CN105781048A - Fireproof heat-preservation waterproof anti-crack reflective heat insulation material system and construction process thereof - Google Patents

Fireproof heat-preservation waterproof anti-crack reflective heat insulation material system and construction process thereof Download PDF

Info

Publication number
CN105781048A
CN105781048A CN201610060408.7A CN201610060408A CN105781048A CN 105781048 A CN105781048 A CN 105781048A CN 201610060408 A CN201610060408 A CN 201610060408A CN 105781048 A CN105781048 A CN 105781048A
Authority
CN
China
Prior art keywords
layer
warming plate
construction
insulation
heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610060408.7A
Other languages
Chinese (zh)
Other versions
CN105781048B (en
Inventor
刘学影
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Andeli energy saving building materials Co.,Ltd.
Original Assignee
Tianchang Andeli Energy Conservation Building Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianchang Andeli Energy Conservation Building Materials Co Ltd filed Critical Tianchang Andeli Energy Conservation Building Materials Co Ltd
Priority to CN201610060408.7A priority Critical patent/CN105781048B/en
Publication of CN105781048A publication Critical patent/CN105781048A/en
Application granted granted Critical
Publication of CN105781048B publication Critical patent/CN105781048B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a fireproof heat-preservation waterproof anti-crack reflective heat insulation material system. The system comprises a construction wall face. A heat-preservation glue layer and heat-preservation boards are arranged outside the construction wall face in sequence. The heat-preservation boards are provided with dividing joints. The construction wall face, the heat-preservation glue layer and the heat-preservation boards are connected through rivets. A reflective heat insulation layer is arranged on the heat-preservation boards. In this way, after the construction wall face and the heat-preservation boards are bonded, the heat-preservation boards and the construction wall face are fixed through the rivets, and thus the fixation firmness of the heat-preservation boards and the construction wall face can be greatly improved. In addition, the heat-preservation boards are connected through heat-preservation board brackets, and the heat-preservation boards are in a smooth state on the premise that connection between the adjacent heat-preservation boards is improved, so that the whole wall face is more flat and attractive, the reflective heat insulation layer can effectively improve reflection and heat insulation of the construction wall face to external light, and the energy consumption of buildings is reduced.

Description

Fireproof heat insulating water-proofing anticracking reflective insulation material system and construction technology thereof
Technical field
The present invention relates to construction, particularly to fireproof heat insulating water-proofing anticracking reflective insulation material system and construction technology thereof.
Background technology
Warming plate say easy-to-understand be exactly insulation to building plank.Warming plate is to add other supplementary material and poly-containing thing with polystyrene resin for raw material, it is injected simultaneously into catalyst by heating mixing, then extrusion molding extrusion molding and the rigid foam plate that manufactures, there is protection against the tide, water resistance, minimizing building envelope thickness can be made, thus increasing indoor usable floor area.
Chinese patent " a kind of construction method of sticking heat-preservation plate on metope " such as 201110260245.4 discloses a kind of construction method of sticking heat-preservation plate on metope.Sticking heat-preservation plate on the outer surface of wall of building, is the effective measures of energy-saving and emission-reduction in building field, and this measure effect is obvious, advantages.
Although, this this construction method saves cost, and material is easy to get, simple to operate, intensity is higher, and compared with tradition method of attaching, efficiency of construction is doubled.
But, in this work progress, warming plate and metope are by together with being pasted and fixed on, thus once of long duration, for sticking the warming plate adhesive with body of wall by after microorganism or animal damage, warming plate is possible to fall down from metope, and then is also possible to people are damaged.
Summary of the invention
It is an object of the invention to provide a kind of fireproof heat insulating water-proofing anticracking reflective insulation material system and construction technology thereof.
The above-mentioned purpose of the present invention has the technical scheme that a kind of fireproof heat insulating water-proofing anticracking reflective insulation material system, including construction metope, insulation glue-line, warming plate it is sequentially provided with outside described construction metope, described warming plate is provided with dividing joint, described construction metope, insulation glue-line are connected by rivet with warming plate, and described warming plate is provided with reflective insulation layer.
