CN105585881A - Water-based matte laser transfer coating for preparing anti-counterfeit material through film transfer - Google Patents

Water-based matte laser transfer coating for preparing anti-counterfeit material through film transfer Download PDF

Info

Publication number
CN105585881A
CN105585881A CN201610157034.0A CN201610157034A CN105585881A CN 105585881 A CN105585881 A CN 105585881A CN 201610157034 A CN201610157034 A CN 201610157034A CN 105585881 A CN105585881 A CN 105585881A
Authority
CN
China
Prior art keywords
parts
water
film
preparing
agent
Prior art date
Application number
CN201610157034.0A
Other languages
Chinese (zh)
Inventor
徐祥祥
Original Assignee
江苏金恒新型包装材料有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 江苏金恒新型包装材料有限公司 filed Critical 江苏金恒新型包装材料有限公司
Priority to CN201610157034.0A priority Critical patent/CN105585881A/en
Publication of CN105585881A publication Critical patent/CN105585881A/en

Abstract

The invention discloses water-based matte laser transfer coating for preparing an anti-counterfeit material through film transfer. The coating is prepared from 5-20 parts of aqurous ployurethane, 2-10 parts of PVA, 0.05-2 parts of butyl p-hydroxybenzoate, 0.5-2 parts of stearic acid, 0.1-1.5 parts of film-forming agent, 0.5-2 parts of cross-linking agent, 1-2 parts of wetting agent, 0.2-1 part of thickening agent, 0.05-1 part of light absorbing powder, 0.5-2.5 parts of vinyl acetate, 0.05-0.5 part of butyl ester, 0.1-2 parts of release agent and 1-10 parts of water. Water-based raw materials are adopted in the formula to prepare the water-based matte laser transfer coating, and therefore the volatilization of toxic gas in the drying process of an oily transfer coating is prevented, and the obtained package material is suitable for packaging products directly eaten by humans and meets the green production requirement; the product is good in stripping effect, high in rate of finished products and easy to popularize in the market when used for preparing the anti-counterfeit package material through a film transfer method.

Description

A kind of water-based dumb light laser transfer coatings of preparing anti-fake material that shifts for film
Technical field
The invention belongs to field of packaging material, be specifically related to a kind of water-based dumb light of preparing anti-fake material that shifts for filmLaser transfer coatings.
Background technology
Laser anti-counterfeiting technology is to utilize LASER Light Source within the extremely short time, light wave amplitude information and corresponding information to be remembered simultaneouslyRecord is got off, and utilizes interference of light principle to reflect each particle of composing images, is made into unique false proof plate, fromAnd reach false proof object.
How current each manufacturer, for ensureing product quality, is applied to laser anti-counterfeiting technology the packing of product or directly applies toOn product, to prevent that fake products from destroying corporate image. Particularly for high-grade tobacco and wine packaging industry, false smoke, fake wineAppearance not only damages businessman and consumer's economic interests and has also damaged the healthy of consumer, need strictly stop. Radium-shineAnti-counterfeiting technology is applied on packaging material the operation principle mainly shifting based on film, the whole course of work comprise plate-making,The operations such as film forming, film shift and peel off, still exist film to shift not thoroughly, peel off the problems such as unclean in whole operation;In addition, along with the aggravation of problem of environmental pollution, people's environmental consciousness is more and more stronger, for the green of packaging materialChange requirement also more and more higher, therefore, in the time preparing packaging material, will ensure to produce green and the feature of environmental protection of materials.
Summary of the invention
Goal of the invention: the object of the invention is for the deficiencies in the prior art, and a kind of green, environmental protection and easily stripping are providedFrom shift and prepare the water-based dumb light laser transfer coatings of anti-fake material for film.
Technical scheme: a kind of water-based dumb light laser transfer coatings of preparing anti-fake material that shifts for film of the present invention,Comprise following component:
In weight fraction.
Preferably, described water-based dumb light laser transfer coatings comprises following component:
In weight fraction.
Preferably, described film forming agent is aqueous polyurethane film forming agent or modified polyvinyl acetate glass fibre film forming agent or glassGlass fiber film forming agent.
Preferably, described releasing agent comprises following component:
In weight fraction.
Preferably, described releasing agent comprises following component:
In weight fraction.
Beneficial effect: select aqueous materials in the present invention's formula, prepare aqueous laser transfer coatings, avoided oilProperty transfer coatings in the volatilization of drying course Poisoning gas, it is directly edible that the packaging material that obtain are applicable to pack the mankindProduct, meets greenization production requirement; This product is for film transfer method while preparing anti-counterfeiting packing material, peel off effective,The yield rate of product is high, is easy to marketing.
Detailed description of the invention
Below by embodiment, technical solution of the present invention is elaborated, but protection scope of the present invention is not limited toDescribed embodiment.
Embodiment 1: a kind of water-based dumb light laser transfer coatings of preparing anti-fake material that shifts for film, comprises following component:
In weight fraction.
Preferably, described film forming agent is modified polyvinyl acetate glass fibre film forming agent.
Described releasing agent comprises following component:
In weight fraction.
Embodiment 2: a kind of water-based dumb light laser transfer coatings of preparing anti-fake material that shifts for film, comprises following component:
In weight fraction.
Described film forming agent is aqueous polyurethane film forming agent.
Described releasing agent comprises following component:
In weight fraction.
Embodiment 3: a kind of water-based dumb light laser transfer coatings of preparing anti-fake material that shifts for film, comprises following component:
In weight fraction.
Described film forming agent is glass fibre film forming agent.
Described releasing agent comprises following component:
In weight fraction.
The Performance Ratio of product of the present invention and existing product is in table 1;
Table 1 embodiment 1~3 and existing product performance test results
Product Existing product Embodiment 1 Embodiment 2 Embodiment 3
Peel off rate (%) 90 99.6 98.9 99.4
Yield rate (%) 88 98.6 98.5 98.6
As mentioned above, although represented and explained the present invention with reference to specific preferred embodiment, it shall not be construed asTo the present invention's self restriction. Do not departing under the spirit and scope of the present invention prerequisite of claims definition, can be rightIt makes various variations in the form and details.

Claims (5)

1. shift for film a water-based dumb light laser transfer coatings of preparing anti-fake material, it is characterized in that comprising followingComponent:
2. the water-based dumb light laser transfer coatings of preparing anti-fake material that shifts for film according to claim 1, itsBe characterised in that and comprise following component:
3. the water-based dumb light laser transfer coatings of preparing anti-fake material that shifts for film according to claim 1 and 2,It is characterized in that: described film forming agent is aqueous polyurethane film forming agent or modified polyvinyl acetate glass fibre film forming agent or glassGlass fiber film forming agent.
4. the water-based dumb light laser transfer coatings of preparing anti-fake material that shifts for film according to claim 1 and 2,It is characterized in that: described releasing agent comprises following component:
5. the water-based dumb light laser transfer coatings of preparing anti-fake material that shifts for film according to claim 4, itsBe characterised in that: described releasing agent comprises following component:
CN201610157034.0A 2016-03-18 2016-03-18 Water-based matte laser transfer coating for preparing anti-counterfeit material through film transfer CN105585881A (en)