CN105524400B - A kind of preparation method of high anti-folding SBS composite sole materials - Google Patents
A kind of preparation method of high anti-folding SBS composite sole materials Download PDFInfo
- Publication number
- CN105524400B CN105524400B CN201610037540.6A CN201610037540A CN105524400B CN 105524400 B CN105524400 B CN 105524400B CN 201610037540 A CN201610037540 A CN 201610037540A CN 105524400 B CN105524400 B CN 105524400B
- Authority
- CN
- China
- Prior art keywords
- sbs
- mah
- folding
- high anti
- composite sole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of preparation method of high anti-folding SBS composite sole materials, its step are as follows:(1) mesh polypropylene-fibre is dissolved in toluene, oil stain and impurity are removed in vibration, and taking-up is washed with deionized water only, drying, moved in plasma processing chamber, carries out plasma treatment, takes out, obtain modified polypropene reticular fibre;(2) SBS, MAH are dissolved in MEK, moved to after being completely dissolved in constant temperature water bath, led to nitrogen protection and BPO is added dropwise, be evaporated under reduced pressure after reaction, extracting removes SBS, the MAH for not participating in reaction, dries to constant weight, obtains SBS g MAH;(3) SBS, PTFE, SBS g MAH are added into high-speed mixer and mixing, obtain blend composition, it is uniformly dispersed after blend composition is mixed with acetone, obtain prepreg, modified polypropene reticular fibre is soaked in prepreg, taking-up is dried, and is laid in after cutting in mould, it is molded with platen-press, high anti-folding SBS composite sole materials is obtained after cooling and demolding.The material for sole of shoe of the present invention has good fracture resistance and heat resistance.
Description
Technical field:
The present invention relates to a kind of material for sole of shoe, more particularly to a kind of preparation method of high anti-folding SBS composite sole materials.
Background technology:
Styrene series thermoplastic elastomer (also known as styrene block copolymer Styreneic Block
Copolymers, abbreviation SBCs), it is currently that yield is maximum in the world, a kind of thermoplastic elastic the most similar to rubber performance
Body.At present, mainly there are 4 types in SBCs series of products, i.e.,:SBS (SBS);Benzene
Ethene-isoprene-styrene block copolymer (SIS);Styrene-ethylene-butylene-styrene block copolymer (SEBS);
Styrene ethylene-propylene-styrene type block copolymer (SEPS), wherein, SEBS and SEPS are SBS and SIS hydrogenation respectively
Copolymer.
SBS styrene analog thermoplastic elastomers be in SBCs yield maximum (accounting for more than 70%), cost it is minimum, using wider
A kind, be using styrene, butadiene as the triblock copolymer of monomer, have the characteristic of plastics and rubber concurrently, be referred to as
" third generation synthetic rubber ".Similar to butadiene-styrene rubber, SBS can contact with water, weak acid, alkali etc., have excellent tensile strength,
Big surface friction coefficient, low temperature performance well, excellent electrical properties, the characteristics such as processing characteristics is good, turn into the maximum heat of current consumption figure
Thermoplastic elastic.SBS is mainly used in rubber, four big field of modifier, adhesive and asphalt modifier at present, in rubber
In terms of glue product, SBS pressings are mainly used in shoemaking (sole) industry, i.e. SBS material for sole of shoe.
Publication No. CN103483759A, publication date 2014.01.01, the artificial Wujiang Dongxin Plastic Package Factory of application
Chinese patent disclose " a kind of SBS shoe plastic ", its composition and mass fraction are:SBS100 parts;AMS10-25
Part;PS50-60 parts;HIPS10-20 parts;Dibutyl tin laurate 0.5-1 parts;Calcium carbonate 20-40 parts;Anti-oxidant DLTP 0.1-
1 part;UV-1020.5-1 parts;Antioxidant 1010 0.2-0.5 parts;Paraffin 10-20 parts;Toluene di-isocyanate(TDI) 30-40 parts;It is stearic
Sour zinc 0.2-0.5 parts;Triethylene diamine 0.2-0.5 parts.The footwear material plastics add antioxidant, improve the ageing resistance of product
Can, and antioxidant 1010 has cooperative effect with anti-oxidant DLTP, substantially increases performance;Relative density is 0.3-0.5, stretching
Intensity is 3-4MPa;Tearing strength 25-30N/mm, elongation at break 200-250%;It is product acid and alkali-resistance, wear-resisting, it can give birth to extensively
Produce and constantly replace current material.However, the footwear material plastics that the patent provides still have the defects of certain:Heat resistance is not
It is good, and fracture resistance is poor, is easily broken off when by bending external force effect.
