CN105801064A - 一种轻质隔热保温砖的制备工艺 - Google Patents

一种轻质隔热保温砖的制备工艺 Download PDF

Info

Publication number
CN105801064A
CN105801064A CN201410847725.4A CN201410847725A CN105801064A CN 105801064 A CN105801064 A CN 105801064A CN 201410847725 A CN201410847725 A CN 201410847725A CN 105801064 A CN105801064 A CN 105801064A
Authority
CN
China
Prior art keywords
heat
weight
less
light
lytag
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410847725.4A
Other languages
English (en)
Inventor
陈建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongyi New Material Research Institute (Chongqing) Co., Ltd.
Original Assignee
陈建
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 陈建 filed Critical 陈建
Priority to CN201410847725.4A priority Critical patent/CN105801064A/zh
Publication of CN105801064A publication Critical patent/CN105801064A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种轻质隔热保温砖的制备工艺，其工艺步骤包括配料、混合搅拌等，原料包括复合轻质骨料、石灰石等，通过本发明制备的保温砖具有轻质、导热系数低、强度高、隔热保温效果好的特点，工艺简单成本低廉，涉及耐火材料领域，其适合用于高温窑炉内衬，为工业窑炉设备提供高效节能的保证。

Description

一种轻质隔热保温砖的制备工艺
技术领域
本发明涉及耐火材料领域，尤其涉及一种轻质隔热保温砖的制备工艺。
背景技术
工业窑炉是工业生产中的主要耗能设备，耗能巨大，尤其在陶瓷、玻璃、化工及机电等企业中有着广泛的应用。然而通常其的热损失一般都较高，因此需要性能优良的隔热保温材料来降低能耗。目前窑炉内衬隔热材料使用较为常见的是硅酸铝类耐火纤维，但其导热系数较小、价格贵、强度低、寿命短。为此市场相继开发出了一些轻质耐火砖作为工业窑炉内衬，较为常见的有钙长石系列轻质耐火砖、莫来石轻质耐火砖等。但上述材料也存在使用温度低、寿命短或节能效果差的问题。因此，开发具有低导热系数、高强度的轻质耐火砖及工艺具有重要意义。
发明内容
本发明旨在提供一种轻质隔热保温砖的制备工艺，与现有技术相比该工艺简单成本低，制备出的产品具有强度高、导热系数低、使用寿命长等特点，能有效延长工业窑炉的使用寿命。
本发明还提供了一种所述保温砖的制备方法，其包括如下工艺步骤，a、首先是将原料按配比称量，搅拌混合均匀形成混合料；b、然后将混合料磨细至小于0.08mm；c、将磨细后的物料与10－28％（占磨细物料重量）的水搅拌得到泥料；d、采用振动浇注成形或浇注成形；e、成形后的坯体在在干燥窑中于100～150℃烘干6－8小时；f、将经干燥的砖坯在窑中烧成，烧成温度为1450～1500℃，待冷却后将砖坯按所需尺寸切割，即得本发明的轻质隔热保温砖。
所述原料包括如下组分（按重量份计）：膨胀珍珠岩20-30份，粉煤灰陶粒20-30份，蛭石5-10份，石灰石2-10份，石膏20-30份，高铝矾土5-10份，硅微粉2-6份，氮化硅5-10份，二氧化锆4-6份，纳米碳化硅4-6份，磷酸铝水泥2-5份，复合稀土氧化物3-6份，铝酸钙水泥2-5份，水玻璃2-3份，三聚磷酸钠2-3份，硅酸铝耐火纤维1-2份，耐热钢纤维0.5-1份、水8－12份。所述复合稀土氧化物为质量比为1-2:1的氧化钇和氧化铈，所述膨胀珍珠岩、粉煤灰陶粒、蛭石的粒度为小于1.5mm，高铝矾土、石灰石粒度为小于0.2mm，硅微粉、氮化硅、二氧化锆的粒度小于5微米，纳米碳化硅粒径为20-60nm，所述硅酸铝耐火纤维长度为2-8mm，所述膨胀珍珠岩、粉煤灰陶粒、蛭石经硅溶胶浸泡处理，所述硅溶胶的浓度（按质量百分比计）为20－30%。
具体实施方式
下面结合实施例对本发明作示例性说明：
实施例1
其包括如下工艺步骤，a、首先是将所述原料按配比称量，搅拌混合均匀形成混合料；b、然后将混合料磨细至小于0.08mm；c、将磨细后的物料与10－28％（占磨细物料重量）的水搅拌得到泥料；d、采用振动浇注成形或浇注成形；e、成形后的坯体在在干燥窑中于100～150℃烘干6－8小时；f、将经干燥的砖坯在窑中烧成，烧成温度为1450～1500℃，待冷却后将砖坯按所需尺寸切割，即得本发明的轻质隔热保温砖。
所述原料包括如下组分（按重量份计）：膨胀珍珠岩30份，粉煤灰陶粒20份，蛭石8份，石灰石5份，石膏25份，高铝矾土6份，硅微粉4份，氮化硅8份，二氧化锆6份，纳米碳化硅4份，磷酸铝水泥2份，复合稀土氧化物3份，铝酸钙水泥4份，水玻璃2份，三聚磷酸钠2份，硅酸铝耐火纤维1份，耐热钢纤维0.5份、水10份。所述复合稀土氧化物为质量比为1:1的氧化钇和氧化铈，所述膨胀珍珠岩、粉煤灰陶粒、蛭石的粒度为小于1.5mm，高铝矾土、石灰石粒度为小于0.2mm，硅微粉、氮化硅、二氧化锆的粒度小于5微米，纳米碳化硅粒径为20-60nm，所述硅酸铝耐火纤维长度为2-8mm，所述膨胀珍珠岩、粉煤灰陶粒、蛭石经硅溶胶浸泡处理，所述硅溶胶的浓度（按质量百分比计）为25%。
本发明不局限于上述方式，任何在本发明的启示下作出的变化，或与本发明具有相同或相近的技术方案，均落入本发明的保护范围之内。

