial effect that a kind of thermoplastic glass of the present invention is fine
Dimension strengthens PP composite special glass fiber cloth, reduces production cost, simplifies moulding process, improves
Production efficiency, it is also possible to avoid because injection moulding is because pressure is irregular or material flowing difference is easily generated defect system
The possibility of product.
Detailed description of the invention two:
This detailed description of the invention the technical scheme is that its Making programme is as follows:
One, the preparation of blend fibre yarn: increase on the alkali-free glass fibre special table of pool kiln wiredrawing production line
Add PP yarn reeling-up reeling-out device, during drawing woven glass roving fabric, by glass fibre: PP fiber
=6: 4 (fluctuation ± 10% up and down) Proportionality design yarn number, by non-twist with alkali-free glass fibre thermoplasticity for PP yarn
Rove rolling together is molded, and then obtains required alkali-free glass fibre after drying and shaping fine with PP yarn blending
Dimension yarn, the technique of this blend fibre yarn is as follows: total yarn number is 1870 ± 93tex, and glass fibre: PP is fine
Dimension=6: 4 (fluctuation ± 10% up and down), winding ratio is 6.4, and package is 17 ± 1.0kg, oil content (glass
Glass fiber) it is 0.55 ± 0.15%；
Two, the preparation of glass fabric: above-mentioned blend fibre yarn is placed on warping creel, all yarns
Gluing with adhesive tape after discharge is good, be wound in warp beam, the fabric width of warp beam is 2220 ± 10mm, warp beam is pressed
Gaiting successively according to being organized as 2/2 or 1/3 twill, plug in reed, upper shaft, weave cotton cloth, its weaving process is nominal
Total amount is 980g/m2, it is 1870 ± 93tex through yarn number number, weft yarn number is 1870 ± 93tex, through close *
Filling density be 2.6*2.6 root/cm deviation range be ± 10%, roll up a length of 100 ± 1m；
Three, postorder processes: according to required shape, the above-mentioned fiber cloth woven is carried out cutting, according to mould
The shape of tool is laid in a mold, i.e. available required goods after heating and melting.
Detailed description of the invention three:
This detailed description of the invention the technical scheme is that its Making programme is as follows:
One, the preparation of blend fibre yarn: increase on the alkali-free glass fibre special table of pool kiln wiredrawing production line
Add PP yarn reeling-up reeling-out device, during drawing woven glass roving fabric, by glass fibre: PP fiber
=6: 4 (fluctuation ± 10% up and down) Proportionality design yarn number, by non-twist with alkali-free glass fibre thermoplasticity for PP yarn
Rove rolling together is molded, and then obtains required alkali-free glass fibre after drying and shaping fine with PP yarn blending
Dimension yarn, the technique of this blend fibre yarn is as follows: total yarn number is 3650 ± 182tex, and glass fibre: PP is fine
Dimension=6: 4 (fluctuation ± 10% up and down), winding ratio is 4.2, and package is 17 ± 1.0kg, oil content (glass
Glass fiber) it is 0.55 ± 0.15%；
Two, the preparation of glass fabric: above-mentioned blend fibre yarn is placed on warping creel, all yarns
Gluing with adhesive tape after discharge is good, be wound in warp beam, the fabric width of warp beam is 2220 ± 10mm, warp beam is pressed
Gaiting successively according to being organized as 2/2 or 1/3 twill, plug in reed, upper shaft, weave cotton cloth, its weaving process is nominal
Total amount is 1500 ± 75g/m2, it is 3650 ± 182tex through yarn number number, weft yarn number is 3650 ± 182tex,
Being 2.0*2.0 root/cm through close * filling density, deviation range is ± 10%, rolls up a length of 100 ± 1m；
Three, postorder processes: according to required shape, the above-mentioned fiber cloth woven is carried out cutting, according to mould
The shape of tool is laid in a mold, i.e. available required goods after heating and melting.
The above, is only in order to technical scheme to be described and unrestricted, ordinary skill people
Other amendment or equivalent that technical scheme is made by member, without departing from skill of the present invention
The spirit and scope of art scheme, all should contain in the middle of scope of the presently claimed invention.
Claims (1)
1. a thermoplastic glass fiber reinforced PP composite special glass fiber cloth, it is characterised in that:
Its Making programme is as follows:
(1), the preparation of blend fibre yarn: on the alkali-free glass fibre special table of pool kiln wiredrawing production line
Increase PP yarn unwinding device, during drawing woven glass roving fabric, by glass fibre: PP is fine
Dimension=6: 4 (up and down fluctuation ± 10%) Proportionality design yarn number, by PP yarn and alkali-free glass fibre thermoplasticity without
Twist with the fingers rove rolling together shaping, then after drying and shaping, obtain required alkali-free glass fibre and PP yarn blending
Silvalin, the technique of this blend fibre yarn is as follows: total yarn number is 800 ± 40tex, and glass fibre: PP is fine
Dimension=6: 4 (± 10%), winding ratio is 7.2, and package is 17 ± 1.0kg, and oil content is 0.55 ± 0.15%；
(2), the preparation of glass fabric: above-mentioned blend fibre yarn is placed on warping creel, all yarns
Line glues with adhesive tape after discharging, and is wound in warp beam, and the fabric width of warp beam is 2220 ± 10mm, by warp beam
According to be organized as 2/2 twill or 1/3 satin weave is gaited successively, plug in reed, upper shaft, weave cotton cloth, its weaver
Skill be nominal total amount be 510 ± 25g/m2, it is 800 ± 40tex through yarn number number, weft yarn number is 800 ±
40tex, is 3.2*3.2 root/cm through close * filling density, and deviation range is ± 10%, rolls up a length of 100 ± 1m；
(3), postorder process: the above-mentioned fiber cloth woven is carried out cutting according to required shape, according to
The shape of mould is laid in a mold, i.e. available required goods after heating and melting.