CN105780581B - A heating wrapper non-burning type tobacco manufacturing process - Google Patents

A heating wrapper non-burning type tobacco manufacturing process Download PDF

Info

Publication number
CN105780581B
CN105780581B CN 201610158977 CN201610158977A CN105780581B CN 105780581 B CN105780581 B CN 105780581B CN 201610158977 CN201610158977 CN 201610158977 CN 201610158977 A CN201610158977 A CN 201610158977A CN 105780581 B CN105780581 B CN 105780581B
Authority
CN
Grant status
Grant
Patent type
Application number
CN 201610158977
Other languages
Chinese (zh)
Other versions
CN105780581A (en )
Inventor
徐祥祥
Original Assignee
江苏金恒新型包装材料有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Abstract

本发明公开一种加热非燃烧型烟草的包装纸生产工艺,包括内包装纸的制备和外包装纸的制备,所述内包装纸的制备包括如下步骤:(1)制备燃烧层、(2)制备导热层、(3)施胶复合;所述外包装纸的制备包括如下步骤:(4)制备外包装层,在外包装纸的背面镀满铝箔作为隔热层;(5)将水性哑光镭射转移涂料涂布于PET薄膜上;(6)采用模压机进行模压,得到哑光镭射膜;(7)将哑光镭射膜贴附于外包装层的胶层上,得到外包装纸;(8)将外包装纸的隔热层贴附在内包装纸的燃烧层上,通过机械挤压的方法,将内、外包装纸复合为一体。 The present invention discloses a non-flammable heating tobacco paper production process, Preparation inner wrapper and the outer wrapper includes preparing the inner wrapper comprising the steps of: (1) Preparation of a combustion layer, (2) preparation of thermally conductive layer (3) sizing compound; prepared outer wrapper comprising the steps of: (4) preparation of outer layer, the back surface of the outer wrapper over an aluminum foil as a heat insulating layer coated; (5) the aqueous matte laser transfer coating material was applied onto a PET film; (6) was molded by compression molding machine to obtain matt radium; (7) attached on the radium matt outer layer, subbing layer, to obtain an outer wrapping; ( 8) the heat insulating layer of the outer wrapper is attached to the combustor inner wrapper layer, by mechanical extrusion of the inner and outer wrappers as a whole compound. 本发明的烟草包装由内包装纸和外包装纸组成,燃烧产生烟雾少、可对烟丝充分加热。 The present invention consists of tobacco packaging inner wrapper and an outer wrapper composition, combustion smoke less tobacco can be heated sufficiently.

Description

一种加热非燃烧型烟草的包装纸生产工艺 A heating wrapper non-burning type tobacco manufacturing process

技术领域 FIELD

[0001] 本发明属于烟草包装领域,具体是一种加热非燃烧型烟草的包装纸生产工艺。 [0001] The present invention belongs to the field of packaging of tobacco, in particular a non-flammable heating tobacco wrapping paper production process.

背景技术 Background technique

[0002] 近年来,随着国际控烟运动的脚步愈发加快,各国政府对吸烟尤其是在公共场所吸烟的限制愈加严格。 [0002] In recent years, with the pace accelerating international tobacco control movement increasingly, governments of smoking, especially in public smoking restrictions become more stringent. 在一背景下,以低温卷烟(加热非燃烧)、无烟气烟草制品、电子烟等为代表的新型烟草制品受到国内外广大烟草消费者的青睐,菲莫国际、英美烟草、日本烟草等跨国烟草公司也从战略高度积极研发推广新型烟草制品,我国也在积极开展新型烟草制品研发工作,目前新型烟草制品的设计研发成为国内外烟草行业一个新的研究热点课题。 In a context, a cigarette at a low temperature (heating non-burning), smoke-free tobacco products, electronic cigarettes and other tobacco products as the representative of the new home and abroad by the majority of consumers of tobacco, Philip Morris International, British American Tobacco, Japan Tobacco and other transnational tobacco companies also from a strategic perspective and actively promote research and development of new tobacco products, China is also active in research and development of new tobacco products, tobacco products present new design and development of domestic and international tobacco industry has become a new hot topic of research.

[0003] 作为新型烟草制品一种的加热非燃烧型卷烟,其主要特点是不燃烧烟草,仅有少量的二手烟气,从而得到国际各大烟草公司的关注。 [0003] As a new article of the non-combustion heat tobacco cigarette, its main feature is not burning tobacco, only a small amount of secondhand smoke, resulting in major international tobacco companies concerned. 目前加热非燃烧型卷烟产品主要有两部分构成:烟支和加热装置,其中烟支与普通卷烟基本无差异,其符合加热非燃烧型卷烟的特点,而加热则有多种实现方式,如:碳加热、反应热加热、红外加热、电阻丝加热等多种方式,但这些加热方式通常需要一定的装置才能实现,给消费者带来诸多不便。 Currently non-combustion heat of cigarette products mainly include two parts: a heating device and cigarettes, wherein a conventional cigarette and cigarettes substantially no difference, which is in line with the characteristics of non-combustion heat of cigarettes, and a variety of implementations are heated, such as: carbon heating, reaction heat heating, infrared heating, resistance wire heating and other methods, but these generally require heating to achieve a certain apparatus, inconvenience to consumers.