So after construction metope and warming plate bond, with rivet, warming plate and construction metope are fixed again, so just warming plate and the fix tightly soundness of construction metope can greatly be improved, and add warming plate bracket and warming plate is coupled together, so improving on the connection basis of adjacent warming plate, warming plate can be made again to be in smooth state, thus whole metope is more smooth attractive in appearance, and reflective insulation layer can be effectively improved the reflection of construction metope light to external world and heat insulation, thus decreasing the energy expenditure of building, and reflective insulation layer can be aluminum paper tinsel, JGT235-2014 architectural reflective heat-insulation paint or TiO2/ BiOCl reflection type thermal insulation material etc..
As preferably, described insulation glue-line includes insulation glue, fire retardant and preservative.
As preferably, the parts by weight of described insulation glue are 31~36 parts, and the parts by weight of fire retardant are 11~15 parts, and the parts by weight of preservative are 1.5~2.3 parts.
As preferably, described insulation glue is organic siliconresin glue, and described fire retardant is brominated Polystyrene, and preservative is potassium sorbate.
Due to the cancellated polysiloxane that organic silicon resin glue is highly cross-linked, the surface area of the relatively general adhesive glue of its surface area wants big many, so it is not when affecting construction metope and warming plate connection area, fire retardant and preservative can be launched fully again, thus the fire-retardant and antiseptical ability of the contact portion constructed between metope and warming plate obtains effective lifting, such organic siliconresin glue makes the bonding between warming plate and construction metope more lasting.
The bromine content of brominated Polystyrene is about 68%.The advantages such as heat decomposition temperature, more than 330 DEG C, has molecular weight big, Heat stability is good, and dispersibility and compatibility are good in high polymer, it is easy to processing, non-blooming, so it can more further improve the flame retardant effect of expanded perlite thermal-nsulation plate as fire retardant.
And potassium sorbate is added in insulation glue, a part as insulation glue is used for bonding construction metope and warming plate, this is to make potassium sorbate can carry out completely cutting off with air, thus avoiding potassium sorbate and air contact and oxidized, itself just there is the stronger effect suppressing putrefaction bacteria and fungus growth simultaneously, such warming plate does not easily go mouldy or by bacterial corrosion in long-term use procedure between warming plate and construction metope, and brominated Polystyrene is weakly acidic, and under the state of acidity, the erosion resistance of potassium sorbate, antibacterial ability again than its in neutral or alkaline environment strong on 3-5 times, so which further increases the anti-mildew antiseptical ability of expanded perlite thermal-nsulation plate.The more important thing is what injury human body is substantially free of by potassium sorbate, be a kind of free of contamination preservative.
As preferably, being provided with TPV layer and abs layer outside reflective insulation layer from inside to outside.
Owing to TPV layer has good aging-resistant ability; plus its combination with crack-resistant layer; can effectively ensure that TPV layer will occur fracture to cause the fracture of TPV layer because of structure sheaf below within the permanent time; so outside air and ultraviolet are difficult to be entered into putty layer and the warming plate place of inside by TPV layer; thus also just can effectively warming plate and putty layer be played a protective role, extend their service life.And TPV layer becomes some rectangular blocks to arrange, so can reducing TPV layer when the effect being subject to different temperatures, its effect expanded with heat and contract with cold to himself causing tremendous influence, and will not make himself internal break.
And abs layer has good shock resistance; so dope layer and the warming plate of internal layer can be effectively protected; and its smooth surface; so being not easy dirty; there is good self-cleaning property; meanwhile, it also has aging resistance and corrosion resistant ability, so effectively extending the service life of internal dope layer.
As preferably, being provided with uvioresistant nylon fiber layer between TPV layer and abs layer.
First uvioresistant nylon fiber layer has anti-ultraviolet ability, it is owing to being fiber condition, so it can as junctional complex between TPV layer and abs layer, and TPV and the ABS of two layer contact positions has been carried out substantial portion of mixing by uvioresistant nylon fiber layer, so that both combine together in junction, strengthen both relatednesss, improve TPV layer and the abs layer stability on warming plate.
