CN105801041A - 一种防火内墙干粉砂浆 - Google Patents
一种防火内墙干粉砂浆 Download PDFInfo
- Publication number
- CN105801041A CN105801041A CN201410837694.4A CN201410837694A CN105801041A CN 105801041 A CN105801041 A CN 105801041A CN 201410837694 A CN201410837694 A CN 201410837694A CN 105801041 A CN105801041 A CN 105801041A
- Authority
- CN
- China
- Prior art keywords
- powder
- interior wall
- fire prevention
- mixed mortar
- dry powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种防火内墙干粉砂浆，由如下重量百分比的组分组成：硅酸盐水泥、石英砂、填料、膨润土、可再分散乳胶粉、纤维素醚、柠檬酸、纳米级二氧化钛。本发明的产品与基面有很好的粘附力，材料经济实用，可节约成本，同时经该材料处理后的基层不会空鼓起壳，可保证施工现场清洁，更符合环保要求；采用煤矸石代替部分黄砂，不但可以减少污染、降低成本，还能起到防火作用。
Description
技术领域
本发明属于建筑材料领域，具体涉及一种防火内墙干粉砂浆及其制备方法。
背景技术
随着建筑业的快速发展，对建筑业质量的要求越来越高。由于受到施工人员的技术熟练程度及水泥、砂子等个各种原材料的影响，施工现场配置的砂浆，无论是砌筑砂浆、抹面砂浆还是地面找平砂浆，常常出现建筑物抹灰砂浆开裂现象（即便是最传统的黏土墙砖使用水泥砂浆抹灰也会出现大面积开裂），从而造成工程质量不稳定、强度打不到要求、甚至质量低劣的情况时有发生，已成为建筑质量通病。此外，随着生活水平的提高，人们对自身生活环境的要求也日益剧增，房屋的修建过程中，采取了保温、隔热和静音的措施，在主体工程的表面增加了一层隔热层。最开始的材料为聚苯板隔热层，后有保温砂浆层，其原理都是若干微小的真空气泡形成一层薄膜而达到保温、隔热和静音的效果。但是其中聚苯板的耐高温效果极差，防火效果也不理想，曾经造成过上海、沈阳等地的火灾，国家强制禁止了聚苯板的使用。而无机玻化微珠保温砂浆由于以不燃烧的无机材料组成，相对来说比较安全，但是其造价高，会导致工程总体成本上升。寻找一种脆性低、抗拉强度大、保温节能并且成本低的砂浆一直是建材行业内的研究热点。
发明内容
本发明的目的在于针对现有技术存在的问题，提供一种抗拉强度大、成本低并且节能的内墙干粉砂浆。
本发明提供了一种防火内墙干粉砂浆，由如下重量百分比的组分组成：
硅酸盐水泥35%-60%
石英砂10-15%
填料30%-45%
膨润土3%-5%
可再分散乳胶粉0.1%-0.3%
纤维素醚0.3%-0.5%
柠檬酸0.2-0.5%
纳米级二氧化钛1-3%
优选的，所述硅酸盐水泥为32.5R或者42.5R水泥；
优选的，所述膨润土为有机膨润土；
优选的，所述可再分散乳胶粉为聚醋酸乙烯酯与聚乙烯醇经过共聚反应生成的胶粉；
优选的，所述纤维素醚为甲基羟乙基纤维素醚或者甲基羟丙基纤维素醚。
一、胶凝材料：
本发明所述原材料中，硅酸盐水泥起粘结作用,优选的为32.5R或者42.5R硅酸盐水泥；
二、骨料
石英砂是石英石经破碎加工而成的石英颗粒，石英石是一种非金属矿物质，是一种坚硬、耐磨、化学性能稳定的硅酸盐矿物，其主要矿物成分是二氧化硅，本发明所选取的石英砂中二氧化硅含量不低于98%，强度高、耐磨性能好；
三、填料