The content of the invention:
The technical problem to be solved in the present invention is to provide a kind of preparation method of high anti-folding SBS composite sole materials, prepares
The material for sole of shoe gone out has good fracture resistance and heat resistance.
In order to solve the above technical problems, the technical scheme is that:
A kind of preparation method of high anti-folding SBS composite sole materials, its step are as follows:
(1) mesh polypropylene-fibre is dissolved in toluene, is placed in vibration in ultrasonator and removes mesh polypropylene-fibre table
The oil stain and impurity in face, take out and be washed with deionized water only after 2 hours, be placed in baking oven and dry 2 hours, move to plasma processing chamber
In, argon gas is passed through after vacuumizing and opens radio-frequency power supply progress plasma treatment, is taken out after 3 minutes, obtains modified polypropene net
Shape fiber is standby;
(2) SBS, MAH are dissolved in MEK, stirring is moved in constant temperature water bath to after being completely dissolved, and is led under nitrogen protection
BPO is added dropwise, reaction is evaporated under reduced pressure after 1 hour and removes MEK, and SBS, the MAH for not participating in reaction are removed with ketone extracting, is put
In vacuum drying chamber drying to constant weight, it is standby to obtain SBS-g-MAH;
(3) SBS-g-MAH for obtaining SBS, PTFE, step (2) adds high-speed mixer and mixing 10 minutes, is blended
Material, is stirred by ultrasonic to being uniformly dispersed after blend composition is mixed with acetone, obtains prepreg, the modification poly- third that step (1) is obtained
Alkene reticular fibre is soaked in prepreg, is taken out and is dried after 20 hours, is laid in mould after cutting, is molded with platen-press,
High anti-folding SBS composite sole materials are obtained after cooling and demolding.
Preferably, in step (1) of the present invention, the temperature of drying is 70 DEG C.
Preferably, in step (1) of the present invention, the discharge power of radio-frequency power supply is 80W.
Preferably, in step (2) of the present invention, SBS, MAH, BPO weight ratio are 100:40:3.
Preferably, in step (2) of the present invention, the temperature of constant temperature water bath is 82 DEG C.
Preferably, in step (2) of the present invention, dry temperature is 90 DEG C.
Preferably, in the step (3), by weight, SBS 52-63 parts, PTFE 10-14 parts, SBS-g-MAH 5-
6 parts, modified polypropene reticular fibre 25-30 parts.
Preferably, in step (3) of the present invention, the temperature of high mixer mixing is 120 DEG C.
Preferably, in step (3) of the present invention, the temperature of molding is 140 DEG C, and the pressure of molding is 1.2MPa.
Compared with prior art, the invention has the advantages that:
(1) mesh polypropylene-fibre be using modified polypropene as raw material, extruded, stretching, networking, surface treatment, be chopped
The netted organic fiber being process etc. process, it has very high tensile strength, by plasma treatment post plasma at it
Surface generates etching action, greatly increases the roughness on its surface, and generates many grooves and crackle, can significantly increase
Mechanical riveted effect between mesh polypropylene-fibre and SBS matrixes, improves adhesion strength therebetween, formed consistency compared with
High network structure, when composite sole material is by bending external force, mesh polypropylene-fibre can produce larger drawing-resistant function
Power, bending external force can consume substantial amounts of energy when fractureing or extracting mesh polypropylene-fibre so that SBS matrixes are subject to broken
It is bad to be reduced to minimum level, so as to substantially increase the fracture resistance of composite sole material.
