CN105623065A - Oil-proof low-smoke zero-halogen sheath for offshore drilling - Google Patents

Oil-proof low-smoke zero-halogen sheath for offshore drilling Download PDF

Info

Publication number
CN105623065A
CN105623065A CN201610084349.7A CN201610084349A CN105623065A CN 105623065 A CN105623065 A CN 105623065A CN 201610084349 A CN201610084349 A CN 201610084349A CN 105623065 A CN105623065 A CN 105623065A
Authority
CN
China
Prior art keywords
halogen sheath
low smoke
oil resistant
zero halogen
oil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610084349.7A
Other languages
Chinese (zh)
Inventor
吴疆
姚玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Applast Polymer Technology Yixing Co Ltd
Original Assignee
Applast Polymer Technology Yixing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Applast Polymer Technology Yixing Co Ltd filed Critical Applast Polymer Technology Yixing Co Ltd
Priority to CN201610084349.7A priority Critical patent/CN105623065A/en
Publication of CN105623065A publication Critical patent/CN105623065A/en
Pending legal-status Critical Current

Abstract

The invention discloses an oil-proof low-smoke zero-halogen sheath for offshore drilling. The oil-proof low-smoke zero-halogen sheath for offshore drilling is composed of, by weight, 50-100 parts of Levapren, 20-60 parts of hydrogenated nitrile butadiene, 40-150 parts of magnesium hydroxide, 40-150 parts of aluminum hydroxide, 0.5-2.5 parts of anti-aging agent TMQ, 1-3 parts of auxiliary crosslinking agent TMPTMA and 1-4 parts of vulcanizing agent BIBP. The tensile strength of the oil-proof low-smoke zero-halogen sheath for offshore drilling is larger than or equal to 9Mpa; the elongation of the oil-proof low-smoke zero-halogen sheath for offshore drilling is larger than or equal to 125%; the oil-proof low-smoke zero-halogen sheath for offshore drilling is excellent in performance, resistant to 902# and 903# oil and resistant to calcium bromine seawater and oil-based mud.