[0004] 为了解决上述问题,目前也有一种改进的加热非燃烧型的烟草,与普通卷烟外观没有差异,同样需要卷烟纸、卷烟滤嘴和卷烟烟丝等材料,在抽吸时,通过燃烧层(即传统的卷烟纸)燃烧产生的热量,隔着导热层(铝箱层)加热烟丝,从而实现低温非燃烧的新型烟草制品。 [0004] In order to solve the above problems, there is also an improved non-combustion heat tobacco, the appearance of a conventional cigarette and there is no difference, the same need to cigarette paper, cigarette filter and cigarette tobacco and other materials, while suction through the combustion layer (i.e., conventional cigarette paper) heat produced by combustion, through the thermally conductive layer (layer Aluminum) was heated tobacco, tobacco products in order to achieve the new low non-burning. 在一定程度上解决了原需要加热装置加热烟丝的种种缺陷,并且市场接受度也较高。 To some extent, solve the original need for heating means for heating the tobacco shortcomings, and market acceptance is higher. 但是于此同时,该新型的烟草制品也仍然存在一定的不足,由于烟丝本身需要借助于卷烟纸的燃烧产生的热量进行加热,传统的卷烟纸燃烧较快,产热量有限,导致烟丝不能被充分加热,而选择燃烧时间长的材料制备卷烟纸,又会导致卷烟纸燃烧产生的烟雾较多,不仅影响烟草本身的口感,大量的不完全燃烧产生的固体小颗粒被人吸入后,还会导致健康问题, 并且产生的烟雾较多也偏离了加热非燃烧型的烟草本身的生产要求。 At the same time, however, the novel tobacco products still exists some disadvantages, since the need for heating the tobacco itself by means of heat produced by combustion of the cigarette paper, the conventional cigarette paper and rapid combustion, heat production is limited, resulting in tobacco can not be sufficiently heating, a long time is selected burning cigarette paper prepared material, will result in more combustion smoke cigarette paper, not only affect the taste of the tobacco itself, a large amount of incomplete combustion of solid small particles after being inhaled, will cause health problems, and more fumes also deviated from the non-combustion heating type tobacco production requirements itself.

发明内容 SUMMARY

[0005] 发明目的:本发明目的在于针对现有技术的不足,提供一种燃烧烟雾少、烟丝加热充分的加热非燃烧型烟草的包装纸的生产工艺。 [0005] Object of the invention: The present invention aims deficiencies of the prior art, to provide a combustion smoke less tobacco is heated sufficiently non-flammable heating tobacco wrapping paper production process.

[0006] 技术方案:本发明所述加热非燃烧型烟草的包装纸生产工艺,包括内包装纸的制备和外包装纸的制备, [0006] The technical scheme: the present invention is non-flammable heating tobacco paper production process, Preparation inner wrapper and outer wrapper comprising,

[0007] 所述内包装纸的制备包括如下步骤: Preparation [0007] The inner wrapper comprises steps of:

[0008] (1)制备燃烧层:将植物纤维与水混合,再加入燃烧填料、助剂、醚化剂,搅拌均匀, 搅拌完成后过滤出浆料,浆料与玉米粉、马铃薯粉、谷皮粉和甲基纤维素混合完成纸浆制备,纸浆压榨脱水成形,烘干后在压纸机上压制; [0008] (1) Preparation of the combustion stratum of: plant fibers with water, then add combustion fillers, additives, etherifying agent, uniformly stirring, the slurry was filtered after the completion of stirring, the slurry with corn flour, potato flour, cereal Paper powder and mixing to complete preparation of cellulose pulp, pulp dewatering molded, dried and compressed in the pressing machine;

[0009] (2)制备导热层:使用与步骤(1)相同的制备方法制备原纸层,在原纸层的下表面镀满铝箱作为加热层,在原纸层的上表面镀网格状铝箱作为传热层,使用激光穿孔或针刺穿孔的方法在导热层上均匀穿孔; [0009] (2) Preparation of thermally conductive layer: used in step (1) the same preparation method of the base paper layer at the surface of the base paper layer coated over the heating layer as Aluminum, Aluminum coated on the grid-like surface of the base paper layer, as the heat transfer layer, using laser perforation methods or needle perforation perforated uniformly over the thermally conductive layer;

[0010] (3)施胶复合:在燃烧层的一侧涂抹胶层,将导热层的网格状铝箱面贴附于施胶面上,并再热压辊下进行热压复合,热压温度为160〜200°C,压力为0.45〜0.5MPa,辊速为18 〜25m/min,得到内包装纸; [0010] (3) sizing compound: the combustion stratum side glue applicator, the grid-like surface of the thermally conductive layer is Aluminum is attached to the surface sizing, and then hot-pressed composite under hot roll, hot pressure temperature 160~200 ° C, a pressure of 0.45~0.5MPa, roller speed of 18 ~25m / min, to give the inner wrapper;

[0011] 所述外包装纸的制备包括如下步骤: [0011] Preparation of the wrapper comprising the steps of:

[0012] (4)使用与步骤(1)相同的制备方法制备外包装层,在外包装纸的背面镀满铝箱作为隔热层; [0012] (4) used in step (1) prepared in the same preparation method of the outer layer, the back surface of the outer wrapper over Aluminum plating as a heat insulating layer;

[0013] (5)将水性哑光镭射转移涂料在涂布速度为20〜30m/min的条件下涂布于PET薄膜上,然后置于烘箱内,在160〜185 °C下烘干,烘干车速为30〜40m/min; The [0013] (5) The aqueous matte coating applied laser transfer speed 20~30m / min condition coated on a PET film, and then placed in an oven dried at 160~185 ° C, drying dry the vehicle speed is 30~40m / min;

[0014] ⑹采用模压机对涂布水性哑光镭射转移涂料的PET薄膜进行模压,得到哑光镭射膜; [0014] ⑹ PET film molding machine using the coated aqueous coating is matt laser transfer molding, to obtain matt radium;

[0015] ⑺在步骤⑷制备的外包装层的正面涂抹胶层,将哑光镭射膜贴附于外包装层的胶层上,并再热压辊下进行热压复合,热压温度为130〜180°C,压力为0.6〜0.7MPa,辊速为20〜25m/min,冷却后去除PET薄膜,得到外包装纸; [0015] ⑺ outer layer on the front step of preparing an applicator ⑷ subbing layer, the subbing layer on the matte radium is attached to the outer layer, and then hot-pressed composite under heat and pressure roller, pressing temperature of 130 ~180 ° C, a pressure of 0.6~0.7MPa, roller speed 20~25m / min, the PET film is removed after cooling to obtain outer wrapping;

[0016] 内、外包装纸复合: [0016] The inner and outer wrapping compound:

[0017] (8)将外包装纸的隔热层贴附在内包装纸的燃烧层上,通过机械挤压的方法,将内、外包装纸复合为一体。 [0017] (8) of the insulating layer of the outer wrapper is attached to the combustor inner wrapper layer, by mechanical extrusion of the inner and outer wrappers as a whole compound.

