CN105886028A - 一种球磨机专用添加剂 - Google Patents
一种球磨机专用添加剂 Download PDFInfo
- Publication number
- CN105886028A CN105886028A CN201510333095.3A CN201510333095A CN105886028A CN 105886028 A CN105886028 A CN 105886028A CN 201510333095 A CN201510333095 A CN 201510333095A CN 105886028 A CN105886028 A CN 105886028A
- Authority
- CN
- China
- Prior art keywords
- parts
- ball mills
- tert
- ball mill
- repaired
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种球磨机专用添加剂,由以下质量百分比的原料配方组分组成:3-4份二甲苯、2-5份乙酸丁酯、2-3份丙酮、2-5份木质素磺酸钠、5-10份钙基润滑脂、2-3份N-甲基吡咯烷酮、3-5份十二烷基苯磺酸钠、3-4份马来酰亚胺、2-3份聚异丁烯丁二酸酐、3-5份聚乙烯亚胺、5-8份苯并三氮唑、4-6份4,4-硫代双6-叔丁基对甲酚、3-5份邻叔丁基苯酚。该球磨机专用添加剂能有效修复磨损,减小摩擦系数,可快速、简单,有效修复不同种类,不同的运行状态、不同磨损情况的球磨机,磨损表面得到修复,恢复光滑干整,始终保持最大的接触面积,避免了间隙的产生,使修复后的设备寿命大大增加,解决球磨机的磨损问题。
Description
技术领域
本发明涉及添加剂的技术领域,尤其涉及一种球磨机专用添加剂。
背景技术
球磨机是物料被破碎之后,再进行粉碎的关镶设备。它广泛应用于水泥,硅酸盐制品、新型建筑材料,耐火材料,化肥、黑与有色金属选矿以及玻璃陶瓷等生产行业。但其能量利用率仅为6%左右,其余大部分转变为热能,球磨机本身的功率消耗高达10%,机械摩擦损大功耗为10-15%,而磨损则是球磨机零部件失效的主要原因。随着国内球磨机的应用越来越广泛,其数量日渐增加,球磨机自身摩擦消耗的能源、资源日益增多。例如水泥厂球磨机磨粉作业用电量达到水泥厂用电总量的2/3以上,而生产每吨水泥耗电量则不低于70KM/H。随着球磨机市局竞争的日益激烈,如何减少球磨机内部摩擦磨损,减小振动,降低噪音,降低能耗,延长球磨机使用寿命成为人们关注的焦点。
发明内容
本发明的目的是为了克服上述现有技术的缺点,提供一种球磨机专用添加剂,该球磨机专用添加剂能有效修复磨损,减小摩擦系数,可快速、简单,有效修复不同种类,不同的运行状态、不同磨损情况的球磨机,磨损表面得到修复,恢复光滑干整,始终保持最大的接触面积,避免了间隙的产生,使修复后的设备寿命大大增加,解决球磨机的磨损问题。
本发明解决其技术问题所采用的技术方案是:一种球磨机专用添加剂,由以下质量百分比的原料配方组分组成:3-4份二甲苯、2-5份乙酸丁酯、2-3份丙酮、2-5份木质素磺酸钠、5-10份钙基润滑脂、2-3份N-甲基吡咯烷酮、3-5份十二烷基苯磺酸钠、3-4份马来酰亚胺、2-3份聚异丁烯丁二酸酐、3-5份聚乙烯亚胺、5-8份苯并三氮唑、4-6份4,4-硫代双6-叔丁基对甲酚、3-5份邻叔丁基苯酚。