The construction technology of fireproof heat insulating water-proofing anticracking reflective insulation material system, comprises the following steps: S1, add fire retardant, preservative carry out Homogeneous phase mixing in insulation glue;S2, the insulation glue obtained by S1 spread upon on construction metope equably;S3, warming plate is fitted in insulation glue on, and with rivet by warming plate and construction metope be fixed, between adjacent warming plate formed dividing joint;S4, by S3 some be fitted in construction metope on warming plate warming plate brackets be fixedly connected with;S5, in S4, on warming plate, uniformly pull on flexible putty layer, natural drying 4 hours;S6, etc. after flexible putty layer natural drying, flexible putty layer is spread reflective insulation layer;S7, on reflective insulation layer TPV layer, uvioresistant nylon fiber layer and abs layer in roller coating.
So after construction metope and warming plate bond, with rivet, warming plate and construction metope are fixed again, so just warming plate and the fix tightly soundness of construction metope can greatly be improved, and add warming plate bracket and warming plate is coupled together, so improving on the connection basis of adjacent warming plate, warming plate can be made again to be in smooth state, thus whole metope is more smooth attractive in appearance.
As preferably, described dividing joint is also filled up with flexible putty.
Owing to flexible putty layer has the effect with waterproof, and it has the effect of cracking resistance, by it when brushing flat metope, fill up again the gap between adjacent warming plate, enter between warming plate and construction metope from gap such that it is able to be effectively prevented from water, thus can be effectively prevented from water and the insulation glue between construction metope and warming plate is caused erosion, improve the bonding firmness of construction metope and warming plate, and dividing joint can as the runner of water, the droplet on construction metope can be will be distributed over rapidly pool the dynamic water column of plume and flow to ground.
In sum, the method have the advantages that this construction technology is convenient, warming plate is fixing with construction metope more firm, and the warming plate metope after construction have well anticorrosive, waterproof, fire prevention, ageing-resistant and not easy fracture ability.
Accompanying drawing explanation
Fig. 1 is the structural representation of fireproof heat insulating water-proofing anticracking reflective insulation material system.
In figure, 1, construction metope;2, organic siliconresin glue;3, warming plate;4, rivet;5, flexible putty layer;6, dividing joint;7, reflective insulation layer;8, TPV layer;9, abs layer;10, uvioresistant nylon fiber layer;11, warming plate bracket.
Detailed description of the invention
Below in conjunction with accompanying drawing 1, the present invention is described in further detail.
Embodiment one:
S1, in the organic siliconresin glue 2 that parts by weight are 31 parts, add brominated Polystyrene that parts by weight are 11 parts, parts by weight are that the potassium sorbate of 1.5 parts carries out Homogeneous phase mixing;S2, the organic siliconresin glue 2 obtained by S1 spread upon on construction metope 1 equably;S3, warming plate 3 is fitted on construction metope 1, and with rivet 4, warming plate 3 and construction metope 1 is fixed;S4, by S3 some be fitted in construction wall on warming plate 3 warming plate brackets 11 be fixedly connected with;S5, being fitted with on the construction metope 1 of warming plate 3 in S4, uniformly pull on flexible putty layer 5, flexible putty is also filled in the gap between adjacent warming plate 3, and becomes the dividing joint 6 of warming plate 3, meanwhile, makes flexible putty natural drying 4 hours;S6, etc. after flexible putty layer 5 natural drying, flexible putty layer 5 is spread reflective insulation layer 7;S7, on reflective insulation layer 7 is brushed TPV layer 8, simultaneously before TPV is not dry, spread uvioresistant nylon fiber layer 10, then brush flat with abs layer 9 on uvioresistant nylon fiber layer 10 again.Tensile stress between warming plate 3 and construction body of wall is 19.7MPa, and hydrophobicity is 98.3%, and flame retardant rating is 5VA, and heat conductivity is only 0.043W/ (m K), and luminous reflectance reaches 93.3%.
