CN105819825B - A kind of large size ceramic decoration slab and Recipe - Google Patents

A kind of large size ceramic decoration slab and Recipe Download PDF

Info

Publication number
CN105819825B
CN105819825B CN201610132371.4A CN201610132371A CN105819825B CN 105819825 B CN105819825 B CN 105819825B CN 201610132371 A CN201610132371 A CN 201610132371A CN 105819825 B CN105819825 B CN 105819825B
Authority
CN
China
Prior art keywords
layer
glaze paint
formula
green
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610132371.4A
Other languages
Chinese (zh)
Other versions
CN105819825A (en
Inventor
程石明
任富国
李利方
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MANLEY (CHINA) Co Ltd
Original Assignee
MANLEY (CHINA) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MANLEY (CHINA) Co Ltd filed Critical MANLEY (CHINA) Co Ltd
Priority to CN201610132371.4A priority Critical patent/CN105819825B/en
Publication of CN105819825A publication Critical patent/CN105819825A/en
Application granted granted Critical
Publication of CN105819825B publication Critical patent/CN105819825B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A kind of large size ceramic decoration slab and Recipe, large size ceramic decoration slab is made up of green body layer and glazed layer, green body layer is divided into front and bonding plane, front is plane and bonding plane is reeded male and fomale(M&F), the specification of green body layer is at least 900mm × 1800mm, thickness is 20mm, glazed layer is divided into glaze paint bottom, patterned layer and glaze paint surface layer, glaze paint bottom uniform fold is in the front of green body layer, patterned layer is printed on glaze paint bottom, glaze paint surface layer is covered in patterned layer and glaze paint bottom, and the thickness of glazed layer is at least 0.3 mm.Formula includes base substrate layer formula, glaze paint bottom formula and glaze paint surface layer formula.The firing temperature of technological process important step is upper 1202 DEG C of temperature, lower 1200 DEG C of temperature, firing period 124min.

Description

A kind of large size ceramic decoration slab and Recipe
Technical field
The present invention relates to a kind of ceramic wafer and technical recipe, more particularly to a kind of large size ceramic decoration slab and formula work Skill, belong to technical field of ceramic industry.
Background technology
Architectural pottery has been one of widely known Important building finishing material, is pattern in architectural pottery family Kind is numerous, is not at all to describe with tinkling of jades meet the eye on every side.Development of the architectural pottery Jing Guo long history, permitted although having introduced More up to date technics, its quality, specification and pattern have suitable progress, but technological layer is constantly subjected in terms of specification Restriction without too big progress.Because the constraint of specification causes the wall joints after decoration too many, it can not give and to the greatest extent may be used The associative perception of energy.
The content of the invention
In order to solve the small technological deficiency for influenceing overall sense organ of above-mentioned architectural pottery specification, the present invention provides a kind of big specification Ceramic decoration slab and Recipe.
The technical solution adopted in the present invention is:A kind of large size ceramic decoration slab and Recipe, by green body layer and Glazed layer is formed, and green body layer is divided into front and bonding plane, and front is plane and bonding plane is reeded male and fomale(M&F), green body layer Specification is at least 900mm × 1800mm, thickness 20mm, and glazed layer is divided into glaze paint bottom, patterned layer and glaze paint surface layer, glaze paint bottom Layer uniform fold is in the front of green body layer, and patterned layer is printed on glaze paint bottom, and glaze paint surface layer is covered in patterned layer and glaze paint bottom, The thickness of glazed layer is at least 0.3 mm;Formula includes base substrate layer formula, glaze paint bottom formula and glaze paint surface layer formula, technique stream Dry-pressing formed pressure is 260MPa in journey, and dry temperature is 120 DEG C~338 DEG C, arid cycle 106min, firing temperature For upper 1202 DEG C of temperature, lower 1200 DEG C of temperature, firing period 124min.
The formula of green body layer includes Longhai City's feldspar 13.84%, big level ground chicken girt 13.84%, Yongan albite by weight percentage 13.35%, Zhangping land waste 13.35%, Zhangpu dirt 11.87%, Zhangping feldspar in lump 7.9%, east of a river washing soil 7.4%, great Nan carclazytes 6.92%, Changtai kaolin 3.46%, diopside 3.46%, Yichuan black talc 2.5%, bentonite 0.98%, sodium humate 0.41%, silicon Sour sodium 0.41%, the methylcellulose 0.01% of attapulgite 0.3%.
The formula of glaze paint bottom includes quartz 42.74%, Longyan albite 13.8%, planetesimal kaolin by weight percentage 9.8%, calcite 7.3%, zirconium silicate 7%, frit 5.4%, calcined kaolin 5%, lucky polo soil 3.4%, talcum powder 2.6%, oxidation Zinc 2.5%, sodium tripolyphosphate 0.4%, methylcellulose 0.06%.
The formula of glaze paint surface layer includes silica 33%, white frit 17.65%, calcined kaolin 15.7%, dragon by weight percentage Rock albite 14.2%, burn talcum 6.25%, vanadium titanium black 6.07%, lucky polo soil 4.85%, aluminum oxide 1.76%, sodium tripolyphosphate 0.46%, methylcellulose 0.06%.
The beneficial effects of the invention are as follows:It is that seam is few after decorating first, gives whole structure sense organ as far as possible, secondly It is that speed of application is fast, pastes one piece big specification decorative panel equivalent to some blocks of small dimension walltiles are pasted, greatly improve construction Efficiency.
Brief description of the drawings
The present invention is further described below in conjunction with the accompanying drawings:
Fig. 1 is the cross-sectional structure schematic diagram of the present invention.
1, green body layer in figure, 2, glaze paint bottom, 3, patterned layer, 4, glaze paint surface layer.
Embodiment
In the embodiment in figure 1, a kind of large size ceramic decoration slab and Recipe, by green body layer 1 and glazed layer structure Into, it is characterized in that:Green body layer 1 divide for front and bonding plane, front is plane and bonding plane is reeded male and fomale(M&F), green body layer 1 specification is at least 900mm × 1800mm, thickness 20mm, and glazed layer is divided into glaze paint bottom 2, patterned layer 3 and glaze paint surface layer 3, For the uniform fold of glaze paint bottom 2 in the front of green body layer 1, patterned layer 3 is printed on glaze paint bottom 2, and glaze paint surface layer 4 is covered in patterned layer 3 and glaze paint bottom 2, the thickness of glazed layer be at least 0.3 mm;Formula includes that green body layer 1 is formulated, glaze paint bottom 2 is formulated and glaze paint Surface layer 3 is formulated, and dry-pressing formed pressure is 260MPa in technological process, and dry temperature is 120 DEG C~338 DEG C, arid cycle For 106min, firing temperature is upper 1202 DEG C of temperature, lower 1200 DEG C of temperature, firing period 124min.
The formula of green body layer 1 includes Longhai City's feldspar 13.84%, big level ground chicken girt 13.84%, Yongan albite by weight percentage 13.35%, Zhangping land waste 13.35%, Zhangpu dirt 11.87%, Zhangping feldspar in lump 7.9%, east of a river washing soil 7.4%, great Nan carclazytes 6.92%, Changtai kaolin 3.46%, diopside 3.46%, Yichuan black talc 2.5%, bentonite 0.98%, sodium humate 0.41%, silicon Sour sodium 0.41%, the methylcellulose 0.01% of attapulgite 0.3%.
The formula of glaze paint bottom 2 quartz 42.74% by weight percentage, Longyan albite 13.8%, planetesimal kaolin 9.8%, calcite 7.3%, zirconium silicate 7%, frit 5.4%, calcined kaolin 5%, lucky polo soil 3.4%, talcum powder 2.6%, oxidation Zinc 2.5%, sodium tripolyphosphate 0.4%, methylcellulose 0.06%.
The formula of glaze paint surface layer 4 includes silica 33% by weight percentage, white frit 17.65%, calcined kaolin 15.7%, Longyan albite 14.2%, burn talcum 6.25%, vanadium titanium black 6.07%, lucky polo soil 4.85%, aluminum oxide 1.76%, tripolyphosphate Sodium 0.46%, methylcellulose 0.06%.
Embodiment:It is in proportion that raw material preparation is good first, then add water to put into the mud that ball mill wears into high fineness raw material Starch, being sent into powder drying tower after iron removaling of sieving after mud milled is spray-dried, and dried powder is passed through large-scale Hydraulic press is dry-pressing formed on mould, and the large size ceramic slab body after shaping is sent into drying kiln drying;It is certain dry to reaching Progress patterned layer 3 is ink-jet printed after the ceramic body of dry degree carries out application glaze paint bottom 2, then applies glaze paint surface layer 4.Finally will The large size ceramic slab body feeding roller kiln burning for completing technique early stage is made including green body layer 1, glaze paint bottom 2, the and of patterned layer 3 Large size ceramic decoration slab including glaze paint surface layer 4, then can be used as finished product storage after edging sorting packing.

