CN105778632B - A kind of water-fast net taste type Water-based ceramic-imitating coating and preparation method thereof - Google Patents
A kind of water-fast net taste type Water-based ceramic-imitating coating and preparation method thereof Download PDFInfo
- Publication number
- CN105778632B CN105778632B CN201610348562.4A CN201610348562A CN105778632B CN 105778632 B CN105778632 B CN 105778632B CN 201610348562 A CN201610348562 A CN 201610348562A CN 105778632 B CN105778632 B CN 105778632B
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- based ceramic
- preparation
- taste type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to paint field, discloses a kind of water-fast net taste type Water-based ceramic-imitating coating and preparation method thereof.The coating includes the component of following mass parts：10 20 parts of calcite in powder, 10 20 parts of dry powder, 8 12 parts of calcium carbonate, 24 parts of bletilla striata powder, 13 parts of cornstarch, 0.5 1.5 parts of carboxymethyl cellulose, 0.5 1.5 parts of phenoxy resin, 0.5 1.5 parts of glutaraldehyde, 13 parts of purification of air particle, 45 55 parts of water.The water-fast net taste type Water-based ceramic-imitating coating of the present invention has preferable water resistance, and has air-cleaning function, and adsorption capacity is big, purification timeliness length, good air purification effect.
Description
Technical field
The present invention relates to paint field, more particularly to a kind of water-fast net taste type Water-based ceramic-imitating coating and preparation method thereof.
Background technology
As the improvement of people's living standards, also increasingly paid close attention to for the health of itself.In recent years on new finishing after
Room air pollution and the report of incidence of disease relation of leukaemia be also more common in media.Therefore, people finishing when increasingly
Focus on the feature of environmental protection of finishing material.
Indoors in fitment process, all more or less containing formaldehyde, benzene homologues etc. in plank, glue, wall covering, furniture
Harmful substance, several years after finishing even all can gradually it distribute in many decades, so as to influence the health of human body.In the market
Water-based ceramic-imitating coating, it is inexpensive because its decorative effect is fine and smooth, bright and clean, simple and elegant, and be formulated environmental protection, gradually promoted.But
It is that its construction technology is numerous and diverse, wet-rub resistance is poor.
Meanwhile also there is the coating with air-cleaning function compared with multiple types in current in the market.Such as Application No.
201410251188.7 Chinese patent discloses water-based purification of air paint, includes the component of following mass percent：Water
25%~30%；Dispersant 0.5%~1%；Nanometer anion powder 10%；Color filters：25%~30%；Purification of air auxiliary agent
1%~5%；Acrylic emulsion：30%~35%；Auxiliary agent：1%~3%.
The harmful substance such as water-based purification of air paint energy Long-term absorption made of the invention and decomposition formaldehyde in indoor air, from
And play a part of purifying air, it can also be absorbed by photocatalyst effect and decompose cigarette taste, the decomposed odour weight in air
The peculiar smell such as acetaldehyde, acetic acid and ammonia, can be with antimildew and antibacterial, while this purification of air paint is without harmful organic solvent,
Nontoxic, tasteless, green, water-fast, weather-proof, ageing-resistant, cold-hot good cycle, adhesive force is strong, and paint film is smooth soft, dress
Decorations effect is good, and storing and transporting security is easy to use, can be widely used on the exterior wall and interior wall of building construction.
The purification of air composition of above-mentioned coating is activated carbon, and activated carbon has higher porosity, has preferably absorption
Effect.But at present using activated carbon as major air purify composition coating there is also many shortcomings：1. the absorption of activated carbon
Capacity is smaller, and in general adsorbed effective duration as 1 year, and the release of pernicious gas is long-term, therefore can not meet to grow
The purification of air requirement of phase；2. activated carbon has preferable hygroscopicity, while pernicious gas is adsorbed, can also adsorb substantial amounts of
Moisture, the adsorption capacity for causing it originally limited are occupied.