Description

A kind of marine drilling oil resistant low smoke and zero halogen sheath
Technical field:
The invention belongs to field of cables, particularly to a kind of marine drilling oil resistant low smoke and zero halogen sheath.
Background technology:
Day by day strengthening with the exploitation dynamics of landing field petroleum resources, oil and gas reserves constantly reduces, and the offshore petroleum resources accounting for global resources total amount about 34% have become the focus of people's concern and the focus of new round oil-gas exploration and development. One of important equipment that marine drilling platform is developed as exploratory engineering of off-shore petroleum/gas reservoir, and along with the exploration and development of world ocean oil gas, the marine drilling sheath of oil resistant low smoke and zero halogen also becomes necessary demand.
It is disclosed in the information of this background section and is merely intended to increase the understanding of the general background to the present invention, and be not construed as admitting or imply in any form that this information structure is for prior art that persons skilled in the art are known.
Summary of the invention:
It is an object of the invention to provide a kind of marine drilling oil resistant low smoke and zero halogen sheath, thus overcoming above-mentioned defect of the prior art.
For achieving the above object, the invention provides
A kind of marine drilling oil resistant low smoke and zero halogen sheath, its component is:
Preferably, in technical scheme, second Warburg Pincus is 80-100 part.
Preferably, in technical scheme, hydrogenated butyronitrile is 20-50 part.
Preferably, in technical scheme, magnesium hydroxide is 50-100 part.
Preferably, in technical scheme, aluminium hydroxide is 50-100 part.
Preferably, in technical scheme, age resistor TMQ is 0.5-2 part.
Preferably, in technical scheme, assistant crosslinking agent TMPTMA is 1-2 part.
Preferably, in technical scheme, vulcanizing agent BIBP is 2-3 part.
Preferably, in technical scheme, marine drilling oil resistant low smoke and zero halogen sheath hot strength >=9Mpa, percentage elongation >=125%.
Compared with prior art, there is advantages that
Marine drilling oil resistant low smoke and zero halogen sheath hot strength >=9Mpa, percentage elongation >=125%, function admirable, resistance to 902# and 903# machine oil, the bromine of resistance to calcium sea water and oil-base mud.
Detailed description of the invention:
Below the specific embodiment of the present invention is described in detail, it is to be understood that protection scope of the present invention is not by the restriction of detailed description of the invention.
Explicitly indicate that unless otherwise other, otherwise in entire disclosure and claims, term " includes " or its conversion will be understood to comprise the element or ingredient stated at such as " comprising " or " including " etc., and does not get rid of other element or other ingredient.
Embodiment 1
A kind of marine drilling oil resistant low smoke and zero halogen sheath, its component is:
Being mixed according to described weight portion by each component that to obtain marine drilling oil resistant low smoke and zero halogen sheath hot strength be 9MPa, percentage elongation is 150%.
Embodiment 2
A kind of marine drilling oil resistant low smoke and zero halogen sheath, its component is:
Being mixed according to described weight portion by each component that to obtain marine drilling oil resistant low smoke and zero halogen sheath hot strength be 10MPa, percentage elongation is 150%.
Embodiment 3
A kind of marine drilling oil resistant low smoke and zero halogen sheath, its component is:
Being mixed according to described weight portion by each component that to obtain marine drilling oil resistant low smoke and zero halogen sheath hot strength be 9.6MPa, percentage elongation is 140%.
Embodiment 4
A kind of marine drilling oil resistant low smoke and zero halogen sheath, its component is:
Being mixed according to described weight portion by each component that to obtain marine drilling oil resistant low smoke and zero halogen sheath hot strength be 10.5MPa, percentage elongation is 160%.
The aforementioned description to the specific illustrative embodiment of the present invention illustrates that and the purpose of illustration. These describe and are not wishing to limit the invention to disclosed precise forms, and it will be apparent that according to above-mentioned instruction, it is possible to carry out much changing and change. Purpose exemplary embodiment selected and describe is in that to explain the certain principles of the present invention and practical application thereof, so that those skilled in the art is capable of and utilizes the various different exemplary of the present invention and various different selection and change. The scope of the present invention is intended to be limited by claims and equivalents thereof.

Claims (9)

1. a marine drilling oil resistant low smoke and zero halogen sheath, it is characterised in that: its component is:
2. marine drilling oil resistant low smoke and zero halogen sheath according to claim 1, it is characterised in that: described second Warburg Pincus is 80-100 part.
3. marine drilling oil resistant low smoke and zero halogen sheath according to claim 1, it is characterised in that: described hydrogenated butyronitrile is 20-50 part.
4. marine drilling oil resistant low smoke and zero halogen sheath according to claim 1, it is characterised in that: described magnesium hydroxide is 50-100 part.
5. marine drilling oil resistant low smoke and zero halogen sheath according to claim 1, it is characterised in that: described aluminium hydroxide is 50-100 part.
6. marine drilling oil resistant low smoke and zero halogen sheath according to claim 1, it is characterised in that: described age resistor TMQ is 0.5-2 part.
7. marine drilling oil resistant low smoke and zero halogen sheath according to claim 1, it is characterised in that: described assistant crosslinking agent TMPTMA is 1-2 part.
8. marine drilling oil resistant low smoke and zero halogen sheath according to claim 1, it is characterised in that: described vulcanizing agent BIBP is 2-3 part.
9. marine drilling oil resistant low smoke and zero halogen sheath according to claim 1, it is characterised in that: described marine drilling oil resistant low smoke and zero halogen sheath hot strength >=9Mpa, percentage elongation >=125%.
CN201610084349.7A 2016-02-04 2016-02-04 Oil-proof low-smoke zero-halogen sheath for offshore drilling Pending CN105623065A (en)