CN105861911A - Surface strengthening nickel base alloy for casting - Google Patents
Surface strengthening nickel base alloy for casting Download PDFInfo
- Publication number
- CN105861911A CN105861911A CN201610245780.5A CN201610245780A CN105861911A CN 105861911 A CN105861911 A CN 105861911A CN 201610245780 A CN201610245780 A CN 201610245780A CN 105861911 A CN105861911 A CN 105861911A
- Authority
- CN
- China
- Prior art keywords
- accounts
- parts
- nickel
- base alloy
- surface peening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a surface strengthening nickel base alloy for casting. The surface strengthening nickel base alloy is composed of, by weight, 35-40 parts of nickel, 28-32 parts of chromium, 19-23 parts of iron, 14-18 parts of copper, 13-16 parts of molybdenum, 10-14 parts of tin, 7-11 parts of platinum and 5-9 parts of phosphorus. Being composed of the nickel, the chromium, the iron, the copper, the molybdenum, the tin, the platinum and the phosphorus, the surface strengthening nickel base alloy has the advantages of being resistant to wear, high in strength, resistant to oxidization and long in service life.
Description
Technical field
The present invention relates to alloy field, be specifically related to a kind of casting surface peening nickel-base alloy.
Background technology
In recent years, Chinese Foundry equipment industry achieves swift and violent development, mo(u)lding equipment, coremaking equipment, sand preparing machine, casting equipment etc. all achieve significant progress at aspects such as properties of product, reliability, automaticities, and progressively stride forward to Green foundry direction.
In prior art, the various product surfaces of use are generally required for carrying out coating process, thus reach to protect the purpose of product, and as ensured the long-time use of product, in prior art, the coating of use is the most as easy as rolling off a log is worn, and the most aging, using effect is not good enough.
Summary of the invention
It is an object of the invention to provide and a kind of use nickel, chromium, ferrum, copper, molybdenum, stannum, platinum and eight kinds of one-tenth of phosphorus to be grouped into, have wear-resistant, intensity is high, the casting surface peening nickel-base alloy of the feature of antioxidation, length in service life.
The technical scheme is that, surface peening nickel-base alloy is used in a kind of casting, described casting surface peening nickel-base alloy is grouped into by nickel, chromium, ferrum, copper, molybdenum, stannum, platinum and eight kinds of one-tenth of phosphorus, and in described casting surface peening nickel-base alloy, parts by weight shared by each composition are respectively as follows: described nickel and account for 35-40 part, and described chromium accounts for 28-32 part, described ferrum accounts for 19-23 part, described copper accounts for 14-18 part, and described molybdenum accounts for 13-16 part, and described stannum accounts for 10-14 part, described platinum accounts for 7-11 part, and described phosphorus accounts for 5-9 part.
In a preferred embodiment of the present invention, in described casting surface peening nickel-base alloy, parts by weight shared by each composition are particularly as follows: described nickel accounts for 36 parts, described chromium accounts for 29 parts, described ferrum accounts for 20 parts, described copper accounts for 15 parts, and described molybdenum accounts for 14 parts, and described stannum accounts for 11 parts, described platinum accounts for 8 parts, and described phosphorus accounts for 6 parts.
In a preferred embodiment of the present invention, in described casting surface peening nickel-base alloy, parts by weight shared by each composition are particularly as follows: described nickel accounts for 39 parts, described chromium accounts for 31 parts, described ferrum accounts for 22 parts, described copper accounts for 17 parts, and described molybdenum accounts for 15 parts, and described stannum accounts for 13 parts, described platinum accounts for 10 parts, and described phosphorus accounts for 8 parts.
Of the present invention is a kind of casting surface peening nickel-base alloy, and the present invention uses nickel, chromium, ferrum, copper, molybdenum, stannum, platinum and eight kinds of one-tenth of phosphorus to be grouped into, have wear-resistant, intensity is high, antioxidation, the feature of length in service life.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail, so that advantages and features of the invention can be easier to be readily appreciated by one skilled in the art, thus protection scope of the present invention is made apparent clear and definite defining.
Of the present invention is a kind of casting surface peening nickel-base alloy, described casting surface peening nickel-base alloy is grouped into by nickel, chromium, ferrum, copper, molybdenum, stannum, platinum and eight kinds of one-tenth of phosphorus, in described casting surface peening nickel-base alloy, parts by weight shared by each composition are respectively as follows: described nickel and account for 35-40 part, described chromium accounts for 28-32 part, and described ferrum accounts for 19-23 part, and described copper accounts for 14-18 part, described molybdenum accounts for 13-16 part, described stannum accounts for 10-14 part, and described platinum accounts for 7-11 part, and described phosphorus accounts for 5-9 part.
Further, in described casting surface peening nickel-base alloy, shared by each composition, parts by weight are particularly as follows: described nickel accounts for 36 parts, and described chromium accounts for 29 parts, described ferrum accounts for 20 parts, and described copper accounts for 15 parts, and described molybdenum accounts for 14 parts, described stannum accounts for 11 parts, and described platinum accounts for 8 parts, and described phosphorus accounts for 6 parts.
Further, in described casting surface peening nickel-base alloy, shared by each composition, parts by weight are particularly as follows: described nickel accounts for 39 parts, and described chromium accounts for 31 parts, described ferrum accounts for 22 parts, and described copper accounts for 17 parts, and described molybdenum accounts for 15 parts, described stannum accounts for 13 parts, and described platinum accounts for 10 parts, and described phosphorus accounts for 8 parts.
Proportioning is carried out so that the functional alloy property height obtained differs by each composition Different Weight percentage ratio.
Of the present invention is a kind of casting surface peening nickel-base alloy, and the present invention uses nickel, chromium, ferrum, copper, molybdenum, stannum, platinum and eight kinds of one-tenth of phosphorus to be grouped into, have wear-resistant, intensity is high, antioxidation, the feature of length in service life.
The foregoing is only the detailed description of the invention of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the technical scope that disclosed herein; the change can expected without creative work or replacement, all should contain within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims are limited.
Claims (3)
1. surface peening nickel-base alloy is used in a casting, it is characterized in that: described casting surface peening nickel-base alloy is grouped into by nickel, chromium, ferrum, copper, molybdenum, stannum, platinum and eight kinds of one-tenth of phosphorus, in described casting surface peening nickel-base alloy, parts by weight shared by each composition are respectively as follows: described nickel and account for 35-40 part, described chromium accounts for 28-32 part, and described ferrum accounts for 19-23 part, and described copper accounts for 14-18 part, described molybdenum accounts for 13-16 part, described stannum accounts for 10-14 part, and described platinum accounts for 7-11 part, and described phosphorus accounts for 5-9 part.
Casting surface peening nickel-base alloy the most according to claim 1, it is characterized in that: in described casting surface peening nickel-base alloy, parts by weight shared by each composition are particularly as follows: described nickel accounts for 36 parts, described chromium accounts for 29 parts, described ferrum accounts for 20 parts, described copper accounts for 15 parts, and described molybdenum accounts for 14 parts, and described stannum accounts for 11 parts, described platinum accounts for 8 parts, and described phosphorus accounts for 6 parts.
Casting surface peening nickel-base alloy the most according to claim 1, it is characterized in that: in described casting surface peening nickel-base alloy, parts by weight shared by each composition are particularly as follows: described nickel accounts for 39 parts, described chromium accounts for 31 parts, described ferrum accounts for 22 parts, described copper accounts for 17 parts, and described molybdenum accounts for 15 parts, and described stannum accounts for 13 parts, described platinum accounts for 10 parts, and described phosphorus accounts for 8 parts.