The content of the invention
In order to solve the above-mentioned technical problem, the invention provides a kind of water-fast net taste type Water-based ceramic-imitating coating and its preparation side
Method.The water-fast net taste type Water-based ceramic-imitating coating of the present invention has preferable water resistance, and has air-cleaning function, adsorption capacity
Greatly, timeliness length, good air purification effect are purified.
The present invention concrete technical scheme be：A kind of water-fast net taste type Water-based ceramic-imitating coating, include the group of following mass parts
Point：
Calcite in powder 10-20 parts,
Dry powder 10-20 parts,
Calcium carbonate 8-12 parts,
Bletilla striata powder 2-4 parts,
Cornstarch 1-3 parts,
Carboxymethyl cellulose 0.5-1.5 parts,
Phenoxy resin 0.5-1.5 parts,
Glutaraldehyde 0.5-1.5 parts,
Purification of air particle 1-3 parts,
Water 45-55 parts.
As the preferred of the technical program, the water-fast net taste type Water-based ceramic-imitating coating also includes 50-150 part pigment.
A kind of preparation method of water-fast net taste type Water-based ceramic-imitating coating, step are：
1), by activated carbon composite colloidal sol, TiO 2 sol, aluminium hydroxide 50-70 in mass ratio:30-50:1-3 is well mixed,
Complex sol is obtained, after complex sol is aged into 36-72h, solvent displacement 24- is carried out to complex sol with the absolute ethyl alcohol of excess
48h, solvent displacement 12-36h is then carried out to complex sol with the n-hexane of excess, then removes n-hexane, obtained compound solidifying
Glue；30-40min is dried at 60-100 DEG C to plural gel；Then half is carried out between 200-500 DEG C to carbonize, obtain half charcoal
Compound, half carbide is cleaned, dried, after crushing, obtains half charing aerogel particle；Trim,ethylchlorosilane and n-hexane are pressed
Volume ratio is 1-3:10 mixing, obtain hydrophobically modified liquid, and half charing aerogel particle is dispersed into the hydrophobic of its 5-10 times of quality
In modification liquid, modified 4-8h, is made purification of air particle at 30-40 DEG C.
In the inventive solutions, purification of air particle is compounded with dope preparing process, the purification of air grain
Mixed sols is first made using activated carbon composite colloidal sol and TiO 2 sol as primary raw material in son, after colloidal sol is made into plural gel, first
Moisture removal is dried, then carries out half and carbonizes, half charing aerogel particle is obtained after half charing；Half charcoal made from this method
Change aerogel particle, there is higher one-tenth porosity, specific surface area is big, and adsorption capacity is big, and the absorption to harmful substance in air is imitated
Fruit is preferable.And because its charing is incomplete, the intensity of internal gutter structure is higher, and good stability of the dimension, structure is less likely to occur
Brittle fracture.Half-and-half charing aerogel particle carries out hydrophobically modified, on the one hand can avoid coating water swelling, cracking, lifting
Water resistance；On the other hand can its prevent from largely adsorbing moisture in air, occupy inner space.Aluminium hydroxide can be after heated
Resolve into aluminum oxide and water, aluminum oxide can lift the wearability of coating, water after by thermal evaporation can pore in the material, enhancing
Adsorption capacity, kill two birds with one stone.
2) water, is warming up to 80-100 DEG C, the bletilla striata powder of 100 mesh sieves will be crossed under agitation, cross the corn of 100 mesh sieves
Starch and carboxymethyl cellulose are at the uniform velocity added in water in 10-20min；70-80 DEG C is cooled to, under agitation by air
Purification particle is added in water.