进一步的,包括3份二甲苯、2份乙酸丁酯、2份丙酮、2份木质素磺酸钠、5份钙基润滑脂、2份N-甲基吡咯烷酮、3份十二烷基苯磺酸钠、3份马来酰亚胺、2份聚异丁烯丁二酸酐、3份聚乙烯亚胺、5份苯并三氮唑、4份4,4-硫代双6-叔丁基对甲酚、3份邻叔丁基苯酚。
或者是,包括4份二甲苯、5份乙酸丁酯、3份丙酮、5份木质素磺酸钠、10份钙基润滑脂、3份N-甲基吡咯烷酮、5份十二烷基苯磺酸钠、4份马来酰亚胺、3份聚异丁烯丁二酸酐、5份聚乙烯亚胺、8份苯并三氮唑、6份4,4-硫代双6-叔丁基对甲酚、5份邻叔丁基苯酚。
综上所述,本发明的有益效果是:本发明的球磨机专用添加剂能有效修复磨损,减小摩擦系数,可快速、简单,有效修复不同种类,不同的运行状态、不同磨损情况的球磨机,磨损表面得到修复,恢复光滑干整,始终保持最大的接触面积,避免了间隙的产生,使修复后的设备寿命大大增加,解决球磨机的磨损问题。
具体实施方式
实施例1
本实施例1所描述的一种球磨机专用添加剂,由以下质量百分比的原料配方组分组成: 包括3份二甲苯、2份乙酸丁酯、2份丙酮、2份木质素磺酸钠、5份钙基润滑脂、2份N-甲基吡咯烷酮、3份十二烷基苯磺酸钠、3份马来酰亚胺、2份聚异丁烯丁二酸酐、3份聚乙烯亚胺、5份苯并三氮唑、4份4,4-硫代双6-叔丁基对甲酚、3份邻叔丁基苯酚。
实施例2
本实施例2所描述的一种球磨机专用添加剂,由以下质量百分比的原料配方组分组成: 包括4份二甲苯、5份乙酸丁酯、3份丙酮、5份木质素磺酸钠、10份钙基润滑脂、3份N-甲基吡咯烷酮、5份十二烷基苯磺酸钠、4份马来酰亚胺、3份聚异丁烯丁二酸酐、5份聚乙烯亚胺、8份苯并三氮唑、6份4,4-硫代双6-叔丁基对甲酚、5份邻叔丁基苯酚。
以上所述,仅是本发明的较佳实施例而已,并非对本发明的原理和框架作任何形式上的限制。凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均仍属于本发明的技术方案的范围内。
Claims (3)
1.一种球磨机专用添加剂,其特征在于,由以下质量百分比的原料配方组分组成:3-4份二甲苯、2-5份乙酸丁酯、2-3份丙酮、2-5份木质素磺酸钠、5-10份钙基润滑脂、2-3份N-甲基吡咯烷酮、3-5份十二烷基苯磺酸钠、3-4份马来酰亚胺、2-3份聚异丁烯丁二酸酐、3-5份聚乙烯亚胺、5-8份苯并三氮唑、4-6份4,4-硫代双6-叔丁基对甲酚、3-5份邻叔丁基苯酚。
2.根据权利要求1所述的一种球磨机专用添加剂,其特征在于,包括3份二甲苯、2份乙酸丁酯、2份丙酮、2份木质素磺酸钠、5份钙基润滑脂、2份N-甲基吡咯烷酮、3份十二烷基苯磺酸钠、3份马来酰亚胺、2份聚异丁烯丁二酸酐、3份聚乙烯亚胺、5份苯并三氮唑、4份4,4-硫代双6-叔丁基对甲酚、3份邻叔丁基苯酚。
3.根据权利要求1所述的一种球磨机专用添加剂,其特征在于,包括4份二甲苯、5份乙酸丁酯、3份丙酮、5份木质素磺酸钠、10份钙基润滑脂、3份N-甲基吡咯烷酮、5份十二烷基苯磺酸钠、4份马来酰亚胺、3份聚异丁烯丁二酸酐、5份聚乙烯亚胺、8份苯并三氮唑、6份4,4-硫代双6-叔丁基对甲酚、5份邻叔丁基苯酚。