CN105648307A - 高强度钢筋 - Google Patents
高强度钢筋 Download PDFInfo
- Publication number
- CN105648307A CN105648307A CN201610036570.5A CN201610036570A CN105648307A CN 105648307 A CN105648307 A CN 105648307A CN 201610036570 A CN201610036570 A CN 201610036570A CN 105648307 A CN105648307 A CN 105648307A
- Authority
- CN
- China
- Prior art keywords
- percent
- cast iron
- high strength
- reinforcing bar
- strength reinforcement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高强度钢筋,涉及建筑材料技术领域,它具有以下质量百分含量的化学成分:C≦0.15%,Si0.2-0.4%,Mn0.3-0.6%,S≦0.03%,P≦0.03%,V0.1-0.2%,Ni0.01-0.03%,Cr≦0.1%,Mo0.06-0.08%,Al0.006-0.01%,其余为Fe及不可避免的杂质。本发明解决了现有高强钢筋存在塑性较低,易发生脆断的问题。
Description
技术领域
本发明涉及建筑材料技术领域,尤其是一种高强度钢筋。
背景技术
钢筋是现代各种建筑结构中被广泛应用的建筑用钢材,钢筋性能对混凝土建筑结构的安全性能和寿命有着直接的影响,随着建筑朝高层化和大跨度结构方向的发展以及防范地质灾害的需求,建筑行业对钢筋的强度提出了更高的要求,现有的高强钢筋相比于传统的普通钢筋,其具有更好的力学性能,能有效保证工程质量,同时,也能减少钢筋的使用量,有利于节约钢材,降低工程物资的成本。钢筋用钢的合金元素及其含量直接影响着钢筋的力学性能,但是现有的钢筋的塑性较低,易发生脆断。
发明内容
本发明的目的是提供一种高强度钢筋,它能够解决现有高强钢筋存在塑性较低,易发生脆断的问题。
为了解决上述问题,本发明采用的技术方案是:一种高强度钢筋具有以下质量百分含量的化学成分:C≦0.15%,Si0.2-0.4%,Mn0.3-0.6%,S≦0.03%,P≦0.03%,V0.1-0.2%,Ni0.01-0.03%,Cr≦0.1%,Mo0.06-0.08%,Al0.006-0.01%,其余为Fe及不可避免的杂质。
上述高强度钢筋的技术方案中,更具体的技术方案还可以是:C0.06%,Si0.28%,Mn0.42%,S0.02%,P0.02%,V0.15%,Ni0.02%,Cr0.05%,Mo0.068%,Al0.008%,其余为Fe及不可避免的杂质。
进一步的,C0.1%,Si0.2%,Mn0.3%,S0.03%,P0.03%,V0.1%,Ni0.01%,Cr0.1%,Mo0.08%,Al0.006%,其余为Fe及不可避免的杂质。
进一步的,C0.15%,Si0.4%,Mn0.6%,S0.015%,P0.015%,V0.2%,Ni0.03%,Cr0.02%,Mo0.06%,Al0.01%,其余为Fe及不可避免的杂质。
由于采用了上述技术方案,本发明与现有技术相比具有如下有益效果:降低C含量,在保证钢筋强度的前提下来提高塑性;Mn、Si能显著增加钢的强度,控制Mn含量,能避免钢材塑性降低;控制S、P含量,能有效避免钢材力学性能和耐腐蚀性能的降低;加入V、Ni、Cr和Mo,能提高钢的耐磨性能并增加其强度,保持良好的塑性和韧性;加入Al可增加钢筋的硬度;钢筋的屈服强度提高到700MPa以上,抗拉强度在900MPa以上,伸长率大于10%。
具体实施方式
下面结合实施例对本发明作进一步的详述:
实施例1
本实施例的高强度钢筋具有以下质量百分含量的化学成分:C0.06%,Si0.28%,Mn0.42%,S0.02%,P0.02%,V0.15%,Ni0.02%,Cr0.05%,Mo0.068%,Al0.008%,其余为Fe及不可避免的杂质。
制备时,将质量百分含量的化学成分加入转炉中冶炼钢水,出钢前在炉外钢包吹氩气进行精炼;钢水出钢,浇铸成小方钢坯,将钢坯送入加热炉中加热,进行粗轧和精轧得到钢筋,将钢筋淬火加热,保温一段时间,在冷却后进行回火,水冷即得。
本实施例高强度钢筋的性能如下:屈服强度759MPa,抗拉强度在985MPa,伸长率12.3%。
实施例2
本实施例的高强度钢筋具有以下质量百分含量的化学成分:C0.1%,Si0.2%,Mn0.3%,S0.03%,P0.03%,V0.1%,Ni0.01%,Cr0.1%,Mo0.08%,Al0.006%,其余为Fe及不可避免的杂质。
制备时,将质量百分含量的化学成分加入转炉中冶炼钢水,出钢前在炉外钢包吹氩气进行精炼;钢水出钢,浇铸成小方钢坯,将钢坯送入加热炉中加热,进行粗轧和精轧得到钢筋,将钢筋淬火加热,保温一段时间,在冷却后进行回火,水冷即得。
本实施例高强度钢筋的性能如下:屈服强度721MPa,抗拉强度在933MPa,伸长率11.5%。
实施例3
本实施例的高强度钢筋具有以下质量百分含量的化学成分:C0.15%,Si0.4%,Mn0.6%,S0.015%,P0.015%,V0.2%,Ni0.03%,Cr0.02%,Mo0.06%,Al0.01%,其余为Fe及不可避免的杂质。
制备时,将质量百分含量的化学成分加入转炉中冶炼钢水,出钢前在炉外钢包吹氩气进行精炼;钢水出钢,浇铸成小方钢坯,将钢坯送入加热炉中加热,进行粗轧和精轧得到钢筋,将钢筋淬火加热,保温一段时间,在冷却后进行回火,水冷即得。
本实施例高强度钢筋的性能如下:屈服强度702MPa,抗拉强度在911MPa,伸长率10.2%。
Claims (4)
1.一种高强度钢筋,其特征在于具有以下质量百分含量的化学成分:C≦0.15%,Si0.2-0.4%,Mn0.3-0.6%,S≦0.03%,P≦0.03%,V0.1-0.2%,Ni0.01-0.03%,Cr≦0.1%,Mo0.06-0.08%,Al0.006-0.01%,其余为Fe及不可避免的杂质。
2.根据权利要求1所述的高强度钢筋,其特征在于:C0.06%,Si0.28%,Mn0.42%,S0.02%,P0.02%,V0.15%,Ni0.02%,Cr0.05%,Mo0.068%,Al0.008%,其余为Fe及不可避免的杂质。
3.根据权利要求1所述的高强度钢筋,其特征在于:C0.1%,Si0.2%,Mn0.3%,S0.03%,P0.03%,V0.1%,Ni0.01%,Cr0.1%,Mo0.08%,Al0.006%,其余为Fe及不可避免的杂质。
4.根据权利要求1所述的高强度钢筋,其特征在于:C0.15%,Si0.4%,Mn0.6%,S0.015%,P0.015%,V0.2%,Ni0.03%,Cr0.02%,Mo0.06%,Al0.01%,其余为Fe及不可避免的杂质。