CN105602452A - Wear-resistant wood floor - Google Patents
Wear-resistant wood floor Download PDFInfo
- Publication number
- CN105602452A CN105602452A CN201610036678.4A CN201610036678A CN105602452A CN 105602452 A CN105602452 A CN 105602452A CN 201610036678 A CN201610036678 A CN 201610036678A CN 105602452 A CN105602452 A CN 105602452A
- Authority
- CN
- China
- Prior art keywords
- parts
- particle diameter
- microns
- micron
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wear-resistant wood floor and belongs to the technical field of production of building materials. As special wear-resistant paint which is prepared by adding nickel slag with specific particle size, titanium dioxide, cattle hide and bentonite into a paint base is coated on surfaces of wood floor, the wood floor is of high wear resistance property.
Description
Technical field
The invention belongs to building material field, relate in particular to a kind of wearproof wooden floor.
Background technology
Timber floor refers to the floor made from timber, is the building material product that a kind of common household is used. Along with the growth of service time, easily there is wearing and tearing situation in its surface, if wood floor surface not carried out to abrasionproof processing, not only affects the attractive in appearance of timber floor, also has influence on its service life.
Summary of the invention
Technical problem to be solved by this invention is to provide the wearproof wooden floor that a kind of anti-wear performance is good.
In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is:
A kind of wearproof wooden floor, its covering with paint technique is that first the surface in timber floor applies the common paint of one deck, then applies one deck wear-resistant coating on the surface of timber floor, it is characterized in that: described wear-resistant coating adopts the raw material of following parts by weight:
1 part～4 parts of 10 parts～20 parts, the ox-hide that particle diameter is 1 part～5 parts of the nickel minerals slags of 1 micron～10 microns, 5 parts～8 parts of titanium dioxide that particle diameter is 1 micron～10 microns, particle diameter is 1 micron～10 microns, 0.5 part～2 parts of the bentonites that particle diameter is 1 micron～10 microns, 2 parts～6 parts of 50 parts～60 parts of 5 parts～10 parts of pigment, emulsions, dispersants that particle diameter is 1 micron～10 microns and coalescents;
Its preparation method is: at 50 DEG C～60 DEG C, the nickel minerals slag of above-mentioned parts by weight, titanium dioxide, bentonite, ox-hide, pigment, emulsion, dispersant and coalescents are mixed, stirred 4 hours～6 hours, make.
In technique scheme, technical scheme is more specifically: particle diameter is that 1 part of nickel minerals slag, the particle diameter of 1 micron～10 microns is that 5 parts of titanium dioxide, the particle diameter of 1 micron～10 microns is that 10 parts, ox-hide, the particle diameter of 1 micron～10 microns is that 2 parts of bentonites, the particle diameter of 1 micron～10 microns is 1 part of 6 parts of 50 parts of 10 parts of pigment, emulsions, the dispersants of 1 micron～10 microns and coalescents;
Further, particle diameter is that 5 parts of nickel minerals slags, the particle diameter of 1 micron～10 microns are that 8 parts of titanium dioxide, the particle diameter of 1 micron～10 microns is that 20 parts, ox-hide, the particle diameter of 1 micron～10 microns is that 0.5 part of bentonite, the particle diameter of 1 micron～10 microns is 4 parts of 2 parts of 60 parts of 5 parts of pigment, emulsions, the dispersants of 1 micron～10 microns and coalescents;
Further, particle diameter is that 3 parts of nickel minerals slags, the particle diameter of 1 micron～10 microns are that 6 parts of titanium dioxide, the particle diameter of 1 micron～10 microns is that 17 parts, ox-hide, the particle diameter of 1 micron～10 microns is that 1 part of bentonite, the particle diameter of 1 micron～10 microns is 3 parts of 5 parts of 52 parts of 8 parts of pigment, emulsions, the dispersants of 1 micron～10 microns and coalescents.
Owing to adopting technique scheme, the present invention has following beneficial effect:
The present invention makes special wear-resistant paint by the nickel minerals slag, titanium dioxide, ox-hide and the bentonite that add specified particle diameter on coating base material, and this wear-resistant paint is applied to the surface of timber floor, thereby makes timber floor have good anti-wear performance.
Detailed description of the invention
Below in conjunction with instantiation, the invention will be further described:
Embodiment 1
This wearproof wooden floor, its covering with paint technique is that first the surface in timber floor applies the common paint of one deck, then applies one deck wear-resistant coating on the surface of timber floor, this wear-resistant coating adopts following raw material:
Particle diameter is nickel minerals slag 10g, the titanium dioxide 50g that particle diameter is 1 micron, ox-hide 100g, the bentonite 20g that particle diameter is 1 micron, pigment 100g, emulsion 500g, dispersant 60g and the coalescents 10g that particle diameter is 1 micron that particle diameter is 1 micron of 1 micron;
Its preparation method is: at 55 DEG C, above-mentioned nickel minerals slag, titanium dioxide, bentonite, ox-hide, pigment, emulsion, dispersant and coalescents are mixed, stirred 5 hours, make.
