CN105585285A - Preparation method of synthetic building clay brick - Google Patents
Preparation method of synthetic building clay brick Download PDFInfo
- Publication number
- CN105585285A CN105585285A CN201410634182.8A CN201410634182A CN105585285A CN 105585285 A CN105585285 A CN 105585285A CN 201410634182 A CN201410634182 A CN 201410634182A CN 105585285 A CN105585285 A CN 105585285A
- Authority
- CN
- China
- Prior art keywords
- brick
- slurry
- preparation
- clay brick
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of synthetic building clay bricks. The preparation method comprises the steps of grinding lime, quartz sand, sand or fine sandstone, and waste building stone materials according to specified meshes to form fine powders, placing the fine powders according to the proportion of 1:1.5:3 into a reaction kettle, adding 425-type cement and water according to 2:1, stirring the mixture to form slurry, adding 7% of a mortar binder to the stirred slurry, stirring the slurry for 20 min continuously, pouring the slurry into a clay brick mould, press-moulding a brick in a semi-dry manner, autoclaving the brick under a high-temperature autoclaving condition, and performing demoulding and maintaining the brick by spraying water to obtain a finish product.
Description
Technical field:
The present invention relates to technical field of buildings, especially a kind of preparation technology who builds composite brick.
Background technology:
At present, along with the process of China's building industry development deepens continuously, the use of construction material is also in continuous increase. The use of clay brick especially for building has occupied very large share in construction application. But, need a large amount of loessland exploitations owing to producing clay brick, directly affect to a great extent or destroyed peasant's agro-farming soil, affect peasant's income, the gas discharging in sintering procedure has polluted surrounding air.
Summary of the invention:
The present invention seeks to produce for present building clay brick the problem existing; and a kind of preparation technology who builds composite brick is provided, and can utilize obsolete material preparation to the building clay brick of existing use according to this method, save tilling the land of peasant; protect environment, avoided rubbish to huddle and left about. Its method is simple, saves soil, twice laid, environmental protection and energy saving.
For realizing above-mentioned technical purpose, the present invention seeks to be achieved through the following technical solutions: a kind of preparation technology who builds composite brick, comprise pug processing, moulding, dry and roasting, it is characterized in that: 1, first get lime, quartz sand, sand or packsand, construction waste building stones, by above-mentioned material respectively order number be according to the rules milled to into fine powder, stand-by; 2, the fine powder of above-mentioned milled is added in reactor in the ratio of 1:1.5:3, then add 425 type cement and the appropriate water of 2:1, form slurry stirs; 3, by the above-mentioned slurry being stirred, add 7% mortar adhesive, continue to stir 20 minutes, pour in clay brick mould, compressing by semidry method, be placed on steam pressure under autoclave at high temperature condition, demoulding wet curing is to finished product.
Owing to taking above technical scheme, the present invention can utilize obsolete material preparation to the building clay brick of existing use, has saved tilling the land of peasant, has protected environment, has avoided rubbish to huddle and has left about. Its method is simple, saves soil, twice laid, environmental protection and energy saving.
Detailed description of the invention:
Further set forth the present invention below in conjunction with embodiment:
A kind of preparation technology who builds composite brick, comprise pug processing, moulding, dry and roasting, it is characterized in that first getting lime, quartz sand, sand or packsand, construction waste building stones, by above-mentioned material respectively order number be according to the rules milled to into fine powder, the fine powder of above-mentioned milled is added in reactor in the ratio of 1:1.5:3, the 425 type cement and the appropriate water that add again 2:1, form slurry stirs; By the above-mentioned slurry being stirred, add 7% mortar adhesive, continue to stir 20 minutes, pour in clay brick mould, compressing by semidry method, be placed on steam pressure under autoclave at high temperature condition, demoulding wet curing is to finished product.
Claims (1)
1. the invention discloses a kind of preparation technology who builds composite brick, to get lime, quartz sand, sand or packsand, construction waste building stones, be milled to into respectively fine powder, the fine powder of above-mentioned milled is added in reactor in proportion, then add cement and appropriate water, form slurry stirs, add again mortar adhesive, after stirring, pour in clay brick mould, compressing by semidry method, be placed on steam pressure under autoclave at high temperature condition, demoulding wet curing is to finished product.