It is green from bletilla striata powder, this kind of natural material of cornstarch.Carboxymethyl cellulose, bletilla striata powder, corn are formed sediment
Powder first stirs at relatively high temperatures, and reason is that at such a temperature, have substantial amounts of colloid substance to be released in bletilla striata powder,
Cooled again, preferable vicidity and mobility can be made it have.Due to the hydrophobicity of purification of air particle, cause its
Aqueous dispersion is poor, and bletilla striata powder and cornstarch have stronger cladding ability after being dissolved in water at high temperature, plays connection
The effect of material, purification of air particle can be wrapped up and aid in it to disperse.And in the painting process of coating, bletilla striata powder
It is preferable with the film forming of cornstarch, the flatness and film forming of coating can be lifted.
3) batch mixing, is carried out to calcite in powder, dry powder, calcium carbonate, batch mixing is carried out to phenoxy resin and glutaraldehyde, stirred
Under the conditions of the material after batch mixing is added in the water of step 2).
Glutaraldehyde and phenoxy resin play a part of binding agent, in addition, glutaraldehyde also possesses sterilizing ability, can be to air
Sterilized, phenoxy resin can also lift the water resistance of coating and resistance to shrinkage, make coating scrubbing resistance and be not easy shrinkage cracking.
4), under heat-retaining condition, 30-40min is dispersed with stirring, is cooled down, water-fast net taste type Water-based ceramic-imitating coating is made.As
The technical program it is preferred, the particle diameter of the purification of air particle is 400-1000 microns.
As the preferred of the technical program, half carbonization process of the plural gel is：By plural gel with 8-12 DEG C/
Min speed is warming up to 200-300 DEG C, keeps 30-50min；Then it is warming up to 400-500 DEG C again with 18-22 DEG C of speed.
Half is carried out as stated above to carbonize, and on the one hand can be strengthened the intensity of product, on the other hand can partly carbonized
Pore is carried out in journey, raising contains porosity.
As the preferred of the technical program, the preparation method of the activated carbon composite colloidal sol is：By furfural, water soluble phenolic resin
Fat, CNT, carboxymethyl cellulose, brucite fiber, sodium acid carbonate and water 3-5 in mass ratio:1:0.3-0.5:0.1-
0.2:0.03-0.05:0.01-0.03:100 mixing, obtain the first mixed liquor, are by concentration under agitation after stirring
0.25-0.75mol/L ammoniacal liquor is added drop-wise in the first mixed liquor, makes the first mixed liquor in neutrality；Then reacted at 65-75 DEG C
8-24h, activated carbon composite colloidal sol is made.
CNT is in hollow tubular, has the duct of nano-scale, is not influenceing activated carbon composite colloidal sol one-tenth porosity as far as possible
Under the premise of, it is possible to increase the intensity of material, brucite fiber can improve the toughness of material.Sodium acid carbonate being capable of pore.
As the preferred of the technical program, the rate of addition of the ammoniacal liquor is 10-20mL/min.
As the preferred of the technical program, the preparation method of the TiO 2 sol is：By butyl titanate, anhydrous second
Alcohol, sodium acid carbonate in mass ratio 1:20-40:0.1-0.3 is mixed, and obtains the second mixed liquor；By 1-2mol/L hydrochloric acid solution, nothing
Water-ethanol and water 4-6 by volume:8-16:5 are mixed, and obtain the 3rd mixed liquor；Under agitation by the 3rd mixed liquor
It is added drop-wise in the second isometric mixed liquor；Then 12-24h is reacted at 40-50 DEG C, obtains TiO 2 sol.
As the preferred of the technical program, the rate of addition of the 3rd mixed liquor is 8-12mL/min.
It is compared with the prior art, the beneficial effects of the invention are as follows：The water-fast net taste type Water-based ceramic-imitating coating of the present invention has
Preferable water resistance, and there is air-cleaning function, adsorption capacity is big, purification timeliness length, good air purification effect.
Embodiment
With reference to embodiment, the invention will be further described.