Claims (1)

1. a kind of large size ceramic decorates slab, it is characterized in that:Large size ceramic decoration slab is made up of green body layer and glazed layer, Green body layer is divided into front and bonding plane, and front is plane and bonding plane is reeded male and fomale(M&F), and the specification of green body layer is at least 900mm × 1800mm, thickness 20mm, glazed layer are divided into glaze paint bottom, patterned layer and glaze paint surface layer, glaze paint bottom uniform fold In the front of green body layer, patterned layer is printed on glaze paint bottom, and glaze paint surface layer is covered in patterned layer and glaze paint bottom, the thickness of glazed layer Degree is at least 0.3 mm;Formula include base substrate layer formula, glaze paint bottom formula and glaze paint surface layer formula, in technological process dry-pressing into The pressure of type is 260MPa, and dry temperature is 120 DEG C~338 DEG C, arid cycle 106min, firing temperature is upper temperature 1202 DEG C, lower 1200 DEG C of temperature, firing period 124min;The formula of green body layer includes Longhai City's feldspar 13.84% by weight percentage, greatly Level ground chicken girt 13.84%, Yongan albite 13.35%, Zhangping land waste 13.35%, Zhangpu dirt 11.87%, Zhangping feldspar in lump 7.9%, East of a river washing 7.4%, great Nan of soil carclazytes 6.92%, Changtai kaolin 3.46%, diopside 3.46%, Yichuan black talc 2.5%, swelling Soil 0.98%, sodium humate 0.41%, sodium metasilicate 0.41%, attapulgite 0.3%, methylcellulose 0.01%;Glaze paint bottom is matched somebody with somebody Side includes quartz 42.74%, Longyan albite 13.8%, planetesimal kaolin 9.8%, calcite 7.3%, silicic acid by weight percentage Zirconium 7%, frit 5.4%, calcined kaolin 5%, lucky polo soil 3.4%, talcum powder 2.6%, zinc oxide 2.5%, sodium tripolyphosphate 0.4%, methylcellulose 0.06%;The formula of glaze paint surface layer includes silica 33%, white frit 17.65%, calcination by weight percentage Kaolin 15.7%, Longyan albite 14.2%, burn talcum 6.25%, vanadium titanium black 6.07%, lucky polo soil 4.85%, aluminum oxide 1.76%, sodium tripolyphosphate 0.46%, methylcellulose 0.06%.
CN201610132371.4A 2016-03-10 2016-03-10 A kind of large size ceramic decoration slab and Recipe Active CN105819825B (en)