[0018] 本发明进一步优选地技术方案为,步骤⑴中所述燃烧层包含如下重量份的组分: 植物纤维30〜40份; 玉米粉4~6份; 马铃薯粉4~6份, 谷皮粉8〜10份; It is further preferred aspect [0018] of the present invention, in the combustion step ⑴ layer comprises by weight parts of the following components: 30 to 40 parts by plant fibers; parts corn flour 4-6; 4-6 parts of potato flour, bran 8~10 parts powder;

[0019] 甲基纤维素1〜3份; 醚化剂3〜5份; 燃烧填料30〜60份: 助剂5〜10份。 [0019] 1 ~ 3 parts of methyl cellulose; ~ 5 parts by etherification agent; combustion 30~60 parts filler: 5 to 10 parts adjuvant.

[0020] 优选地,所述植物纤维为废竹肩、废棉、玉米杆、稻草、麦杆、棉花杆、花生杆、薯渣、 豆腐渣其中一种或几种混合而成;所述燃烧填料为碳粉和碳酸钙的混合物;所述助剂为氯酸钾。 [0020] Preferably, the shoulder bamboo plant fiber waste, cotton waste, corn stover, rice straw, wheat straw, cotton stalk, peanut bar, potato residue, wherein one or more rubbish mixed; the combustion the filler is a mixture of carbon powder and calcium carbonate; the adjuvant is potassium chlorate.

[0021] 优选地,步骤(3)、(7)中所述胶层为水性聚氨酯胶层或丙烯酸酯改性水性聚氨酯胶层或魔芋粉-壳聚糖-聚乙烯醇共混胶层或丙烯酸胶层。 [0021] Preferably, step (3), (7) the aqueous polyurethane adhesive layer is a subbing layer or subbing layer acrylated aqueous polyurethane or konjac flour - Chitosan - PVA hybrid glue or acrylic acid adhesive layer.

[0022] 优选地,步骤⑸中所述水性哑光镭射转移涂料包括以下组分: 水溶性聚氨酯:5〜20份; 水溶性丙烯酸酯2~ IO形h 交联剂0.5〜2份; [0022] Preferably, the step of said aqueous matte ⑸ laser transfer coating comprising the following components: water-soluble polyurethane: 5~20 parts; 2 ~ IO 0.5~2 parts of a water-soluble crosslinking agent is h-shaped acrylate;

[0023] 润湿剂1~2份; 增稠剂0.2~]份; 吸光粉0 05〜丨份; 醋酸乙烯酯0.5〜2.5份; 丁酯0.05〜0,5份; [0023] 1 to 2 parts of a wetting agent; ~ 0.2] parts of a thickener; 0 05~ Shu light-absorbing powder parts; 0.5~2.5 parts of vinyl acetate; butyl 0.05~0,5 parts;

[0024] 水1〜10份:; [0024] Water 1~10 parts:;

[0025] 以重量分数计。 [0025] The weight fraction.

[0026] 有益效果:本发明的烟草包装由内包装纸和外包装纸组成,内包装纸包括燃烧层和导热层,燃烧层燃烧产生热量,再通过导热层传热对烟丝进行加热,燃烧层和导热层均包含有玉米粉、马铃薯粉、谷皮粉和甲基纤维素等可以增加燃烧时间的燃烧材料,同时,材料又能够充分燃烧,产生的固定颗粒少,不会对烟草本身的口味产生影响;另外本发明的燃烧层和导热层产生的热量大,克服传统的加热非燃烧型烟草加热不充分的缺陷,在导热层中还设置有网格状铝箱层,通过该铝箱层可将燃烧位置产生的热量传递到烟支的后端,促进烟丝各段加热均匀。 [0026] Advantageous Effects: The present invention consists of tobacco packaging inner wrapper and an outer wrapper composition, the wrapper comprising a combustion layer and the conductive layer, a layer of combustion heat produced by combustion, and then the tobacco is heated by a heat transfer layer, a combustion layer and the conductive layer may increase with both the time of burning combustible material corn flour, potato flour, bran powder and methyl cellulose and the like, at the same time, the combustion material being sufficiently less immobilized particles produced without the taste of the tobacco itself impact; large combustion heat further layer and the conductive layer of the present invention is produced, to overcome the conventional non-combustion type heating tobacco insufficient heating of defects, in the thermally conductive layer is provided with a further layer of mesh-like Aluminum, Aluminum layer by the combustion heat can be transferred to the rear end position produced cigarettes, tobacco segments facilitate uniform heating. 外包装层的铝箱层与燃烧层直接接触,在烟支抽吸过程中,燃烧层产生的热量由铝箱层隔离反射,对烟支进行加热,减少热量的损失;同时在原纸层上贴附防伪镭射层,不仅提高烟支的外观,还可以起到防伪的功能。 Aluminum layer directly contacts the outer layer and the combustion layer, the cigarettes in the aspiration process, the heat generated in the combustion layer Aluminum layer is reflected by the isolation of the cigarette is heated to reduce heat loss; posted while the base paper layer security laser attachment layer, not only improve the appearance of cigarettes, may also play a security function.

