CN105772623A - 一种t型零件的精密锻造工艺 - Google Patents

一种t型零件的精密锻造工艺 Download PDF

Info

Publication number
CN105772623A
CN105772623A CN201510840219.7A CN201510840219A CN105772623A CN 105772623 A CN105772623 A CN 105772623A CN 201510840219 A CN201510840219 A CN 201510840219A CN 105772623 A CN105772623 A CN 105772623A
Authority
CN
China
Prior art keywords
forging
blank
shaped
shaped part
lower mold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510840219.7A
Other languages
English (en)
Inventor
刘守生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kunshan Huizhong Machine Co Ltd
Original Assignee
Kunshan Huizhong Machine Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kunshan Huizhong Machine Co Ltd filed Critical Kunshan Huizhong Machine Co Ltd
Priority to CN201510840219.7A priority Critical patent/CN105772623A/zh
Publication of CN105772623A publication Critical patent/CN105772623A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种T型零件的精密锻造工艺，包括如下步骤：（1）坯料选取，选择直径为28mm，高度为52mm的圆柱型坯料；（2）坯料加热，利用中频感应炉对圆柱形坯料加热至1000℃‑1100℃；（3）墩粗，对加热后的圆柱体坯料墩粗至高度为20mm的圆饼状；（4）初锻，将圆饼状坯料竖直立放在下模型腔中，锻造出T型形状，T型上部锻出半球型凸台；（5）精锻，将初锻完成的T型零件放入精锻下模中，锻造出精确形状及尺寸，且保证T型零件的下部充满，并利用锻机顶出机构保证零件脱模；（6）切边，将精锻完的零件放入切边模具中，利用零件与下模剪切作用使零件与飞边分离；（7）等温正火。

Description

一种T型零件的精密锻造工艺
技术领域
本发明涉及了一种T型零件的精密锻造工艺，属于锻造加工技术领域。
背景技术
用于汽车缓速器结构中的T型零件要求精度高，性能好。零件外形为T型，长椭圆形平台下有较长的圆柱凸台，平台表面凸起物不对称。由于零件特殊形状，锻造下模具凸台型腔较深，容易有锻不足的缺陷，因此设计工艺为闭式模锻，在保证材料总量不变的情况下，最大程度保证整个模腔充满。
发明内容
本发明所要解决的技术问题是提供一种T型零件的精密锻造工艺，成功解决了T型零件在锻造时下部锻造不足的缺陷，保证了零件的成品率。
为了解决上述技术问题，本发明所采用的技术方案是：
一种T型零件的精密锻造工艺，其特征在于：包括如下步骤：
（1）坯料选取，选择直径为28mm，高度为52mm的圆柱型坯料；
（2）坯料加热，利用中频感应炉对圆柱形坯料加热至1000℃-1100℃；
（3）墩粗，对加热后的圆柱体坯料墩粗至高度为20mm的圆饼状；
（4）初锻，将圆饼状坯料竖直立放在下模型腔中，锻造出T型形状；
（5）精锻，将初锻完成的T型零件放入精锻下模中，锻造出精确形状及尺寸，且保证T型零件的下部充满，并利用锻机顶出机构保证零件脱模；
（6）切边，将精锻完的零件放入切边模具中，利用零件与下模剪切作用使零件与飞边分离；
（7）等温正火，锻件冷却至500℃-600℃后进保温炉加热至800℃-900℃，保温90-100分钟，后随炉冷却至650℃，在650℃保温60-90分钟，后随炉冷却至室温。
前述的一种T型零件的精密锻造工艺，其特征在于：将正火完的锻件放入喷丸机中喷丸20至30分钟，清除氧化皮，提高表面质量。
前述的一种T型零件的精密锻造工艺，其特征在于：所述步骤（3）中墩粗后的圆饼状坯料的最大外径处为48.4mm。
前述的一种T型零件的精密锻造工艺，其特征在于：所述步骤（7）中等温正火时，锻件冷却至550℃后进保温炉加热至880℃，保温90分钟，后随炉冷却至650℃，在650℃保温60分钟，后随炉冷却至室温。
前述的一种T型零件的精密锻造工艺，其特征在于：所述步骤（2）中坯料加热至1050℃。
本发明的有益效果是：本工艺设计在初锻件上部添加半球形凸台，此凸台可在零件终锻时使下部凸台继续充型，此锻造工艺成功解决了T型零件在锻造时下部锻造不足的缺陷，保证了零件的成品率。
具体实施方式
下面将结合具体实施方式，对本发明做进一步的说明。
一种T型零件的精密锻造工艺，包括如下步骤：
（1）坯料选取，选择直径为28mm，高度为52mm的圆柱型坯料；
（2）坯料加热，利用中频感应炉对圆柱形坯料加热至1000℃-1100℃；
（3）墩粗，对加热后的圆柱体坯料墩粗至高度为20mm的圆饼状；
（4）初锻，将圆饼状坯料竖直立放在下模型腔中，锻造出T型形状，T型上部锻出半球型凸台；凸台可以在精锻时让材料更容易向下部填充。
（5）精锻，将初锻完成的T型零件放入精锻下模中，锻造出精确形状及尺寸，且保证T型零件的下部充满，并利用锻机顶出机构保证零件脱模；
（6）切边，将精锻完的零件放入切边模具中，利用零件与下模剪切作用使零件与飞边分离；
（7）等温正火，锻件冷却至500℃-600℃后进保温炉加热至800℃-900℃，保温90-100分钟，后随炉冷却至650℃，在650℃保温60-90分钟，后随炉冷却至室温。
本工艺设计在初锻件上部添加半球形凸台，此凸台可在零件终锻时使下部凸台继续充型，此锻造工艺成功解决了T型零件在锻造时下部锻造不足的缺陷，保证了零件的成品率。
将正火完的锻件放入喷丸机中喷丸20至30分钟，清除氧化皮，提高表面质量。
本实施例中，所述步骤（3）中墩粗后的圆饼状坯料的最大外径处为48.4mm，便于后期的初锻和精锻。
经过反复试验，其中，所述步骤2中坯料加热至1050℃，所述步骤（7）中等温正火时，锻件冷却至550℃后进保温炉加热至880℃，保温90分钟，后随炉冷却至650℃，在650℃保温60分钟，后随炉冷却至室温时得到的零件性能最佳。
综上所述，本发明提供的一种T型零件的精密锻造工艺，成功解决了T型零件在锻造时下部锻造不足的缺陷，保证了零件的成品率。
以上显示和描述了本发明的基本原理、主要特征及优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界。