(2) PTFE is that the English of polytetrafluoroethylene (PTFE) is write a Chinese character in simplified form, and the bond energy of its intramolecule C-F keys is very high, therefore with fine
Resistance to elevated temperatures, but its compatibility between SBS matrixes is bad, therefore the present invention has been made compatible by graft reaction
Compatibility between agent SBS-g-MAH, MAH maleic anhydride and PTFE is preferable, thus SBS-g-MAH can be effectively improved PTFE with
Compatibility between SBS matrixes simultaneously forms good interface cohesion, and then greatly improves the heat resistance of composite sole material;This
Outside, PTFE also has good corrosion resistance, weatherability and very low wearing coefficient, therefore can also effectively improve composite sole
Corrosion resistance, weatherability and the wearability of material.
Embodiment:
The present invention is described in detail below in conjunction with specific embodiment, herein illustrative examples and explanation of the invention
For explaining the present invention, but it is not as a limitation of the invention.
Embodiment 1
A kind of preparation method of high anti-folding SBS composite sole materials, its step are as follows:
(1) mesh polypropylene-fibre is dissolved in toluene, is placed in vibration in ultrasonator and removes mesh polypropylene-fibre table
The oil stain and impurity in face, take out and be washed with deionized water only after 2 hours, be placed in baking oven at 70 DEG C and dry 2 hours, move to plasma
In process chamber, argon gas is passed through after vacuumizing and opens radio-frequency power supply progress plasma treatment, is taken out after 3 minutes, radio-frequency power supply
Discharge power is 80W, and it is standby to obtain modified polypropene reticular fibre;
(2) SBS, MAH being dissolved in MEK, stirring is moved to after being completely dissolved in the constant temperature water bath that temperature is 82 DEG C,
Logical nitrogen protection is lower to be added dropwise BPO, and SBS, MAH, BPO weight ratio are 100:40:3, reaction is evaporated under reduced pressure after 1 hour and removes first and second
Ketone, SBS, the MAH for not participating in reaction are removed with ketone extracting, be placed at 90 DEG C of vacuum drying chamber and dry to constant weight, obtain
SBS-g-MAH is standby;
(3) SBS-g-MAH for obtaining 55 parts by weight SBS, 10.5 parts by weight PTFE, 6 parts by weight steps (2) adds high mixed
Mixed 10 minutes at 120 DEG C in machine, obtain blend composition, be stirred by ultrasonic to being uniformly dispersed, obtain after blend composition is mixed with acetone
Prepreg, the modified polypropene reticular fibre that 27 parts by weight steps (1) obtain is soaked in prepreg, takes out and dry in the air after 20 hours
It is dry, it is laid in mould after cutting, is molded with platen-press, the temperature of molding is 140 DEG C, and the pressure of molding is 1.2MPa, cold
But high anti-folding SBS composite sole materials are obtained after being stripped.
Embodiment 2
A kind of preparation method of high anti-folding SBS composite sole materials, its step are as follows:
(1) mesh polypropylene-fibre is dissolved in toluene, is placed in vibration in ultrasonator and removes mesh polypropylene-fibre table
The oil stain and impurity in face, take out and be washed with deionized water only after 2 hours, be placed in baking oven at 70 DEG C and dry 2 hours, move to plasma
In process chamber, argon gas is passed through after vacuumizing and opens radio-frequency power supply progress plasma treatment, is taken out after 3 minutes, radio-frequency power supply
Discharge power is 80W, and it is standby to obtain modified polypropene reticular fibre;
(2) SBS, MAH being dissolved in MEK, stirring is moved to after being completely dissolved in the constant temperature water bath that temperature is 82 DEG C,
Logical nitrogen protection is lower to be added dropwise BPO, and SBS, MAH, BPO weight ratio are 100:40:3, reaction is evaporated under reduced pressure after 1 hour and removes first and second
Ketone, SBS, the MAH for not participating in reaction are removed with ketone extracting, be placed at 90 DEG C of vacuum drying chamber and dry to constant weight, obtain
SBS-g-MAH is standby;
(3) SBS-g-MAH for obtaining 52 parts by weight SBS, 14 parts by weight PTFE, 5.5 parts by weight steps (2) adds high mixed
Mixed 10 minutes at 120 DEG C in machine, obtain blend composition, be stirred by ultrasonic to being uniformly dispersed, obtain after blend composition is mixed with acetone
Prepreg, the modified polypropene reticular fibre that 26 parts by weight steps (1) obtain is soaked in prepreg, takes out and dry in the air after 20 hours
It is dry, it is laid in mould after cutting, is molded with platen-press, the temperature of molding is 140 DEG C, and the pressure of molding is 1.2MPa, cold
But high anti-folding SBS composite sole materials are obtained after being stripped.