Embodiment two:
S1, in the organic siliconresin glue 2 that parts by weight are 36 parts, add brominated Polystyrene that parts by weight are 15 parts, parts by weight are that the potassium sorbate of 2.3 parts carries out Homogeneous phase mixing;S2, the organic siliconresin glue 2 obtained by S1 spread upon on construction metope 1 equably;S3, warming plate 3 is fitted on construction metope 1, and hammers into the center of warming plate 3 with rivet 4 and make itself and construction metope 1 be fixed;S4, by S3 some be fitted in construction wall on warming plate 3 warming plate brackets 11 be fixedly connected with;S5, being fitted with in S4 on warming plate 3 metope, uniformly pull on flexible putty layer 5, flexible putty is also filled in the gap between adjacent warming plate 3, and becomes the dividing joint 6 of warming plate 3, meanwhile, makes flexible putty natural drying 4 hours;S6, etc. after flexible putty layer 5 natural drying, flexible putty layer 5 is spread reflective insulation layer 7;S7, on reflective insulation layer 7 is brushed TPV layer 8, simultaneously before TPV is not dry, spread uvioresistant nylon fiber layer 10, then brush flat with abs layer 9 on uvioresistant nylon fiber layer 10 again.Tensile stress between warming plate 3 and construction body of wall is 20.3MPa, and hydrophobicity is 98.7%, and flame retardant rating is 5VA, and heat conductivity is only 0.041W/ (m K), and luminous reflectance reaches 95.1%.
Embodiment three:
S1, in the organic siliconresin glue 2 that parts by weight are 33 parts, add brominated Polystyrene that parts by weight are 13 parts, parts by weight are that the potassium sorbate of 1.9 parts carries out Homogeneous phase mixing;S2, the organic siliconresin glue 2 obtained by S1 spread upon on construction metope 1 equably;S3, warming plate 3 is fitted on construction metope 1, and hammers into the center of warming plate 3 with rivet 4 and make itself and construction metope 1 be fixed;S4, by S3 some be fitted in construction wall on warming plate 3 warming plate brackets 11 be fixedly connected with;S5, being fitted with in S4 on warming plate 3 metope, uniformly pull on flexible putty layer 5, flexible putty is also filled in the gap between adjacent warming plate 3, and becomes the dividing joint 6 of warming plate 3, meanwhile, makes flexible putty natural drying 4 hours;S6, etc. after flexible putty layer 5 natural drying, flexible putty layer 5 is spread reflective insulation layer 7;S7, on reflective insulation layer 7 is brushed TPV layer 8, simultaneously before TPV is not dry, spread uvioresistant nylon fiber layer 10, then brush flat with abs layer 9 on uvioresistant nylon fiber layer 10 again.Tensile stress between warming plate 3 and construction body of wall is 20.1MPa, and hydrophobicity is 98.6%, and flame retardant rating is 5VA, and heat conductivity is only 0.041W/ (m K), and luminous reflectance reaches 94.4%.
Embodiment four:
S1, in the organic siliconresin glue 2 that parts by weight are 31 parts, add brominated Polystyrene that parts by weight are 15 parts, parts by weight are that the potassium sorbate of 2.3 parts carries out Homogeneous phase mixing;S2, the organic siliconresin glue 2 obtained by S1 spread upon on construction metope 1 equably;S3, warming plate 3 is fitted on construction metope 1, and hammers into the center of warming plate 3 with rivet 4 and make itself and construction metope 1 be fixed;S4, by S3 some be fitted in construction wall on warming plate 3 warming plate brackets 11 be fixedly connected with;S5, being fitted with in S4 on warming plate 3 metope, uniformly pull on flexible putty layer 5, flexible putty is also filled in the gap between adjacent warming plate 3, and becomes the dividing joint 6 of warming plate 3, meanwhile, makes flexible putty natural drying 4 hours;S6, etc. after flexible putty layer 5 natural drying, flexible putty layer 5 is spread reflective insulation layer 7;S7, on reflective insulation layer 7 is brushed TPV layer 8, simultaneously before TPV is not dry, spread uvioresistant nylon fiber layer 10, then brush flat with abs layer 9 on uvioresistant nylon fiber layer 10 again.Tensile stress between warming plate 3 and construction body of wall is 20.2MPa, and hydrophobicity is 98.6%, and flame retardant rating is 5VA, and heat conductivity is only 0.040W/ (m K), and luminous reflectance reaches 93.5%.