Claims (1)

1.一种轻质隔热保温砖的制备工艺，其包括如下工艺步骤，a、首先是将原料按配比称量，搅拌混合均匀形成混合料；b、然后将混合料磨细至小于0.08mm；c、将磨细后的物料与10－28％（占磨细物料重量）的水搅拌得到泥料；d、采用振动浇注成形或浇注成形；e、成形后的坯体在在干燥窑中于100～150℃烘干6－8小时；f、将经干燥的砖坯在窑中烧成，烧成温度为1450～1500℃，待冷却后将砖坯按所需尺寸切割，即得本发明的轻质隔热保温砖；所述原料包括如下组分（按重量份计）：膨胀珍珠岩20-30份，粉煤灰陶粒20-30份，蛭石5-10份，石灰石2-10份，石膏20-30份，高铝矾土5-10份，硅微粉2-6份，氮化硅5-10份，二氧化锆4-6份，纳米碳化硅4-6份，磷酸铝水泥2-5份，复合稀土氧化物3-6份，铝酸钙水泥2-5份，水玻璃2-3份，三聚磷酸钠2-3份，硅酸铝耐火纤维1-2份，耐热钢纤维0.5-1份、水8－12份；所述复合稀土氧化物为质量比为1-2:1的氧化钇和氧化铈，所述膨胀珍珠岩、粉煤灰陶粒、蛭石的粒度为小于1.5mm，高铝矾土、石灰石粒度为小于0.2mm，硅微粉、氮化硅、二氧化锆的粒度小于5微米，纳米碳化硅粒径为20-60nm，所述硅酸铝耐火纤维长度为2-8mm，所述膨胀珍珠岩、粉煤灰陶粒、蛭石经硅溶胶浸泡处理，所述硅溶胶的浓度（按质量百分比计）为20－30%。
CN201410847725.4A 2014-12-29 2014-12-29 一种轻质隔热保温砖的制备工艺 Pending CN105801064A (zh)