CN105562012A - 一种Ni-La(OH)3催化剂的制备方法 - Google Patents

一种Ni-La(OH)3催化剂的制备方法 Download PDF

Info

Publication number
CN105562012A
CN105562012A CN201510804559.4A CN201510804559A CN105562012A CN 105562012 A CN105562012 A CN 105562012A CN 201510804559 A CN201510804559 A CN 201510804559A CN 105562012 A CN105562012 A CN 105562012A
Authority
CN
China
Prior art keywords
catalyst
preparation
stirring
obtains
treatment consists
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510804559.4A
Other languages
English (en)
Inventor
李长英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi Jujiehan Chemical Co Ltd
Original Assignee
Shaanxi Jujiehan Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaanxi Jujiehan Chemical Co Ltd filed Critical Shaanxi Jujiehan Chemical Co Ltd
Priority to CN201510804559.4A priority Critical patent/CN105562012A/zh
Publication of CN105562012A publication Critical patent/CN105562012A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种催化剂的制备方法，特别涉及一种负载了Ni离子的La(OH)3催化剂的制备方法。一种Ni-La(OH)3催化剂的制备方法，其特征在于包括以下步骤：（1）0.2mol和1gCTAB溶于240mL去离子水中；（2）充分搅拌条件下,通过恒流泵滴加氨水溶液至pH=10；（3）搅拌1h后,将乳白色悬浊液移入100？mL水热反应釜,于180℃下水热处理12h；本发明所述一种Ni-La(OH)3催化剂的制备方法，制备方法简单，获得的产物活性强，可工业化生产。

Description

一种Ni-La(OH)3催化剂的制备方法
技术领域
本发明涉及一种催化剂的制备方法，特别涉及一种负载了Ni离子的La(OH)3催化剂的制备方法。
背景技术
随着化石资源的日益枯竭和环境问题日益严重,可再生资源如生物质能、风能、潮汐能等高效利用转化越来越引起人们的重视。生物质因其储量大、分布广、可再生且无温室气体排放等优点而成为当今研究的热点。木质纤维素是储量最为丰富的生物质资源,通过水解加氢过程可得糖醇化物。糖醇是重要的生物质衍生平台化合物,可通过氢解、氧化、选择性还原等反应转化为高附加值的化学品和燃料,其中,山梨醇、木糖醇等已被列为未来生物质开发过程中重要的基础化学原料,这一路线的研发为生物质基原料生产大宗化学品提供了可能。近年来,随着乙二醇(EG)、丙二醇(PG)等低碳二元醇的市场需求量不断增加,通过糖醇催化氢解制备低碳二元醇已成为研究热点。糖醇催化氢解制备低碳二元醇需要金属与碱中心的协同催化作用。根据Keyi等对糖醇氢解机理的研究,糖醇分子上的羟基首先在金属活性位上发生脱氢反应,进而在碱性催化剂的作用下发生逆羟醛缩合反应(retro-aldol)促使C-C键的断裂,随后在金属活性位加氢生成小分子的多元醇；同时也可以发生脱水加氢反应,促使C-O键断裂,生成脱羟基产物。目前,对糖醇催化氢解反应的研究主要集中在催化剂的筛选与调控上。研究较多的催化剂体系主要包括Ni、Pt、Ru和Cu基催化剂,而碱性助剂主要是Ca(OH)2。Banu等将金属Ni和Pt负载在碱性NaY分子筛上氢解山梨醇,Ni/NaY催化氢解主要产物是1,2-PG,而Pt/NaY催化氢解主要产物是甘油。Zhao等以化学气相沉积制备碳纳米纤维(CNFs)作为载体负载金属Ru,结果表明,CNFs比活性炭(AC)作为载体具有更高的活性和产物的选择性。Chen等采用共沉淀方法制备了一系列的Ni/MgO催化剂用于山梨醇氢解,得出Ni/Mg物质的量比为3：7时催化剂氢解活性最高,在优化条件下达到了67%的转化率和超过80%的目标产物(EG,1,2-PG和甘油)的总选择性。另外五元糖醇氢解也是多元醇氢解研究的一个热点,Huang等就通过不同的金属(Ni、Cu)催化剂体系,在碱性促进剂CaO的作用下氢解木糖醇得到达70%多元醇收率。
发明内容
本发明旨在提出一种Ni-La(OH)3催化剂的制备方法。
本发明所述一种Ni-La(OH)3催化剂的制备方法，其包括以下步骤：（1）0.2mol和1gCTAB溶于240mL去离子水中；（2）充分搅拌条件下,通过恒流泵滴加氨水溶液至pH=10；（3）搅拌1h后,将乳白色悬浊液移入100mL水热反应釜,于180℃下水热处理12h；（4）水热处理结束后,所得白色固体粉末经洗涤过滤后,于100℃干燥10h得La(OH)3样品；（5）配制一定浓度的Ni(CH3COO)2·4H2O水溶液,加入La(OH)3,充分搅拌3h后将所得混合物于85℃下蒸干多余水分；（6）将步骤（5）获得的产物经100℃干燥后,于不同的温度(500～800℃)下分别焙烧4h得Ni/La(OH)3催化剂。
本发明所述一种Ni-La(OH)3催化剂的制备方法，制备方法简单，获得的产物活性强，可工业化生产。
具体实施方式
一种Ni-La(OH)3催化剂的制备方法，其包括以下步骤：（1）0.2mol和1gCTAB溶于240mL去离子水中；（2）充分搅拌条件下,通过恒流泵滴加氨水溶液至pH=10；（3）搅拌1h后,将乳白色悬浊液移入100mL水热反应釜,于180℃下水热处理12h；（4）水热处理结束后,所得白色固体粉末经洗涤过滤后,于100℃干燥10h得La(OH)3样品；（5）配制一定浓度的Ni(CH3COO)2·4H2O水溶液,加入La(OH)3,充分搅拌3h后将所得混合物于85℃下蒸干多余水分；（6）将步骤（5）获得的产物经100℃干燥后,于不同的温度(500～800℃)下分别焙烧4h得Ni/La(OH)3催化剂。

Claims (1)

1.一种Ni-La(OH)3催化剂的制备方法，其特征在于包括以下步骤：（1）0.2mol和1gCTAB溶于240mL去离子水中；（2）充分搅拌条件下,通过恒流泵滴加氨水溶液至pH=10；（3）搅拌1h后,将乳白色悬浊液移入100mL水热反应釜,于180℃下水热处理12h；（4）水热处理结束后,所得白色固体粉末经洗涤过滤后,于100℃干燥10h得La(OH)3样品；（5）配制一定浓度的Ni(CH3COO)2·4H2O水溶液,加入La(OH)3,充分搅拌3h后将所得混合物于85℃下蒸干多余水分；（6）将步骤（5）获得的产物经100℃干燥后,于不同的温度(500～800℃)下分别焙烧4h得Ni/La(OH)3催化剂。
CN201510804559.4A 2015-11-20 2015-11-20 一种Ni-La(OH)3催化剂的制备方法 Pending CN105562012A (zh)