The compression strength of the present embodiment wearproof wooden floor is 70MPa, rupture strength 5.0MPa, wear-resistant length 40mm.
Embodiment 2
This wearproof wooden floor, its covering with paint technique is that first the surface in timber floor applies the common paint of one deck, then applies one deck wear-resistant coating on the surface of timber floor, this wear-resistant coating adopts following raw material:
Particle diameter is nickel minerals slag 50g, the titanium dioxide 80g that particle diameter is 10 microns, ox-hide 200g, the bentonite 5g that particle diameter is 10 microns, pigment 50g, emulsion 600g, dispersant 20g and the coalescents 40g that particle diameter is 10 microns that particle diameter is 10 microns of 10 microns;
Its preparation method is: at 60 DEG C, above-mentioned nickel minerals slag, titanium dioxide, bentonite, ox-hide, pigment, emulsion, dispersant and coalescents are mixed, stirred 4 hours, make.
The compression strength of the present embodiment wearproof wooden floor is 70MPa, rupture strength 5.0MPa, wear-resistant length 40mm.
Embodiment 3
This wearproof wooden floor, its covering with paint technique is that first the surface in timber floor applies the common paint of one deck, then applies one deck wear-resistant coating on the surface of timber floor, this wear-resistant coating adopts following raw material:
Particle diameter is nickel minerals slag 30g, the titanium dioxide 60g that particle diameter is 6 microns, ox-hide 170g, the bentonite 10g that particle diameter is 6 microns, pigment 80g, emulsion 520g, dispersant 50g and the coalescents 30g that particle diameter is 6 microns that particle diameter is 6 microns of 6 microns;
Its preparation method is: at 50 DEG C, above-mentioned nickel minerals slag, titanium dioxide, bentonite, ox-hide, pigment, emulsion, dispersant and coalescents are mixed, stirred 6 hours, make.
The compression strength of the present embodiment wearproof wooden floor is 70MPa, rupture strength 5.0MPa, wear-resistant length 40mm.
Claims (4)
1. a wearproof wooden floor, its covering with paint technique is that first the surface in timber floor applies the common paint of one deck, then applies one deck wear-resistant coating on the surface of timber floor, it is characterized in that: described wear-resistant coating adopts the raw material of following parts by weight:
1 part～4 parts of 10 parts～20 parts, the ox-hide that particle diameter is 1 part～5 parts of the nickel minerals slags of 1 micron～10 microns, 5 parts～8 parts of titanium dioxide that particle diameter is 1 micron～10 microns, particle diameter is 1 micron～10 microns, 0.5 part～2 parts of the bentonites that particle diameter is 1 micron～10 microns, 2 parts～6 parts of 50 parts～60 parts of 5 parts～10 parts of pigment, emulsions, dispersants that particle diameter is 1 micron～10 microns and coalescents;
Its preparation method is: at 50 DEG C～60 DEG C, the nickel minerals slag of above-mentioned parts by weight, titanium dioxide, bentonite, ox-hide, pigment, emulsion, dispersant and coalescents are mixed, stirred 4 hours～6 hours, make.
2. wearproof wooden floor according to claim 1, is characterized in that: particle diameter is that 1 part of nickel minerals slag, the particle diameter of 1 micron～10 microns is that 5 parts of titanium dioxide, the particle diameter of 1 micron～10 microns is that 10 parts, ox-hide, the particle diameter of 1 micron～10 microns is that 2 parts of bentonites, the particle diameter of 1 micron～10 microns is 1 part of 6 parts of 50 parts of 10 parts of pigment, emulsions, the dispersants of 1 micron～10 microns and coalescents.
3. wearproof wooden floor according to claim 1, is characterized in that: particle diameter is that 5 parts of nickel minerals slags, the particle diameter of 1 micron～10 microns is that 8 parts of titanium dioxide, the particle diameter of 1 micron～10 microns is that 20 parts, ox-hide, the particle diameter of 1 micron～10 microns is that 0.5 part of bentonite, the particle diameter of 1 micron～10 microns is 4 parts of 2 parts of 60 parts of 5 parts of pigment, emulsions, the dispersants of 1 micron～10 microns and coalescents.
4. wearproof wooden floor according to claim 1, is characterized in that: particle diameter is that 3 parts of nickel minerals slags, the particle diameter of 1 micron～10 microns is that 6 parts of titanium dioxide, the particle diameter of 1 micron～10 microns is that 17 parts, ox-hide, the particle diameter of 1 micron～10 microns is that 1 part of bentonite, the particle diameter of 1 micron～10 microns is 3 parts of 5 parts of 52 parts of 8 parts of pigment, emulsions, the dispersants of 1 micron～10 microns and coalescents.