具体实施方式 detailed description

[0027] 下面对本发明技术方案进行详细说明,但是本发明的保护范围不局限于所述实施例。 [0027] Next, the technical solution of the present invention in detail, but the scope of the present invention is not limited to the embodiments.

[0028] 实施例1: 一种加热非燃烧型烟草的包装纸生产工艺,包括内包装纸的制备和外包装纸的制备, Preparation of the inner wrapper and the outer wrapper of the non-combustion type of heating tobacco paper production process, comprising: 1 [0028] Example

[0029] 所述内包装纸的制备包括如下步骤: Preparation [0029] The inner wrapper comprises steps of:

[0030] (1)制备燃烧层:将植物纤维与水混合,再加入燃烧填料、助剂、醚化剂,搅拌均匀, 搅拌完成后过滤出浆料,浆料与玉米粉、马铃薯粉、谷皮粉和甲基纤维素混合完成纸浆制备,纸浆压榨脱水成形,烘干后在压纸机上压制; [0030] (1) Preparation of the combustion stratum of: plant fibers with water, then add combustion fillers, additives, etherifying agent, uniformly stirring, the slurry was filtered after the completion of stirring, the slurry with corn flour, potato flour, cereal Paper powder and mixing to complete preparation of cellulose pulp, pulp dewatering molded, dried and compressed in the pressing machine;

[0031] (2)制备导热层:使用与步骤(1)相同的制备方法制备原纸层,在原纸层的下表面镀满铝箱作为加热层,在原纸层的上表面镀网格状铝箱作为传热层,使用激光穿孔或针刺穿孔的方法在导热层上均匀穿孔; [0031] (2) Preparation of thermally conductive layer: used in step (1) the same preparation method of the base paper layer at the surface of the base paper layer coated over the heating layer as Aluminum, Aluminum coated on the grid-like surface of the base paper layer, as the heat transfer layer, using laser perforation methods or needle perforation perforated uniformly over the thermally conductive layer;

[0032] (3)施胶复合:在燃烧层的一侧涂抹胶层,将导热层的网格状铝箱面贴附于施胶面上,并再热压辊下进行热压复合,热压温度为160°C,压力为0.45MPa,辊速为18m/min,得到内包装纸; [0032] (3) sizing compound: the combustion stratum side glue applicator, the grid-like surface of the thermally conductive layer is Aluminum is attached to the surface sizing, and then hot-pressed composite under hot roll, hot press temperature 160 ° C, a pressure of 0.45MPa, roller speed of 18m / min, to give the inner wrapper;

[0033] 所述外包装纸的制备包括如下步骤: [0033] Preparation of the wrapper comprising the steps of:

[0034] (4)使用与步骤(1)相同的制备方法制备外包装层,在外包装纸的背面镀满铝箱作为隔热层; [0034] (4) used in step (1) prepared in the same preparation method of the outer layer, the back surface of the outer wrapper over Aluminum plating as a heat insulating layer;

[0035] (5)将水性哑光镭射转移涂料在涂布速度为20m/min的条件下涂布于PET薄膜上, 然后置于烘箱内,在160 °C下烘干,烘干车速为30m/min; The [0035] (5) The aqueous matte coating applied laser transfer speed of 20m / min conditions applied onto a PET film, and then placed in an oven dried at 160 ° C, the drying speed of 30m / min;

[0036] ⑹采用模压机对涂布水性哑光镭射转移涂料的PET薄膜进行模压,得到哑光镭射膜; [0036] ⑹ PET film molding machine using the coated aqueous coating is matt laser transfer molding, to obtain matt radium;

[0037] ⑺在步骤⑷制备的外包装层的正面涂抹胶层,将哑光镭射膜贴附于外包装层的胶层上,并再热压辊下进行热压复合,热压温度为130°C,压力为0.6MPa,辊速为20m/min,冷却后去除PET薄膜,得到外包装纸; [0037] ⑺ outer layer on the front step of preparing an applicator ⑷ subbing layer, the subbing layer on the matte radium is attached to the outer layer, and then hot-pressed composite under heat and pressure roller, pressing temperature of 130 ° C, a pressure of 0.6MPa, roller speed of 20m / min, the PET film is removed after cooling to obtain outer wrapping;

[0038] 内、外包装纸复合: [0038] The inner and outer wrapping compound:

[0039] (8)将外包装纸的隔热层贴附在内包装纸的燃烧层上,通过机械挤压的方法,将内、外包装纸复合为一体。 [0039] (8) of the insulating layer of the outer wrapper is attached to the combustor inner wrapper layer, by mechanical extrusion of the inner and outer wrappers as a whole compound.

[0040] 步骤⑴中所述燃烧层包含如下重量份的组分: 植物纤维30份; 玉米粉4 (分; 马铃薯粉4份; 谷皮粉8份; [0040] Step ⑴ said combustion layer comprises the following parts by weight of component: 30 parts of vegetable fiber; corn flour 4 (points; 4 parts of potato flour; bran powder, 8 parts;

[0041] 甲基纤维素1份, 醚化剂3 (分; 燃烧填料30份: 助剂5份。 [0041] 1 part of methyl cellulose, the etherifying agent 3 (points; combustion filler 30 parts: 5 parts of auxiliaries.

[0042] 所述植物纤维为废竹肩、废棉、玉米杆、稻草、麦杆、棉花杆、花生杆、薯渣、豆腐渣其中一种或几种混合而成;所述燃烧填料为碳粉和碳酸钙的混合物;所述助剂为氯酸钾。 [0042] The plant fiber is a bamboo shoulder waste, cotton waste, corn stover, rice straw, wheat straw, cotton stalk, peanut bar, potato residue, wherein one or more rubbish mixed; the filler is a carbon combustion a mixture of powder and calcium carbonate; the adjuvant is potassium chlorate.