Embodiment 3
A kind of preparation method of high anti-folding SBS composite sole materials, its step are as follows:
(1) mesh polypropylene-fibre is dissolved in toluene, is placed in vibration in ultrasonator and removes mesh polypropylene-fibre table
The oil stain and impurity in face, take out and be washed with deionized water only after 2 hours, be placed in baking oven at 70 DEG C and dry 2 hours, move to plasma
In process chamber, argon gas is passed through after vacuumizing and opens radio-frequency power supply progress plasma treatment, is taken out after 3 minutes, radio-frequency power supply
Discharge power is 80W, and it is standby to obtain modified polypropene reticular fibre;
(2) SBS, MAH being dissolved in MEK, stirring is moved to after being completely dissolved in the constant temperature water bath that temperature is 82 DEG C,
Logical nitrogen protection is lower to be added dropwise BPO, and SBS, MAH, BPO weight ratio are 100:40:3, reaction is evaporated under reduced pressure after 1 hour and removes first and second
Ketone, SBS, the MAH for not participating in reaction are removed with ketone extracting, be placed at 90 DEG C of vacuum drying chamber and dry to constant weight, obtain
SBS-g-MAH is standby;
(3) SBS-g-MAH for obtaining 60 parts by weight SBS, 12 parts by weight PTFE, 5.4 parts by weight steps (2) adds high mixed
Mixed 10 minutes at 120 DEG C in machine, obtain blend composition, be stirred by ultrasonic to being uniformly dispersed, obtain after blend composition is mixed with acetone
Prepreg, the modified polypropene reticular fibre that 25 parts by weight steps (1) obtain is soaked in prepreg, takes out and dry in the air after 20 hours
It is dry, it is laid in mould after cutting, is molded with platen-press, the temperature of molding is 140 DEG C, and the pressure of molding is 1.2MPa, cold
But high anti-folding SBS composite sole materials are obtained after being stripped.
Embodiment 4
A kind of preparation method of high anti-folding SBS composite sole materials, its step are as follows:
(1) mesh polypropylene-fibre is dissolved in toluene, is placed in vibration in ultrasonator and removes mesh polypropylene-fibre table
The oil stain and impurity in face, take out and be washed with deionized water only after 2 hours, be placed in baking oven at 70 DEG C and dry 2 hours, move to plasma
In process chamber, argon gas is passed through after vacuumizing and opens radio-frequency power supply progress plasma treatment, is taken out after 3 minutes, radio-frequency power supply
Discharge power is 80W, and it is standby to obtain modified polypropene reticular fibre;
(2) SBS, MAH being dissolved in MEK, stirring is moved to after being completely dissolved in the constant temperature water bath that temperature is 82 DEG C,
Logical nitrogen protection is lower to be added dropwise BPO, and SBS, MAH, BPO weight ratio are 100:40:3, reaction is evaporated under reduced pressure after 1 hour and removes first and second
Ketone, SBS, the MAH for not participating in reaction are removed with ketone extracting, be placed at 90 DEG C of vacuum drying chamber and dry to constant weight, obtain
SBS-g-MAH is standby;
(3) SBS-g-MAH for obtaining 63 parts by weight SBS, 11 parts by weight PTFE, 5 parts by weight steps (2) adds high mixer
In mix 10 minutes at 120 DEG C, obtain blend composition, be stirred by ultrasonic after blend composition is mixed with acetone to being uniformly dispersed, obtained pre-
Leaching material, the modified polypropene reticular fibre that 30 parts by weight steps (1) obtain is soaked in prepreg, is taken out and is dried in the air after 20 hours
It is dry, it is laid in mould after cutting, is molded with platen-press, the temperature of molding is 140 DEG C, and the pressure of molding is 1.2MPa, cold
But high anti-folding SBS composite sole materials are obtained after being stripped.
