CN105712631A - Low-temperature crackled glaze and preparation method thereof - Google Patents

Low-temperature crackled glaze and preparation method thereof Download PDF

Info

Publication number
CN105712631A
CN105712631A CN201610174693.5A CN201610174693A CN105712631A CN 105712631 A CN105712631 A CN 105712631A CN 201610174693 A CN201610174693 A CN 201610174693A CN 105712631 A CN105712631 A CN 105712631A
Authority
CN
China
Prior art keywords
parts
low
glaze
temperature
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610174693.5A
Other languages
Chinese (zh)
Inventor
葛宜翔
何畏
孙素强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Yixiang Ceramic Technology Co Ltd
Original Assignee
Jiangsu Yixiang Ceramic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Yixiang Ceramic Technology Co Ltd filed Critical Jiangsu Yixiang Ceramic Technology Co Ltd
Priority to CN201610174693.5A priority Critical patent/CN105712631A/en
Publication of CN105712631A publication Critical patent/CN105712631A/en
Pending legal-status Critical Current

Abstract

The invention belongs to the technical field of ceramics and particularly relates to low-temperature crackled glaze and a preparation method thereof. The low-temperature crackled glaze is prepared from, by mass, 75-90 parts of feldspar, 15-25 parts of quartz, 48-52 parts of heavy calcium carbonate, 15-20parts of light calcium carbonate, 50-70 parts of frits, 25-30 parts of zinc oxide and 15-20 parts of copper carbonate. The frits are prepared from, by mass, 0.5-1 part of aluminum oxide, 10-20 parts of borax, 3-5 parts of zinc oxide, 2-5 parts of sodium oxide and 17-21 parts of albite. According to the low-temperature crackled glaze and the preparation method thereof, the crackled glaze is fired at a low temperature, energy is saved, the yield is high, and a remarkable crackling effect is achieved.

Description

Low-temperature cracks glaze and preparation method thereof
Technical field
The invention belongs to ceramic technology field, be specifically related to a kind of low-temperature cracks glaze and preparation method thereof.
Background technology
Crack glaze refers to have on the glaze layer of ceramic tiny crackle, and it makes ceramic have specific artistic effect and get the favour of people.General when gloss firing, about 1100 DEG C belong to easy fired, about 1200 DEG C belong to middle temperature and burn till, about 1300 DEG C belong to high temperature and burn till, current most crack glaze belongs to middle high temperature when burning till and burns till, although high temperature burns till can ensure that good crack effect, but the ability that most crackle glaze adaptation quick high-temp burns till is poor, defect ware is more, relatively costly.
Summary of the invention
For above-mentioned technical problem, the present invention provides a kind of low-temperature cracks glaze and preparation method thereof, reduces production cost.
The technical scheme is that
Low-temperature cracks glaze, is prepared gained by following methods:
Following raw material is according to mass fraction proportioning: Anhydrite 75-90 part, quartz 15-25 part, ground calcium carbonate 48-52 part, precipitated calcium carbonate 15-20 part, frit 50-70 part, zinc oxide 25 ~ 30, curpic carbonate 15-20 part；
Frit includes following component, according to mass fraction: aluminium oxide 0.5 ~ 1 part, Borax 10 ~ 20, zinc oxide 3-5 parts, sodium oxide 2-5 part, albite 17 ~ 21 parts.
Above-mentioned dispensing is ground after mixing with water, goes out cylinder and sieve after grinding, adds water and is diluted to 60 ~ 65 Baume degrees and prepares glaze slip.
Low-temperature cracks glaze that the present invention provides and preparation method thereof, burns till crack glaze under relatively low temperature, energy-conservation, and yield rate is high, has significant crack effect.
Detailed description of the invention
In conjunction with detailed description of the invention, technical scheme is described.
Low-temperature cracks glaze, is prepared gained by following methods:
Following raw material is according to mass fraction proportioning: Anhydrite 75 parts, 20 parts of quartz, ground calcium carbonate 50 parts, precipitated calcium carbonate 20 parts, frit 67 parts, zinc oxide 27, curpic carbonate 20 parts；
Frit includes following component, according to mass fraction: aluminium oxide 0.5 part, Borax 14, zinc oxide 5 parts, sodium oxide 4 parts, albite 19 parts.
Above-mentioned dispensing is ground after mixing with water, goes out cylinder and sieve after grinding, adds water and is diluted to 60 ~ 65 Baume degrees and prepares glaze slip.

Claims (1)

1. low-temperature cracks glaze, it is characterised in that prepared gained by following methods:
Following raw material is according to mass fraction proportioning: Anhydrite 75-90 part, quartz 15-25 part, ground calcium carbonate 48-52 part, precipitated calcium carbonate 15-20 part, frit 50-70 part, zinc oxide 25 ~ 30, curpic carbonate 15-20 part；
Frit includes following component, according to mass fraction: aluminium oxide 0.5 ~ 1 part, Borax 10 ~ 20, zinc oxide 3-5 parts, sodium oxide 2-5 part, albite 17 ~ 21 parts；
Above-mentioned dispensing is ground after mixing with water, goes out cylinder and sieve after grinding, adds water and is diluted to 60 ~ 65 Baume degrees and prepares glaze slip.
CN201610174693.5A 2016-03-25 2016-03-25 Low-temperature crackled glaze and preparation method thereof Pending CN105712631A (en)