[0043] 步骤⑶、(7)中所述胶层为水性聚氨酯胶层或丙烯酸酯改性水性聚氨酯胶层或魔芋粉-壳聚糖-聚乙烯醇共混胶层或丙烯酸胶层。 [0043] Step ⑶, (7) the aqueous polyurethane adhesive layer is a subbing layer or subbing layer acrylated aqueous polyurethane or konjac flour - Chitosan - PVA hybrid glue or an acrylic glue.

[0044] 步骤⑸中所述水性哑光镭射转移涂料包括以下组分: 水溶性聚氨酯5份; 水溶性丙烯酸酯2份; 交联剂0.5份; 润湿剂1份; [0044] Step ⑸ said aqueous matte coating laser transfer include the following components: 5 parts of a water-soluble polyurethane; 2 parts water-soluble acrylate; 0.5 parts crosslinker; 1 part of a wetting agent;

[0045] 增稠剂0,2份; 吸光粉0.05份: 醋酸乙烯酯0.5份; 丁酯0.05份; 水1份; [0045] 0,2 parts of a thickener; 0.05 parts of a light absorbing powder: 0.5 parts of vinyl acetate; butyl 0.05 parts; water to 1 part;

[0046] 以重量分数计。 [0046] The weight fraction.

[0047] 实施例2:—种加热非燃烧型烟草的包装纸生产工艺,包括内包装纸的制备和外包装纸的制备, [0047] Example 2: - Preparation of the inner wrapper and the outer wrapper non-flammable tobacco paper production process, comprising heating the species,

[0048] 所述内包装纸的制备包括如下步骤: Preparation [0048] The inner wrapper comprises steps of:

[0049] (1)制备燃烧层:将植物纤维与水混合,再加入燃烧填料、助剂、醚化剂,搅拌均匀, 搅拌完成后过滤出浆料,浆料与玉米粉、马铃薯粉、谷皮粉和甲基纤维素混合完成纸浆制备,纸浆压榨脱水成形,烘干后在压纸机上压制; [0049] (1) Preparation of the combustion stratum of: plant fibers with water, then add combustion fillers, additives, etherifying agent, uniformly stirring, the slurry was filtered after the completion of stirring, the slurry with corn flour, potato flour, cereal Paper powder and mixing to complete preparation of cellulose pulp, pulp dewatering molded, dried and compressed in the pressing machine;

[0050] (2)制备导热层:使用与步骤(1)相同的制备方法制备原纸层,在原纸层的下表面镀满铝箱作为加热层,在原纸层的上表面镀网格状铝箱作为传热层,使用激光穿孔或针刺穿孔的方法在导热层上均匀穿孔; [0050] (2) Preparation of thermally conductive layer: used in step (1) the same preparation method of the base paper layer at the surface of the base paper layer coated over the heating layer as Aluminum, Aluminum coated on the grid-like surface of the base paper layer, as the heat transfer layer, using laser perforation methods or needle perforation perforated uniformly over the thermally conductive layer;

[0051] (3)施胶复合:在燃烧层的一侧涂抹胶层,将导热层的网格状铝箱面贴附于施胶面上,并再热压辊下进行热压复合,热压温度为200°C,压力为0.5MPa,辊速为25m/min,得到内包装纸; [0051] (3) sizing compound: the combustion stratum side glue applicator, the grid-like surface of the thermally conductive layer is Aluminum is attached to the surface sizing, and then hot-pressed composite under hot roll, hot press temperature 200 ° C, a pressure of 0.5MPa, roller speed of 25m / min, to give the inner wrapper;

[0052] 所述外包装纸的制备包括如下步骤: [0052] Preparation of the wrapper comprising the steps of:

[0053] (4)使用与步骤(1)相同的制备方法制备外包装层,在外包装纸的背面镀满铝箱作为隔热层; [0053] (4) used in step (1) prepared in the same preparation method of the outer layer, the back surface of the outer wrapper over Aluminum plating as a heat insulating layer;

[0054] (5)将水性哑光镭射转移涂料在涂布速度为30m/min的条件下涂布于PET薄膜上, 然后置于烘箱内,在185 °C下烘干,烘干车速为40m/min; The [0054] (5) The laser transfer matt coating an aqueous coating speed of 30m / min conditions applied onto a PET film, and then placed in an oven dried at 185 ° C, the drying speed of 40m / min;

[0055] ⑹采用模压机对涂布水性哑光镭射转移涂料的PET薄膜进行模压,得到哑光镭射膜; [0055] ⑹ PET film molding machine using the coated aqueous coating is matt laser transfer molding, to obtain matt radium;

[0056] ⑺在步骤⑷制备的外包装层的正面涂抹胶层,将哑光镭射膜贴附于外包装层的胶层上,并再热压辊下进行热压复合,热压温度为180°C,压力为0.7MPa,辊速为25m/min,冷却后去除PET薄膜,得到外包装纸; [0056] ⑺ outer layer on the front step of preparing an applicator ⑷ subbing layer, the subbing layer on the matte radium is attached to the outer layer, and then hot-pressed composite under heat and pressure roller, the pressing temperature was 180 ° C, a pressure of 0.7MPa, roller speed of 25m / min, the PET film is removed after cooling to obtain outer wrapping;

[0057] 内、外包装纸复合: [0057] The inner and outer wrapping compound:

[0058] (8)将外包装纸的隔热层贴附在内包装纸的燃烧层上,通过机械挤压的方法,将内、外包装纸复合为一体。 [0058] (8) of the insulating layer of the outer wrapper is attached to the combustor inner wrapper layer, by mechanical extrusion of the inner and outer wrappers as a whole compound.