Embodiment 5
A kind of preparation method of high anti-folding SBS composite sole materials, its step are as follows:
(1) mesh polypropylene-fibre is dissolved in toluene, is placed in vibration in ultrasonator and removes mesh polypropylene-fibre table
The oil stain and impurity in face, take out and be washed with deionized water only after 2 hours, be placed in baking oven at 70 DEG C and dry 2 hours, move to plasma
In process chamber, argon gas is passed through after vacuumizing and opens radio-frequency power supply progress plasma treatment, is taken out after 3 minutes, radio-frequency power supply
Discharge power is 80W, and it is standby to obtain modified polypropene reticular fibre;
(2) SBS, MAH being dissolved in MEK, stirring is moved to after being completely dissolved in the constant temperature water bath that temperature is 82 DEG C,
Logical nitrogen protection is lower to be added dropwise BPO, and SBS, MAH, BPO weight ratio are 100:40:3, reaction is evaporated under reduced pressure after 1 hour and removes first and second
Ketone, SBS, the MAH for not participating in reaction are removed with ketone extracting, be placed at 90 DEG C of vacuum drying chamber and dry to constant weight, obtain
SBS-g-MAH is standby;
(3) SBS-g-MAH for obtaining 62 parts by weight SBS, 10 parts by weight PTFE, 5.6 parts by weight steps (2) adds high mixed
Mixed 10 minutes at 120 DEG C in machine, obtain blend composition, be stirred by ultrasonic to being uniformly dispersed, obtain after blend composition is mixed with acetone
Prepreg, the modified polypropene reticular fibre that 29 parts by weight steps (1) obtain is soaked in prepreg, takes out and dry in the air after 20 hours
It is dry, it is laid in mould after cutting, is molded with platen-press, the temperature of molding is 140 DEG C, and the pressure of molding is 1.2MPa, cold
But high anti-folding SBS composite sole materials are obtained after being stripped.
Embodiment 6
A kind of preparation method of high anti-folding SBS composite sole materials, its step are as follows:
(1) mesh polypropylene-fibre is dissolved in toluene, is placed in vibration in ultrasonator and removes mesh polypropylene-fibre table
The oil stain and impurity in face, take out and be washed with deionized water only after 2 hours, be placed in baking oven at 70 DEG C and dry 2 hours, move to plasma
In process chamber, argon gas is passed through after vacuumizing and opens radio-frequency power supply progress plasma treatment, is taken out after 3 minutes, radio-frequency power supply
Discharge power is 80W, and it is standby to obtain modified polypropene reticular fibre;
(2) SBS, MAH being dissolved in MEK, stirring is moved to after being completely dissolved in the constant temperature water bath that temperature is 82 DEG C,
Logical nitrogen protection is lower to be added dropwise BPO, and SBS, MAH, BPO weight ratio are 100:40:3, reaction is evaporated under reduced pressure after 1 hour and removes first and second
Ketone, SBS, the MAH for not participating in reaction are removed with ketone extracting, be placed at 90 DEG C of vacuum drying chamber and dry to constant weight, obtain
SBS-g-MAH is standby;
(3) SBS-g-MAH for obtaining 54 parts by weight SBS, 13 parts by weight PTFE, 5.2 parts by weight steps (2) adds high mixed
Mixed 10 minutes at 120 DEG C in machine, obtain blend composition, be stirred by ultrasonic to being uniformly dispersed, obtain after blend composition is mixed with acetone
Prepreg, the modified polypropene reticular fibre that 28 parts by weight steps (1) obtain is soaked in prepreg, takes out and dry in the air after 20 hours
It is dry, it is laid in mould after cutting, is molded with platen-press, the temperature of molding is 140 DEG C, and the pressure of molding is 1.2MPa, cold
But high anti-folding SBS composite sole materials are obtained after being stripped.