Embodiment 1
A kind of water-fast net taste type Water-based ceramic-imitating coating, include the component of following mass parts：
15 parts of calcite in powder, 15 parts of dry powder, 10 parts of calcium carbonate, 3 parts of bletilla striata powder, 2 parts of cornstarch, carboxymethyl cellulose
1 part, 1 part of phenoxy resin, 1 part of glutaraldehyde, 2 parts of purification of air particle, 50 parts of water.
The preparation process of the water-fast net taste type Water-based ceramic-imitating coating of the present embodiment is：
1), the preparation of activated carbon composite colloidal sol：By furfural, water soluble phenol resin, CNT, carboxymethyl cellulose, water magnesium
Mineral wool, sodium acid carbonate and water in mass ratio 4:1:0.4:0.15:0.04:0.02:100 mixing, first is obtained after stirring
Mixed liquor, the ammoniacal liquor that concentration is 0.5mol/L is added drop-wise in the first mixed liquor with 15mL/min speed under agitation,
Make the first mixed liquor in neutrality；Then 16h is reacted at 70 DEG C, activated carbon composite colloidal sol is made.
The preparation of TiO 2 sol：By butyl titanate, absolute ethyl alcohol, sodium acid carbonate in mass ratio 1:30:0.2 mixing,
Obtain the second mixed liquor；By 1.5mol/L hydrochloric acid solution, absolute ethyl alcohol and water by volume 5:12:5 are mixed, and obtain
Three mixed liquors；The 3rd mixed liquor is added drop-wise in the second isometric mixed liquor with 10mL/min speed under agitation；
Then 18h is reacted at 45 DEG C, obtains TiO 2 sol.
By activated carbon composite colloidal sol, TiO 2 sol, aluminium hydroxide in mass ratio 60:40:2 is well mixed, obtains compound molten
Glue, after complex sol is aged into 54h, solvent displacement 36h is carried out to complex sol with the absolute ethyl alcohol of excess, then with excess
N-hexane carries out solvent displacement 36h to complex sol, then removes n-hexane, obtains plural gel；To plural gel at 80 DEG C
Lower dry 35min；Then plural gel is warming up to 150 DEG C with 10 DEG C/min speed, keeps 40min；Then again with 20 DEG C
Speed be warming up to 450 DEG C, obtain half carbide, by half carbide clean, dry, crush after, obtain half charing aeroge
Grain.It is 2 by volume by trim,ethylchlorosilane and n-hexane:10 mixing, obtain hydrophobically modified liquid, will half charing aerogel particle
It is dispersed in the hydrophobically modified liquid of its 7.5 times of quality, modified 6h, it is net for the air of 400-1000 microns to be made particle diameter at 35 DEG C
Change particle.
2) water, is warming up to 90 DEG C, the bletilla striata powder of 100 mesh sieves will be crossed under agitation, cross the cornstarch of 100 mesh sieves
At the uniform velocity it is added to carboxymethyl cellulose in 15min in water；75 DEG C are cooled to, under agitation adds purification of air particle
It is added in water.
3) batch mixing, is carried out to calcite in powder, dry powder, calcium carbonate, batch mixing is carried out to phenoxy resin and glutaraldehyde, stirred
Under the conditions of the material after batch mixing is added in the water of step 2).
4), under heat-retaining condition, 35min is dispersed with stirring, is cooled down, water-fast net taste type Water-based ceramic-imitating coating is made.
Embodiment 2
A kind of water-fast net taste type Water-based ceramic-imitating coating, include the component of following mass parts：
10 parts of calcite in powder, 20 parts of dry powder, 8 parts of calcium carbonate, 4 parts of bletilla striata powder, 3 parts of cornstarch, carboxymethyl cellulose
0.5 part, 0.5 part of phenoxy resin, 0.5 part of glutaraldehyde, 1 part of purification of air particle, 52.5 parts of water.