[0059] 步骤⑴中所述燃烧层包含如下重量份的组分: 植物纤维40份; 玉米粉6份; 马铃薯粉6份; [0059] Step ⑴ said combustion layer comprises the following parts by weight of component: 40 parts of plant fibers; 6 parts of corn flour; 6 parts of potato flour;

[0060] 谷皮粉1〇份; 甲基纤维素3份; 醚化剂5份; 燃烧填料60份; [0060] The bran flour 1〇 parts; 3 parts of methyl cellulose; 5 parts by etherification agent; combustor 60 parts filler;

[0061] 助剂1〇份。 [0061] aid 1〇 parts.

[0062] 所述植物纤维为废竹肩、废棉、玉米杆、稻草、麦杆、棉花杆、花生杆、薯渣、豆腐渣其中一种或几种混合而成;所述燃烧填料为碳粉和碳酸钙的混合物;所述助剂为氯酸钾。 [0062] The plant fiber is a bamboo shoulder waste, cotton waste, corn stover, rice straw, wheat straw, cotton stalk, peanut bar, potato residue, wherein one or more rubbish mixed; the filler is a carbon combustion a mixture of powder and calcium carbonate; the adjuvant is potassium chlorate.

[0063] 步骤⑶、(7)中所述胶层为水性聚氨酯胶层或丙烯酸酯改性水性聚氨酯胶层或魔芋粉-壳聚糖-聚乙烯醇共混胶层或丙烯酸胶层。 [0063] Step ⑶, (7) the aqueous polyurethane adhesive layer is a subbing layer or subbing layer acrylated aqueous polyurethane or konjac flour - Chitosan - PVA hybrid glue or an acrylic glue.

[0064] 步骤⑸中所述水性哑光镭射转移涂料包括以下组分: 水溶性聚氨酯20份; 水溶性丙烯酸酯10份; 交联剂2份; 润湿剂2份; [0064] Step ⑸ said aqueous matte coating laser transfer include the following components: 20 parts of a water-soluble polyurethane; 10 parts of a water-soluble acrylate; 2 parts of a crosslinking agent; 2 parts wetting agent;

[0065] 增稠剂1份; 吸光粉1份; 醋酸乙烯酯2.5份; 丁酯0.5份; 水10份; [0065] 1 part of a thickener; light-absorbing powder 1; 2.5 parts of vinyl acetate; butyl 0.5 parts; 10 parts of water;

[0066] 以重量分数计。 [0066] The weight fraction.

[0067] 实施例3:—种加热非燃烧型烟草的包装纸生产工艺,包括内包装纸的制备和外包装纸的制备, [0067] Example 3: - Preparation of the inner wrapper and the outer wrapper non-flammable tobacco paper production process, comprising heating the species,

[0068] 所述内包装纸的制备包括如下步骤: Preparation [0068] The inner wrapper comprises steps of:

[0069] (1)制备燃烧层:将植物纤维与水混合,再加入燃烧填料、助剂、醚化剂,搅拌均匀, 搅拌完成后过滤出浆料,浆料与玉米粉、马铃薯粉、谷皮粉和甲基纤维素混合完成纸浆制备,纸浆压榨脱水成形,烘干后在压纸机上压制; [0069] (1) Preparation of the combustion stratum of: plant fibers with water, then add combustion fillers, additives, etherifying agent, uniformly stirring, the slurry was filtered after the completion of stirring, the slurry with corn flour, potato flour, cereal Paper powder and mixing to complete preparation of cellulose pulp, pulp dewatering molded, dried and compressed in the pressing machine;

[0070] (2)制备导热层:使用与步骤(1)相同的制备方法制备原纸层,在原纸层的下表面镀满铝箱作为加热层,在原纸层的上表面镀网格状铝箱作为传热层,使用激光穿孔或针刺穿孔的方法在导热层上均匀穿孔; [0070] (2) Preparation of thermally conductive layer: used in step (1) the same preparation method of the base paper layer at the surface of the base paper layer coated over the heating layer as Aluminum, Aluminum coated on the grid-like surface of the base paper layer, as the heat transfer layer, using laser perforation methods or needle perforation perforated uniformly over the thermally conductive layer;

[0071] (3)施胶复合:在燃烧层的一侧涂抹胶层,将导热层的网格状铝箱面贴附于施胶面上,并再热压辊下进行热压复合,热压温度为180°C,压力为0.48MPa,辊速为20m/min,得到内包装纸; [0071] (3) sizing compound: the combustion stratum side glue applicator, the grid-like surface of the thermally conductive layer is Aluminum is attached to the surface sizing, and then hot-pressed composite under hot roll, hot press temperature 180 ° C, a pressure of 0.48MPa, roller speed of 20m / min, to give the inner wrapper;

[0072] 所述外包装纸的制备包括如下步骤: [0072] Preparation of the wrapper comprising the steps of:

[0073] (4)使用与步骤(1)相同的制备方法制备外包装层,在外包装纸的背面镀满铝箱作为隔热层; [0073] (4) used in step (1) prepared in the same preparation method of the outer layer, the back surface of the outer wrapper over Aluminum plating as a heat insulating layer;

[0074] (5)将水性哑光镭射转移涂料在涂布速度为25m/min的条件下涂布于PET薄膜上, 然后置于烘箱内,在170 °C下烘干,烘干车速为35m/min; The [0074] (5) The laser transfer matt coating an aqueous coating speed of 25m / min conditions applied onto a PET film, and then placed in an oven dried at 170 ° C, the drying speed of 35m / min;

[0075] ⑹采用模压机对涂布水性哑光镭射转移涂料的PET薄膜进行模压,得到哑光镭射膜; [0075] ⑹ PET film molding machine using the coated aqueous coating is matt laser transfer molding, to obtain matt radium;

[0076] ⑺在步骤⑷制备的外包装层的正面涂抹胶层,将哑光镭射膜贴附于外包装层的胶层上,并再热压辊下进行热压复合,热压温度为150°C,压力为0.65MPa,辊速为22m/min, 冷却后去除PET薄膜,得到外包装纸; [0076] ⑺ outer layer on the front step of preparing an applicator ⑷ subbing layer, the subbing layer on the matte radium is attached to the outer layer, and then hot-pressed composite under heat and pressure roller, pressing temperature 150 ° C, a pressure of 0.65MPa, roller speed of 22m / min, the PET film is removed after cooling to obtain outer wrapping;

[0077] 内、外包装纸复合: [0077] The inner and outer wrapping compound:

[0078] (8)将外包装纸的隔热层贴附在内包装纸的燃烧层上,通过机械挤压的方法,将内、外包装纸复合为一体。 [0078] (8) of the insulating layer of the outer wrapper is attached to the combustor inner wrapper layer, by mechanical extrusion of the inner and outer wrappers as a whole compound.