本发明所述的填料为黄砂与煤矸石的混合物；煤矸石是采煤过程和洗煤过程中排放的固体废物，是一种在成煤过程中与煤层伴生的一种含碳量较低、比煤坚硬的黑灰色岩石。包括巷道掘进过程中的掘进矸石、采掘过程中从顶板、底板及夹层里采出的矸石以及洗煤过程中挑出的洗矸石。其主要成分是Al2O3、SiO2，另外还含有数量不等的Fe2O3、CaO、MgO、Na2O、K2O、P2O5、SO3和微量稀有元素（镓、钒、钛、钴）。
传统的干粉砂浆采用黄砂做填料，黄砂一般按其产源不同，可分为河砂，海砂和山砂。这三类砂均从自然界取得，采矿过程中成本高还影响自然环境，而煤矸石是采煤过程和洗煤过程中排放的固体废物，是国家大力发展循环经济，按照减量化、再利用、再循环的原则，重点治理的废弃物。
本发明采用煤矸石代替部分黄砂，不但可以减少污染、降低成本，还由于煤矸石特殊的结构，与石英砂、海泡石粉等添加在一起还可以起到较好的防火效果。
本发明加入二氧化钛作为填料，一方面是把二氧化钛作为白色颜料，对煤矸石的黑色进行遮蔽；另一方面大量加入二氧化钛可以加强与纳米级二氧化钛的相互作用力，增强纳米级二氧化钛净化空气的效果。
四、保水剂
纤维素醚在粉刷涂料领域是一种常用的保水剂，它可以使砂浆中的水分不易失去，并在较长的一段时间内逐步释放，赋予砂浆良好的保水性和工作性，
膨润土是以蒙脱石为主的含水粘土层，它具有优良的离子交换性、膨胀性、粘附性、可塑性、耐火性，膨润土有较强的吸水性，可以提高材料的强度；它还有独特的选择性吸附性，可以对砌块材料中的放射性物质永久性吸附固化，具有净化和修复环境的功能。
五、增稠剂
粉体建材成型后常受热胀冷缩及气候、温度、湿度等影响，干燥、开裂、脱落等现象时有发生，尤其是材料遇水和受力后，这种现象更趋严重。为此本发明加入适量的增稠剂的方法来达到产品防裂和增加弹性的作用。可再分散乳胶粉具有突出的粘结强度，可提高粘合剂的弹性，并赋予粘合剂优良的耐碱性；
六、缓凝剂
水泥缓凝剂能推迟水泥水化反应，从而延长粉刷材料的凝结时间，使其能较长时间保持可塑性，方便浇筑，提高施工效率。柠檬酸同时还可以有效抑制材料泛碱等现象产生；
七、纳米级二氧化钛
纳米级二氧化钛可以起到净化空气的作用，国内外对此已经有大量报道，本发明中将纳米级二氧化钛与表面积大、吸附能力强的海泡石粉相结合，可以有效提升纳米级二氧化钛净化空气的作用。
本发明的有益有效在于：与基面有很好的粘附力，材料经济实用，可节约成本，同时经该材料处理后的基层不会空鼓起壳，可保证施工现场清洁，更符合环保要求；采用煤矸石代替部分黄砂，不但可以减少污染、降低成本，还能起到防火作用。
具体实施方式
实施例1
一种防火内墙干粉砂浆，由如下重量百分比的组分组成：
硅酸盐水泥44%
石英砂12%
黄砂10%
煤矸石粉15%
二氧化钛细粉13%
膨润土3%
可再分散乳胶粉0.2%
纤维素醚0.4%
柠檬酸0.4%
纳米级二氧化钛2%
所述硅酸盐水泥为42.5R水泥；
所述的石英砂粒径为200目；
所述的黄砂为河砂，含泥量为1%，密度为2500kg/m3；
所述的煤矸石粉的粒径为600目；
所述的二氧化钛细粉的粒径为600目；
所述膨润土为有机膨润土；
所述可再分散乳胶粉为聚醋酸乙烯酯与聚乙烯醇经过共聚反应生成的胶粉；
所述纤维素醚为甲基羟乙基纤维素醚；
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (5)
1.一种防火内墙干粉砂浆，其特征在于，由如下重量百分比的组分组成：
硅酸盐水泥35%-60%
石英砂10-15%
填料30%-45%
膨润土3%-5%
可再分散乳胶粉0.1%-0.3%
纤维素醚0.3%-0.5%
柠檬酸0.2-0.5%
纳米级二氧化钛1-3%。
2.如权利要求1所述的防火内墙干粉砂浆，其特征在于，所述硅酸盐水泥为32.5R或者42.5R水泥。
3.如权利要求1所述的防火内墙干粉砂浆，其特征在于，所述膨润土为有机膨润土。
4.如权利要求1所述的防火内墙干粉砂浆，其特征在于，所述可再分散乳胶粉为聚醋酸乙烯酯与聚乙烯醇经过共聚反应生成的胶粉。
5.如权利要求1所述的防火内墙干粉砂浆，其特征在于，所述纤维素醚为甲基羟乙基纤维素醚或者甲基羟丙基纤维素醚。