The preparation process of the water-fast net taste type Water-based ceramic-imitating coating of the present embodiment is：
1), the preparation of activated carbon composite colloidal sol：By furfural, water soluble phenol resin, CNT, carboxymethyl cellulose, water magnesium
Mineral wool, sodium acid carbonate and water in mass ratio 3:1:0.3:0.1:0.03:0.01:100 mixing, it is mixed to obtain first after stirring
Liquid is closed, the ammoniacal liquor that concentration is 0.25mol/L is added drop-wise in the first mixed liquor with 10mL/min speed under agitation, made
First mixed liquor is in neutrality；Then 8h is reacted at 65 DEG C, activated carbon composite colloidal sol is made.
The preparation of TiO 2 sol：By butyl titanate, absolute ethyl alcohol, sodium acid carbonate in mass ratio 1:20:0.1 mixing,
Obtain the second mixed liquor；By 1mol/L hydrochloric acid solution, absolute ethyl alcohol and water by volume 4:8:5 are mixed, and obtain the 3rd
Mixed liquor；The 3rd mixed liquor is added drop-wise in the second isometric mixed liquor with 8mL/min speed under agitation；Then
24h is reacted at 40 DEG C, obtains TiO 2 sol.
By activated carbon composite colloidal sol, TiO 2 sol, aluminium hydroxide in mass ratio 50:30:1 is well mixed, obtains compound molten
Glue, after complex sol is aged into 36h, solvent displacement 24h is carried out to complex sol with the absolute ethyl alcohol of excess, then with excess
N-hexane carries out solvent displacement 12h to complex sol, then removes n-hexane, obtains plural gel；To plural gel at 60 DEG C
Lower dry 40min；Then plural gel is warming up to 200 DEG C with 8 DEG C/min speed, keeps 50min；Then again with 18 DEG C
Speed is warming up to 400 DEG C, obtains half carbide, and half carbide is cleaned, dried, after crushing, obtains half charing aerogel particle.
It is 1 by volume by trim,ethylchlorosilane and n-hexane:10 mixing, obtain hydrophobically modified liquid, will half charing aerogel particle point
It is dissipated in the hydrophobically modified liquid of its 5 times of quality, the modified 8h at 30 DEG C, the purification of air grain that particle diameter is 400-1000 microns is made
Son.
2) water, is warming up to 80 DEG C, the bletilla striata powder of 100 mesh sieves will be crossed under agitation, cross the cornstarch of 100 mesh sieves
At the uniform velocity it is added to carboxymethyl cellulose in 10min in water；70 DEG C are cooled to, under agitation adds purification of air particle
It is added in water.
3) batch mixing, is carried out to calcite in powder, dry powder, calcium carbonate, batch mixing is carried out to phenoxy resin and glutaraldehyde, stirred
Under the conditions of the material after batch mixing is added in the water of step 2).
4), under heat-retaining condition, 30min is dispersed with stirring, is cooled down, water-fast net taste type Water-based ceramic-imitating coating is made.
Embodiment 3
A kind of water-fast net taste type Water-based ceramic-imitating coating, include the component of following mass parts：
20 parts of calcite in powder, 10 parts of dry powder, 12 parts of calcium carbonate, 2 parts of bletilla striata powder, 1 part of cornstarch, carboxymethyl cellulose
1.5 parts, 1.5 parts of phenoxy resin, 1.5 parts of glutaraldehyde, 3 parts of purification of air particle, 47.5 parts of water.
The preparation process of the water-fast net taste type Water-based ceramic-imitating coating of the present embodiment is：
1), the preparation of activated carbon composite colloidal sol：By furfural, water soluble phenol resin, CNT, carboxymethyl cellulose, water magnesium
Mineral wool, sodium acid carbonate and water in mass ratio 5:1:0.5:0.2:0.05:0.03:100 mixing, it is mixed to obtain first after stirring
Liquid is closed, the ammoniacal liquor that concentration is 0.75mol/L is added drop-wise in the first mixed liquor with 20mL/min speed under agitation, made
First mixed liquor is in neutrality；Then 8h is reacted at 75 DEG C, activated carbon composite colloidal sol is made.