Claims (5)

1.一种T型零件的精密锻造工艺，其特征在于：包括如下步骤：
（1）坯料选取，选择直径为28mm，高度为52mm的圆柱型坯料；
（2）坯料加热，利用中频感应炉对圆柱形坯料加热至1000℃-1100℃；
（3）墩粗，对加热后的圆柱体坯料墩粗至高度为20mm的圆饼状；
（4）初锻，将圆饼状坯料竖直立放在下模型腔中，锻造出T型形状，T型上部锻出半球型凸台；
（5）精锻，将初锻完成的T型零件放入精锻下模中，锻造出精确形状及尺寸，且保证T型零件的下部充满，并利用锻机顶出机构保证零件脱模；
（6）切边，将精锻完的零件放入切边模具中，利用零件与下模剪切作用使零件与飞边分离；
（7）等温正火，锻件冷却至500℃-600℃后进保温炉加热至800℃-900℃，保温90-100分钟，后随炉冷却至650℃，在650℃保温60-90分钟，后随炉冷却至室温。
2.根据权利要求1所述的一种T型零件的精密锻造工艺，其特征在于：将正火完的锻件放入喷丸机中喷丸20至30分钟，清除氧化皮，提高表面质量。
3.根据权利要求1所述的一种T型零件的精密锻造工艺，其特征在于：所述步骤（3）中墩粗后的圆饼状坯料的最大外径处为48.4mm。
4.根据权利要求1所述的一种T型零件的精密锻造工艺，其特征在于：所述步骤（7）中等温正火时，锻件冷却至550℃后进保温炉加热至880℃，保温90分钟，后随炉冷却至650℃，在650℃保温60分钟，后随炉冷却至室温。
5.根据权利要求1所述的一种T型零件的精密锻造工艺，其特征在于：所述步骤（2）中坯料加热至1050℃。
CN201510840219.7A 2015-11-27 2015-11-27 一种t型零件的精密锻造工艺 Pending CN105772623A (zh)