CN105506600A - 一种硅酸盐清洁钝化液及其制备方法 - Google Patents

一种硅酸盐清洁钝化液及其制备方法 Download PDF

Info

Publication number
CN105506600A
CN105506600A CN201410496642.5A CN201410496642A CN105506600A CN 105506600 A CN105506600 A CN 105506600A CN 201410496642 A CN201410496642 A CN 201410496642A CN 105506600 A CN105506600 A CN 105506600A
Authority
CN
China
Prior art keywords
parts
silicate
water
hydrogen peroxide
ethanol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410496642.5A
Other languages
English (en)
Inventor
蒋勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410496642.5A priority Critical patent/CN105506600A/zh
Publication of CN105506600A publication Critical patent/CN105506600A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种硅酸盐清洁钝化液及其制备方法，硅酸盐清洁钝化液包括如下重量份的组份：硅酸钠5-10份、硼酸2-4份、过氧化氢5-10份、浓硫酸3-10份、柠檬酸盐5-15份、氟化钠1-2份、氨水1-2份、乙醇50-60份、香料1-2份和水1-2份。本发明的优点为该硅酸盐清洁钝化液能够显著提高电镀锌及锌铁合金的耐蚀性，克服了铬酸盐钝化技术毒性大、不环保等的缺点。同时，该硅酸盐清洁钝化液生产成本低，制备工艺简单，适合工业化生产。

Description

一种硅酸盐清洁钝化液及其制备方法
技术领域
本发明涉及一种化工用品，尤其涉及一种硅酸盐清洁钝化液及其制备方法。
背景技术
现有的钝化液对电镀锌及锌铁合金具有耐蚀性，且铬酸盐钝化技术毒性大、不环保。同时，现有的钝化液生产成本高，制备工艺复杂，不适合工业化生产。
发明内容
发明目的：本发明的第一目的是提供一种硅酸盐清洁钝化液，本发明的第二目的是提供该硅酸盐清洁钝化液的制备方法。
技术方案：本发明所述的硅酸盐清洁钝化液，包括如下重量份的组份：硅酸钠5-10份、硼酸2-4份、过氧化氢5-10份、浓硫酸3-10份、柠檬酸盐5-15份、氟化钠1-2份、氨水1-2份、乙醇50-60份、香料1-2份和水1-2份。
其中，所述硅酸钠5-8份、硼酸2-3份、过氧化氢5-8份、浓硫酸3-8份、柠檬酸盐5-10份、氟化钠1-2份、氨水1-2份、乙醇50-55份、香料1-2份和水1-2份。
其中，所述硅酸钠7份、硼酸3份、过氧化氢7份、浓硫酸7份、柠檬酸盐10份、氟化钠1份、氨水2份、乙醇55份、香料1份和水2份。
其中，所述硅酸钠9份、硼酸3份、过氧化氢6份、浓硫酸6份、柠檬酸盐6份、氟化钠1份、氨水2份、乙醇50份、香料1份和水1份。
本发明所述硅酸盐清洁钝化液的制备方法，包括如下步骤：首先，将硅酸钠、硼酸、过氧化氢、浓硫酸、柠檬酸盐、氟化钠和氨水搅拌均匀；其次加入乙醇，搅拌30分钟；最后，加入香料和水搅拌均匀，既得成品。
有益效果：本发明与现有技术相比，其显著优点为：该硅酸盐清洁钝化液能够显著提高电镀锌及锌铁合金的耐蚀性，克服了铬酸盐钝化技术毒性大、不环保等的缺点。同时，该硅酸盐清洁钝化液生产成本低，制备工艺简单，适合工业化生产。
具体实施方式：
实施例1：
配方：硅酸钠5份、硼酸2份、过氧化氢5份、浓硫酸3份、柠檬酸盐5份、氟化钠1份、氨水1份、乙醇50份、香料1份和水1份。
制备方法：首先，将硅酸钠、硼酸、过氧化氢、浓硫酸、柠檬酸盐、氟化钠和氨水搅拌均匀；其次加入乙醇，搅拌30分钟；最后，加入香料和水搅拌均匀，既得成品。
实施例2：
配方：硅酸钠10份、硼酸4份、过氧化氢10份、浓硫酸10份、柠檬酸盐15份、氟化钠2份、氨水2份、乙醇60份、香料2份和水2份。
制备方法同实施例1。
实施例3：
配方：硅酸钠7份、硼酸3份、过氧化氢7份、浓硫酸7份、柠檬酸盐10份、氟化钠1份、氨水2份、乙醇55份、香料1份和水2份。
制备方法同实施例1。
实施例4：
配方：硅酸钠9份、硼酸3份、过氧化氢6份、浓硫酸6份、柠檬酸盐6份、氟化钠1份、氨水2份、乙醇50份、香料1份和水1份。
制备方法同实施例1。
实施例5：
配方：硅酸钠6份、硼酸2份、过氧化氢5份、浓硫酸7份、柠檬酸盐15份、氟化钠2份、氨水1份、乙醇58份、香料2份和水1份。
制备方法同实施例1。

Claims (5)

1.一种硅酸盐清洁钝化液，其特征在于由以下重量配比的原料制成：硅酸钠5-10份、硼酸2-4份、过氧化氢5-10份、浓硫酸3-10份、柠檬酸盐5-15份、氟化钠1-2份、氨水1-2份、乙醇50-60份、香料1-2份和水1-2份。
2.根据权利要求1所述硅酸盐清洁钝化液，其特征在于：硅酸钠5-8份、硼酸2-3份、过氧化氢5-8份、浓硫酸3-8份、柠檬酸盐5-10份、氟化钠1-2份、氨水1-2份、乙醇50-55份、香料1-2份和水1-2份。
3.根据权利要求1所述硅酸盐清洁钝化液，其特征在于：硅酸钠7份、硼酸3份、过氧化氢7份、浓硫酸7份、柠檬酸盐10份、氟化钠1份、氨水2份、乙醇55份、香料1份和水2份。
4.根据权利要求1所述硅酸盐清洁钝化液，其特征在于：硅酸钠9份、硼酸3份、过氧化氢6份、浓硫酸6份、柠檬酸盐6份、氟化钠1份、氨水2份、乙醇50份、香料1份和水1份。
5.根据权利要求1所述硅酸盐清洁钝化液的制备方法，其特征在于包括如下步骤：首先，将硅酸钠、硼酸、过氧化氢、浓硫酸、柠檬酸盐、氟化钠和氨水搅拌均匀；其次加入乙醇，搅拌30分钟；最后，加入香料和水搅拌均匀，既得成品。
CN201410496642.5A 2014-09-25 2014-09-25 一种硅酸盐清洁钝化液及其制备方法 Pending CN105506600A (zh)