The preparation of TiO 2 sol：By butyl titanate, absolute ethyl alcohol, sodium acid carbonate in mass ratio 1:40:0.3 mixing,
Obtain the second mixed liquor；By 2mol/L hydrochloric acid solution, absolute ethyl alcohol and water by volume 6:16:5 are mixed, and obtain the 3rd
Mixed liquor；The 3rd mixed liquor is added drop-wise in the second isometric mixed liquor with 12mL/min speed under agitation；So
12h is reacted at 50 DEG C afterwards, obtains TiO 2 sol.
By activated carbon composite colloidal sol, TiO 2 sol, aluminium hydroxide in mass ratio 70:50:3 is well mixed, obtains compound molten
Glue, after complex sol is aged into 72h, solvent displacement 48h is carried out to complex sol with the absolute ethyl alcohol of excess, then with excess
N-hexane carries out solvent displacement 36h to complex sol, then removes n-hexane, obtains plural gel；To plural gel at 100 DEG C
Lower dry 30min；Then plural gel is warming up to 300 DEG C with 12 DEG C/min speed, keeps 30min；Then again with 22 DEG C
Speed be warming up to 500 DEG C, obtain half carbide, by half carbide clean, dry, crush after, obtain half charing aeroge
Grain.It is 3 by volume by trim,ethylchlorosilane and n-hexane:10 mixing, obtain hydrophobically modified liquid, will half charing aerogel particle
It is dispersed in the hydrophobically modified liquid of its 10 times of quality, modified 4h, it is net for the air of 400-1000 microns to be made particle diameter at 40 DEG C
Change particle.
2) water, is warming up to 100 DEG C, the bletilla striata powder for crossing 100 mesh sieves, the corn for crossing 100 mesh sieves formed sediment under agitation
Powder and carboxymethyl cellulose are at the uniform velocity added in water in 20min；70-80 DEG C is cooled to, under agitation by purification of air
Particle is added in water.
3) batch mixing, is carried out to calcite in powder, dry powder, calcium carbonate, batch mixing is carried out to phenoxy resin and glutaraldehyde, stirred
Under the conditions of the material after batch mixing is added in the water of step 2).
4), under heat-retaining condition, 40min is dispersed with stirring, is cooled down, water-fast net taste type Water-based ceramic-imitating coating is made.
Raw materials used in the present invention, equipment, it is the conventional raw material, equipment of this area unless otherwise noted；In the present invention
Method therefor, it is the conventional method of this area unless otherwise noted.
Water-fast net taste type Water-based ceramic-imitating coating produced by the present invention, it adsorbs timeliness and is 3-5, and after 5 years also
35-45% adsorption efficiency can be kept.
It is described above, only it is presently preferred embodiments of the present invention, not the present invention is imposed any restrictions, it is every according to the present invention
Any simple modification, change and the equivalent transformation that technical spirit is made to above example, still fall within the technology of the present invention side
The protection domain of case.