Embodiment five:
S1, in the organic siliconresin glue 2 that parts by weight are 36 parts, add brominated Polystyrene that parts by weight are 11 parts, parts by weight are that the potassium sorbate of 1.7 parts carries out Homogeneous phase mixing;S2, the organic siliconresin glue 2 obtained by S1 spread upon on construction metope 1 equably;S3, warming plate 3 is fitted on construction metope 1, and hammers into the center of warming plate 3 with rivet 4 and make itself and construction metope 1 be fixed;S4, by S3 some be fitted in construction wall on warming plate 3 warming plate brackets 11 be fixedly connected with;S5, being fitted with in S4 on warming plate 3 metope, uniformly pull on flexible putty layer 5, flexible putty is also filled in the gap between adjacent warming plate 3, and becomes the dividing joint 6 of warming plate 3, meanwhile, makes flexible putty natural drying 4 hours;S6, etc. after flexible putty layer 5 natural drying, flexible putty layer 5 is spread reflective insulation layer 7;S7, on reflective insulation layer 7 is brushed TPV layer 8, simultaneously before TPV is not dry, spread uvioresistant nylon fiber layer 10, then brush flat with abs layer 9 on uvioresistant nylon fiber layer 10 again.Tensile stress between warming plate 3 and construction body of wall is 20.4MPa, and hydrophobicity is 98.8%, and flame retardant rating is 5VA, and heat conductivity is only 0.041W/ (m K), and luminous reflectance reaches 94.1%.
This specific embodiment is only explanation of the invention; it is not limitation of the present invention; the present embodiment can be made the amendment not having creative contribution as required by those skilled in the art after reading this specification, but as long as being affected by the protection of Patent Law in scope of the presently claimed invention.

Claims (8)

1. a fireproof heat insulating water-proofing anticracking reflective insulation material system, it is characterized in that: include construction metope, insulation glue-line, warming plate it is sequentially provided with outside described construction metope, described warming plate is provided with dividing joint, described construction metope, insulation glue-line are connected by rivet with warming plate, and described warming plate is provided with reflective insulation layer.
2. fireproof heat insulating water-proofing anticracking reflective insulation material system according to claim 1, it is characterised in that: described insulation glue-line includes insulation glue, fire retardant and preservative.
3. fireproof heat insulating water-proofing anticracking reflective insulation material system according to claim 2, it is characterised in that: the parts by weight of described insulation glue are 31~36 parts, and the parts by weight of fire retardant are 11~15 parts, and the parts by weight of preservative are 1.5~2.3 parts.
4. fireproof heat insulating water-proofing anticracking reflective insulation material system according to claim 3, it is characterised in that: described insulation glue is organic siliconresin glue, and described fire retardant is brominated Polystyrene, and preservative is potassium sorbate.
5. fireproof heat insulating water-proofing anticracking reflective insulation material system according to claim 1, it is characterised in that: it is provided with TPV layer and abs layer outside reflective insulation layer from inside to outside.
6. fireproof heat insulating water-proofing anticracking reflective insulation material system according to claim 5, it is characterised in that: between TPV layer and abs layer, it is provided with uvioresistant nylon fiber layer.
7. the construction technology of the fireproof heat insulating water-proofing anticracking reflective insulation material system as described in claim 1~6 any one claim, comprises the following steps: S1, add fire retardant, preservative carry out Homogeneous phase mixing in insulation glue;S2, the insulation glue obtained by S1 spread upon on construction metope equably;S3, warming plate is fitted in insulation glue on, and with rivet by warming plate and construction metope be fixed, between adjacent warming plate formed dividing joint;S4, by S3 some be fitted in construction metope on warming plate warming plate brackets be fixedly connected with;S5, in S4, on warming plate, uniformly pull on flexible putty layer, natural drying 4 hours;S6, etc. after flexible putty layer natural drying, flexible putty layer is spread reflective insulation layer;S7, on reflective insulation layer TPV layer, uvioresistant nylon fiber layer and abs layer in roller coating.
8. fireproof heat insulating water-proofing anticracking reflective insulation material system according to claim 7, it is characterised in that: described dividing joint is also filled up with flexible putty.
CN201610060408.7A 2016-01-27 2016-01-27 Fireproof heat insulating water-proofing anticracking reflective insulation material system and its construction technology Active CN105781048B (en)