The fracture resistance and heat resistance of embodiment 1-6 material for sole of shoe and comparative example are tested, wherein,
Comparative example is Publication No. CN103483759A Chinese patent;
Fracture resistance tests the bending strength of detected materials according to GB/T 6569-86 on universal testing machine, to be measured
The specification of material is 3mm × 4mm × 35mm, is measured using three-point bending method, span 30mm, loading speed 0.5mm/min,
5 detected materials of each data test, then average, bending strength shows that more greatly fracture resistance is better;
Heat resistance tests the heat decomposition temperature of detected materials, condition N according to thermogravimetric analysis (TG)2Atmosphere, heating speed
Spend for 10 DEG C/min, room temperature~800 DEG C.
Test result is as follows:
As seen from the above table, the bending strength of material for sole of shoe produced by the present invention, heat decomposition temperature be obviously higher than comparative example,
With good fracture resistance and heat resistance.
The above-described embodiments merely illustrate the principles and effects of the present invention, not for the limitation present invention.It is any ripe
Know the personage of this technology all can carry out modifications and changes under the spirit and scope without prejudice to the present invention to above-described embodiment.Cause
This, those of ordinary skill in the art is complete without departing from disclosed spirit and institute under technological thought such as
Into all equivalent modifications or change, should by the present invention claim be covered.
Claims (7)
- A kind of 1. preparation method of high anti-folding SBS composite sole materials, it is characterised in that:Its step is as follows:(1) mesh polypropylene-fibre is dissolved in toluene, is placed in vibration in ultrasonator and removes mesh polypropylene-fibre surface Oil stain and impurity, take out and be washed with deionized water only after 2 hours, be placed in baking oven and dry 2 hours, move in plasma processing chamber, Argon gas is passed through after vacuumizing and opens radio-frequency power supply and carries out plasma treatment, is taken out after 3 minutes, obtains the netted fibre of modified polypropene Tie up standby;(2) SBS, MAH are dissolved in MEK, stirring is moved in constant temperature water bath to after being completely dissolved, and leads to the lower dropwise addition of nitrogen protection BPO, SBS, MAH, BPO weight ratio are 100:40:3, reaction is evaporated under reduced pressure after 1 hour and removes MEK, is gone with ketone extracting Except SBS, MAH for not participating in reaction, vacuum drying chamber drying is placed in constant weight, it is standby to obtain SBS-g-MAH;(3) SBS-g-MAH for obtaining SBS, PTFE, step (2) adds high-speed mixer and mixing 10 minutes, obtains blend composition, will Blend composition is stirred by ultrasonic after being mixed with acetone to being uniformly dispersed, and obtains prepreg, and the modified polypropene that step (1) is obtained is netted Fiber is soaked in prepreg, is taken out and is dried after 20 hours, be laid in mould after cutting, be molded with platen-press, cooling is de- High anti-folding SBS composite sole materials are obtained after mould;In the step (3), by weight, SBS 52-63 parts, PTFE 10-14 parts, SBS-g-MAH 5-6 parts, it is modified poly- Propylene reticular fibre 25-30 parts.
- A kind of 2. preparation method of high anti-folding SBS composite sole materials according to claim 1, it is characterised in that:It is described In step (1), the temperature of drying is 70 DEG C.
- A kind of 3. preparation method of high anti-folding SBS composite sole materials according to claim 1, it is characterised in that:It is described In step (1), the discharge power of radio-frequency power supply is 80W.
- A kind of 4. preparation method of high anti-folding SBS composite sole materials according to claim 1, it is characterised in that:It is described In step (2), the temperature of constant temperature water bath is 82 DEG C.
- A kind of 5. preparation method of high anti-folding SBS composite sole materials according to claim 1, it is characterised in that:It is described In step (2), dry temperature is 90 DEG C.
- A kind of 6. preparation method of high anti-folding SBS composite sole materials according to claim 1, it is characterised in that:It is described In step (3), the temperature of high mixer mixing is 120 DEG C.
- A kind of 7. preparation method of high anti-folding SBS composite sole materials according to claim 1, it is characterised in that:It is described In step (3), the temperature of molding is 140 DEG C, and the pressure of molding is 1.2MPa.