[0079] 步骤⑴中所述燃烧层包含如下重量份的组分: 植物纤维35份; 玉米粉5份; 马铃薯粉5汾; [0079] Step ⑴ said combustion layer comprises the following parts by weight of component: 35 parts of vegetable fiber; 5 parts of corn flour; 5 Fen potato flour;

[0080] 谷皮粉9份甲基纤维素2份; 醚化剂4扮; 燃烧填料45份; [0080] 9 parts bran flour 2 parts of methyl cellulose; 4 play an etherifying agent; combustor 45 parts filler;

[0081] 助剂7份。 [0081] 7 parts auxiliaries.

[0082]所述植物纤维为废竹肩、废棉、玉米杆、稻草、麦杆、棉花杆、花生杆、薯渣、豆腐渣其中一种或几种混合而成;所述燃烧填料为碳粉和碳酸钙的混合物;所述助剂为氯酸钾。 [0082] The plant fiber is a bamboo shoulder waste, cotton waste, corn stover, rice straw, wheat straw, cotton stalk, peanut bar, potato residue, wherein one or more rubbish mixed; the filler is a carbon combustion a mixture of powder and calcium carbonate; the adjuvant is potassium chlorate.

[0083] 步骤⑶、(7)中所述胶层为水性聚氨酯胶层或丙烯酸酯改性水性聚氨酯胶层或魔芋粉-壳聚糖-聚乙烯醇共混胶层或丙烯酸胶层。 [0083] Step ⑶, (7) the aqueous polyurethane adhesive layer is a subbing layer or subbing layer acrylated aqueous polyurethane or konjac flour - Chitosan - PVA hybrid glue or an acrylic glue.

[0084] 步骤⑸中所述水性哑光镭射转移涂料包括以下组分: 水溶性聚氨酯16份; 水溶性丙烯酸酯7份; 交联剂1份; 润湿剂1.5汾; [0084] Step ⑸ said aqueous matte coating laser transfer include the following components: 16 parts of a water-soluble polyurethane; 7 parts of a water-soluble acrylates; 1 part of a crosslinking agent; wetting agent 1.5 Fen;

[0085] 增稠剂0.6份; 吸光粉0.3份; 醋酸乙烯酯L2份; 丁酯0.2汾; 水:6份; [0085] 0.6 parts of a thickener; light-absorbing powder, 0.3 parts; L2 of parts of vinyl acetate; butyl Fen 0.2; water: 6 parts;

[0086] 以重量分数计。 [0086] The weight fraction.

[0087] 本发明的实施例1〜3与现有加热非燃烧型烟草包装纸的比较结果见表1: [0087] Example embodiments of the present invention with the comparison result 1~3 conventional non-combustion heat the tobacco wrapper in Table 1:

[0088] [0088]

Figure CN105780581BD00111

[0090]如上所述,尽管参照特定的优选实施例已经表示和表述了本发明,但其不得解释为对本发明自身的限制。 [0090] As described above, although reference to particular embodiments have been shown and is preferably expressed in the present invention, but should not be construed as limiting the invention itself. 在不脱离所附权利要求定义的本发明的精神和范围前提下,可对其在形式上和细节上作出各种变化。 Under the premise of the spirit and scope of the present invention without departing from the appended claims is defined, that various changes may be made in form and detail.

Claims (4)