Claims (7)
- A kind of 1. water-fast net taste type Water-based ceramic-imitating coating, it is characterised in that：Include the component of following mass parts：Calcite in powder 10-20 parts,Dry powder 10-20 parts,Calcium carbonate 8-12 parts,Bletilla striata powder 2-4 parts,Cornstarch 1-3 parts,Carboxymethyl cellulose 0.5-1.5 parts,Phenoxy resin 0.5-1.5 parts,Glutaraldehyde 0.5-1.5 parts,Purification of air particle 1-3 parts,Water 45-55 parts；The preparation method of described water-fast net taste type Water-based ceramic-imitating coating, step are：1), by activated carbon composite colloidal sol, TiO 2 sol, aluminium hydroxide 50-70 in mass ratio:30-50:1-3 is well mixed, and is obtained Complex sol, after complex sol is aged into 36-72h, solvent displacement 24-48h is carried out to complex sol with the absolute ethyl alcohol of excess, Then solvent displacement 12-36h is carried out to complex sol with the n-hexane of excess, then removes n-hexane, obtain plural gel；It is right Plural gel dries 30-40min at 60-100 DEG C；Then half is carried out between 200-500 DEG C to carbonize, obtain half carbide, Half carbide is cleaned, dried, after crushing, obtains half charing aerogel particle；Trim,ethylchlorosilane and n-hexane are pressed into volume Than for 1-3:10 mixing, obtain hydrophobically modified liquid, and half charing aerogel particle is dispersed to the hydrophobically modified of its 5-10 times of quality In liquid, modified 4-8h, is made purification of air particle at 30-40 DEG C；2) water, is warming up to 80-100 DEG C, the bletilla striata powder of 100 mesh sieves will be crossed under agitation, cross the cornstarch of 100 mesh sieves At the uniform velocity it is added to carboxymethyl cellulose in 10-20min in water；70-80 DEG C is cooled to, under agitation by purification of air Particle is added in water；3) batch mixing, is carried out to calcite in powder, dry powder, calcium carbonate, batch mixing is carried out to phenoxy resin and glutaraldehyde, in stirring condition The lower material by after batch mixing is added in the water of step 2)；4), under heat-retaining condition, 30-40min is dispersed with stirring, is cooled down, water-fast net taste type Water-based ceramic-imitating coating is made.
- A kind of 2. preparation method of water-fast net taste type Water-based ceramic-imitating coating as claimed in claim 1, it is characterised in that the sky The particle diameter of gas purification particle is 400-1000 microns.
- 3. the preparation method of a kind of water-fast net taste type Water-based ceramic-imitating coating as claimed in claim 1, it is characterised in that described multiple Close gel half carbonization process be：Plural gel is warming up to 200-300 DEG C with 8-12 DEG C/min speed, keeps 30- 50min；Then it is warming up to 400-500 DEG C again with 18-22 DEG C of speed.
- 4. the preparation method of a kind of water-fast net taste type Water-based ceramic-imitating coating as claimed in claim 1, it is characterised in that described multiple Close charcoal colloidal sol preparation method be：By furfural, water soluble phenol resin, CNT, carboxymethyl cellulose, brucite fiber, Sodium acid carbonate and water 3-5 in mass ratio:1:0.3-0.5:0.1-0.2:0.03-0.05:0.01-0.03:100 mixing, stirring are equal The first mixed liquor is obtained after even, the ammoniacal liquor that concentration is 0.25-0.75mol/L is added drop-wise to the first mixed liquor under agitation In, make the first mixed liquor in neutrality；Then 8-24h is reacted at 65-75 DEG C, activated carbon composite colloidal sol is made.
- A kind of 5. preparation method of water-fast net taste type Water-based ceramic-imitating coating as claimed in claim 4, it is characterised in that the ammonia The rate of addition of water is 10-20mL/min.
- 6. the preparation method of a kind of water-fast net taste type Water-based ceramic-imitating coating as claimed in claim 1, it is characterised in that described two The preparation method of titanium oxide sol is：By butyl titanate, absolute ethyl alcohol, sodium acid carbonate in mass ratio 1:20-40:0.1-0.3 is mixed Close, obtain the second mixed liquor；By 1-2mol/L hydrochloric acid solution, absolute ethyl alcohol and water 4-6 by volume:8-16:5 are mixed Close, obtain the 3rd mixed liquor；The 3rd mixed liquor is added drop-wise in the second isometric mixed liquor under agitation；Then exist 12-24h is reacted at 40-50 DEG C, obtains TiO 2 sol.
- 7. the preparation method of a kind of water-fast net taste type Water-based ceramic-imitating coating as claimed in claim 6, it is characterised in that described the The rate of addition of three mixed liquors is 8-12mL/min.