CN105601293A - Silicon fire-resistant brick - Google Patents

Silicon fire-resistant brick Download PDF

Info

Publication number
CN105601293A
CN105601293A CN201511011011.0A CN201511011011A CN105601293A CN 105601293 A CN105601293 A CN 105601293A CN 201511011011 A CN201511011011 A CN 201511011011A CN 105601293 A CN105601293 A CN 105601293A
Authority
CN
China
Prior art keywords
parts
resistant brick
silicon fire
resistant
brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201511011011.0A
Other languages
Chinese (zh)
Inventor
韦燕
刘洪岩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yixing Jichuang New Material Technology Co Ltd
Original Assignee
Yixing Jichuang New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yixing Jichuang New Material Technology Co Ltd filed Critical Yixing Jichuang New Material Technology Co Ltd
Priority to CN201511011011.0A priority Critical patent/CN105601293A/en
Publication of CN105601293A publication Critical patent/CN105601293A/en
Pending legal-status Critical Current

Abstract

The invention relates to a high-temperature-resistant material, in particular to a silicon fire-resistant brick. The silicon fire-resistant brick is prepared from the following ingredients in parts by weight: 65 parts to 70 parts of zirconite fine powder, 12 parts to 15 parts of chromite fines, 20 parts to 25 parts of magnesite and 12 parts to 15 parts of refractory clay. The silicon fire-resistant brick provided by the invention can meet high-temperature performance requirements, and also has the acid-and-alkaline-corrosion-resistant performance.

Description

Silica fire resistant brick
Technical field
The present invention relates to a kind of exotic material, be specially silica fire resistant brick.
Background technology
The refractory brick that boiler or oven inner liner use also needs antiacid alkali to corrode under some special environment. Can only meet high-temperature behavior requirement and existing refractory brick is resistance to, antiacid alkali erosiveness can not reach.
Summary of the invention
For solving the problems of the technologies described above, the invention provides one has refractory brick, has antiacid alkali erosiveness energy, not fragile.
Concrete technical scheme is:
Silica fire resistant brick, prepare gained by following raw material: according to parts by weight, 65 parts～70 parts of zircon fine powders, 12 parts～15 parts of chromite powders, 20 parts～25 parts, magnesite, 12 parts～15 parts of fire clays.
Silica fire resistant brick provided by the invention, can meet high-temperature behavior requirement, also has antiacid alkali erosiveness energy simultaneously.
Detailed description of the invention
The specific embodiment of the invention is described in conjunction with the embodiments.
Embodiment 1
Silica fire resistant brick, prepare gained by following raw material: according to parts by weight, 15 parts of 70 parts of zircon fine powders, 12 parts of chromite powders, 20 parts of parts of magnesite, fire clay.
Embodiment 2
Silica fire resistant brick, prepare gained by following raw material: according to parts by weight, 65 parts of parts of zircon fine powder, 15 parts of chromite powders, 25 parts, magnesite, 12 parts of fire clays.
Embodiment 3
Silica fire resistant brick, prepare gained by following raw material: according to parts by weight, 68 parts of parts of zircon fine powder, 12 parts of chromite powders, 22 parts, magnesite, 12 parts of fire clays.

Claims (1)

1. silica fire resistant brick, is characterized in that, prepares gained by following raw material: according to parts by weight, and 65 parts～70 parts of zircon fine powders, 12 parts～15 parts of chromite powders, 20 parts～25 parts, magnesite, 12 parts～15 parts of fire clays.
CN201511011011.0A 2015-12-30 2015-12-30 Silicon fire-resistant brick Pending CN105601293A (en)