  1. 1. 一种加热非燃烧型烟草的包装纸生产工艺,其特征在于,包括内包装纸的制备和外包装纸的制备, 所述内包装纸的制备包括如下步骤: (1) 制备燃烧层:将植物纤维与水混合,再加入燃烧填料、助剂、醚化剂,搅拌均匀,搅拌完成后过滤出浆料,浆料与玉米粉、马铃薯粉、谷皮粉和甲基纤维素混合完成纸浆制备,纸浆压榨脱水成形,烘干后在压纸机上压制;所述燃烧层包含如下重量份的组分: 植物纤维30〜40份; 玉米粉4〜6份; 马铃薯粉4〜6份; 谷皮粉8〜10份; 甲基纤维素1〜3份; 醚化剂3〜5份; 燃烧填料30〜60份; 助剂5〜10份; (2) 制备导热层:使用与步骤(1)相同的制备方法制备原纸层,在原纸层的下表面镀满铝箱作为加热层,在原纸层的上表面镀网格状铝箱作为传热层,使用激光穿孔或针刺穿孔的方法在导热层上均匀穿孔; (3) 施胶复合:在燃烧 A non-combustion type heating tobacco paper production process, wherein Preparation inner wrapper and outer wrapper comprises preparing said inner wrapper comprises steps of: (1) preparing a layer of combustion: mixed plant fibers with water, then add combustion fillers, additives, etherifying agent, uniformly stirring, the slurry was filtered after the completion of stirring, the slurry with corn flour, potato flour, bran powder and methyl cellulose pulp mixing is complete prepared, molded pulp dewatering, and drying are compressed on the machine; the combustion layer comprises by weight parts of the following components: 30 to 40 parts by plant fibers; 4 ~ 6 parts of corn flour; 4 ~ 6 parts of potato flour; Valley Hide powder 8~10 parts; ~ 3 parts of methyl cellulose; ~ 5 parts by etherifying agents; fillers 30~60 parts by combustion; 5 to 10 parts by aid; (2) preparation of thermally conductive layer: used in step (1 ) the same preparation method of the base paper layer, coated on the surface of the base paper over the Aluminum layer, a heating layer, lattice Aluminum plating as a heat transfer layer on the surface layer of the base paper, a method using a laser or needle perforation in the perforated perforations uniformly thermally conductive layer; (3) sizing compound: combustion 层的一侧涂抹胶层,将导热层的网格状铝箱面贴附于施胶面上, 并在热压辊下进行热压复合,热压温度为160〜200 °C,压力为0.45〜0.5 MPa,辊速为18〜25 m/min,得到内包装纸; 所述外包装纸的制备包括如下步骤: (4) 使用与步骤(1)相同的制备方法制备外包装层,在外包装纸的背面镀满铝箱作为隔执层. (5) 将水性哑光镭射转移涂料在涂布速度为20〜30 m/min的条件下涂布于PET薄膜上, 然后置于烘箱内,在160〜185 °C下烘干,烘干车速为30〜40 m/min; (6) 采用模压机对涂布水性哑光镭射转移涂料的PET薄膜进行模压,得到哑光镭射膜; (7) 在步骤(4)制备的外包装层的正面涂抹胶层,将哑光镭射膜贴附于外包装层的胶层上,并在热压辊下进行热压复合,热压温度为130〜180 °C,压力为0.6〜0.7 MPa,辊速为20〜 25 m/min,冷却后去除PET薄膜,得到外包装纸; 内、外包装纸复 Smear layer side adhesive layer, the grid-like surface of the thermally conductive layer is Aluminum is attached to the surface sizing, and pressing the composite at hot roll pressing temperature is 160~200 ° C, a pressure of 0.45 ~0.5 MPa, roller speed of 18~25 m / min, to give the wrapper; prepared outer wrapper comprising the steps of: (4) used in step (1) prepared by the same method of preparing outer layer, the outer Aluminum coated side of the paper as a separator full execution layer (5) the aqueous coating matt laser transfer coating speed was coated on a PET film under the conditions of 20~30 m / min, and then placed in an oven at at 160~185 ° C. the drying speed of 30~40 m / min; (6) by compression molding machine matte PET film coated with an aqueous coating material is laser transfer molding, to obtain matt radium; (7) subbing layer applied on the front outer layer in step (4) are prepared, adhered to the matte radium outer layer on the adhesive layer, and pressing the composite at hot roll, hot-pressing temperature is 130~180 ° C, a pressure of 0.6~0.7 MPa, roll speed is 20~ 25 m / min, the PET film is removed after cooling to obtain outer wrapping; inner, outer wrapping complex : (8) 将外包装纸的隔热层贴附在内包装纸的燃烧层上,通过机械挤压的方法,将内、夕卜包装纸复合为一体。 : (8) of the insulating layer of the outer wrapper is attached to the combustor inner wrapper layer, by mechanical pressing of the inner wrapper Bu Xi composite integrally.
  2. 2. 根据权利要求1所述的加热非燃烧型烟草的包装纸生产工艺,其特征在于,所述植物纤维为废竹肩、废棉、玉米杆、稻草、麦杆、棉花杆、花生杆、薯渣、豆腐渣其中一种或几种混合而成;所述燃烧填料为碳粉和碳酸钙的混合物;所述助剂为氯酸钾。 The heating according to claim 1 in a non-combustion type tobacco paper production process, wherein said plant fiber is a bamboo shoulder waste, cotton waste, corn stover, rice straw, wheat straw, cotton stalk, peanut bar, potato residue, wherein one or more rubbish mixed; is a mixture of carbon powder and calcium carbonate fillers of the combustion; the adjuvant is potassium chlorate.
  3. 3. 根据权利要求1所述的加热非燃烧型烟草的包装纸生产工艺,其特征在于,步骤(3)、 (7)中所述胶层为水性聚氨酯胶层或丙烯酸酯改性水性聚氨酯胶层或魔芋粉-壳聚糖-聚乙烯醇共混胶层或丙烯酸胶层。 The combustion heating according to a non-tobacco wrapping paper production process as claimed in claim, wherein step (3), (7) the aqueous polyurethane adhesive layer is a subbing layer or acrylate-modified aqueous polyurethane adhesive layer or konjac flour - chitosan - PVA hybrid glue or an acrylic glue.
  4. 4. 根据权利要求1所述的加热非燃烧型烟草的包装纸生产工艺,其特征在于,步骤(5) 中所述水性哑光镭射转移涂料包括以下组分: 水溶性聚氨酯5〜20份; 水溶性丙烯酸酯2〜10份; 交联剂0.5〜2份; 润湿剂1〜2份; 增稠剂〇.2〜1份; 吸光粉0.05〜1份; 醋酸乙烯酯0.5〜2.5份; 丁酯0.05〜0.5份; 水1〜10份, 各组分以重量分数计。 The combustion heating according to a non-tobacco wrapping paper production process as claimed in claim, wherein said step (5) in the aqueous coating matt laser transfer include the following components: water-soluble polyurethane 5~20 parts; 2~10 parts of the water-soluble acrylate; 0.5~2 parts crosslinker; ~ 2 parts wetting agent; a thickener 〇.2~1 parts; light-absorbing powder 0.05~1 parts; 0.5~2.5 parts of vinyl acetate; 0.05~0.5 parts butyl; 1~10 parts of water, by weight fraction of each component.
CN 201610158977 2016-03-18 2016-03-18 A heating wrapper non-burning type tobacco manufacturing process CN105780581B (en)